CN107009686A - A kind of stalk cellulose corrugated paper moistureproof with antibacterial and preparation method thereof - Google Patents
A kind of stalk cellulose corrugated paper moistureproof with antibacterial and preparation method thereof Download PDFInfo
- Publication number
- CN107009686A CN107009686A CN201710316427.6A CN201710316427A CN107009686A CN 107009686 A CN107009686 A CN 107009686A CN 201710316427 A CN201710316427 A CN 201710316427A CN 107009686 A CN107009686 A CN 107009686A
- Authority
- CN
- China
- Prior art keywords
- parts
- paper
- stalk
- stalk cellulose
- corrugating medium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of stalk cellulose corrugated paper moistureproof with antibacterial, including corrugating medium and panel paper, panel paper is pasted onto corrugating medium's upper and lower surface with paperboard bonding agent, corrugating medium is made up of stalk cellulose, starch, talcum powder, polyvinyl alcohol, zeolite with carrying silver powder, silica-gel desiccant, panel paper is made up of stalk cellulose, zeolite with carrying silver powder, glass fibre, sepiolite, EVA resin, panel paper surface is coated with one layer of paraffin, and paperboard bonding agent is made up of silicate, aluminum oxide, starch, natural resin, polyvinyl alcohol.The beneficial effects of the invention are as follows：Polyvinyl alcohol is added in corrugating medium and zeolite with carrying silver powder plays antibacterial, silica-gel desiccant is added and plays dry effect；Zeolite with carrying silver powder is added in panel paper and plays a part of antibacterial, adds the effect that glass fibre, sepiolite, EVA resin play protection against the tide；One layer of paraffin is coated with panel paper surface, the effect of corrugated paper is penetrated into water is prevented.
Description
Technical field
Manufacture field the present invention relates to corrugated paper, more particularly to a kind of stalk cellulose corrugated paper moistureproof with antibacterial and
Its preparation method.
Background technology
Corrugated paper be as sheet lining and by corrugated roller process formed by waveform the plate object that is bonded of corrugated paper,
Single wall corrugated board and the class of double-layer corrugated cardboard two are generally divided into, is divided into according to the size of corrugation：The type of A, B, C, E, F five.Corrugation
The invention of paper and application have more than 100 years history history, with cost is low, light weight, processing easily, intensity is big, printing adaptability sample is excellent
It is good, storage convenient in carrying the advantages of, more than 80% corrugated paper can be by reclaiming, and corrugated paper can be used as food or number
The packaging of code product, it is relatively environment-friendly, using relatively broad.
Stalk is the general name of ripe crops cauline leaf (fringe) part.It is often referred to wheat, paddy rice, corn, potato class, rape, cotton
The remainder of flower, sugarcane and other crops (being usually coarse food grain) after harvest seed.The photosynthetic product of crops has
More than half is present in stalk, and stalk is rich in nitrogen, phosphorus, potassium, calcium, magnesium and organic matter etc., be it is a kind of have it is multiduty can be again
Raw living resources.Stalk crude fiber content height (30%-40%), and containing lignin the features such as.
It is one of important directions that stalk resource is recycled, corrugated paper to manufacture corrugated paper currently with stalk cellulose
Preferable antibacterial and moisture-proof function are needed as packaging material, the present invention is intended to provide a kind of stalk moistureproof with antibacterial is fine
The plain corrugated paper of dimension.
The content of the invention
It is an object of the invention to overcome the problem above that prior art is present, there is provided a kind of stalk moistureproof with antibacterial
Cellulose corrugated paper and preparation method thereof, the corrugated paper has preferably moistureproof, anti-microbial property.
To realize above-mentioned technical purpose and the technique effect, the present invention is achieved through the following technical solutions：
A kind of stalk cellulose corrugated paper moistureproof with antibacterial, including corrugating medium and panel paper, the panel paper are used
Paperboard bonding agent is pasted onto corrugating medium's upper and lower surface, and the corrugating medium is by stalk cellulose, starch, talcum powder, polyethylene
Alcohol, zeolite with carrying silver powder, silica-gel desiccant composition, the panel paper is by stalk cellulose, zeolite with carrying silver powder, glass fibre, Hai Pao
Stone, EVA resin composition, the panel paper surface are coated with one layer of paraffin, the paperboard bonding agent by silicate, aluminum oxide, starch,
Natural resin, polyvinyl alcohol composition.
It is preferred that, corrugating medium's each component parts by weight are 60~80 parts of stalk cellulose, 10~25 parts of starch, slided
8~12 parts of stone flour, 10~15 parts of polyvinyl alcohol, 1~3 part of zeolite with carrying silver powder, 2~8 parts of silica-gel desiccant.
It is preferred that, the panel paper each component parts by weight be 65~90 parts of stalk cellulose, 1~5 part of zeolite with carrying silver powder,
15~30 parts of glass fibre, 8~15 parts of sepiolite, 10~18 parts of EVA resin.
It is preferred that, the paperboard bonding agent each component parts by weight are 5~13 parts of silicate, 1~3 part of aluminum oxide, starch 5
~15 parts, 30~50 parts of natural resin, 8~14 parts of polyvinyl alcohol.
It is preferred that, the natural resin is rosin or natural gum or lignin.
It is preferred that, the paraffin is coated on one side of the panel paper away from corrugating medium.
A kind of preparation method of the stalk cellulose corrugated paper moistureproof with antibacterial, comprises the following steps：
1), stalk is cut into the stalk section of 3~6 centimeter lengths, then cleans with water stalk section, then using drying machine drying or
Dry, crushed the stalk section of drying using pulverizer, screened out with screen cloth do not crush thoroughly stalk section to obtain stalk fibre
Element；
2) stalk cellulose, starch, talcum powder, polyvinyl alcohol, zeolite with carrying silver powder, silica-gel desiccant, are weighed by deal, is put
Enter and mixing mashing is carried out in beater, while being slowly injected into running water into beater, beating time is 18~24min, will be mixed
Dry or dry in corrugating medium's oar injection mould after conjunction and corrugating medium is made；
3) stalk cellulose, zeolite with carrying silver powder, glass fibre, sepiolite, EVA resin, are weighed by deal, beater is put into
Interior progress mixing mashing, while being slowly injected into running water into beater, beating time is 30~36min, after well mixed
Panel paper oar injection mould in dry or dry panel paper is made, then in one layer of paraffin of coated on one side of panel paper；
4) silicate, aluminum oxide, starch, natural resin, polyvinyl alcohol, are weighed by deal and is put into progress in beater
Mixing mashing, while being slowly injected into running water into beater, beating time is 36~40min, and the freedom for making oar material is 180
~199CSF, slurry weight in wet base is 7.0~7.8g, and temperature is 45~49 DEG C；
5) two pieces of steps 3, are taken) manufacture panel paper, on surface, the one side of uncoated paraffin paints step 4) manufacture paper
Plate adhesive, then take one piece of step 2) manufacture corrugating medium, the panel paper for being brushed with paperboard bonding agent is pasted onto corrugated core
The upper and lower surface of paper, is flattened with trigger squeeze and is compacted.
The beneficial effects of the invention are as follows：Polyvinyl alcohol is added in corrugating medium and zeolite with carrying silver powder plays antibacterial, is added
Silica-gel desiccant plays dry effect；Zeolite with carrying silver powder is added in panel paper and plays a part of antibacterial, adds glass fibre, sea
Afrodite, EVA resin play the effect of protection against the tide；One layer of paraffin is coated with panel paper surface, the work of corrugated paper is penetrated into water is prevented
With；Using the paperboard bonding agent being made up of silicate, aluminum oxide, starch, natural resin, polyvinyl alcohol, with sticky strong, waterproof
The good effect of property.
Embodiment
Embodiment one：
A kind of stalk cellulose corrugated paper moistureproof with antibacterial, including corrugating medium and panel paper, panel paper cardboard
Adhesive is pasted onto corrugating medium's upper and lower surface, and corrugating medium is by stalk cellulose, starch, talcum powder, polyvinyl alcohol, load silver boiling
Stone flour, silica-gel desiccant composition, panel paper is by stalk cellulose, zeolite with carrying silver powder, glass fibre, sepiolite, EVA resin group
Into panel paper surface is coated with one layer of paraffin, and paperboard bonding agent is by silicate, aluminum oxide, starch, natural resin, polyvinyl alcohol group
Into.
Wherein, corrugating medium's each component parts by weight are 60 parts of stalk cellulose, 10 parts of starch, 8 parts of talcum powder, polyethylene
10 parts of alcohol, 1 part of zeolite with carrying silver powder, 2 parts of silica-gel desiccant.
Wherein, panel paper each component parts by weight be 65 parts of stalk cellulose, 1 part of zeolite with carrying silver powder, 15 parts of glass fibre,
8 parts of sepiolite, 10 parts of EVA resin.
Wherein, paperboard bonding agent each component parts by weight are 5 parts of silicate, 1 part of aluminum oxide, 5 parts of starch, natural resin 30
Part, 8 parts of polyvinyl alcohol.
Wherein, natural resin is rosin or natural gum or lignin.
Wherein, paraffin is coated on one side of the panel paper away from corrugating medium.
A kind of preparation method of the stalk cellulose corrugated paper moistureproof with antibacterial, comprises the following steps：
1), stalk is cut into the stalk section of 3~6 centimeter lengths, then cleans with water stalk section, then using drying machine drying or
Dry, crushed the stalk section of drying using pulverizer, screened out with screen cloth do not crush thoroughly stalk section to obtain stalk fibre
Element；
2) stalk cellulose, starch, talcum powder, polyvinyl alcohol, zeolite with carrying silver powder, silica-gel desiccant, are weighed by deal, is put
Enter and mixing mashing is carried out in beater, while being slowly injected into running water into beater, beating time is 18min, after mixing
Corrugating medium oar injection mould in dry or dry corrugating medium is made；
3) stalk cellulose, zeolite with carrying silver powder, glass fibre, sepiolite, EVA resin, are weighed by deal, beater is put into
Interior progress mixing mashing, while being slowly injected into running water into beater, beating time is 30min, the face after being well mixed
Dry or dry in paperboard oar injection mould and panel paper is made, then in one layer of paraffin of coated on one side of panel paper；
4) silicate, aluminum oxide, starch, natural resin, polyvinyl alcohol, are weighed by deal and is put into progress in beater
Mixing mashing, while being slowly injected into running water into beater, beating time is 36min, and the freedom for making oar material is 180CSF,
Slurry weight in wet base is 7.0g, and temperature is 45 DEG C；
5) two pieces of steps 3, are taken) manufacture panel paper, on surface, the one side of uncoated paraffin paints step 4) manufacture paper
Plate adhesive, then take one piece of step 2) manufacture corrugating medium, the panel paper for being brushed with paperboard bonding agent is pasted onto corrugated core
The upper and lower surface of paper, is flattened with trigger squeeze and is compacted.
Embodiment two：
A kind of stalk cellulose corrugated paper moistureproof with antibacterial, including corrugating medium and panel paper, panel paper cardboard
Adhesive is pasted onto corrugating medium's upper and lower surface, and corrugating medium is by stalk cellulose, starch, talcum powder, polyvinyl alcohol, load silver boiling
Stone flour, silica-gel desiccant composition, panel paper is by stalk cellulose, zeolite with carrying silver powder, glass fibre, sepiolite, EVA resin group
Into panel paper surface is coated with one layer of paraffin, and paperboard bonding agent is by silicate, aluminum oxide, starch, natural resin, polyvinyl alcohol group
Into.
Wherein, corrugating medium's each component parts by weight are 70 parts of stalk cellulose, 15 parts of starch, 10 parts of talcum powder, poly- second
13 parts of enol, 2 parts of zeolite with carrying silver powder, 5 parts of silica-gel desiccant.
Wherein, panel paper each component parts by weight be 78 parts of stalk cellulose, 3 parts of zeolite with carrying silver powder, 22 parts of glass fibre,
12 parts of sepiolite, 15 parts of EVA resin.
Wherein, paperboard bonding agent each component parts by weight are 10 parts of silicate, 2 parts of aluminum oxide, 10 parts of starch, natural resin
40 parts, 11 parts of polyvinyl alcohol.
Wherein, natural resin is rosin or natural gum or lignin.
Wherein, paraffin is coated on one side of the panel paper away from corrugating medium.
A kind of preparation method of the stalk cellulose corrugated paper moistureproof with antibacterial, comprises the following steps：
1), stalk is cut into the stalk section of 3~6 centimeter lengths, then cleans with water stalk section, then using drying machine drying or
Dry, crushed the stalk section of drying using pulverizer, screened out with screen cloth do not crush thoroughly stalk section to obtain stalk fibre
Element；
2) stalk cellulose, starch, talcum powder, polyvinyl alcohol, zeolite with carrying silver powder, silica-gel desiccant, are weighed by deal, is put
Enter and mixing mashing is carried out in beater, while being slowly injected into running water into beater, beating time is 20min, after mixing
Corrugating medium oar injection mould in dry or dry corrugating medium is made；
3) stalk cellulose, zeolite with carrying silver powder, glass fibre, sepiolite, EVA resin, are weighed by deal, beater is put into
Interior progress mixing mashing, while being slowly injected into running water into beater, beating time is 33min, the face after being well mixed
Dry or dry in paperboard oar injection mould and panel paper is made, then in one layer of paraffin of coated on one side of panel paper；
4) silicate, aluminum oxide, starch, natural resin, polyvinyl alcohol, are weighed by deal and is put into progress in beater
Mixing mashing, while being slowly injected into running water into beater, beating time is 38min, and the freedom for making oar material is 190CSF,
Slurry weight in wet base is 7.5g, and temperature is 47 DEG C；
5) two pieces of steps 3, are taken) manufacture panel paper, on surface, the one side of uncoated paraffin paints step 4) manufacture paper
Plate adhesive, then take one piece of step 2) manufacture corrugating medium, the panel paper for being brushed with paperboard bonding agent is pasted onto corrugated core
The upper and lower surface of paper, is flattened with trigger squeeze and is compacted.
Embodiment three：
A kind of stalk cellulose corrugated paper moistureproof with antibacterial, including corrugating medium and panel paper, panel paper cardboard
Adhesive is pasted onto corrugating medium's upper and lower surface, and corrugating medium is by stalk cellulose, starch, talcum powder, polyvinyl alcohol, load silver boiling
Stone flour, silica-gel desiccant composition, panel paper is by stalk cellulose, zeolite with carrying silver powder, glass fibre, sepiolite, EVA resin group
Into panel paper surface is coated with one layer of paraffin, and paperboard bonding agent is by silicate, aluminum oxide, starch, natural resin, polyvinyl alcohol group
Into.
Wherein, corrugating medium's each component parts by weight are 80 parts of stalk cellulose, 25 parts of starch, 12 parts of talcum powder, poly- second
15 parts of enol, 3 parts of zeolite with carrying silver powder, 8 parts of silica-gel desiccant.
Wherein, panel paper each component parts by weight be 90 parts of stalk cellulose, 5 parts of zeolite with carrying silver powder, 30 parts of glass fibre,
15 parts of sepiolite, 18 parts of EVA resin.
Wherein, paperboard bonding agent each component parts by weight are 13 parts of silicate, 3 parts of aluminum oxide, 15 parts of starch, natural resin
50 parts, 14 parts of polyvinyl alcohol.
Wherein, natural resin is rosin or natural gum or lignin.
Wherein, paraffin is coated on one side of the panel paper away from corrugating medium.
A kind of preparation method of the stalk cellulose corrugated paper moistureproof with antibacterial, comprises the following steps：
1), stalk is cut into the stalk section of 3~6 centimeter lengths, then cleans with water stalk section, then using drying machine drying or
Dry, crushed the stalk section of drying using pulverizer, screened out with screen cloth do not crush thoroughly stalk section to obtain stalk fibre
Element；
2) stalk cellulose, starch, talcum powder, polyvinyl alcohol, zeolite with carrying silver powder, silica-gel desiccant, are weighed by deal, is put
Enter and mixing mashing is carried out in beater, while being slowly injected into running water into beater, beating time is 24min, after mixing
Corrugating medium oar injection mould in dry or dry corrugating medium is made；
3) stalk cellulose, zeolite with carrying silver powder, glass fibre, sepiolite, EVA resin, are weighed by deal, beater is put into
Interior progress mixing mashing, while being slowly injected into running water into beater, beating time is 36min, the face after being well mixed
Dry or dry in paperboard oar injection mould and panel paper is made, then in one layer of paraffin of coated on one side of panel paper；
4) silicate, aluminum oxide, starch, natural resin, polyvinyl alcohol, are weighed by deal and is put into progress in beater
Mixing mashing, while being slowly injected into running water into beater, beating time is 40min, and the freedom for making oar material is 199CSF,
Slurry weight in wet base is 7.8g, and temperature is 49 DEG C；
5) two pieces of steps 3, are taken) manufacture panel paper, on surface, the one side of uncoated paraffin paints step 4) manufacture paper
Plate adhesive, then take one piece of step 2) manufacture corrugating medium, the panel paper for being brushed with paperboard bonding agent is pasted onto corrugated core
The upper and lower surface of paper, is flattened with trigger squeeze and is compacted.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.
Claims (7)
1. a kind of stalk cellulose corrugated paper moistureproof with antibacterial, including corrugating medium and panel paper, the panel paper paper
Plate adhesive is pasted onto corrugating medium's upper and lower surface, it is characterised in that the corrugating medium is by stalk cellulose, starch, talcum
Powder, polyvinyl alcohol, zeolite with carrying silver powder, silica-gel desiccant composition, the panel paper is by stalk cellulose, zeolite with carrying silver powder, glass
Fiber, sepiolite, EVA resin composition, the panel paper surface are coated with one layer of paraffin, and the paperboard bonding agent is by silicate, oxygen
Change aluminium, starch, natural resin, polyvinyl alcohol composition.
2. the stalk cellulose corrugated paper moistureproof with antibacterial according to claim 1, it is characterised in that：The corrugated core
Paper each component parts by weight be 60~80 parts of stalk cellulose, 10~25 parts of starch, 8~12 parts of talcum powder, polyvinyl alcohol 10~
15 parts, 1~3 part of zeolite with carrying silver powder, 2~8 parts of silica-gel desiccant.
3. the stalk cellulose corrugated paper moistureproof with antibacterial according to claim 1, it is characterised in that：The panel paper
Each component parts by weight are 65~90 parts of stalk cellulose, 1~5 part of zeolite with carrying silver powder, 15~30 parts of glass fibre, sepiolite 8
~15 parts, 10~18 parts of EVA resin.
4. the stalk cellulose corrugated paper moistureproof with antibacterial according to claim 1, it is characterised in that：The cardboard glues
Mixture each component parts by weight be 5~13 parts of silicate, 1~3 part of aluminum oxide, 5~15 parts of starch, 30~50 parts of natural resin,
8~14 parts of polyvinyl alcohol.
5. the stalk cellulose corrugated paper moistureproof with antibacterial according to claim 1, it is characterised in that：The natural tree
Fat is rosin or natural gum or lignin.
6. the stalk cellulose corrugated paper moistureproof with antibacterial according to claim 1, it is characterised in that：The paraffin is applied
Cloth is in one side of the panel paper away from corrugating medium.
7. a kind of preparation method with the moistureproof stalk cellulose corrugated paper of antibacterial for described in claim 1, its feature
It is：Comprise the following steps：
1), stalk is cut into the stalk section of 3~6 centimeter lengths, then stalk section is cleaned with water, drying machine drying is then used or dries in the air
It is dry, the stalk section of drying is crushed using pulverizer, screened out with screen cloth do not crush thoroughly stalk section to obtain stalk cellulose；
2) stalk cellulose, starch, talcum powder, polyvinyl alcohol, zeolite with carrying silver powder, silica-gel desiccant, are weighed by deal, is put into and beats
Mixing mashing is carried out in pulp grinder, while being slowly injected into running water into beater, beating time is 18~24min, after mixing
Corrugating medium oar injection mould in dry or dry corrugating medium is made；
3) stalk cellulose, zeolite with carrying silver powder, glass fibre, sepiolite, EVA resin, are weighed by deal, is put into beater
Row mixing mashing, while being slowly injected into running water into beater, beating time is 30~36min, the face after being well mixed
Dry or dry in paperboard oar injection mould and panel paper is made, then in one layer of paraffin of coated on one side of panel paper；
4), silicate, aluminum oxide, starch, natural resin, polyvinyl alcohol is weighed by deal to be put into beater and mixed
Mashing, while be slowly injected into running water into beater, beating time is 36~40min, make the freedom of oar material for 180~
199CSF, slurry weight in wet base is 7.0~7.8g, and temperature is 45~49 DEG C；
5) two pieces of steps 3, are taken) manufacture panel paper, on surface, the one side of uncoated paraffin paints step 4) manufacture cardboard glue
Mixture, then take one piece of step 2) manufacture corrugating medium, the panel paper for being brushed with paperboard bonding agent is pasted onto corrugating medium
Upper and lower surface, is flattened with trigger squeeze and is compacted.