CN106380899A - Fireproof paint - Google Patents
Fireproof paint Download PDFInfo
- Publication number
- CN106380899A CN106380899A CN201610771555.5A CN201610771555A CN106380899A CN 106380899 A CN106380899 A CN 106380899A CN 201610771555 A CN201610771555 A CN 201610771555A CN 106380899 A CN106380899 A CN 106380899A
- Authority
- CN
- China
- Prior art keywords
- parts
- fireproof coating
- fireproof
- fireproof paint
- following components
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fireproof paint. The fireproof paint is composed of the following components in parts by weight: 10 to 15 parts of borax, 2 to 5 parts of titanium dioxide, 2 to 5 parts of triethanolamine, 3 to 6 parts of hydroxymethyl cellulose, 1 to 4 parts of tartaric acid, 1 to 4 parts of magnesium oxide, 5 to 10 parts of heavy calcium carbonate, and 1 to 3 parts of antibacterial agent. The provided fireproof paint has the advantages of simple components, low cost, and strong fireproof performance, and has the characteristics of long flame retardant time, high tensile viscosity, and good fireproof property.
Description
Technical field
The present invention relates to building material technical field, especially a kind of fireproof coating.
Background technology
Fireproof coating is applied to flammable substrates surface, and in order to change material surface combustion characteristics, retardance fire is climing rapidly
Prolong;Or be applied on building element, in order to improve the sapecial coating of the fire endurance of component.Fireproof coating is exactly to pass through coating
Brush, on the surface of those combustible materials, can improve the refractory ability of material, slow down propagation of flame spread speed, or in certain time
Interior energy stops burning.
At present, fireproof coating has two big class in the world:One class is the fireproof coating of non-expansion type, though there being very strong fire resisting
With water resistance, but thermal insulation is bad, and fire protecting performance is not high.Another kind of is intumescent coating, especially can shape when meeting fire
Become the thermal insulation layer of honeycomb microbubble structure, heat-proof quality is good, this kind of coating is typically using organic polymer as filmogen, this kind of
Coating excellent in heat insulating performance, fire protecting performance is good, but foam insulation mechanical strength is low, easily drops, cause fire protecting performance to reduce or
Lost efficacy, relatively costly in addition, dicoration is also not ideal enough.
Content of the invention
The purpose of the present invention is for the problems referred to above, provides the fire prevention that a kind of bond effect is good, attachment is tight, fire resistance is good
Coating.
The present invention provide technical scheme be:
A kind of fireproof coating, by weight, composed of the following components:
Preferably, described fireproof coating, by weight, composed of the following components:
The preparation method of above-mentioned fireproof coating, comprises the steps:Each component is proportionally added into, mixes,
Under the conditions of 100-120 DEG C heat 8-12min, during do not stop stir, obtain fireproof coating.
The invention has the beneficial effects as follows:The fireproof coating of the present invention, component is simple, with low cost, and its refractory ability is good,
It has, and duration of fire resistance is long, and tensile viscosity is high, the good feature of fire line.
Specific embodiment
In order that the objects, technical solutions and advantages of the present invention become more apparent, with reference to embodiments, to the present invention
It is described in further detail.It should be appreciated that specific embodiment described herein is only in order to explain the present invention, and without
Invent in limiting.
Embodiment 1
A kind of fireproof coating, by weight, composed of the following components:
The preparation method of above-mentioned fireproof coating, comprises the steps:Each component is proportionally added into, mixes, 120
Under the conditions of DEG C heat 8min, during do not stop stir, obtain fireproof coating.
Embodiment 2
A kind of fireproof coating, by weight, composed of the following components:
The preparation method of above-mentioned fireproof coating, comprises the steps:Each component is proportionally added into, mixes, 110
Under the conditions of DEG C heat 10min, during do not stop stir, obtain fireproof coating.
Embodiment 3
A kind of fireproof coating, by weight, composed of the following components:
The preparation method of above-mentioned fireproof coating, comprises the steps:Each component is proportionally added into, mixes, 120
Under the conditions of DEG C heat 8min, during do not stop stir, obtain fireproof coating.
Claims (3)
1. a kind of fireproof coating is it is characterised in that by weight, composed of the following components:
2. fireproof coating according to claim 1 is it is characterised in that by weight, composed of the following components:
3. the preparation method of fireproof coating according to claim 1 and 2 is it is characterised in that comprise the steps:By each group
Point be proportionally added into, mix, under the conditions of 100-120 DEG C, heat 8-12min, during do not stop to stir, obtain fire prevention and apply
Material.