CN101956277A - Fabrics having velcro effect and made of sea island yarn and production method thereof - Google Patents
Fabrics having velcro effect and made of sea island yarn and production method thereof Download PDFInfo
- Publication number
- CN101956277A CN101956277A CN2010102571057A CN201010257105A CN101956277A CN 101956277 A CN101956277 A CN 101956277A CN 2010102571057 A CN2010102571057 A CN 2010102571057A CN 201010257105 A CN201010257105 A CN 201010257105A CN 101956277 A CN101956277 A CN 101956277A
- Authority
- CN
- China
- Prior art keywords
- typing
- finished product
- dyeing
- fabrics
- island yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses fabrics having velcro effect and made of sea island yarn and a production method thereof. The method comprises the following steps of the weaving of the sea island yarn, the sizing of gray fabrics, alkali decrement, neutralizing, dyeing, fabric drying, the forming of a semi-finished product, the forming of a finished product and the inspection of the finished product. The fabrics produced by the method have the superstrong adsorptive capacity, the velcro effect, soft handfeel and luster.
Description
Technical field:
The present invention relates to a kind of fabric and production method thereof, be specifically related to a kind of fabric with Velcro effect and production method of making by the island yarn thereof.
Background technology:
Velcro is the popular call of double buckle, it is exactly a kind of connection auxiliary material commonly used on the clothes, divide the male and female two sides, one side is the fiber of small, flexible, and another side is harder thing of grabbing as little Mao, once just sticked together, be subjected under certain pulling force, whippy colluding is straightened, loose glue from the pile loop and opening, recover original type that colludes then again, folding can reach more than 10,000 friendships so repeatedly.
The island yarn is the form of two kinds of polymer overmold, comprises sea component and island component.Common island yarn fiber fabric generally all is to have the peach face effect at present.The island yarn is carried out some special treatments, make its fabric have the Velcro effect and yet there are no report.
Summary of the invention:
The purpose of this invention is to provide a kind of strong absorption affinity that has, as Velcro can stick human body, have the fabric and the production method thereof made by the island yarn of soft feel.
The present invention carries out the alkali decrement to the island yarn and opens fine the processing, go the sea component of island yarn fiber is molten, the island component is separated form superfine fibre, thereby obtain the superfine fibre fabric of unique style, thereby increase the specific area of fabric, generation has the effect of Velcro, thereby has realized purpose of the present invention.
The fabric of being made by the island yarn with Velcro effect of the present invention is produced by following method, and this method comprises: with the island yarn weave cotton cloth, grey cloth typing, alkali decrement treatment, neutralization, dyeing, dried cloth, semi-finished product typing, finished product typing, finished product inspection:
The typing condition of described grey cloth typing is: setting temperature is 180～185 ℃, and machine speed is 15～20m/min;
Described alkali decrement treatment is: with the typing grey cloth in bath raio 1: 8～11, add NaOH to concentration be 15～18g/l, at 75～90 ℃, insulation 70～75min, and then wash more than 2 times, reduction rate is 37～40%, add the HAc neutralization then, water at normal temperature is washed till to be waited to dye only;
The typing condition of described semi-finished product typing is: setting temperature is 180～185 ℃, setting machine joint number 8, and machine speed is 18～22m/min;
The typing condition of described finished product typing is: setting temperature is 110～115 ℃, and shaping time is 10 seconds, setting machine joint number 8.
Described dyeing is preferably: contain DISPERSE DYES, 1～1.5g/l anti-creasing agent, 1.5～2g/l dispersant and 0.3～0.5% (owf) levelling agent of high fastness in the dyeing liquor, dyeing temperature is 130 ℃-135 ℃, dyes the back and carries out reduction cleaning with reductant, neutralization.Through this kind colouring method, can solve the normal dyeing method dyeing of this kind material is caused problems such as folding line, dyeing flower, fastness.
The present invention is by selection and control to alkaline agent concentration, decrement bath raio, temperature, time and weight-loss ratio, make molten the going of sea component in the yarn fiber of island, the island component is separated form superfine fibre, obtain the superfine fibre fabric of unique style, thereby increase the specific area of fabric, generation has the effect of Velcro.Alkali decrement treatment technology of the present invention makes molten the going of sea component of island yarn fiber just, island component not damaged, make it separate form superfine fibre, may be thereby avoid owing to alkali decrement deficiency, can't bring into play the quality of superfine fibre, feel is coarse, adsorptivity is not enough, decrement is too high, causes island component damage easily, and decrement is excessive, can make fiber composition part tendering, a powerful difficult problem that descends.The fabric of producing through production method of the present invention has superpower adsorption capacity, and is soft, and more glossy.
The specific embodiment:
Below be to further specify to of the present invention, rather than limitation of the present invention.
Embodiment 1:
50D island yarn+40D spandex plain cloth 103.87kg, dyeing water ratio is 1: 11, color: yellowish pink
Through deciding the typing of base machine: setting temperature is 180 ℃, machine speed 15m/min.
The alkali decrement treatment: under 1: 8 condition of bath raio, adding NaOH is 18g/l to final concentration through the grey cloth of typing, and at 75 ℃, insulation 70min, and then wash 2 times adds the HAc neutralization of 1g/l, and water at normal temperature is washed till to be waited to dye only.This alkali decrement treatment: the former weight of grey cloth: 320g/m
2, weight after the decrement: 283g/m
2, reduction rate: 37%.
Dyeing and condition: according to above-mentioned dyeing water ratio, in dyeing liquor, add FIBREGUARD CN (anti-creasing agent) 1.173kg, univadine DPS (dispersant) 2.346kg, ADVANLEV CWD (levelling agent) 0.383kg, and 0.03% (owf) NAVY S2GRL of high fastness, 1.5% (owf) UVITEX RSB, 0.03% (owf) MEKICRONBLUE WXF, dyeing temperature is 130 ℃, dyeing time is 20 minutes, and then add reductant (6.7kgNaOH and 4.5kg sodium hydrosulfite) cleaning, at last with 0.58kg HAC neutralization.
Behind dried cloth, finalize the design through semi-finished product: the typing condition is again, setting temperature is 180 ℃, and the setting machine joint number is 8, and machine speed is 18m/min.
And then through the finished product typing, its typing condition is: setting temperature is 115 ℃, and shaping time is 10 seconds, and the setting machine joint number is 8, after above-mentioned processing, can obtain finished product.
This finished product is after testing:
Fastness assessment: wash 3.5 grades of AATCC 5 times
Adsorptivity compares: the employing method is that this product and common like product are cut to the wide fabric swatch of the long 10cm of 1m, is placed on earlier on the same wood-block, and wood-block sees that gradually to movement in vertical direction fabric swatch can fall down on a certain angle then.Present common like product will fall at gradient 30 degree, and the product that present embodiment system is produced just can fall at 80 degree.This shows that the present embodiment finished product has strong adsorption capacity, have the effect of Velcro, can stick on the person on the certain angle.And this finished product is soft, and more glossy.
Embodiment 2:
50D island yarn plain cloth 31.75kg, dyeing water ratio: 1: 8, color: off-white
Through deciding the typing of embryo machine: setting temperature is 185 ℃, machine speed 20m/min;
The alkali decrement treatment: through the grey cloth of typing under 1: 11 condition of bath raio, add NaOH to final concentration be 15g/l, under 90 ℃, insulation 70min, and then wash 3 times, add the HAc neutralization of 1g/l, water at normal temperature is washed till to be waited to dye only.This alkali decrement treatment: the former weight of grey cloth: 325g/m2, weight after the decrement: 285g/m2, reduction rate: 40%;
Dyeing and condition: according to above-mentioned dyeing water ratio, in dyeing liquor, add FIBREGUARD CN (anti-creasing agent) 0.3kg, univadine DPS (dispersant) 0.46kg, ADVANLEV CWD (levelling agent) 0.1kg, sky dyes, dyeing temperature is 135 ℃, dyeing time is 10 minutes, adds 0.58kg HAC neutralization at last.
Behind dried cloth, finalize the design through semi-finished product: the typing condition is again, setting temperature is 185 ℃, and the setting machine joint number is 8, and machine speed is 20m/min.
The finished product typing: the typing condition is: setting temperature is 110 ℃, and shaping time is 10 seconds, and the setting machine joint number is 8, obtains finished product after this is handled.
This finished product is after testing:
Fastness assessment: wash 4 grades of 5 AATCC
Adsorptivity compares: the employing method is that this product and common like product are cut to the wide fabric swatch of the long 10cm of 1m, is placed on earlier on the same wood-block, and wood-block sees that gradually to movement in vertical direction fabric swatch can fall down on a certain angle then.Present common like product will fall at gradient 30 degree, and the product that present embodiment system is produced just can fall at 80 degree.This shows that the present embodiment finished product has strong adsorption capacity, have the effect of Velcro, can stick on the person on the certain angle.And this finished product is soft, and more glossy.
Embodiment 3:
The special island of 50D yarn+40D spandex plain cloth 52.16kg, the water ratio: 1: 10, color: khaki
Through deciding the typing of embryo machine: setting temperature is 180 ℃, machine speed 18m/min;
The alkali decrement treatment: under 1: 9 condition of bath raio, adding NaOH is 16g/l to final concentration through the grey cloth of typing, and at 80 ℃, insulation 75min, and then wash 4 times adds the HAc neutralization of 1g/l, and water at normal temperature is washed till to be waited to dye only.This alkali decrement treatment: 315g/m
2, weight after the decrement: 278g/m
2, reduction rate: 38%.
Dyeing and condition: according to above-mentioned dyeing water ratio, in dyeing liquor, add FIBREGUARD CN (anti-creasing agent) 0.782kg, univadine DPS (dispersant) 0.8kg, ADVANLEV CWD (levelling agent) 0.26kg, and 0.03% (owf) NAVY S2GRL of high fastness, 0.2% (owf) MEKICRON BLUE WXF, dyeing temperature is 130 ℃, dyeing time is 20 minutes, add reductant (1.67kg NaOH and 2.08kg sodium hydrosulfite) then and clean, add the 0.3kgHAc neutralization at last.
Behind dried cloth, finalize the design through semi-finished product: the typing condition is again, setting temperature is 180 ℃, and the setting machine joint number is 8, and machine speed is 22m/min.
And then through the finished product typing, its typing condition is: setting temperature is 115 ℃, and shaping time is 10 seconds, and the setting machine joint number is 8, after above-mentioned processing, can obtain finished product.
Finished product test:
Fastness assessment: wash 3.5 grades of 5 AATCC.
Adsorptivity compares: the employing method is that this product and common like product are cut to the wide fabric swatch of the long 10cm of 1m, is placed on earlier on the same wood-block, and wood-block sees that gradually to movement in vertical direction fabric swatch can fall down on a certain angle then.Present common like product will fall at gradient 30 degree, and the product that present embodiment system is produced is that 75 degree just can fall in gradient.This shows that the present embodiment finished product has strong adsorption capacity, have the effect of Velcro, can stick on the person on the certain angle.And this finished product is soft, and more glossy.
Claims (3)
1. the manufacturing method of fabrics of being made by the island yarn with Velcro effect is characterized in that, comprising: with the island yarn weave cotton cloth, grey cloth typing, alkali decrement treatment, neutralization, dyeing, dried cloth, semi-finished product typing, finished product typing and finished product inspection:
The typing condition of described grey cloth typing is: setting temperature is 180～185 ℃, and machine speed is 15～20m/min;
Described alkali decrement treatment is: with the typing grey cloth in bath raio 1: 8～11, add NaOH to concentration be 15～18g/l, at 75～90 ℃, insulation 70～75min, and then wash more than 2 times, reduction rate is 37～40%, add the HAc neutralization then, water at normal temperature is washed till to be waited to dye only;
The typing condition of described semi-finished product typing is: setting temperature is 180～185 ℃, setting machine joint number 8, and machine speed is 18～22m/min;
The typing condition of described finished product typing is: setting temperature is 110～115 ℃, and shaping time is 10 seconds, setting machine joint number 8.
2. the manufacturing method of fabrics of making by the island yarn according to claim 1 with Velcro effect, it is characterized in that, described dyeing is: the DISPERSE DYES, 1～1.5g/l anti-creasing agent, 1.5～2g/l dispersant and 0.3～0.5% (owf) levelling agent that contain high fastness in the dyeing liquor, dyeing temperature is 130～135 ℃, dye the back and carry out reduction cleaning, neutralization with reductant.
3. fabric that the manufacturing method of fabrics of being made by the island yarn with Velcro effect according to claim 1 is produced.