CN106396590A - Novel inorganic external wallboard - Google Patents
Novel inorganic external wallboard Download PDFInfo
- Publication number
- CN106396590A CN106396590A CN201610768291.8A CN201610768291A CN106396590A CN 106396590 A CN106396590 A CN 106396590A CN 201610768291 A CN201610768291 A CN 201610768291A CN 106396590 A CN106396590 A CN 106396590A
- Authority
- CN
- China
- Prior art keywords
- parts
- novel inorganic
- side fascia
- inorganic side
- additive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel inorganic external wallboard, which comprises the following raw materials in parts by weight: 80 to 120 parts of gypsum, 30 to 60 parts of cement, 30 to 50 parts of fine aggregate, 20 to 30 parts of filler, 5 to 10 parts of waterproof agent, 1 to 3 parts of flame retardant, 0.01 to 0.03 part of chlorpheniramine maleate, and 1 to 7 parts of additive, wherein the waterproof agent is composed of polyvinyl alcohol, ammonia liquor, and progesterone. The provided novel inorganic external wallboard has a good antibacterial effect; due to the characteristics of added chlorpheniramine maleate, after chlorpheniramine maleate is mixed with other components, the pressure resistant and corrosion resistant performance of the external wallboard is effectively enhanced; moreover, the raw material sources are wide, raw materials are easily available, and the external wallboard can be produced without using any complicated technology.
Description
Technical field
The present invention relates to a kind of artificial Side fascia, particularly to a kind of novel inorganic Side fascia.
Background technology
Various composite exterior wall decorative panels on existing market, main include polymer matrix decorative panel, Metal Substrate decorative panel, no
Machine class decorative panel, wherein polymer matrix decorative panel with resin type dalle, with vitreous body, ceramic matrix in mineral-type decorative panel
Decorative panel makes it apply limitation, the surface characteristic of inorganic decorating board and microcellular structure special because of itself fragility and ecological drawback
Levy, form the beneficial ecological ornamental plate improving spatial environmentss.And the inorganic Side fascia having now, most effect on driving birds is not good.Part
Using the inorganic trim panel of photocatalysis so as to have the effect of antibacterial, effect is preferable, but high cost.
The information being disclosed in this background section is merely intended to increase the understanding of the general background to the present invention, and should not
Recognize when being considered or imply in any form that this information structure has been the prior art well known to persons skilled in the art.
Content of the invention
It is an object of the invention to provide a kind of novel inorganic Side fascia, thus organic Side fascia in prior art is overcome to resist
Bacterium DeGrain, the shortcoming of high cost.
For achieving the above object, the technical scheme that the present invention provides is as follows：
A kind of novel inorganic Side fascia, according to ratio of weight and number, comprises following components raw material：80～120 parts of Gypsum Fibrosum, cement
30～60 parts, 30～50 parts of fine aggregate, 20～30 parts of filler, 5～10 parts of waterproofing agent, 1～3 part of fire retardant, maleic acid chlorobenzene
That quick 0.01～0.03 part and 1～7 part of additive；Wherein, described waterproofing agent is made up of polyvinyl alcohol, ammonia and Progesterone.
Wherein, described fine aggregate for modulus of fineness be 2.4～2.8 artificial sand or stone that modulus of fineness is 2.0～2.3
Sand.
Wherein, described filler is kieselguhr or vermiculite power.
Wherein, described waterproofing agent, according to ratio of weight and number, by 20～30 parts of polyvinyl alcohol, 15～20 parts of ammonia and Huang
0.1～0.5 part of composition of body ketone.
Wherein, described ammoniacal liquor mass concentration is 50%.
Wherein, described fire retardant is in magnesium hydroxide, antimony oxide, HBCD or tetrabromobisphenol A
Kind.
Wherein, described additive by Borax, tertiary sodium phosphate, glycosylglycerol and, zinc oxide and homosalate form.
Wherein, described additive, according to ratio of weight and number, by 1～5 part of Borax, 10～20 parts of tertiary sodium phosphate, glycerol Portugal
1～3 part of glucosides, 10～12 parts of zinc oxide and 3～5 parts of compositions of homosalate.
Above-mentioned novel inorganic Side fascia, takes after raw material mixing by common mask-making technology hot rolling, cold rolling, makes exterior wall
Plate.
Compared with prior art, the present invention has the advantages that：
Novel inorganic antibacterial Side fascia of the present invention, antibacterial effect is good, the Chlorphenamine Maleate of interpolation because of its nature and flavor, with this
After the mixing of invention other components interacts, can effectively strengthen exterior wall resistance to compression, corrosion resistant effect；Further, the present invention
Each component raw material sources extensively, are drawn materials convenient it is not necessary to can obtain the present invention through complicated technique.
Specific embodiment
It is described in detail with reference to specific embodiment, it is to be understood that protection scope of the present invention is not subject to specifically
The restriction of embodiment.
Embodiment 1
A kind of novel inorganic Side fascia, in units of kg, weighs required each component raw material：Gypsum Fibrosum 100kg, cement
45kg, fine aggregate modulus of fineness be 2.0～2.3 quartz sand 40kg, filler vermiculite power 25kg, waterproofing agent 8kg, fire retardant hydrogen
Magnesium oxide 2kg, Chlorphenamine Maleate 0.02kg and additive 4kg；Wherein, waterproofing agent is by polyvinyl alcohol 25kg, mass concentration
Ammonia 18kg for 50% and Progesterone 0.3kg composition；Wherein, additive is by Borax 3kg, tertiary sodium phosphate 15kg, glycerol glucose
Glycosides 2kg, zinc oxide 11kg and homosalate 4kg composition.
Above-mentioned novel inorganic Side fascia, takes after raw material mixing by common mask-making technology hot rolling, cold rolling, makes exterior wall
Plate.
Embodiment 2
A kind of novel inorganic Side fascia, in units of kg, weighs required each component raw material：Gypsum Fibrosum 80kg, cement 30kg,
Fine aggregate modulus of fineness be 2.0～2.3 quartz sand 30kg, filler kieselguhr 20kg, waterproofing agent 5kg, fire retardant hexabromo ring
Dodecane 1kg, Chlorphenamine Maleate 0.01kg and additive 1kg；Wherein, waterproofing agent is by polyvinyl alcohol 20kg, mass concentration
Ammonia 15kg for 50% and Progesterone 0.1kg composition；Wherein, additive is by Borax 1kg, tertiary sodium phosphate 10kg, glycerol glucose
Glycosides 1kg, zinc oxide 10kg and homosalate 3kg composition.
Above-mentioned novel inorganic Side fascia, takes after raw material mixing by common mask-making technology hot rolling, cold rolling, makes exterior wall
Plate.
Embodiment 3
A kind of novel inorganic Side fascia, in units of kg, weighs required each component raw material：Gypsum Fibrosum 120kg, cement
60kg, fine aggregate modulus of fineness be 2.4～2.8 artificial sand 50kg, filler kieselguhr 30kg, waterproofing agent 10kg, fire retardant
Antimony oxide 3kg, Chlorphenamine Maleate 0.03kg and additive 7kg；Wherein, waterproofing agent is by polyvinyl alcohol 30kg, quality
Concentration is 50% ammonia 20kg and Progesterone 0.5kg composition；Wherein, additive is by Borax 5kg, tertiary sodium phosphate 20kg, glycerol
Glucoside 3kg, zinc oxide 12kg and homosalate 5kg composition.
Above-mentioned novel inorganic Side fascia, takes after raw material mixing by common mask-making technology hot rolling, cold rolling, makes exterior wall
Plate.
Embodiment 4
A kind of novel inorganic Side fascia, in units of kg, weighs required each component raw material：Gypsum Fibrosum 100kg, cement
45kg, fine aggregate modulus of fineness be 2.0～2.3 quartz sand 40kg, filler vermiculite power 25kg, waterproofing agent 8kg, fire retardant hydrogen
Magnesium oxide 2kg and additive 4kg；Wherein, waterproofing agent is 50% by polyvinyl alcohol 25kg, mass concentration ammonia 18kg and corpus luteum
Ketone 0.3kg forms；Wherein, additive is by Borax 3kg, tertiary sodium phosphate 15kg, glycosylglycerol 2kg, zinc oxide 11kg and Hu Mo
Willow ester 4kg forms.
Above-mentioned novel inorganic Side fascia, takes after raw material mixing by common mask-making technology hot rolling, cold rolling, makes exterior wall
Plate.
Embodiment 5
A kind of novel inorganic Side fascia, in units of kg, weighs required each component raw material：Gypsum Fibrosum 100kg, cement
45kg, fine aggregate modulus of fineness be 2.0～2.3 quartz sand 40kg, filler vermiculite power 25kg, waterproofing agent 8kg, fire retardant hydrogen
Magnesium oxide 2kg, Chlorphenamine Maleate 0.02kg；Wherein, the ammonia that waterproofing agent is 50% by polyvinyl alcohol 25kg, mass concentration
18kg and Progesterone 0.3kg composition.
Above-mentioned novel inorganic Side fascia, takes after raw material mixing by common mask-making technology hot rolling, cold rolling, makes exterior wall
Plate.
Detection
It is as shown in table 1 that embodiment 1～embodiment 5 prepares gained novel inorganic Side fascia.
Table 1
From data in table 1, the Chlorphenamine Maleate added in the present invention is outer because its architectural characteristic can effectively strengthen
The resistance to compression of wallboard, corrosion resistance, can effectively improve the comprcssive strength of exterior wall, further additive of the present invention can be more preferably simultaneously
Improvement, optimize product properties of the present invention, while making resistance to compression, corrosion resistance, comprcssive strength that product had high, matter
More preferably, cost is lower for amount.
The description of the aforementioned specific illustrative embodiment to the present invention illustrate that and illustration purpose.These descriptions
It is not wishing to limit the invention to disclosed precise forms, and it will be apparent that according to above-mentioned teaching, can much be changed
And change.The purpose of selecting and describing the exemplary embodiment is that explaining that the certain principles of the present invention and its reality should
With so that those skilled in the art be capable of and utilize the present invention various different exemplary and
Various different selections and change.The scope of the present invention is intended to be limited by claims and its equivalents.
Claims (8)
1. a kind of novel inorganic Side fascia is it is characterised in that according to ratio of weight and number, comprise following components raw material：Gypsum Fibrosum 80～
120 parts, 30～60 parts of cement, 30～50 parts of fine aggregate, 20～30 parts of filler, 5～10 parts of waterproofing agent, 1～3 part of fire retardant,
0.01～0.03 part of Chlorphenamine Maleate and 1～7 part of additive；Wherein, described waterproofing agent is by polyvinyl alcohol, ammonia and Huang
Body ketone forms.
2. according to claim 1 novel inorganic Side fascia it is characterised in that：Described fine aggregate is 2.4 for modulus of fineness
～2.8 artificial sand or the quartz sand that modulus of fineness is 2.0～2.3.
3. according to claim 1 novel inorganic Side fascia it is characterised in that：Described filler is kieselguhr or Vermiculitum
Powder.
4. according to claim 1 novel inorganic Side fascia it is characterised in that：Described waterproofing agent, according to ratio of weight and number,
It is made up of 20～30 parts of polyvinyl alcohol, 15～20 parts of ammonia and 0.1～0.5 part of Progesterone.
5. according to claim 4 novel inorganic Side fascia it is characterised in that：Described ammoniacal liquor mass concentration is 50%.
6. according to claim 1 novel inorganic Side fascia it is characterised in that：Described fire retardant is magnesium hydroxide, three oxygen
Change one of two antimony, HBCD or tetrabromobisphenol A.
7. according to claim 1 novel inorganic Side fascia it is characterised in that：Described additive by Borax, tertiary sodium phosphate,
Glycosylglycerol and, zinc oxide and homosalate composition.
8. according to claim 1 novel inorganic Side fascia it is characterised in that：Described additive, according to ratio of weight and number,
By 1～5 part of Borax, 10～20 parts of tertiary sodium phosphate, 1～3 part of glycosylglycerol, 10～12 parts of zinc oxide and 3～5 parts of homosalate
Composition.