CN106336713A - Pulley for hoisting equipment - Google Patents
Pulley for hoisting equipment Download PDFInfo
- Publication number
- CN106336713A CN106336713A CN201610709896.XA CN201610709896A CN106336713A CN 106336713 A CN106336713 A CN 106336713A CN 201610709896 A CN201610709896 A CN 201610709896A CN 106336713 A CN106336713 A CN 106336713A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- wheel shaft
- metal wheel
- weight portion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a pulley for hoisting equipment. The pulley comprises a metal wheel shaft, which undergoes coating treatment. The coating treatment comprises the following steps: 1) successively pouring 1-2 parts by weight of sodium dodecyl benzene sulfonate, 1.1 parts by weight of coco fatty acid diethanol amide, 2.5 parts by weight of carboxymethyl cellulose and 0.8 part by weight of sodium n-butylnaphthalenesulfonate into 45 parts by weight of deionized water, and uniformly stirring; 2) successively pouring 5.6 parts by weight of 2-ethylhexyl acrylate, 9.8 parts by weight of hydrogenated polyisobutene, 1.3 parts by weight of secondary alkyl sodium sulfonate and 3.5 parts by weight of polyacrylate, continuously stirring until the materials are fully and uniformly mixed so as to prepare a coating treating fluid; and 3) impregnating the metal wheel shaft in the coating treating fluid, taking out the metal wheel shaft and drying. According to the pulley for hoisting equipment, the surface of the metal wheel shaft is coated with a protective film such that performance is good and surface smoothness is good.
Description
Technical field
The present invention relates to hanging device coaster.
Background technology
Existing hanging device coaster, antirust, abrasion-resistant, the antioxidation of its metal wheel shaft, corrosion-resistant, heat-resisting, cold-resistant, resistance to
Wait performance to have much room for improvement, and surface smoothness is also not ideal enough.
Content of the invention
It is an object of the invention to provide a kind of hanging device coaster, its metal wheel shaft is through aluminum coated steel, metal wheel
Axle surface is covered with protecting film, has excellent antirust, abrasion-resistant, antioxidation, corrosion-resistant, heat-resisting, cold-resistant, weather resistance, and table
Face fineness is good.
For achieving the above object, the technical scheme is that a kind of hanging device coaster of design, it includes metal wheel
Axle, through aluminum coated steel, described aluminum coated steel comprises the steps: this metal wheel shaft
1) by 1~2 weight portion dodecylbenzene sodium sulfonate, 1.1 weight portion lauric acid amide of ethanol, 2.5 weight portion carboxylics
Methylcellulose, 0.8 weight portion normal-butyl sodium naphthalene sulfonate put in 45 parts by weight of deionized water successively, stir;
2) 5.6 parts by weight of acrylic acid -2- Octyl Nitrites, 9.8 parts by weight of hydrogenated polyisobutylene, 1.3 weight are put into again successively
Part SAS, 3.5 parts by weight of polypropylene acid esters, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal wheel shaft is inserted dipping in coating treatment liquid, take out post-drying.
Preferably, hanging device coaster, it includes metal wheel shaft, this metal wheel shaft through aluminum coated steel, described overlay film
Process comprises the steps:
1) by 1 weight portion dodecylbenzene sodium sulfonate, 1.1 weight portion lauric acid amide of ethanol, 2.5 weight portion carboxymethyls
Cellulose, 0.8 weight portion normal-butyl sodium naphthalene sulfonate put in 45 parts by weight of deionized water successively, stir;
2) 5.6 parts by weight of acrylic acid -2- Octyl Nitrites, 9.8 parts by weight of hydrogenated polyisobutylene, 1.3 weight are put into again successively
Part SAS, 3.5 parts by weight of polypropylene acid esters, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal wheel shaft is inserted dipping in coating treatment liquid, take out post-drying.
Preferably, hanging device coaster, it includes metal wheel shaft, this metal wheel shaft through aluminum coated steel, described overlay film
Process comprises the steps:
1) by 2 weight portion dodecylbenzene sodium sulfonate, 1.1 weight portion lauric acid amide of ethanol, 2.5 weight portion carboxymethyls
Cellulose, 0.8 weight portion normal-butyl sodium naphthalene sulfonate put in 45 parts by weight of deionized water successively, stir;
2) 5.6 parts by weight of acrylic acid -2- Octyl Nitrites, 9.8 parts by weight of hydrogenated polyisobutylene, 1.3 weight are put into again successively
Part SAS, 3.5 parts by weight of polypropylene acid esters, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal wheel shaft is inserted dipping in coating treatment liquid, take out post-drying.
Preferably, hanging device coaster, it includes metal wheel shaft, this metal wheel shaft through aluminum coated steel, described overlay film
Process comprises the steps:
1) by 1.2 weight portion dodecylbenzene sodium sulfonate, 1.1 weight portion lauric acid amide of ethanol, 2.5 weight portion carboxylic first
Base cellulose, 0.8 weight portion normal-butyl sodium naphthalene sulfonate put in 45 parts by weight of deionized water successively, stir;
2) 5.6 parts by weight of acrylic acid -2- Octyl Nitrites, 9.8 parts by weight of hydrogenated polyisobutylene, 1.3 weight are put into again successively
Part SAS, 3.5 parts by weight of polypropylene acid esters, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal wheel shaft is inserted dipping in coating treatment liquid, take out post-drying.
Advantages of the present invention and having the beneficial effects that: provide a kind of hanging device coaster, its metal wheel shaft is through overlay film
Process, metal wheel shaft surface is covered with protecting film, there is excellent antirust, abrasion-resistant, antioxidation, corrosion-resistant, heat-resisting, cold-resistant, resistance to
Wait performance, and surface smoothness is good.
The performance of " coating treatment liquid " and purposes are determined by its component and proportioning, and in " coating treatment liquid " not
With group, branch influences each other, and component and its proportioning can determine the final performance of " coating treatment liquid ", such as fruit component and its proportioning not
Mutually coordinated, the beneficial effect that single component is brought, even can be eliminated by other components abatement, when serious, different groups
Split-phase is mutually conflicted, and does not have whole synthesis effect, produces negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly
Checking, obtain the optimal component of " coating treatment liquid " and proportioning so that multiple component combine, mutually coordinated and produce
Positive comprehensive effect.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more
Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Hanging device coaster, it includes metal wheel shaft, and through aluminum coated steel, described aluminum coated steel includes this metal wheel shaft
Following steps:
1) by 1~2 weight portion dodecylbenzene sodium sulfonate, 1.1 weight portion lauric acid amide of ethanol, 2.5 weight portion carboxylics
Methylcellulose, 0.8 weight portion normal-butyl sodium naphthalene sulfonate put in 45 parts by weight of deionized water successively, stir;
2) 5.6 parts by weight of acrylic acid -2- Octyl Nitrites, 9.8 parts by weight of hydrogenated polyisobutylene, 1.3 weight are put into again successively
Part SAS, 3.5 parts by weight of polypropylene acid esters, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal wheel shaft is inserted dipping in coating treatment liquid, take out post-drying.
Embodiment 2
Hanging device coaster, it includes metal wheel shaft, and through aluminum coated steel, described aluminum coated steel includes this metal wheel shaft
Following steps:
1) by 1 weight portion dodecylbenzene sodium sulfonate, 1.1 weight portion lauric acid amide of ethanol, 2.5 weight portion carboxymethyls
Cellulose, 0.8 weight portion normal-butyl sodium naphthalene sulfonate put in 45 parts by weight of deionized water successively, stir;
2) 5.6 parts by weight of acrylic acid -2- Octyl Nitrites, 9.8 parts by weight of hydrogenated polyisobutylene, 1.3 weight are put into again successively
Part SAS, 3.5 parts by weight of polypropylene acid esters, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal wheel shaft is inserted dipping in coating treatment liquid, take out post-drying.
Embodiment 3
Hanging device coaster, it includes metal wheel shaft, and through aluminum coated steel, described aluminum coated steel includes this metal wheel shaft
Following steps:
1) by 2 weight portion dodecylbenzene sodium sulfonate, 1.1 weight portion lauric acid amide of ethanol, 2.5 weight portion carboxymethyls
Cellulose, 0.8 weight portion normal-butyl sodium naphthalene sulfonate put in 45 parts by weight of deionized water successively, stir;
2) 5.6 parts by weight of acrylic acid -2- Octyl Nitrites, 9.8 parts by weight of hydrogenated polyisobutylene, 1.3 weight are put into again successively
Part SAS, 3.5 parts by weight of polypropylene acid esters, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal wheel shaft is inserted dipping in coating treatment liquid, take out post-drying.
Embodiment 4
Hanging device coaster, it includes metal wheel shaft, and through aluminum coated steel, described aluminum coated steel includes this metal wheel shaft
Following steps:
1) by 1.2 weight portion dodecylbenzene sodium sulfonate, 1.1 weight portion lauric acid amide of ethanol, 2.5 weight portion carboxylic first
Base cellulose, 0.8 weight portion normal-butyl sodium naphthalene sulfonate put in 45 parts by weight of deionized water successively, stir;
2) 5.6 parts by weight of acrylic acid -2- Octyl Nitrites, 9.8 parts by weight of hydrogenated polyisobutylene, 1.3 weight are put into again successively
Part SAS, 3.5 parts by weight of polypropylene acid esters, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal wheel shaft is inserted dipping in coating treatment liquid, take out post-drying.
Surface through metal wheel shaft in the various embodiments described above is covered with protecting film, has excellent antirust, abrasion-resistant, antioxygen
Change, corrosion-resistant, heat-resisting, cold-resistant, weather resistance, and surface smoothness is good.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. hanging device coaster is it is characterised in that it includes metal wheel shaft, and this metal wheel shaft, through aluminum coated steel, described covers
Film process comprises the steps:
1) by 1~2 weight portion dodecylbenzene sodium sulfonate, 1.1 weight portion lauric acid amide of ethanol, 2.5 weight portion carboxymethyls
Cellulose, 0.8 weight portion normal-butyl sodium naphthalene sulfonate put in 45 parts by weight of deionized water successively, stir;
2) 5.6 parts by weight of acrylic acid -2- Octyl Nitrites, 9.8 parts by weight of hydrogenated polyisobutylene, 1.3 weight portions are put into again successively secondary
Sodium alkyl sulfonate, 3.5 parts by weight of polypropylene acid esters, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal wheel shaft is inserted dipping in coating treatment liquid, take out post-drying.
2. hanging device coaster according to claim 1 is it is characterised in that it includes metal wheel shaft, this metal wheel shaft
Through aluminum coated steel, described aluminum coated steel comprises the steps:
1) by 1 weight portion dodecylbenzene sodium sulfonate, 1.1 weight portion lauric acid amide of ethanol, 2.5 weight portion carboxymethyl celluloses
Element, 0.8 weight portion normal-butyl sodium naphthalene sulfonate put in 45 parts by weight of deionized water successively, stir;
2) 5.6 parts by weight of acrylic acid -2- Octyl Nitrites, 9.8 parts by weight of hydrogenated polyisobutylene, 1.3 weight portions are put into again successively secondary
Sodium alkyl sulfonate, 3.5 parts by weight of polypropylene acid esters, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal wheel shaft is inserted dipping in coating treatment liquid, take out post-drying.
3. hanging device coaster according to claim 1 is it is characterised in that it includes metal wheel shaft, this metal wheel shaft
Through aluminum coated steel, described aluminum coated steel comprises the steps:
1) by 2 weight portion dodecylbenzene sodium sulfonate, 1.1 weight portion lauric acid amide of ethanol, 2.5 weight portion carboxymethyl celluloses
Element, 0.8 weight portion normal-butyl sodium naphthalene sulfonate put in 45 parts by weight of deionized water successively, stir;
2) 5.6 parts by weight of acrylic acid -2- Octyl Nitrites, 9.8 parts by weight of hydrogenated polyisobutylene, 1.3 weight portions are put into again successively secondary
Sodium alkyl sulfonate, 3.5 parts by weight of polypropylene acid esters, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal wheel shaft is inserted dipping in coating treatment liquid, take out post-drying.
4. hanging device coaster according to claim 1 is it is characterised in that it includes metal wheel shaft, this metal wheel shaft
Through aluminum coated steel, described aluminum coated steel comprises the steps:
1) will be fine to 1.2 weight portion dodecylbenzene sodium sulfonate, 1.1 weight portion lauric acid amide of ethanol, 2.5 weight portion carboxymethyls
Dimension element, 0.8 weight portion normal-butyl sodium naphthalene sulfonate put in 45 parts by weight of deionized water successively, stir;
2) 5.6 parts by weight of acrylic acid -2- Octyl Nitrites, 9.8 parts by weight of hydrogenated polyisobutylene, 1.3 weight portions are put into again successively secondary
Sodium alkyl sulfonate, 3.5 parts by weight of polypropylene acid esters, continue stirring, uniform to being sufficiently mixed, prepared coating treatment liquid;
3) metal wheel shaft is inserted dipping in coating treatment liquid, take out post-drying.