CN106363184B - A kind of sintering process of kettle - Google Patents
A kind of sintering process of kettle Download PDFInfo
- Publication number
- CN106363184B CN106363184B CN201510432408.0A CN201510432408A CN106363184B CN 106363184 B CN106363184 B CN 106363184B CN 201510432408 A CN201510432408 A CN 201510432408A CN 106363184 B CN106363184 B CN 106363184B
- Authority
- CN
- China
- Prior art keywords
- kettle
- cooling
- bottle body
- sintering
- water kettle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of sintering process of kettle, it is characterised in that:The technique includes the following steps:A, after silver being carried out Refining, melting is carried out, forms silver paste;B, the bottle body component of different metal material is cast by reverse mould, bottle body component is combined as complete kettle;By each bottle body section into water kettle body;C, silver paste is injected between each bottle body component of water kettle body in linking seam, carries out stage cooling;D, the water kettle body through cooling is sintered;E, the surface of water kettle body is sintered by ceramic glaze;F, numerical control sandblasting is carried out to water kettle body, polished at bottle body sintering.Advantage is:The present invention provides a kind of sintering process of kettle, the technique efficiently solves the problems, such as to be fitted into existing hollow joint between different metal, improve the stability of entire kettle, different metal material is realized simultaneously to present in the form of different component respectively, metal product technique level is improved, adapts to precious metal marketplace development.
Description
【Technical field】
The present invention relates to a kind of manufacture craft of kettle, more particularly to a kind of sintering process of kettle.
【Background technology】
Kettle in the market is generally all molded using a kind of material, such as ceramic kettle only has ceramics, and plastic cement pot is only moulded
Glue, other pot class product bottle bodies generally also only have a kind of material, and especially in metal class kettle field, single material makes kettle
Style cannot meet the aesthetic needs of all kinds of consumer groups, and in order to win the market of objects made from precious metals, some producers pass through engagement
Mode different metal is combined together, but the process is more complicated, and this common juncture, it is impossible to ensure product
Quality, it will usually it is cracked, and be unfavorable for being surface-treated so that manufacture cost is higher, and ornamental value can not still expire
The aesthetic needs of all kinds of consumer groups of foot, with the development and progress of society, by noble metal application life arts already into
For industry focus of attention, the manufacture craft for improving objects made from precious metals is also extremely urgent.
【Invention content】
It is an object of the invention to overcome the deficiencies of the prior art and provide a kind of sintering process of kettle, the technique is effective
It solves the problems, such as to be fitted into existing hollow joint between different metal, improves the stability of entire kettle, while realize different gold
Belong to material to present in the form of different component respectively, improve metal product technique level, adapt to precious metal marketplace development.
The technical proposal of the invention is realized in this way:A kind of sintering process of kettle of the present invention, improvements exist
In:The technique includes the following steps:
A, after silver being carried out Refining, melting is carried out, forms silver paste;
B, the bottle body component of different metal material is cast by reverse mould, bottle body component is combined as complete kettle;It will be each
Bottle body section is into water kettle body;
C, the silver paste in step A is injected into step B between each bottle body component of water kettle body in linking seam, into row order
Section cooling, first stage, cooling temperature are 200 DEG C -300 DEG C, and cooling time is 20 minutes;Second stage, cooling temperature 100
DEG C -150 DEG C, cooling time is 15 minutes;Phase III, cooling temperature are 45 DEG C, and cooling time is 45 minutes;
D, the water kettle body through cooling in step C is sintered, sintering temperature is 500 DEG C -900 DEG C, sintering time 1
Hour was to 1.5 hours;
E, the surface of the water kettle body in step D is sintered by ceramic glaze, sintering temperature is 800 DEG C;
F, numerical control sandblasting is carried out to the water kettle body in step E, polished at bottle body sintering.
Preferably, in step A, melting is carried out to silver, smelting temperature is 800 DEG C -1500 DEG C.
Preferably, the cooling temperature of first stage is 260 DEG C in step C, the cooling temperature of second stage is 120 DEG C.
Preferably, sintering temperature is 600 DEG C in step D.
The beneficial effects of the present invention are:The present invention provides a kind of sintering process of kettle, which efficiently solves
Existing hollow joint problem is fitted between different metal, improves the stability of entire kettle, while realize different metal material
It is presented in the form of different component respectively, improves metal product technique level, adapt to precious metal marketplace development.
【Specific embodiment】
The invention will be further described With reference to embodiment:
Embodiment 1
In the present embodiment, a kind of sintering process of kettle is disclosed, which includes the following steps:
A, after silver being carried out Refining, melting is carried out, forms silver paste;
B, the bottle body component of different metal material is cast by reverse mould, bottle body component is combined as complete kettle;It will be each
Bottle body section is into water kettle body;
C, the silver paste in step A is injected into step B between each bottle body component of water kettle body in linking seam, into row order
Section cooling, first stage, cooling temperature are 200 DEG C, and cooling time is 20 minutes;Second stage, cooling temperature is 100 DEG C, cold
But the time is 15 minutes;Phase III, cooling temperature are 45 DEG C, and cooling time is 45 minutes;
D, the water kettle body through cooling in step C is sintered, sintering temperature be 500 DEG C, sintering time for 1 hour extremely
1.5 hour;
E, the surface of the water kettle body in step D is sintered by ceramic glaze, sintering temperature is 800 DEG C;
F, numerical control sandblasting is carried out to the water kettle body in step E, polished at bottle body sintering.
Embodiment 2
In the present embodiment, a kind of sintering process of kettle is disclosed, which includes the following steps:
A, after silver being carried out Refining, melting is carried out, forms silver paste;
B, the bottle body component of different metal material is cast by reverse mould, bottle body component is combined as complete kettle;It will be each
Bottle body section is into water kettle body;
C, the silver paste in step A is injected into step B between each bottle body component of water kettle body in linking seam, into row order
Section cooling, first stage, cooling temperature are 300 DEG C, and cooling time is 20 minutes;Second stage, cooling temperature is 150 DEG C, cold
But the time is 15 minutes;Phase III, cooling temperature are 45 DEG C, and cooling time is 45 minutes;
D, the water kettle body through cooling in step C is sintered, sintering temperature be 450 DEG C, sintering time for 1 hour extremely
1.5 hour;
E, the surface of the water kettle body in step D is sintered by ceramic glaze, sintering temperature is 800 DEG C;
F, numerical control sandblasting is carried out to the water kettle body in step E, polished at bottle body sintering.
Embodiment 3
In the present embodiment, a kind of sintering process of kettle is disclosed, which includes the following steps:
A, after silver being carried out Refining, melting is carried out, forms silver paste;
B, the bottle body component of different metal material is cast by reverse mould, bottle body component is combined as complete kettle;It will be each
Bottle body section is into water kettle body;
C, the silver paste in step A is injected into step B between each bottle body component of water kettle body in linking seam, into row order
Section cooling, first stage, cooling temperature are 300 DEG C, and cooling time is 20 minutes;Second stage, cooling temperature is 100 DEG C, cold
But the time is 15 minutes;Phase III, cooling temperature are 45 DEG C, and cooling time is 45 minutes;
D, the water kettle body through cooling in step C is sintered, sintering temperature is 500 DEG C, and sintering time is 1 hour;
E, the surface of the water kettle body in step D is sintered by ceramic glaze, sintering temperature is 800 DEG C;
F, numerical control sandblasting is carried out to the water kettle body in step E, polished at bottle body sintering.
Embodiment 4
In the present embodiment, a kind of sintering process of kettle is disclosed, which includes the following steps:
A, after silver being carried out Refining, melting is carried out, forms silver paste;
B, the bottle body component of different metal material is cast by reverse mould, bottle body component is combined as complete kettle;It will be each
Bottle body section is into water kettle body;
C, the silver paste in step A is injected into step B between each bottle body component of water kettle body in linking seam, into row order
Section cooling, first stage, cooling temperature are 300 DEG C, and cooling time is 20 minutes;Second stage, cooling temperature is 150 DEG C, cold
But the time is 15 minutes;Phase III, cooling temperature are 45 DEG C, and cooling time is 45 minutes;
D, the water kettle body through cooling in step C is sintered, sintering temperature is 900 DEG C, and sintering time is 1 hour;
E, the surface of the water kettle body in step D is sintered by ceramic glaze, sintering temperature is 800 DEG C;
F, numerical control sandblasting is carried out to the water kettle body in step E, polished at bottle body sintering.
Embodiment 5
In the present embodiment, a kind of sintering process of kettle is disclosed, which includes the following steps:
A, after silver being carried out Refining, melting is carried out, forms silver paste;
B, the bottle body component of different metal material is cast by reverse mould, bottle body component is combined as complete kettle;It will be each
Bottle body section is into water kettle body;
C, the silver paste in step A is injected into step B between each bottle body component of water kettle body in linking seam, into row order
Section cooling, first stage, cooling temperature are 260 DEG C, and cooling time is 20 minutes;Second stage, cooling temperature is 120 DEG C, cold
But the time is 15 minutes;Phase III, cooling temperature are 45 DEG C, and cooling time is 45 minutes;
D, the water kettle body through cooling in step C is sintered, sintering temperature is 600 DEG C, and sintering time is small for 1.2
When;
E, the surface of the water kettle body in step D is sintered by ceramic glaze, sintering temperature is 800 DEG C;
F, numerical control sandblasting is carried out to the water kettle body in step E, polished at bottle body sintering.
Embodiment 6
In the present embodiment, a kind of sintering process of kettle is disclosed, which includes the following steps:
A, after silver being carried out Refining, melting is carried out, forms silver paste;
B, the bottle body component of different metal material is cast by reverse mould, bottle body component is combined as complete kettle;It will be each
Bottle body section is into water kettle body;
C, the silver paste in step A is injected into step B between each bottle body component of water kettle body in linking seam, into row order
Section cooling, first stage, cooling temperature are 300 DEG C, and cooling time is 20 minutes;Second stage, cooling temperature is 150 DEG C, cold
But the time is 15 minutes;Phase III, cooling temperature are 45 DEG C, and cooling time is 45 minutes;
D, the water kettle body through cooling in step C is sintered, sintering temperature is 700 DEG C, and sintering time is small for 1.5
When;
E, the surface of the water kettle body in step D is sintered by ceramic glaze, sintering temperature is 800 DEG C;
F, numerical control sandblasting is carried out to the water kettle body in step E, polished at bottle body sintering.
It, can be according to the type of bottle body component, accordingly in step, using different melting temperature in above-described embodiment
Degree carries out melting to silver, and smelting temperature general control is at 800 DEG C -1500 DEG C, and the activity and its metallic character of silver paste at this moment are most
It is good, convenient for fusing into one, and sound construction with each bottle body component, it is less prone to crackle.
Described above is only presently preferred embodiments of the present invention, and above-mentioned specific embodiment is not limitation of the present invention.
In the technological thought scope of the present invention, various modifications and modification can occur, all those of ordinary skill in the art according to
Upper description done retouching, modification or equivalent replacement, belong to the range that the present invention is protected.
Claims (4)
1. a kind of sintering process of kettle, it is characterised in that:The technique includes the following steps:
A, after silver is purified, melting is carried out, forms silver paste;
B, the bottle body component of different metal material is cast by reverse mould, bottle body component is combined as complete kettle;By each bottle body
Section is into water kettle body;
C, the silver paste in step A is injected into step B between each bottle body component of water kettle body in linking seam, it is cold carries out the stage
But, first stage, cooling temperature are 200 DEG C -300 DEG C, and cooling time is 20 minutes;Second stage, cooling temperature for 100 DEG C-
150 DEG C, cooling time is 15 minutes;Phase III, cooling temperature are 45 DEG C, and cooling time is 45 minutes;
D, the water kettle body through cooling in step C is sintered, sintering temperature is 500 DEG C -900 DEG C, and sintering time is 1 hour
To 1.5 hours;
E, the surface of the water kettle body in step D is sintered by ceramic glaze, sintering temperature is 800 DEG C;
F, numerical control sandblasting is carried out to the water kettle body in step E, polished at bottle body sintering.
2. a kind of sintering process of kettle according to claim 1, it is characterised in that:In step A, melting is carried out to silver,
Smelting temperature is 800 DEG C -1500 DEG C.
3. a kind of sintering process of kettle according to claim 1, it is characterised in that:The cooling of first stage in step C
Temperature is 260 DEG C, and the cooling temperature of second stage is 120 DEG C.
4. a kind of sintering process of kettle according to claim 1, it is characterised in that:Sintering temperature is 600 in step D
℃。