CN1962531A - Widely-used light composite material production method - Google Patents
Widely-used light composite material production method Download PDFInfo
- Publication number
- CN1962531A CN1962531A CNA2005101198928A CN200510119892A CN1962531A CN 1962531 A CN1962531 A CN 1962531A CN A2005101198928 A CNA2005101198928 A CN A2005101198928A CN 200510119892 A CN200510119892 A CN 200510119892A CN 1962531 A CN1962531 A CN 1962531A
- Authority
- CN
- China
- Prior art keywords
- composite material
- light composite
- production method
- widely
- material production
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a lightweight composite employing fly ash, expanded perlite as lightweight skeletal material, magnesium oxide, magnesium chloride and modified starch adhesive as mixed cementing agent. The materials has the advantages of simple process for manufacturing, low cost, high intensity, fine water-proof and heat-insulating property and light weight.
Description
The invention belongs to a kind of is the production method of the broad-spectrum light composite material of main raw material with the magnesite material.
Magnesite material is high temperature resistant owing to having at present, and certain toughness is arranged, and can saw, can dig, can follow closely, price is low, can be molded and shaped etc. advantage, enlarge its range of application day by day, but with the magnesite material is the light composite material of main raw material, has subject matter at present, is not that water resisting property is poor, yielding, or resistance to compression, folding strength are undesirable, are exactly complex process, the price height, lack product competitiveness, limited it and further developed.
The present invention seeks to design a kind of technology simple, strengthen mend weak effect significantly, cheap again, the purposes of cost light composite material production formula very widely, make it can be advantageously used in fields such as building, packing, decoration, agricultural, by vast enterprise is accepted.
Mainly increase is a kind of with low cost in the present invention's prescription, through chemical modification, has the Starch Adhesive than high-adhesive-strength and water resisting property.This tackiness agent is very affine through test and magnesite material, easily mixes, and it and magnesite adhesives, aglite form a mutual cross-linked network, and reinforced effects is very remarkable, the product strength height, and indeformable, water resisting property is strong, and higher using value is arranged.
The present invention fills a prescription (by weight): with aglite (comprising flyash, pearlstone etc.) is 100 parts, magnesium oxide consumption 5-80 part then, magnesium chloride 3-40 part, modified starch adhesive 5-80 part, the each component consumption has bigger difference according to the requirement difference of products made thereby.Its technology is: after product is determined, takes by weighing the each component siccative by a certain percentage earlier, and, adds modified starch adhesive wet feed and whole siccative mixings at last the whole mixings of siccative, and agglomerating to hold, can scatter with throwing and be advisable.Then that wet feed or the diaphragm mixed thoroughly is molded, or add the molding device extrusion molding.Solidify the demoulding in general 4 hours.Can pack after continuation one week of maintenance and dispatch from the factory.
Light composite material of the present invention can be widely used in building energy conservation product, walling unit, wall dunnage, smallpox partition plate; Make instead of wood plate case, honeycomb carton, packing electronic product in the packing business; Lines, line plate, door trim panels in the adnornment industry; Be used as greenhouse bracket etc. on the agricultural.Have compared with similar products that production technique is simple, facility investment is few, product cost is low, good product performance, fire prevention, heat insulation, high insulating effect, but and can dig, can saw, can follow closely mould molding, indeformable, water repelling property good, the intensity advantages of higher, has extensive use.
Embodiment: to produce the building heat preservation wall dunnage is example: take by weighing 100 kilograms of pearlstones, 50 kilograms in magnesium oxide, 22 kilograms in magnesium chloride, the siccative mixing is mixed thoroughly, adding 40 kilograms-43 kilograms of modified starch adhesives then mixes with whole siccatives and mixes thoroughly, compression molding one by one at last, curing and demolding product.
Claims (1)
- A kind of production method of broad-spectrum light composite material, it is characterized in that by weight, aglite based on flyash, pearlstone is 100 parts, magnesium oxide 5-80 part then, magnesium chloride 3-40 part, treated starch tackiness agent 5-80 part, earlier the each component siccative is mixed and mix thoroughly, then treated starch tackiness agent wet feed and the siccative of mixing thoroughly are mixed, get final product compression molding or extrusion molding, make broad-spectrum light composite material of the present invention.