CN106351056A - High-strength corrugated-paper production process - Google Patents
High-strength corrugated-paper production process Download PDFInfo
- Publication number
- CN106351056A CN106351056A CN201610797616.5A CN201610797616A CN106351056A CN 106351056 A CN106351056 A CN 106351056A CN 201610797616 A CN201610797616 A CN 201610797616A CN 106351056 A CN106351056 A CN 106351056A
- Authority
- CN
- China
- Prior art keywords
- paper
- production technology
- corrugated paper
- paper production
- highly intensified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a high-strength corrugated-paper production process. The high-strength corrugated-paper production process includes the steps: preparing raw materials and smashing the same to produce into paper pulp via grinding, and subjecting the paper pulp to purification treatment of sieving and deslagging; performing hardening treatment on the paper pulp subjected to the purification treatment; producing the paper pulp subjected to the hardening treatment into an original paper base; subjecting the original paper base to coating with a wear-resistant agent through a coating machine; drying and shaping to form the product to be put in storage. The corrugated paper produced with the corrugated-paper production process is high in strength, long in service life, satisfied to use requirement, reasonable in technology design, low in material consumption, low in production cost and wide in application to the technical field of corrugated boxes.
Description
Technical field
The invention belongs to corrugated paper technical field, more particularly, to a kind of highly intensified corrugated paper production technology.
Background technology
Corrugated paper is a kind of universal package paper, have that rational in infrastructure, processing is simple because of it, light weight, low cost with
And it is easy to the advantages of store and transport, become widest paper container package, be widely used in transportation and packing field.Corrugated paper be by
The plate object that the corrugated paper of sheet lining and the waveform being formed by corrugated roller processing is bonded, is generally divided into single wall corrugated board
With double-layer corrugated cardboard two class.
With the extensive application of corrugated case, the prescription also more and more higher to corrugated paper for the packaging industry: require Concha Arcae
Paper possesses strong burst index and ring crush index, and its burst index of existing corrugated paper and ring crush index are all weaker, lead to
Easily rot in corrugated case packaging or transportation.
China Patent Publication No. is cn 105507073 a, the production technology of the entitled corrugated board of innovation and creation, bag
Include following steps: 1) glue: 2) body paper is preheated: 3) by step 2) body paper from paper frame through dancing roll, be attached to one side
In machine, produced: 4) the one side cardboard produced from step 3) single-side machine is conveyed and pass a bridge: 5) will be from step 4) one side
The one side cardboard of machine output is preheated;6) one side cardboard is carried out gluing;7) corrugated board after bonding is dried through heating
Dry;8) after through cutting machine in length and breadth cut required size.Preferably, in upper glue process, the temperature control of glue is at 68~69 DEG C.This
The production technology of invention corrugated board, can improve the adhesive strength of corrugated board, water resistance, comprcssive strength and bear pressure,
And so that corrugated paper is easily stacked, and improve utilization rate of warehouse.But, existing corrugated paper production technology has product matter
The low intensity of amount, service life is short, and technological design is unreasonable, the high problem of production cost.
Therefore, invent a kind of highly intensified corrugated paper production technology and seem very necessary.
Content of the invention
In order to solve above-mentioned technical problem, the present invention provides a kind of highly intensified corrugated paper production technology, existing to solve
Corrugated paper production technology has the low intensity of product quality, and service life is short, complex process, the high problem of production cost.One
Plant highly intensified corrugated paper production technology to comprise the steps of
Step one: with raw material;
Step 2: raw material is pulverized and makes body paper paper pulp;
Step 3: enhancement process is implemented to body paper paper pulp;
Step 4: original paper is prepared by paper machine;
Step 5: dry original paper;
Step 6: make original paper one side coat adhesive using gluing machine;
Step 7: corrugated paper is obtained by Corrugating Machine;
Step 8: dry warehouse-in storage after cutting.
Further, in step one, described raw material adopts agricultural crop straw and waste paper, adds water and carries out bubble slurry, throws
Enter in pulper and pulverize, make raw material dissociate into fiber, and carry out filtering screening and remove crude fibre and impurity, its fibre length is
1.0~2.0mm.
Further, in step 2, described body paper paper pulp preparation temperature is 40 DEG C~50 DEG C.
Further, in step 3, described enhancement process refers to that 80-120 weight portion body paper paper pulp adds 10-15 weight
The vinal of part and the silicon dioxide of 2-4 weight portion, are sufficiently mixed static 1 to 2 hour after uniformly, are subsequently adding sun
Ion gum rosin and wet strength agent;Described wet strength agent is polyamide-based wet strength agent addition is 15-20 weight portion, described sun
Ion gum rosin addition is 20-30 weight portion.
Further, in step 5, described drying temperature is 120 DEG C -150 DEG C.
Further, in step 6, described adhesive adopts starch based sizing agent and reinforcing agent, and degree of sizing controls
0.6-0.8mm;Described starch based sizing agent is 3:1 with the weight of reinforcing agent
Further, in described starch based sizing agent add 2% resin adhesive as auxiliary agent.
Further, in step 6, the temperature control of described adhesive is at 58~62 DEG C.
Further, in step 8, using the cutting of cutting machine in length and breadth, cut-out discharge surface degree of splitting controls 0 for described cutting
~2mm.
Compared with prior art, the invention has the following beneficial effects: adopting prepared watt of corrugated paper production technology of the present invention
Stupefied paper intensity is high, and long service life meets use requirement, and rationally, consumable quantity is low, low production cost for technological design, extensively should
For corrugated case body technique field.
Brief description
Fig. 1 is the highly intensified corrugated paper production technological process of the present invention.
Specific embodiment
Below in conjunction with accompanying drawing, the present invention is described further:
In figure:
Embodiment:
As shown in Figure 1
A kind of highly intensified corrugated paper production technology comprises the steps of
S101: with raw material;
S102: raw material is pulverized and makes body paper paper pulp;
S103: enhancement process is implemented to body paper paper pulp;
S104: original paper is prepared by paper machine;
S105: dry original paper;
S106: make original paper one side coat adhesive using gluing machine;
S107: corrugated paper is obtained by Corrugating Machine;
S108: dry warehouse-in storage after cutting.
Further, in s101, described raw material adopts agricultural crop straw and waste paper, adds water and carries out bubble slurry, puts into
Pulverize in pulper, make raw material dissociate into fiber, and carry out filtering screening and remove crude fibre and impurity, its fibre length is 1.0
~2.0mm.
Further, in s102, described body paper paper pulp preparation temperature is 40 DEG C~50 DEG C.
Further, in s103, described enhancement process refers to that 80-120 weight portion body paper paper pulp adds 10-15 weight portion
Vinal and 2-4 weight portion silicon dioxide, be sufficiently mixed uniformly after static 1 to 2 hour, be subsequently adding sun from
Sub- gum rosin and wet strength agent;Described wet strength agent is polyamide-based wet strength agent addition is 15-20 weight portion, described sun from
Sub- gum rosin addition is 20-30 weight portion.
Further, in s105, described drying temperature is 120 DEG C -150 DEG C.
Further, in s106, described adhesive adopts starch based sizing agent and reinforcing agent, and degree of sizing controls
0.6-0.8mm;Described starch based sizing agent is 3:1 with the weight of reinforcing agent
Further, in described starch based sizing agent add 2% resin adhesive as auxiliary agent.
Further, in s106, the temperature control of described adhesive is at 58~62 DEG C.
Further, in s108, described cutting using the cutting of cutting machine in length and breadth, cut-out discharge surface degree of splitting controls 0~
2mm.
Compared with prior art, the invention has the following beneficial effects: adopting prepared watt of corrugated paper production technology of the present invention
Stupefied paper intensity is high, and long service life meets use requirement, and rationally, consumable quantity is low, low production cost for technological design, extensively should
For corrugated case body technique field.
Checking embodiment:
By determining that above-mentioned process conditions have carried out four batches of test cards, related data is as follows, is shown in Table 1:
1 four batches of trial production checking data of table
The result shows, this product process stabilizing is reliable, high yield rate, suitable industrialization production.
Compared with prior art, the invention has the following beneficial effects: adopting prepared watt of corrugated paper production technology of the present invention
Stupefied paper intensity is high, and long service life meets use requirement, and rationally, consumable quantity is low, low production cost for technological design, extensively should
For corrugated case body technique field.
Using technical solutions according to the invention, or those skilled in the art is under the inspiration of technical solution of the present invention,
Design similar technical scheme, and reach above-mentioned technique effect, all fall into protection scope of the present invention.
Claims (9)
1. a kind of highly intensified corrugated paper production technology is it is characterised in that this highly intensified corrugated paper production technology comprises the steps of
Step one: with raw material;
Step 2: raw material is pulverized and makes body paper paper pulp;
Step 3: enhancement process is implemented to body paper paper pulp;
Step 4: original paper is prepared by paper machine;
Step 5: dry original paper;
Step 6: make original paper one side coat adhesive using gluing machine;
Step 7: corrugated paper is obtained by Corrugating Machine;
Step 8: dry warehouse-in storage after cutting.
2. highly intensified corrugated paper production technology as claimed in claim 1 is it is characterised in that in step one, described former material
Material adopts agricultural crop straw and waste paper, adds water and carries out bubble slurry, puts in pulper and pulverize, make raw material dissociate into fiber, go forward side by side
Row filtering screening removes crude fibre and impurity, and its fibre length is 1.0~2.0mm.
3. highly intensified corrugated paper production technology as claimed in claim 1 is it is characterised in that in step 2, described body paper paper
Slurry preparation temperature is 40 DEG C~50 DEG C.
4. highly intensified corrugated paper production technology as claimed in claim 1 is it is characterised in that in step 3, described enhancing
Process and refer to that 80-120 weight portion body paper paper pulp adds the vinal of 10-15 weight portion and the titanium dioxide of 2-4 weight portion
Silicon, is sufficiently mixed static 1 to 2 hour after uniformly, is subsequently adding cationic rosin size and wet strength agent;Described wet strength agent is polyamides
Amine wet strength agent addition is 15-20 weight portion, and described cationic rosin size addition is 20-30 weight portion.
5. highly intensified corrugated paper production technology as claimed in claim 1 is it is characterised in that in step 5, described drying
Temperature is 120 DEG C -150 DEG C.
6. highly intensified corrugated paper production technology as claimed in claim 1 is it is characterised in that in step 6, described gluing
Agent adopts starch based sizing agent and reinforcing agent, and degree of sizing controls in 0.6-0.8mm;Described starch based sizing agent and reinforcing agent
Weight is 3:1.
7. highly intensified corrugated paper production technology as claimed in claim 6 is it is characterised in that add in described starch based sizing agent
2% resin adhesive is as auxiliary agent.
8. highly intensified corrugated paper production technology as claimed in claim 1 is it is characterised in that in step 6, described adhesive
Temperature control at 58~62 DEG C.
9. highly intensified corrugated paper production technology as claimed in claim 1 is it is characterised in that in step 8, described cutting
Using the cutting of cutting machine in length and breadth, cut-out discharge surface degree of splitting controls in 0~2mm.