CN106366781A - Reinforcing agent for wall surface - Google Patents
Reinforcing agent for wall surface Download PDFInfo
- Publication number
- CN106366781A CN106366781A CN201610752240.6A CN201610752240A CN106366781A CN 106366781 A CN106366781 A CN 106366781A CN 201610752240 A CN201610752240 A CN 201610752240A CN 106366781 A CN106366781 A CN 106366781A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylic emulsion
- styrene
- reinforcing agent
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a reinforcing agent for a wall surface, and belongs to the field of building reinforcing agent. The reinforcing agent for the wall surface is prepared by the following components by quality: 650-850 parts of water, 50-100 parts of styrene-acrylic emulsion containing AA functional monomer, 70-150 parts of common styrene-acrylic emulsion, 3 parts of an antifoaming agent, 2 parts of a preservative, 10-40 parts of aluminum oxide transparent liquid, and 40-60 parts of a thickener. The reinforcing agent for the wall surface has the characteristics of low viscosity, good permeability, low water absorption and strong closure property.
Description
Technical field
The present invention relates to a kind of metope strengthening agent, belong to building strengthening agent field.
Background technology
Before room handed over by new house at present, development of real estate chamber of commerce metope and one layer of putty of ceiling brushing indoors, to strengthen friendship room
When perception, but this this putty is non-watertight, non-moistureproof, simultaneously easy dry linting, and also very poor with basic unit cohesive force, therefore owner is in finishing
Before, all this layer of powder of lacquer putty for use on shovel can be fallen.This can cause unnecessary cost to increase.Current building strengthening agent exists and basic unit
Not, the intensity of the putty layer that strengthening agent is formed itself is not also high simultaneously, and the penetration depth of strengthening agent for the cohesive force of metope
The problems such as not deep.
Content of the invention
The technical problem to be solved is: provide a kind of metope strengthening agent, it solve strengthening agent exist with
Not, the intensity of the putty layer that strengthening agent is formed itself is not also high simultaneously, and the infiltration of strengthening agent for the cohesive force of base course wall
The not deep problem of depth.
The technical problem to be solved takes technical scheme below to realize:
A kind of metope strengthening agent, it is formulated by the component of following mass fraction: 650～850 parts of water, containing aa function monomer
50～100 parts of styrene-acrylic emulsion, 70～150 parts of common styrene-acrylic emulsion, 3 parts of defoamer, 2 parts of preservative, aluminium oxide transparent liquid 10
～40 parts, 40～60 parts of thickening agent.
As preferred embodiment, the described styrene-acrylic emulsion containing aa function monomer contains 4～5% aa function monomer.
As preferred embodiment, described thickening agent is alkali swelling type thickening agent.
The invention has the beneficial effects as follows:
(1) adopt the styrene-acrylic emulsion containing aa function monomer, on the one hand can form metal corsslinking key with metal ion, strengthen and base
The cohesive force of layer, can reinforce the intensity of putty layer itself simultaneously, on the other hand, react with filler, the former putty layer of pineization, strengthen and add
Gu the penetration depth of agent, but the styrene-acrylic emulsion containing aa function monomer is more, can react with filler and cause a large amount of bubbles, thus adopt
It is balanced with common styrene-acrylic emulsion compound system.
(2) common styrene-acrylic emulsion, can improve hydrophobicity, thus having certain protection against the tide to strengthening putty layer intensity after film forming
Function；
(3) alkali swelling type thickening agent no thickening power in acid system, thus ensureing that product is very low in early stage viscosity, makes product
There is good permeability, but form thickening after later stage and alkali substance reaction, prevent sagging from producing, simultaneously therefore thickening agent water conservation
Property is poor, can the moisture in system quickly volatilize；
(4) aluminium oxide transparent liquid acts primarily as strengthening action.
Specific embodiment
In order to be easy to understand to the technological means of the present invention, creation characteristic, reached purpose and effect, further below
Illustrate the present invention.
A kind of metope strengthening agent, it is formulated by the component of following mass fraction: 650～850 parts of water, containing aa function
50～100 parts of the styrene-acrylic emulsion of monomer, 70～150 parts of common styrene-acrylic emulsion, 3 parts of defoamer, 2 parts of preservative, aluminium oxide is transparent
10～40 parts of liquid, 40～60 parts of thickening agent.
Styrene-acrylic emulsion containing aa function monomer contains 4～5% aa function monomer.Thickening agent is alkali swelling type thickening agent
(hase).
Preparation technology:
First according to match ratio precise, weigh and put into jc/t681-2005 planetary cement mortar mixer stirring at low speed and join
Ratio material, stirs 2 minutes.
Operation instruction:
(1) construction temperature should be 5 DEG C～35 DEG C, and relative humidity should not be higher than 80%；
(2) basal plane must reach dustless, free from flaw, no loose, smooth；
(3) twice interfacial agents is brushed on the basal plane cleared up, after a brushing after its surface is done, then brushes second time.
Embodiment 1
It is formulated by the component of following mass fraction: 745 parts of water, 80 parts of the styrene-acrylic emulsion containing aa function monomer, commonly
100 parts of styrene-acrylic emulsion, 3 parts of defoamer, 2 parts of preservative, 30 parts of aluminium oxide transparent liquid, 40 parts of thickening agent.
Styrene-acrylic emulsion containing aa function monomer contains 4～5% aa function monomer.Thickening agent is alkali swelling type thickening agent
(hase).
According to above-mentioned preparation technology and operation instruction construction, property indices are as shown in the table:
The permeability that be can be seen that the present invention by the testing result of embodiment 1 is high, and water absorption rate is low, and adhesion strength is very high.
Ultimate principle and principal character and the advantages of the present invention of the present invention have been shown and described above.The technology of the industry
Personnel it should be appreciated that the present invention is not restricted to the described embodiments, without departing from the spirit and scope of the present invention, this
Bright also have various changes and modifications, these changes and improvements both fall within scope of the claimed invention.Application claims
Protection domain is by appending claims and its equivalent thereof.
Claims (3)
1. a kind of metope strengthening agent is it is characterised in that it is formulated by the component of following mass fraction: 650～850 parts of water,
50～100 parts of styrene-acrylic emulsion containing aa function monomer, 70～150 parts of common styrene-acrylic emulsion, 3 parts of defoamer, 2 parts of preservative,
10～40 parts of aluminium oxide transparent liquid, 40～60 parts of thickening agent.
2. according to claim 1 a kind of metope strengthening agent it is characterised in that: the described styrene-acrylic emulsion containing aa function monomer
Containing 4～5% aa function monomer.
3. according to claim 1 a kind of metope strengthening agent it is characterised in that: described thickening agent be alkali swelling type thickening agent.