CN106398609A - Metallocene catalysis material low-temperature packaging adhesive - Google Patents
Metallocene catalysis material low-temperature packaging adhesive Download PDFInfo
- Publication number
- CN106398609A CN106398609A CN201610751952.6A CN201610751952A CN106398609A CN 106398609 A CN106398609 A CN 106398609A CN 201610751952 A CN201610751952 A CN 201610751952A CN 106398609 A CN106398609 A CN 106398609A
- Authority
- CN
- China
- Prior art keywords
- parts
- catalysis material
- metallocene catalysis
- material low
- low temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a metallocene catalysis material low-temperature packaging adhesive. The adhesive comprises, by mass, 18-22 parts of Fischer-Tropsch wax SX105, 22-27 parts of POE 1950, 8-12 parts of atactic polyolefin 792, and 40-48 parts of C5 petroleum resin 1#. The adhesive has the advantages of reasonable design, fast drying speed, great improvement of the production efficiency, realization of expansion of the application range of commercial products, realization of bonding of materials difficult to stick, and compensation of the gap of like adhesives in domestic markets.
Description
Technical field
The present invention relates to a kind of metallocene catalysis material at low temperature packs glue, it is mainly used in the positioning bondings such as carton, suction pipe.
Background technology
The metallocene catalysis material at low temperature packaging glue commonly used at present, has following defect：
（1）Crystallization rate is slow, low production efficiency；
（2）Low temperature resistant and two contradictory factors of melt viscosity very difficult balance it is impossible to have good mobility and low simultaneously
Warm nature；
（3）The low temperature bonding difference of conventional cartons is it is impossible to meet the bonding to membrane material.
Content of the invention
The technical problem to be solved is the above-mentioned deficiency overcoming in the presence of prior art, and provides one kind to set
Rationally, crystallization effect is good for meter, and product can keep the metallocene catalysis material at low temperature packaging glue of mobility and low temperature properties simultaneously.
The present invention solves above-mentioned technical problem and be employed technical scheme comprise that：A kind of metallocene catalysis material at low temperature packaging
Glue it is characterised in that：Its formula components and its mass fraction are as follows,
Fischer-Tropsch wax SX105,18-22 part,
POE 1950,22-27 part,
Atactic polyolefin 792,8-12 part,
C5 Petropols 1#, 40-48 part.
Preferably, its formula components and its mass fraction are as follows,
Fischer-Tropsch wax SX105,20 parts,
1950,25 parts of POE,
Atactic polyolefin 792,10 parts,
C5 Petropols 1#, 25 parts.
Petropols are coordinated using Fischer-Tropsch wax, is greatly improved its crystallization rate, shorten the open hour, make it more preferable
Meet technology of the package, improve production efficiency.
Using POE, due to its special synthesis technique, product is made to be distributed on molecular weight more uniform, mobility is more preferable,
Its special performance simultaneously, overcoming such product conventional and using EVA is matrix resin, in low temperature resistant and two lances of melt viscosity
The balance of shield factor, makes it there is good mobility and low temperature properties simultaneously.
Add a small amount of nothing and return polyolefin, increase its range of application, the low temperature being allowed to not only be only capable of meeting conventional cartons glues
Knot is moreover it is possible to meet the bonding to membrane material.
The present invention compared with prior art, has following positive effect：
（1）Rapid draing speed is greatly improved production efficiency；
（2）The range of application of market product has been expanded in the interpolation of special material, can achieve the bonding to difficult viscous material；
（3）Compensate for the vacancy in such glue market at home.
Specific embodiment
Below by embodiment, the invention will be further described.
Embodiment：
The formula components of the present embodiment and its mass fraction are as shown in the table.
Furthermore, it is necessary to illustrate, the specific embodiment described in this specification, as long as its part does not specify concrete shape
Shape and size, then this part can be any shape and size being adapted with its structure；Meanwhile, the title that part is taken
Can be different.All equivalent or simple change done according to the construction described in inventional idea of the present invention, feature and principle, are all included in
In the protection domain of patent of the present invention.
Claims (2)
1. a kind of metallocene catalysis material at low temperature packaging glue it is characterised in that：Its formula components and its mass fraction are as follows,
Fischer-Tropsch wax SX105,18-22 part,
POE 1950,22-27 part,
Atactic polyolefin 792,8-12 part,
C5 Petropols 1#, 40-48 part.
2. metallocene catalysis material at low temperature according to claim 1 packaging glue it is characterised in that：Its formula components and its
Mass fraction is as follows,
Fischer-Tropsch wax SX105,20 parts,
1950,25 parts of POE,
Atactic polyolefin 792,10 parts,
C5 Petropols 1#, 25 parts.