CN108587463A - A kind of flame retardant type Emulsificated asphalt water-proof painting material and preparation method thereof - Google Patents

A kind of flame retardant type Emulsificated asphalt water-proof painting material and preparation method thereof Download PDF

Info

Publication number
CN108587463A
CN108587463A CN201810475231.6A CN201810475231A CN108587463A CN 108587463 A CN108587463 A CN 108587463A CN 201810475231 A CN201810475231 A CN 201810475231A CN 108587463 A CN108587463 A CN 108587463A
Authority
CN
China
Prior art keywords
fire
component
flame retardant
proof
retardant type
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810475231.6A
Other languages
Chinese (zh)
Inventor
乔启信
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Lang Kaiqi Waterproof Science And Technology Co Ltd
Original Assignee
Anhui Lang Kaiqi Waterproof Science And Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Lang Kaiqi Waterproof Science And Technology Co Ltd filed Critical Anhui Lang Kaiqi Waterproof Science And Technology Co Ltd
Priority to CN201810475231.6A priority Critical patent/CN108587463A/en
Publication of CN108587463A publication Critical patent/CN108587463A/en
Pending legal-status Critical Current

Abstract

The present invention discloses a kind of flame retardant type Emulsificated asphalt water-proof painting material and preparation method thereof, the water-repellent paint includes 65% first component and 35% second component, wherein, first component includes pitch, Ceramic silicon rubber powder, anionic surfactant, softening oil, deionized water, and component B includes fire-proof packing, fire retardant；The fire-proof packing is made of basic magnesium carbonate, basic copper carbonate, silica.Preparation method is as follows：Pitch and softening oil are heated to 150 DEG C, add Ceramic silicon rubber powder, anionic surfactant and deionized water, after homogeneous cooling, obtains first component；Mixing fire-proof packing and fire retardant obtain second component, and are scattered in first component.The present invention under the high temperature conditions, absorbs heat using fire-proof packing, and concurrent heat decomposition reaction generates CO2And H2O, starvation carry out internal cooling, realize fire-retardant function of independently putting out a fire, do not melt, do not drip in fire hazard environment.

Description

A kind of flame retardant type Emulsificated asphalt water-proof painting material and preparation method thereof
Technical field
The invention belongs to asphalt waterproofing paint fields, and in particular to a kind of flame retardant type Emulsificated asphalt water-proof painting material and its preparation Method.
Background technology
Emulsificated asphalt water-proof painting material, primary raw material pitch is petroleum fractionating product, under the conditions of temperature is higher, easily certainly Fire is ignite, the prior art generally alleviates pitch burning by adding halogenated flame retardant, but autonomous fire extinguishing cooling is still not achieved Effect, and its decomposition product hydrogen halides is discharged into air, can cause environmental pollution, in addition, fire retardant is largely scattered in drip In green base-material, the space structure and mechanical property of film can be destroyed, film is caused to be easy cracking, aging.
Application No. is the patent of CN201410459750.5, discloses the uncured rubber-asphalt waterproof with flame-retarding characteristic and apply Material and preparation method thereof only adds fire retardant to improve coating fire resistance by physics, and flame retardant effect is not ideal enough, and with poly- Ammonium phosphate, hexabromocyclododecane are generated ammonia, hydrogen bromide by thermal decomposition, pollute air as fire retardant.
Invention content
In view of the deficiencies of the prior art, the purpose of the present invention is to provide a kind of flame retardant type Emulsificated asphalt water-proof painting materials And preparation method thereof.
Technical scheme of the present invention is summarized as follows：
A kind of flame retardant type Emulsificated asphalt water-proof painting material, the water-repellent paint include 65% first component and 35% second component, In, first component includes pitch, Ceramic silicon rubber powder, anionic surfactant, softening oil, deionized water, and component B includes Fire-proof packing, fire retardant；The fire-proof packing is made of basic magnesium carbonate, basic copper carbonate, silica.
Preferably, the first component includes following raw material：
Preferably, the anionic surfactant include at least Disodium sulfosuccinate, neopelex, One kind in fatty alcohol-ether sodium sulfate.
Preferably, the softening oil includes at least one kind in turpentine oil, castor oil, palm oil.
Preferably, the component B includes following raw material：
100 parts of fire-proof packing；
3-7 parts of fire retardant.
Preferably, the fire-proof packing includes following weight percent component：Basic magnesium carbonate 40-50%, alkali formula carbon Sour copper 20-25%, silica 30-35%.
Preferably, the fire retardant includes at least antimony oxide, zinc borate, pentaerythritol phosphate, tricresyl phosphate fourth One kind in ester.
The present invention also provides a kind of above-mentioned preparation method of flame retardant type Emulsificated asphalt water-proof painting material, detailed process is as follows：It will Pitch and softening oil are heated to 150 DEG C, add Ceramic silicon rubber powder, anionic surfactant and deionized water, homogeneous After cooling, first component is obtained；Weight percent mixing basic magnesium carbonate, basic copper carbonate, silica, obtain fire-proof packing, then It is stirred evenly with fire retardant, obtains second component, and be scattered in first component and applied to get the flame retardant type emulsified asphalt waterproof Material.
Beneficial effects of the present invention：
For the present invention by Ceramic silicon rubber powder-modified asphalt, the two, which is cross-linked with each other, is solidified into stable three-dimensional ceramic network Structure is not melted in fire hazard environment, is not dripped, and the flame retardant property and mechanical property of coating is greatly improved, and is filled out using fire prevention Material under the high temperature conditions, absorbs heat, and concurrent heat decomposition reaction generates CO2And H2O, starvation carry out internal cooling, real It now independently puts out a fire fire-retardant function, and does not generate any pernicious gas.
Specific implementation mode
With reference to embodiment, the present invention is described in further detail, to enable those skilled in the art with reference to specification Word can be implemented according to this.
The present invention proposes that the flame retardant type Emulsificated asphalt water-proof painting material of an embodiment, the water-repellent paint include 65% first component With 35% second component, wherein first component include pitch, Ceramic silicon rubber powder, anionic surfactant, softening oil, go from Sub- water, component B include fire-proof packing, fire retardant；The fire-proof packing is by basic magnesium carbonate, basic copper carbonate, silica group At.
Wherein, first component, using 20-40 parts of Ceramic silicon rubber powder as modifying agent, is made using 100 parts of pitches as base-material Si-O-Si keys are introduced into pitch skeleton, improve paint structure intensity and chemical stability, and in 150 DEG C of hot conditions, further It is solidified into hard ceramic protective layer, is adhering closely to asphaltene molecule surface, is cross-linked into stable three-dimensional ceramic network structure, It does not melt, drip in fire hazard environment, coating fire-resistance flame retardant property and mechanical property is greatly improved.
Meanwhile using 2-8 parts of anionic surfactants as emulsifier, it is made of 15-35 parts of deionized waters for disperseing Water phase and organic oil phase, include at least Disodium sulfosuccinate, neopelex, one in fatty alcohol-ether sodium sulfate Kind, and asphalt softening point is reduced by 1-5 parts of softening oils, energy loss is reduced, turpentine oil, castor oil, palm oil are included at least In one kind.
Wherein, component B is using 100 parts of fire-proof packings as base-material, by 40-50% basic magnesium carbonates, 20-25% basic carbonates Copper, 30-35% silica composition, when a fire, on the one hand basic magnesium carbonate and basic copper carbonate in filler can be inhaled Heat is received, film ambient temperature is reduced, extends required time when film reaches ignition point, races against time for fire control, it is another Aspect, basic magnesium carbonate and basic copper carbonate are when heated, the effect of decomposing, and generate CO2, it is filled in coating structure, drops Oxygen concentration that is low and completely cutting off film ectonexine achievees the effect that fire smothering, decomposition reaction equation are as follows： Reaction life At water again can Self-extinguishing cooling, realize waterproof coating independently put out a fire it is fire-retardant, and using 3-7 parts of fire retardants as auxiliary material, further The fire retardant performance of coating is improved, is included at least in antimony oxide, zinc borate, pentaerythritol phosphate, tributyl phosphate One kind.
The present invention also provides a kind of above-mentioned preparation method of flame retardant type Emulsificated asphalt water-proof painting material, detailed process is as follows：It will Pitch and softening oil are heated to 150 DEG C, add Ceramic silicon rubber powder, anionic surfactant and deionized water, homogeneous After cooling, first component is obtained；Weight percent mixing basic magnesium carbonate, basic copper carbonate, silica, obtain fire-proof packing, then It is stirred evenly with fire retardant, obtains second component, and be scattered in first component and applied to get the flame retardant type emulsified asphalt waterproof Material.
Following table lists the performance parameter of the specific formula and obtained water-repellent paint of different embodiments：
Subordinate list：
As seen from the above table, water-repellent paint flame retardant property produced by the invention is good, and self-extinguishing cooling is realized in 40s, and With excellent mechanical property and tolerance.
Although the embodiments of the present invention have been disclosed as above, but its is not only in the description and the implementation listed With it can be fully applied to various fields suitable for the present invention, for those skilled in the art, can be easily Realize other modification, therefore without departing from the general concept defined in the claims and the equivalent scope, the present invention is simultaneously unlimited In specific details.

Claims (8)

1. a kind of flame retardant type Emulsificated asphalt water-proof painting material, which is characterized in that the water-repellent paint includes 65% first component and 35% Second component, wherein first component includes pitch, Ceramic silicon rubber powder, anionic surfactant, softening oil, deionized water, second Component includes fire-proof packing, fire retardant；The fire-proof packing is made of basic magnesium carbonate, basic copper carbonate, silica.
2. a kind of flame retardant type Emulsificated asphalt water-proof painting material according to claim 1, which is characterized in that the first component include with Lower raw material：
3. according to a kind of arbitrary flame retardant type Emulsificated asphalt water-proof painting material of claims 1 or 2, which is characterized in that it is described it is cloudy from Sub- surfactant includes at least one kind in Disodium sulfosuccinate, neopelex, fatty alcohol-ether sodium sulfate.
4. according to a kind of arbitrary flame retardant type Emulsificated asphalt water-proof painting material of claims 1 or 2, which is characterized in that the softening Oil includes at least one kind in turpentine oil, castor oil, palm oil.
5. a kind of flame retardant type Emulsificated asphalt water-proof painting material according to claim 1, which is characterized in that the component B include with Lower raw material：
100 parts of fire-proof packing；
3-7 parts of fire retardant.
6. according to claim 1 or a kind of 5 arbitrary flame retardant type Emulsificated asphalt water-proof painting materials, which is characterized in that the fire prevention Filler includes following weight percent component：Basic magnesium carbonate 40-50%, basic copper carbonate 20-25%, silica 30- 35%.
7. according to claim 1 or a kind of 5 arbitrary flame retardant type Emulsificated asphalt water-proof painting materials, which is characterized in that described fire-retardant Agent includes at least one kind in antimony oxide, zinc borate, pentaerythritol phosphate, tributyl phosphate.
8. a kind of preparation method of flame retardant type Emulsificated asphalt water-proof painting material as described in claim any one of 1-7, which is characterized in that Detailed process is as follows：Pitch and softening oil are heated to 150 DEG C, add Ceramic silicon rubber powder, anionic surfactant And deionized water, after homogeneous cooling, obtain first component；Weight percent mixing basic magnesium carbonate, basic copper carbonate, titanium dioxide Silicon obtains fire-proof packing, then is stirred evenly with fire retardant, obtains second component, and is scattered in first component to get the flame retardant type Emulsificated asphalt water-proof painting material.
CN201810475231.6A 2018-05-17 2018-05-17 A kind of flame retardant type Emulsificated asphalt water-proof painting material and preparation method thereof Pending CN108587463A (en)