CN106396601A - Novel indoor decoration magnesium fireproof plate - Google Patents
Novel indoor decoration magnesium fireproof plate Download PDFInfo
- Publication number
- CN106396601A CN106396601A CN201511011528.XA CN201511011528A CN106396601A CN 106396601 A CN106396601 A CN 106396601A CN 201511011528 A CN201511011528 A CN 201511011528A CN 106396601 A CN106396601 A CN 106396601A
- Authority
- CN
- China
- Prior art keywords
- magnesium
- sheet material
- maintenance
- fireproof plate
- new indoor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a novel indoor decoration magnesium fireproof plate, and relates to the field of fireproof plates, especially relates to a raw material proportioning production process of the novel indoor decoration magnesium fireproof plate. The fireproof plate solves the problems that an existing fireproof plate is complex in production process, the pollution is easily caused during the production process and the use process, and the environment and the human body are harmed. The indoor decoration magnesium fireproof plate comprises the following components in percentage by weight: 35-55% of magnesium oxide, 20-35% of magnesium chloride, 15-40% of straw, 1-4% of phosphoric acid, and 1.5-4.5% of foaming agent. The production process is simple, the production efficiency is high, the renewable raw materials such as straws are used, and pollutants such as formaldehyde and the like in the production are not added, and the indoor decoration magnesium fireproof plate is environmentally friendly and has no pollution.
Description
Technical field
The present invention relates to PLASTIC LAMINATED field, a kind of especially raw material proportioning production technology of new indoor finishing magnesium-made fire-proof plate.
Background technology
PLASTIC LAMINATED also known as refractory slab, scientific name is thermosetting resin-impregnated paper high-pressure laminated board, is incrustation refractory building material, has abundant surface color and polish, lines and special logistics performance, are widely used in the fields such as interior decoration, furniture, kitchen cabinet, laboratory face, exterior wall.PLASTIC LAMINATED is the impregnation technology through melamine and phenolic resin for the body paper (titanium valve paper, brown paper), and HTHP is made.Traditional PLASTIC LAMINATED complex manufacturing, and when production process and use, easily produce pollution, harm environment and health.
Content of the invention
For solving existing PLASTIC LAMINATED complex manufacturing, and when production process and use, easily produce pollution, the technical problem of harm environment and health, the present invention provides a kind of new indoor to fit up magnesium-made fire-proof plate.
The technical solution adopted for the present invention to solve the technical problems is：
A kind of new indoor fits up magnesium-made fire-proof plate, has following compositions to constitute by weight percentage：Magnesia 35-55%, magnesium chloride 20-35%, stalk 15-40%, phosphatase 11-4%, foaming agent 1.5-4.5%.
A kind of new indoor fits up the preparation method of magnesium-made fire-proof plate, comprises the following steps：
（1）To put in mixer according to the magnesium oxide aqueous solution that a kind of described new indoor fits up magnesium-made fire-proof board raw material proportioning consumption, place into the magnesium chloride of corresponding weight, mix and blend 3-5 minute, after stirring, puts into the stalk after the pulverizing of respective amount, continue stirring 5-7 minute, add the phosphoric acid of respective amount, after continuing stirring 1-2 minute, squeeze into the foaming agent of respective amount with foaming machine, continuously stirred 3-5 minute, stirs and is mixed into liquid paste to each material.
（2）The sheet material being rolled into different-thickness any surface finish on flow production line machine by roller put into by the material being stirred, and is in pureed type to sheet material.
（3）The sheet material of roller-compaction is put into phase maintenance is interior, the interior temperature of maintenance is pre- 35-40 DEG C mixing up, and sheet material, in phase maintenance interior placement 20-30 hour, makes the sheet material initial stage qualitative.
（4）Then initial set-up sheet material is put into that the second stage of maintenance is interior, between the second stage of maintenance, temperature is pre- 40-45 DEG C mixing up, and humidity is the pre- 60-70% mixing up, product continuous drying 5-7 days, final molding between the second stage of maintenance.
Simple production process of the present invention, production efficiency is high, employs the renewable raw materials such as stalk, and production does not have the easily pollutant such as formaldehyde to add, environment friendly and pollution-free.
Specific embodiment
With reference to specific embodiment, the present invention will be further described：
Embodiment one
A kind of new indoor fits up magnesium-made fire-proof plate, has following compositions to constitute by weight percentage：Magnesia 40%, magnesium chloride 25%, stalk 30%, phosphoric acid 2.5%, foaming agent 2.5%.
A kind of new indoor fits up the preparation method of magnesium-made fire-proof plate, comprises the following steps：
（1）To put in mixer according to the magnesium oxide aqueous solution that a kind of described new indoor fits up magnesium-made fire-proof board raw material proportioning consumption, place into the magnesium chloride of corresponding weight, mix and blend 3 minutes, after stirring, puts into the stalk after the pulverizing of respective amount, continue stirring 5 minutes, add the phosphoric acid of respective amount, after continuing stirring 1 minute, squeeze into the foaming agent of respective amount with foaming machine, continuously stirred 3 minutes, stir and be mixed into liquid paste to each material.
（2）The sheet material being rolled into different-thickness any surface finish on flow production line machine by roller put into by the material being stirred, and is in pureed type to sheet material.
（3）The sheet material of roller-compaction is put into phase maintenance is interior, the interior temperature of maintenance is pre- 35 DEG C mixing up, sheet material is placed 24 hours phase maintenance is interior, makes the sheet material initial stage qualitative.
（4）Then initial set-up sheet material is put into that the second stage of maintenance is interior, between the second stage of maintenance, temperature is pre- 40 DEG C mixing up, humidity be pre- mix up 60%, product continuous drying 5 days, final molding between the second stage of maintenance.
Embodiment two
A kind of new indoor fits up magnesium-made fire-proof plate, has following compositions to constitute by weight percentage：Magnesia 35%, magnesium chloride 30%, stalk 32%, phosphatase 11 .5%, foaming agent 1.5%.
A kind of new indoor fits up the preparation method of magnesium-made fire-proof plate, comprises the following steps：
（1）To put in mixer according to the magnesium oxide aqueous solution that a kind of described new indoor fits up magnesium-made fire-proof board raw material proportioning consumption, place into the magnesium chloride of corresponding weight, mix and blend 5 minutes, after stirring, puts into the stalk after the pulverizing of respective amount, continue stirring 7 minutes, add the phosphoric acid of respective amount, after continuing stirring 2 minutes, squeeze into the foaming agent of respective amount with foaming machine, continuously stirred 5 minutes, stir and be mixed into liquid paste to each material.
（2）The sheet material being rolled into different-thickness any surface finish on flow production line machine by roller put into by the material being stirred, and is in pureed type to sheet material.
（3）The sheet material of roller-compaction is put into phase maintenance is interior, the interior temperature of maintenance is pre- 40 DEG C mixing up, sheet material is placed 30 hours phase maintenance is interior, makes the sheet material initial stage qualitative.
（4）Then initial set-up sheet material is put into that the second stage of maintenance is interior, between the second stage of maintenance, temperature is pre- 45 DEG C mixing up, humidity be pre- mix up 70%, product continuous drying 7 days, final molding between the second stage of maintenance.
Embodiment three
A kind of new indoor fits up magnesium-made fire-proof plate, has following compositions to constitute by weight percentage：Magnesia 35-55%, magnesium chloride 20-35%, stalk 15-40%, phosphatase 11-4%, foaming agent 1.5-4.5%.
A kind of new indoor fits up the preparation method of magnesium-made fire-proof plate, comprises the following steps：
（1）To put in mixer according to the magnesium oxide aqueous solution that a kind of described new indoor fits up magnesium-made fire-proof board raw material proportioning consumption, place into the magnesium chloride of corresponding weight, mix and blend 3-5 minute, after stirring, puts into the stalk after the pulverizing of respective amount, continue stirring 5-7 minute, add the phosphoric acid of respective amount, after continuing stirring 1-2 minute, squeeze into the foaming agent of respective amount with foaming machine, continuously stirred 3-5 minute, stirs and is mixed into liquid paste to each material.
（2）The sheet material being rolled into different-thickness any surface finish on flow production line machine by roller put into by the material being stirred, and is in pureed type to sheet material.
（3）The sheet material of roller-compaction is put into phase maintenance is interior, the interior temperature of maintenance is pre- 35-40 DEG C mixing up, and sheet material, in phase maintenance interior placement 20-30 hour, makes the sheet material initial stage qualitative.
（4）Then initial set-up sheet material is put into that the second stage of maintenance is interior, between the second stage of maintenance, temperature is pre- 40-45 DEG C mixing up, and humidity is the pre- 60-70% mixing up, product continuous drying 5-7 days, final molding between the second stage of maintenance.
Last it should be noted that, above specific embodiment is merely to illustrate technical scheme and unrestricted, although chest explanation has been carried out to the present invention with reference to preferred embodiment, it will be understood by those within the art that, technical scheme can be modified or replace on an equal basis, without deviating from the spirit and scope of technical solution of the present invention, it all should be covered in the middle of scope of the presently claimed invention.
Claims (3)
1. a kind of new indoor finishing magnesium-made fire-proof plate it is characterised in that：Following compositions are had to constitute by weight percentage：Magnesia 35-55%, magnesium chloride 20-35%, stalk 15-40%, phosphatase 11-4%, foaming agent 1.5-4.5%.
2. a kind of new indoor finishing magnesium-made fire-proof plate according to claim 1 it is characterised in that：Constitute as preferred percentage by weight：Magnesia 40%, magnesium chloride 25%, stalk 30%, phosphoric acid 2.5%, foaming agent 2.5%.
3. a kind of new indoor finishing magnesium-made fire-proof plate according to claim 1 it is characterised in that：Described new indoor finishing magnesium-made fire-proof plate preparation method is as follows：
（1）To put in mixer according to the magnesium oxide aqueous solution that a kind of described new indoor fits up magnesium-made fire-proof board raw material proportioning consumption, place into the magnesium chloride of corresponding weight, mix and blend 3-5 minute, after stirring, puts into the stalk after the pulverizing of respective amount, continue stirring 5-7 minute, add the phosphoric acid of respective amount, after continuing stirring 1-2 minute, squeeze into the foaming agent of respective amount with foaming machine, continuously stirred 3-5 minute, stirs and is mixed into liquid paste to each material；
（2）The material being stirred is put on the shallow machine of Production line, is rolled into the sheet material of different-thickness any surface finish by roller, is in pureed type to sheet material；
（3）The sheet material of roller-compaction is put into phase maintenance is interior, the interior temperature of maintenance is pre- 35-40 DEG C mixing up, and sheet material, in phase maintenance interior placement 20-30 hour, makes the sheet material initial stage qualitative；
（4）Then initial set-up sheet material is put into that the second stage of maintenance is interior, between the second stage of maintenance, temperature is pre- 40-45 DEG C mixing up, and humidity is the pre- 60-70% mixing up, product continuous drying 5-7 days, final molding between the second stage of maintenance.