CN106430958A - Ceramic glaze for glass lining - Google Patents
Ceramic glaze for glass lining Download PDFInfo
- Publication number
- CN106430958A CN106430958A CN201610749055.1A CN201610749055A CN106430958A CN 106430958 A CN106430958 A CN 106430958A CN 201610749055 A CN201610749055 A CN 201610749055A CN 106430958 A CN106430958 A CN 106430958A
- Authority
- CN
- China
- Prior art keywords
- parts
- oxide
- enamel
- cordierite
- ceramic glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses ceramic glaze for glass lining. The ceramic glaze is prepared from, by weight, 80-100 parts of silicon oxide, 60-80 parts of potash feldspar, 40-80 parts of soda feldspar, 30-50 parts of calcium oxide, 30-50 parts of sodium borate, 30-40 parts of cordierite, 20-30 parts of magnesium oxide, 1-10 parts of manganese oxide, 1-10 parts of iron sesquioxide, 1-10 parts of copper oxide, 1-5 parts of lanthanum oxide, 1-5 parts of strontium oxide, 1-5 parts of rubidium oxide, 1-5 parts of lithium oxide and 1-5 parts of barium oxide. Compared with a traditional technology, the ceramic glaze is strong in abrasion resistance, high-temperature resistance and corrosion resistance, suitable for long-term use and long in repair period.
Description
Technical field
The invention belongs to chemical material field is and in particular to a kind of enamel enamel.
Background technology
Enamel is that enamel high for silicon content is applied to metal surface, by high temperature enamel firing, makes enamel adherence in metallic iron
Tire surface is made, and has the two-fold advantage of the glazed chemical stability of class and metal strength.Although traditional enamel is stable
Property good and metal strength excellent, but have " hollow " phenomenon through friction posterior surface, be unfavorable for using steadily in the long term.
Content of the invention
Goal of the invention:Present invention aims to the deficiencies in the prior art, provide a kind of enamel enamel.
Technical scheme:In order to reach foregoing invention purpose, the present invention is specifically achieved like this:A kind of enamel porcelain
Glaze, including the component of following parts by weight:80 ~ 100 parts of silica, 60 ~ 80 parts of potassium feldspar, 40 ~ 80 parts of albite, 30
~ 50 parts of calcium oxide, 30 ~ 50 parts of borax, 30 ~ 40 parts of cordierite, 20 ~ 30 parts of magnesia, 1 ~ 10 part of manganese oxide, 1 ~
10 parts of di-iron trioxide, 1 ~ 10 part of cupric oxide, 1 ~ 5 part of lanthana, 1 ~ 5 part of strontium oxide strontia, 1 ~ 5 part of rubidium oxide, 1 ~ 5
Part lithia and 1 ~ 5 part of barium monoxide.
A kind of preferred version, the present invention is grouped into by the group of following parts by weight:90 parts of silica, 70 parts of potassium is long
Stone, 60 parts of albite, 40 parts of calcium oxide, 40 parts of borax, 35 parts of cordierite, 25 parts of magnesia, 5 parts of oxidation
Manganese, 5 parts of di-iron trioxide, 5 parts of cupric oxide, 3 parts of lanthana, 2 parts of strontium oxide strontia, 2 parts of rubidium oxide, 3 parts of oxidation
The barium monoxide of lithium and 3 parts.
Wherein, described potassium feldspar albite, the fineness of cordierite is less than 50 mesh.
Wherein, described barium monoxide is replaced by silicon nitride.
Beneficial effect:, compared with conventional art, Wear-resistant, high-temperature resistant resistance to corrosion is strong for the present invention, and suitable Long-Time Service is repaiied
The benefit cycle is long.
Specific embodiment
Embodiment 1:
A kind of enamel enamel, including the component of following parts by weight:80 ~ 100 parts of silica, 70 parts of potassium feldspar, 60
The albite of part, 40 parts of calcium oxide, 40 parts of borax, 35 parts of cordierite, 25 parts of magnesia, 8 parts of manganese oxide, 7 parts
Di-iron trioxide, 6 parts of cupric oxide, 5 parts of lanthana, 3 parts of strontium oxide strontia, 4 parts of rubidium oxide, 4 parts of lithia and 3 parts
Barium monoxide.
Embodiment 2:
A kind of enamel enamel, including the component of following parts by weight:87 parts of silica, 73 parts of potassium feldspar, 62 parts
Albite, 47 parts of calcium oxide, 36 parts of borax, 33 parts of cordierite, 21 parts of magnesia, 9 parts of manganese oxide, the three of 4 parts
Aoxidize two iron, 5 parts of cupric oxide, 3 parts of lanthana, 2 parts of strontium oxide strontia, 4 parts of rubidium oxide, the oxygen of 3 parts of lithia and 2 parts
Change barium.
Embodiment 3:
A kind of enamel enamel, including the component of following parts by weight:93 parts of silica, 76 parts of potassium feldspar, 77 parts
Albite, 43 parts of calcium oxide, 36 parts of borax, 32 parts of cordierite, 24 parts of magnesia, 7 parts of manganese oxide, the three of 9 parts
Aoxidize two iron, 3 parts of cupric oxide, 2 parts of lanthana, 3 parts of strontium oxide strontia, 3 parts of rubidium oxide, the oxygen of 4 parts of lithia and 2 parts
Change barium.
Embodiment 4:
A kind of enamel enamel, including the component of following parts by weight:82 parts of silica, 74 parts of potassium feldspar, 56 parts
Albite, 42 parts of calcium oxide, 32 parts of borax, 38 parts of cordierite, 24 parts of magnesia, 5 parts of manganese oxide, the three of 5 parts
Aoxidize two iron, the lanthana of 4 parts of 3 parts of cupric oxide, 4 parts of strontium oxide strontia, 3 parts of rubidium oxide, the nitrogen of 2 parts of lithia and 3 parts
SiClx.
Embodiment 5:
A kind of enamel enamel, including the component of following parts by weight:96 parts of silica, 66 parts of potassium feldspar, 53 parts
Albite, 43 parts of calcium oxide, 42 parts of borax, 34 parts of cordierite, 27 parts of magnesia, 7 parts of manganese oxide, the three of 6 parts
Aoxidize two iron, 4 parts of cupric oxide, 3 parts of lanthana, 4 parts of strontium oxide strontia, 2 parts of rubidium oxide, the nitrogen of 3 parts of lithia and 2 parts
SiClx.
Claims (4)
1. a kind of enamel enamel is it is characterised in that include the component of following parts by weight:80 ~ 100 parts of silica, 60 ~
80 parts of potassium feldspar, 40 ~ 80 parts of albite, 30 ~ 50 parts of calcium oxide, 30 ~ 50 parts of borax, 30 ~ 40 parts of cordierite, 20
~ 30 parts of magnesia, 1 ~ 10 part of manganese oxide, 1 ~ 10 part of di-iron trioxide, 1 ~ 10 part of cupric oxide, 1 ~ 5 part of lanthana,
1 ~ 5 part of strontium oxide strontia, 1 ~ 5 part of rubidium oxide, the barium monoxide of 1 ~ 5 part of lithia and 1 ~ 5 part.
2. enamel enamel according to claim 1 is it is characterised in that be grouped into by the group of following parts by weight:90
The silica of part, 70 parts of potassium feldspar, 60 parts of albite, 40 parts of calcium oxide, 40 parts of borax, 35 parts of cordierite, 25
The magnesia of part, 5 parts of manganese oxide, 5 parts of di-iron trioxide, 5 parts of cupric oxide, 3 parts of lanthana, 2 parts of strontium oxide strontia, 2
Part rubidium oxide, the barium monoxide of 3 parts of lithia and 3 parts.
3. enamel enamel according to claim 1 and 2 is it is characterised in that described potassium feldspar albite, cordierite
Fineness is less than 50 mesh.
4. enamel according to claim 1 and 2 with enamel it is characterised in that described barium monoxide is replaced by silicon nitride.