CN106367869B - A kind of preparation method of the non-latex high-elasticity bandage of water proofing property - Google Patents

A kind of preparation method of the non-latex high-elasticity bandage of water proofing property Download PDF

Info

Publication number
CN106367869B
CN106367869B CN201610743111.0A CN201610743111A CN106367869B CN 106367869 B CN106367869 B CN 106367869B CN 201610743111 A CN201610743111 A CN 201610743111A CN 106367869 B CN106367869 B CN 106367869B
Authority
CN
China
Prior art keywords
elasticity
preparation
bandage
refining
base fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610743111.0A
Other languages
Chinese (zh)
Other versions
CN106367869A (en
Inventor
赵晋
吴义香
高为民
许文松
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Province Kang Fu Medical Products Co Ltd
Original Assignee
Anhui Province Kang Fu Medical Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Province Kang Fu Medical Products Co Ltd filed Critical Anhui Province Kang Fu Medical Products Co Ltd
Priority to CN201610743111.0A priority Critical patent/CN106367869B/en
Publication of CN106367869A publication Critical patent/CN106367869A/en
Application granted granted Critical
Publication of CN106367869B publication Critical patent/CN106367869B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of preparation methods of the non-latex high-elasticity bandage of water proofing property, include the following steps：S1, fabric selection；It is S2, concise：Water and waterproof reinforcing material is added in the fluid cylinder of continuous concise machinery, Base fabric is refined using continuous refining machinery, reaction tower is entered back into after refining；S3, washing；S4, elasticity processing；S5, arrangement：It by warp warping restocking, then threads, presses people's hold-down roll, replace filling density gear, the bandage produced that is switched on enters sizing machinery and carries out shaping.The elastic force that bandage is prepared in the present invention has reached 300% or more, it can be used directly using disposable mode and needing to wrap up and fixed skin part, it is light, ventilative, comfort is fine, and due to its non-latex component, reduce the injury to latex allergy crowd, and in preparation process, after the processing of waterproof reinforcing material, the excellent water resistance of bandage of the present invention is imparted, wound can effectively be avoided to meet talent for swimming dye.

Description

A kind of preparation method of the non-latex high-elasticity bandage of water proofing property
Technical field
The present invention relates to the preparation method of bandage more particularly to a kind of preparation methods of the non-latex high-elasticity bandage of water proofing property.
Background technology
Bandage is broadly divided into two major classes currently on the market：One kind is the fabric of sponge material, it can be relatively good Definitely fixed and protective effect, but move that comparison is heavy is restricted；One kind is analogous to the series derivates of rubber In conjunction with certain chemical fibre fabric, such product is relatively frivolous but elastic bad.
The water resistance of bandage and elastic force cannot be satisfied actual demand in the prior art, therefore a kind of high there is an urgent need for developing Elastic water-proof non-latex high-elasticity bandage solves demand in the prior art.
Invention content
To solve technical problem present in background technology, the present invention proposes a kind of system of the non-latex high-elasticity bandage of water proofing property Preparation Method.
A kind of preparation method of the non-latex high-elasticity bandage of water proofing property proposed by the present invention, includes the following steps：
S1, fabric selection：Selection weft yarn is 100% cotton yarn, warp by exposed spandex thread, colour of skin low elastic polyester filament and Raw white spandex is made as base fabric；
It is S2, concise：Water and waterproof reinforcing material are added in the fluid cylinder of continuous concise machinery, it is right using continuous refining machinery Base fabric is refined, and reaction tower is entered back into after refining, and at 100-110 DEG C, Base fabric exists for temperature control in tower Dwell time in the tower control is reacted in 45-60min；
S3, washing：The Base fabric come out from reaction tower is passed through rinsing bowl, and washing time is controlled in 4-6min；
S4, elasticity processing：Base fabric after refining utilizes 90-98 DEG C of high-temperature water and fabric in liquid-flow dyeing machine Warp thread, the weft yarn of base fabric in process are in relaxed state to obtain elasticity；
S5, arrangement：It by warp warping restocking, then threads, presses people's hold-down roll, replace filling density gear, be switched on and produce Bandage enters sizing machinery, through 180-200 DEG C of high temperature, rotating speed 1000-1200r/min, after sizing elastic force be 300% with On.
Preferably, in S1, in warp, the weight ratio of exposed spandex thread, colour of skin low elastic polyester filament and raw white spandex is 1-2： 3-5：4-6.
Preferably, in S1, the fiber number of exposed spandex thread is 420D.
Preferably, in S1, the fiber number of colour of skin low elastic polyester filament is 150D.
Preferably, in S1, the fiber number of raw white spandex is 150D.
Preferably, in S2, the temperature of refining is 65-75 DEG C, and the time of refining is 2-5h.
Preferably, in S2, waterproof reinforcing material is prepared by following technique：By polyvinylpyrrolidone dissolving and positive penta Alcohol is uniformly mixed, ultrasonic 40-50min, and absolute alcohol, deionized water and sodium citrate solution is then added and is uniformly mixed, then Ammonium hydroxide is added to be uniformly mixed, tetraethyl orthosilicate is then added, ultrasonic disperse 1-3min is then anti-in 75-85 DEG C of oil bath pan 16-20h is answered, be washed with deionized 1-3 times and is centrifuged, centrifugal rotational speed 3800-4200r/min, then in 45-55 DEG C Dry 2-4h finally obtains waterproof reinforcing material in baking oven.
Preferably, in S2, in the preparation process of waterproof reinforcing material, polyvinylpyrrolidone, sodium citrate solution and just The weight ratio of tetraethyl orthosilicate is 2-5：1-3：2-4.
A kind of preparation method of the non-latex high-elasticity bandage of water proofing property of the present invention, includes the following steps：S1, fabric selection；S2、 It is concise：Addition water and waterproof reinforcing material in the fluid cylinder of continuous concise machinery, using continuous refining machinery to Base fabric into Row refining, reaction tower is entered back into after refining；S3, washing；S4, elasticity processing；S5, arrangement：By warp warping restocking, then wear Line presses people's hold-down roll, replaces filling density gear, and the bandage produced that is switched on enters sizing machinery and carries out shaping.It is prepared by the present invention The elastic force for obtaining bandage has reached 300% or more, can be used directly using disposable mode and is needing to wrap up and fixed skin Skin position, it is light, ventilative, comfort is fine, and due to its non-latex component, reduce the injury to latex allergy crowd, and In preparation process, after the processing of waterproof reinforcing material, the excellent water resistance of bandage of the present invention is imparted, can effectively be kept away Exempt from wound and meets talent for swimming dye.
Specific implementation mode
The present invention is described in detail with reference to specific embodiment, it should be appreciated that embodiment is served only for illustrating this hair It is bright, rather than for limiting the invention, any modification made on the basis of the present invention, equivalent replacement etc. are in this hair In bright protection domain.
Embodiment 1
A kind of preparation method of the non-latex high-elasticity bandage of water proofing property proposed by the present invention, includes the following steps：
S1, fabric selection：Selection weft yarn is 100% cotton yarn, and warp is by the exposed spandex thread that fiber number is 420D, fiber number The raw white spandex that colour of skin low elastic polyester filament and fiber number for 150D are 150D is made as base fabric；
It is S2, concise：Water and waterproof reinforcing material are added in the fluid cylinder of continuous concise machinery, it is right using continuous refining machinery Base fabric is refined, and the temperature of refining is 70 DEG C, and the time of refining is 3.5h, and reaction tower is entered back into after refining, Temperature control is at 105 DEG C in tower, and Base fabric is in reaction dwell time in the tower control in 52.5min, wherein waterproof reinforcing material It is prepared by following technique：3.5 parts of polyvinylpyrrolidone dissolvings and n-amyl alcohol are uniformly mixed by weight, ultrasound Then 45min is added absolute alcohol, deionized water and 2 parts of sodium citrate solutions and is uniformly mixed, it is equal to be subsequently added into ammonium hydroxide mixing It is even, 3 parts of tetraethyl orthosilicates are then added, then ultrasonic disperse 2min reacts 18h in 80 DEG C of oil bath pans, uses deionized water It washs 2 times and centrifuges, centrifugal rotational speed 4000r/min, then dry 3h finally obtains waterproof enhancing in 50 DEG C of baking ovens Material；
S3, washing：The Base fabric come out from reaction tower is passed through rinsing bowl, and washing time is controlled in 5min；
S4, elasticity processing：High-temperature water and fabric base of the Base fabric in liquid-flow dyeing machine using 94 DEG C after refining Warp thread, the weft yarn of cloth in process are in relaxed state to obtain elasticity；
S5, arrangement：It by warp warping restocking, then threads, presses people's hold-down roll, replace filling density gear, be switched on and produce Bandage enters sizing machinery, and through 190 DEG C of high temperature, rotating speed 1100r/min, elastic force is 310% after sizing.
Embodiment 2
A kind of preparation method of the non-latex high-elasticity bandage of water proofing property proposed by the present invention, includes the following steps：
S1, fabric selection：Selection weft yarn is 100% cotton yarn, and warp is by the exposed spandex thread that fiber number is 420D, fiber number The raw white spandex that colour of skin low elastic polyester filament and fiber number for 150D are 150D is made as base fabric；
It is S2, concise：Water and waterproof reinforcing material are added in the fluid cylinder of continuous concise machinery, it is right using continuous refining machinery Base fabric is refined, and the temperature of refining is 65 DEG C, and the time of refining is 5h, and reaction tower, tower are entered back into after refining Interior temperature control is at 100 DEG C, and Base fabric is in reaction dwell time in the tower control in 60min, wherein waterproof reinforcing material is by such as It is prepared by lower technique：2 parts of polyvinylpyrrolidone dissolvings and n-amyl alcohol are uniformly mixed by weight, ultrasonic 50min, then Absolute alcohol, deionized water and 1 part of sodium citrate solution is added to be uniformly mixed, is subsequently added into ammonium hydroxide and is uniformly mixed, be then added 4 Then part tetraethyl orthosilicate, ultrasonic disperse 1min react 16h in 85 DEG C of oil bath pans, are washed with deionized 3 times and centrifuge Separation, centrifugal rotational speed 3800r/min, then dry 2h finally obtains waterproof reinforcing material in 55 DEG C of baking ovens；
S3, washing：The Base fabric come out from reaction tower is passed through rinsing bowl, and washing time is controlled in 6min；
S4, elasticity processing：High-temperature water and fabric base of the Base fabric in liquid-flow dyeing machine using 90 DEG C after refining Warp thread, the weft yarn of cloth in process are in relaxed state to obtain elasticity；
S5, arrangement：It by warp warping restocking, then threads, presses people's hold-down roll, replace filling density gear, be switched on and produce Bandage enters sizing machinery, and through 200 DEG C of high temperature, rotating speed 1000r/min, elastic force is 320% after sizing.
Embodiment 3
A kind of preparation method of the non-latex high-elasticity bandage of water proofing property proposed by the present invention, includes the following steps：
S1, fabric selection：Selection weft yarn is 100% cotton yarn, and warp is by the exposed spandex thread that fiber number is 420D, fiber number The raw white spandex that colour of skin low elastic polyester filament and fiber number for 150D are 150D is made as base fabric；
It is S2, concise：Water and waterproof reinforcing material are added in the fluid cylinder of continuous concise machinery, it is right using continuous refining machinery Base fabric is refined, and the temperature of refining is 75 DEG C, and the time of refining is 2h, and reaction tower, tower are entered back into after refining Interior temperature control is at 110 DEG C, and Base fabric is in reaction dwell time in the tower control in 45min, wherein waterproof reinforcing material is by such as It is prepared by lower technique：5 parts of polyvinylpyrrolidone dissolvings and n-amyl alcohol are uniformly mixed by weight, ultrasonic 40min, then Absolute alcohol, deionized water and 3 parts of sodium citrate solutions are added to be uniformly mixed, is subsequently added into ammonium hydroxide and is uniformly mixed, be then added 2 Then part tetraethyl orthosilicate, ultrasonic disperse 3min react 20h in 75 DEG C of oil bath pans, are washed with deionized 1 time and centrifuge Separation, centrifugal rotational speed 4200r/min, then dry 4h finally obtains waterproof reinforcing material in 45 DEG C of baking ovens；
S3, washing：The Base fabric come out from reaction tower is passed through rinsing bowl, and washing time is controlled in 4min；
S4, elasticity processing：High-temperature water and fabric base of the Base fabric in liquid-flow dyeing machine using 98 DEG C after refining Warp thread, the weft yarn of cloth in process are in relaxed state to obtain elasticity；
S5, arrangement：It by warp warping restocking, then threads, presses people's hold-down roll, replace filling density gear, be switched on and produce Bandage enters sizing machinery, and through 180 DEG C of high temperature, rotating speed 1200r/min, elastic force is 320% after sizing.
Embodiment 4
A kind of preparation method of the non-latex high-elasticity bandage of water proofing property proposed by the present invention, includes the following steps：
S1, fabric selection：Selection weft yarn is 100% cotton yarn, and warp is by the exposed spandex thread that fiber number is 420D, fiber number The raw white spandex that colour of skin low elastic polyester filament and fiber number for 150D are 150D is made as base fabric；
It is S2, concise：Water and waterproof reinforcing material are added in the fluid cylinder of continuous concise machinery, it is right using continuous refining machinery Base fabric is refined, and the temperature of refining is 66 DEG C, and the time of refining is 4h, and reaction tower, tower are entered back into after refining Interior temperature control is at 102 DEG C, and Base fabric is in reaction dwell time in the tower control in 59min, wherein waterproof reinforcing material is by such as It is prepared by lower technique：3 parts of polyvinylpyrrolidone dissolvings and n-amyl alcohol are uniformly mixed by weight, ultrasonic 48min, then Absolute alcohol, deionized water and 1.5 parts of sodium citrate solutions are added to be uniformly mixed, is subsequently added into ammonium hydroxide and is uniformly mixed, then add Enter 3.5 parts of tetraethyl orthosilicates, then ultrasonic disperse 1.5min reacts 17h in 82 DEG C of oil bath pans, is washed with deionized 3 Secondary and centrifuge, centrifugal rotational speed 3900r/min, then dry 2.5h finally obtains waterproof strengthening material in 52 DEG C of baking ovens Material；
S3, washing：The Base fabric come out from reaction tower is passed through rinsing bowl, and washing time is controlled in 5.5min；
S4, elasticity processing：High-temperature water and fabric base of the Base fabric in liquid-flow dyeing machine using 92 DEG C after refining Warp thread, the weft yarn of cloth in process are in relaxed state to obtain elasticity；
S5, arrangement：It by warp warping restocking, then threads, presses people's hold-down roll, replace filling density gear, be switched on and produce Bandage enters sizing machinery, and through 195 DEG C of high temperature, rotating speed 1050r/min, elastic force is 330% after sizing.
Embodiment 5
A kind of preparation method of the non-latex high-elasticity bandage of water proofing property proposed by the present invention, includes the following steps：
S1, fabric selection：Selection weft yarn is 100% cotton yarn, and warp is by the exposed spandex thread that fiber number is 420D, fiber number The raw white spandex that colour of skin low elastic polyester filament and fiber number for 150D are 150D is made as base fabric；
It is S2, concise：Water and waterproof reinforcing material are added in the fluid cylinder of continuous concise machinery, it is right using continuous refining machinery Base fabric is refined, and the temperature of refining is 74 DEG C, and the time of refining is 3h, and reaction tower, tower are entered back into after refining Interior temperature control is at 108 DEG C, and Base fabric is in reaction dwell time in the tower control in 46min, wherein waterproof reinforcing material is by such as It is prepared by lower technique：4 parts of polyvinylpyrrolidone dissolvings and n-amyl alcohol are uniformly mixed by weight, ultrasonic 42min, then Absolute alcohol, deionized water and 2.5 parts of sodium citrate solutions are added to be uniformly mixed, is subsequently added into ammonium hydroxide and is uniformly mixed, then add Enter 2.5 parts of tetraethyl orthosilicates, then ultrasonic disperse 2.5min reacts 19h in 78 DEG C of oil bath pans, is washed with deionized 1 Secondary and centrifuge, centrifugal rotational speed 4100r/min, then dry 3.5h finally obtains waterproof strengthening material in 48 DEG C of baking ovens Material；
S3, washing：The Base fabric come out from reaction tower is passed through rinsing bowl, and washing time is controlled in 5.5min；
S4, elasticity processing：High-temperature water and fabric base of the Base fabric in liquid-flow dyeing machine using 92 DEG C after refining Warp thread, the weft yarn of cloth in process are in relaxed state to obtain elasticity；
S5, arrangement：It by warp warping restocking, then threads, presses people's hold-down roll, replace filling density gear, be switched on and produce Bandage enters sizing machinery, and through 195 DEG C of high temperature, rotating speed 1050r/min, elastic force is 340% after sizing.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto, Any one skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.

Claims (7)

1. a kind of preparation method of the non-latex high-elasticity bandage of water proofing property, which is characterized in that include the following steps：
S1, fabric selection：It is 100% cotton yarn to select weft yarn, and warp is by exposed spandex thread, colour of skin low elastic polyester filament and raw white Spandex is made as base fabric；
It is S2, concise：Water and waterproof reinforcing material is added in the fluid cylinder of continuous concise machinery, using continuous refining machinery to fabric Base fabric is refined, and reaction tower is entered back into after refining, and at 100-110 DEG C, Base fabric is reacting for temperature control in tower Dwell time in the tower is controlled in 45-60min；
S3, washing：The Base fabric come out from reaction tower is passed through rinsing bowl, and washing time is controlled in 4-6min；
S4, elasticity processing：Base fabric after refining utilizes 90-98 DEG C of high-temperature water and Base fabric in liquid-flow dyeing machine Warp thread, weft yarn in process is in relaxed state to obtain elasticity；
S5, arrangement：By elasticity treated Base fabric enters sizing machinery, through 180-200 DEG C of high temperature, rotating speed 1000- 1200r/min, elastic force is 300% or more after sizing；
Wherein, in S2, waterproof reinforcing material is prepared by following technique：Polyvinylpyrrolidone dissolving and n-amyl alcohol are mixed Uniformly, then ultrasonic 40-50min is added absolute alcohol, deionized water and sodium citrate solution and is uniformly mixed, is subsequently added into ammonia Water is uniformly mixed, and tetraethyl orthosilicate is then added, then ultrasonic disperse 1-3min reacts 16- in 75-85 DEG C of oil bath pan 20h is washed with deionized 1-3 times and centrifuges, centrifugal rotational speed 3800-4200r/min, then in 45-55 DEG C of baking oven Middle dry 2-4h finally obtains waterproof reinforcing material.
2. the preparation method of the non-latex high-elasticity bandage of water proofing property according to claim 1, which is characterized in that in S1, warp In, the weight ratio of exposed spandex thread, colour of skin low elastic polyester filament and raw white spandex is 1-2：3-5：4-6.
3. the preparation method of the non-latex high-elasticity bandage of water proofing property according to claim 1 or 2, which is characterized in that naked in S1 The fiber number for revealing spandex thread is 420D.
4. the preparation method of the non-latex high-elasticity bandage of water proofing property according to claims 1 or 2 item, which is characterized in that in S1, The fiber number of colour of skin low elastic polyester filament is 150D.
5. the preparation method of the non-latex high-elasticity bandage of water proofing property according to claim 1 or 2, which is characterized in that in S1, this The fiber number of white spandex is 150D.
6. the preparation method of the non-latex high-elasticity bandage of water proofing property according to claim 1 or 2, which is characterized in that in S2, essence The temperature of refining is 65-75 DEG C, and the time of refining is 2-5h.
7. the preparation method of the non-latex high-elasticity bandage of water proofing property according to claim 1 or 2, which is characterized in that in S2, prevent In the preparation process of water reinforcing material, the weight ratio of polyvinylpyrrolidone, sodium citrate solution and tetraethyl orthosilicate is 2- 5：1-3：2-4.
CN201610743111.0A 2016-08-26 2016-08-26 A kind of preparation method of the non-latex high-elasticity bandage of water proofing property Active CN106367869B (en)