CN106350990A - Brushed fabric desizing treatment method - Google Patents
Brushed fabric desizing treatment method Download PDFInfo
- Publication number
- CN106350990A CN106350990A CN201610785300.4A CN201610785300A CN106350990A CN 106350990 A CN106350990 A CN 106350990A CN 201610785300 A CN201610785300 A CN 201610785300A CN 106350990 A CN106350990 A CN 106350990A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- weight
- parts
- desizing
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a brushed fabric desizing treatment method. The brushed fabric desizing treatment method comprises the following steps: 1) sequentially adding 1-2 parts of ethylene diamine-polyoxyethylene-polyoxypropylene block polyether, 1.3 parts of vinyltrimethoxysilane, 0.7 part of maleic acid-acrylic acid polymer, 1.2 parts of coconut oil fatty acid diethanolamide and 21 parts of amylase into 65 parts of deionized water, and uniformly stirring; 2) then sequentially adding 1.9 parts of lactic acid, 0.7 part of talcum powder, 1.2 parts of ammonium molybdate and 0.4 part of polyalkyl trialkylammonium chloride, and continuing stirring till uniform mixing to obtain a desizing solution; 3) padding fabric into the desizing solution, taking out, washing and airing. By the brushed fabric desizing treatment method, the desizing rate is high and the desized fabric has a relatively good capillary effect and relatively good mechanical properties.
Description
Technical field
The present invention relates to the desizing processing method of velour.
Background technology
The warp thread of the fabrics such as cotton, viscose glue and synthetic fibers, mostly first passes through sizing before weaving.Slurry is in dyeing and finishing process
The middle wettability that can affect fabric, and hinder chemicals to fiber contacts, therefore fabric dye previous as all carry out at desizing
Reason.
Content of the invention
It is an object of the invention to provide a kind of desizing processing method of velour, its desizing rate height, after desizing is processed
Fabric there is higher capillary effect and mechanical property, be conducive to the carrying out of follow-up dyeing and printing process it is ensured that follow-up printing quality;And
And the effective removal because of slurry, improve the feel of fabric.
For achieving the above object, the technical scheme is that the desizing processing method designing a kind of velour, including
Following steps:
1) by 1~2 weight portion ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1.3 parts by weight of ethylene base trimethoxies
Base silane, 0.7 parts by weight of maleic acrylate copolymer, 1.2 weight portion cocoanut fatty acid diethanolamides, 21 weight portions form sediment
Powder enzyme puts in 65 parts by weight of deionized water successively, stirs;
2) put into successively again 1.9 weight portion lactic acid, 0.7 weight portion Pulvis Talci, 1.2 weight portion amine molybdates, 0.4 weight portion gather
Alkyl tri alkyl ammomium chloride, continues stirring, uniform to being sufficiently mixed, prepared desizing liquid;
3) fabric is padded process in desizing liquid, wash after taking-up and dry.
Preferably, the desizing processing method of velour, comprises the steps:
1) by 1 weight portion ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1.3 parts by weight of ethylene base trimethoxy silicon
Alkane, 0.7 parts by weight of maleic acrylate copolymer, 1.2 weight portion cocoanut fatty acid diethanolamides, 21 weight starch enzymes
Put into successively in 65 parts by weight of deionized water, stir;
2) put into successively again 1.9 weight portion lactic acid, 0.7 weight portion Pulvis Talci, 1.2 weight portion amine molybdates, 0.4 weight portion gather
Alkyl tri alkyl ammomium chloride, continues stirring, uniform to being sufficiently mixed, prepared desizing liquid;
3) fabric is padded process in desizing liquid, wash after taking-up and dry.
Preferably, the desizing processing method of velour, comprises the steps:
1) by 2 weight portion ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1.3 parts by weight of ethylene base trimethoxy silicon
Alkane, 0.7 parts by weight of maleic acrylate copolymer, 1.2 weight portion cocoanut fatty acid diethanolamides, 21 weight starch enzymes
Put into successively in 65 parts by weight of deionized water, stir;
2) put into successively again 1.9 weight portion lactic acid, 0.7 weight portion Pulvis Talci, 1.2 weight portion amine molybdates, 0.4 weight portion gather
Alkyl tri alkyl ammomium chloride, continues stirring, uniform to being sufficiently mixed, prepared desizing liquid;
3) fabric is padded process in desizing liquid, wash after taking-up and dry.
Preferably, the desizing processing method of velour, comprises the steps:
1) by 1.2 weight portion ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1.3 parts by weight of ethylene base trimethoxies
Silane, 0.7 parts by weight of maleic acrylate copolymer, 1.2 weight portion cocoanut fatty acid diethanolamides, 21 weight starch
Enzyme puts in 65 parts by weight of deionized water successively, stirs;
2) put into successively again 1.9 weight portion lactic acid, 0.7 weight portion Pulvis Talci, 1.2 weight portion amine molybdates, 0.4 weight portion gather
Alkyl tri alkyl ammomium chloride, continues stirring, uniform to being sufficiently mixed, prepared desizing liquid;
3) fabric is padded process in desizing liquid, wash after taking-up and dry.
Advantages of the present invention and having the beneficial effects that: provide a kind of desizing processing method of velour, its desizing rate is high,
Fabric after desizing is processed has higher capillary effect and mechanical property, is conducive to the carrying out of follow-up dyeing and printing process it is ensured that follow-up
Printing quality;And the effective removal because of slurry, improves the feel of fabric.
The performance of " desizing liquid " and purposes are determined by its component and proportioning, and the different component meeting in " desizing liquid "
Influence each other, component and its proportioning can determine the final performance of " desizing liquid ", such as fruit component and its proportioning be not mutually coordinated, single
The beneficial effect that component is brought, even can be eliminated by other components abatement, when serious, different component is mutually conflicted, and rises
Less than whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains " desizing
The optimal component of liquid " and proportioning so that multiple component combine, mutually coordinated and produce positive comprehensive effect.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more
Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
The desizing processing method of velour, comprises the steps:
1) by 1~2 weight portion ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1.3 parts by weight of ethylene base trimethoxies
Base silane, 0.7 parts by weight of maleic acrylate copolymer, 1.2 weight portion cocoanut fatty acid diethanolamides, 21 weight portions form sediment
Powder enzyme puts in 65 parts by weight of deionized water successively, stirs;
2) put into successively again 1.9 weight portion lactic acid, 0.7 weight portion Pulvis Talci, 1.2 weight portion amine molybdates, 0.4 weight portion gather
Alkyl tri alkyl ammomium chloride, continues stirring, uniform to being sufficiently mixed, prepared desizing liquid;
3) fabric is padded process in desizing liquid, wash after taking-up and dry.
Embodiment 2
The desizing processing method of velour, comprises the steps:
1) by 1 weight portion ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1.3 parts by weight of ethylene base trimethoxy silicon
Alkane, 0.7 parts by weight of maleic acrylate copolymer, 1.2 weight portion cocoanut fatty acid diethanolamides, 21 weight starch enzymes
Put into successively in 65 parts by weight of deionized water, stir;
2) put into successively again 1.9 weight portion lactic acid, 0.7 weight portion Pulvis Talci, 1.2 weight portion amine molybdates, 0.4 weight portion gather
Alkyl tri alkyl ammomium chloride, continues stirring, uniform to being sufficiently mixed, prepared desizing liquid;
3) fabric is padded process in desizing liquid, wash after taking-up and dry.
Embodiment 3
The desizing processing method of velour, comprises the steps:
1) by 2 weight portion ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1.3 parts by weight of ethylene base trimethoxy silicon
Alkane, 0.7 parts by weight of maleic acrylate copolymer, 1.2 weight portion cocoanut fatty acid diethanolamides, 21 weight starch enzymes
Put into successively in 65 parts by weight of deionized water, stir;
2) put into successively again 1.9 weight portion lactic acid, 0.7 weight portion Pulvis Talci, 1.2 weight portion amine molybdates, 0.4 weight portion gather
Alkyl tri alkyl ammomium chloride, continues stirring, uniform to being sufficiently mixed, prepared desizing liquid;
3) fabric is padded process in desizing liquid, wash after taking-up and dry.
Embodiment 4
The desizing processing method of velour, comprises the steps:
1) by 1.2 weight portion ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1.3 parts by weight of ethylene base trimethoxies
Silane, 0.7 parts by weight of maleic acrylate copolymer, 1.2 weight portion cocoanut fatty acid diethanolamides, 21 weight starch
Enzyme puts in 65 parts by weight of deionized water successively, stirs;
2) put into successively again 1.9 weight portion lactic acid, 0.7 weight portion Pulvis Talci, 1.2 weight portion amine molybdates, 0.4 weight portion gather
Alkyl tri alkyl ammomium chloride, continues stirring, uniform to being sufficiently mixed, prepared desizing liquid;
3) fabric is padded process in desizing liquid, wash after taking-up and dry.
The desizing rate of the various embodiments described above is high, and the fabric after desizing is processed has higher capillary effect and mechanical property, favorably
In follow-up dyeing and printing process carrying out it is ensured that follow-up printing quality;And the effective removal because of slurry, improves the handss of fabric
Sense.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. the desizing processing method of velour is it is characterised in that comprise the steps:
1) by 1~2 weight portion ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1.3 parts by weight of ethylene base trimethoxy silicon
Alkane, 0.7 parts by weight of maleic acrylate copolymer, 1.2 weight portion cocoanut fatty acid diethanolamides, 21 weight starch enzymes
Put into successively in 65 parts by weight of deionized water, stir;
2) 1.9 weight portion lactic acid, 0.7 weight portion Pulvis Talci, 1.2 weight portion amine molybdates, the poly- alkyl of 0.4 weight portion are put into again successively
Tri alkyl ammomium chloride, continues stirring, uniform to being sufficiently mixed, prepared desizing liquid;
3) fabric is padded process in desizing liquid, wash after taking-up and dry.
2. the desizing processing method of velour according to claim 1 is it is characterised in that comprise the steps:
1) by 1 weight portion ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1.3 parts by weight of ethylene base trimethoxy silanes,
0.7 parts by weight of maleic acrylate copolymer, 1.2 weight portion cocoanut fatty acid diethanolamides, 21 weight starch enzymes according to
In secondary input 65 parts by weight of deionized water, stir;
2) 1.9 weight portion lactic acid, 0.7 weight portion Pulvis Talci, 1.2 weight portion amine molybdates, the poly- alkyl of 0.4 weight portion are put into again successively
Tri alkyl ammomium chloride, continues stirring, uniform to being sufficiently mixed, prepared desizing liquid;
3) fabric is padded process in desizing liquid, wash after taking-up and dry.
3. the desizing processing method of velour according to claim 1 is it is characterised in that comprise the steps:
1) by 2 weight portion ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1.3 parts by weight of ethylene base trimethoxy silanes,
0.7 parts by weight of maleic acrylate copolymer, 1.2 weight portion cocoanut fatty acid diethanolamides, 21 weight starch enzymes according to
In secondary input 65 parts by weight of deionized water, stir;
2) 1.9 weight portion lactic acid, 0.7 weight portion Pulvis Talci, 1.2 weight portion amine molybdates, the poly- alkyl of 0.4 weight portion are put into again successively
Tri alkyl ammomium chloride, continues stirring, uniform to being sufficiently mixed, prepared desizing liquid;
3) fabric is padded process in desizing liquid, wash after taking-up and dry.
4. the desizing processing method of velour according to claim 1 is it is characterised in that comprise the steps:
1) by 1.2 weight portion ethylenediamine polyoxyethylene oxypropylene block formula polyethers, 1.3 parts by weight of ethylene base trimethoxy silicon
Alkane, 0.7 parts by weight of maleic acrylate copolymer, 1.2 weight portion cocoanut fatty acid diethanolamides, 21 weight starch enzymes
Put into successively in 65 parts by weight of deionized water, stir;
2) 1.9 weight portion lactic acid, 0.7 weight portion Pulvis Talci, 1.2 weight portion amine molybdates, the poly- alkyl of 0.4 weight portion are put into again successively
Tri alkyl ammomium chloride, continues stirring, uniform to being sufficiently mixed, prepared desizing liquid;
3) fabric is padded process in desizing liquid, wash after taking-up and dry.