CN106336624A - Polyethylene terephthalate (PET) master batch and preparation method thereof - Google Patents
Polyethylene terephthalate (PET) master batch and preparation method thereof Download PDFInfo
- Publication number
- CN106336624A CN106336624A CN201510424985.5A CN201510424985A CN106336624A CN 106336624 A CN106336624 A CN 106336624A CN 201510424985 A CN201510424985 A CN 201510424985A CN 106336624 A CN106336624 A CN 106336624A
- Authority
- CN
- China
- Prior art keywords
- master batch
- pet
- preparation
- pet master
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a PET master batch and a preparation method thereof, especially to a PET master batch capable of preventing fisheye-like bubbles and capable of preventing aging to some extent and a preparation method thereof. The PET master batch comprises 70 to 82% of a carrier, 1 to 5% of a coloring agent, 0.5 to 1.5% of a lubricant, 5 to 8% of an anti-adhesion agent, 9 to 11% of a nucleating agent, 0.5 to 1.5% of an anti-oxidant and 1.5 to 2.5% of a dehydrating agent. According to a technical scheme in the invention, a proper amount of the dehydrating agent is added to prevent PET from the phenomenon of fisheye-like bubbles, so a film has better strength, a cable material has better insulating properties, and a product has a smooth surface, high transparency and improved physical properties; and PET ageing is prevented to some extent, and PET has longer service life and better physical properties.
Description
Technical field
The present invention relates to a kind of pet master batch and preparation method thereof, particularly one kind prevents
Fish-eye shaped bubble simultaneously can prevent aging pet master batch and its preparation side to a certain extent
Method.
Background technology
Pet (polyethylene terephthalate), in nineteen forty-one first by Britain
J.tt.whinfield is succeeded in developing with j.t.dickon, and pet is existing as fibrous raw material
The history of 70 years, chemical formula is-och2-ch2ococ6h4co.Due to its good power
The property learned;Oil resistant, resistance to fatty, resistance to diluted acid, diluted alkaline, resistance to most of solvents;High temperature resistant, low temperature
Property;Resistance gas and water, oil and peculiar smell;Transparency is high, can shielding of ultraviolet, glossiness is good;
Nontoxic, tasteless, wholesomeness etc. characteristic, be widely used in packaging for foodstuff, fiber,
, in pet master batch common at present, there is fish-eye shaped gas in film, engineering plastics, polyester bottles etc.
Bubble, the presence of fish-eye shaped bubble can affect the insulating properties of thin film strength, CABLE MATERIALS, make system
Product rough surface, also can reduce the physical property of whole product;Meanwhile, pet also exists easily
Make moist aging problem, the mechanical performance of aging pet can drastically decline.
Content of the invention
The technical problem to be solved be provide a kind of prevent fish-eye shaped bubble,
And aging pet master batch of pet and preparation method thereof can be prevented to a certain extent.
For solving above-mentioned technical problem, technical scheme is as follows:
A kind of pet master batch, it is by carrier, colouring agent, lubricant, anti-blocking agent, nucleation
Agent, antioxidant and dehydrating agent composition;Wherein each component percetage by weight is: carrier: 70%~
82%th, colouring agent: 1%~5%, lubricant: 0.5%~1.5%, anti-blocking agent: 5%~8%,
Nucleator: 9%~11%, antioxidant: 0.5%~1.5%, dehydrating agent 1.5%~2.5%.
Further, described carrier is pet resin.
Further, described colouring agent be titanium dioxide, cadmium red, chrome yellow, zinc powder, three oxidation two
One of iron.
Further, described lubricant is atoleine (Chinese wax), microcrystalline wax, polyethylene
One of wax.
Further, described anti-blocking agent is in synthetic silica or gas-phase silica
Kind.
Further, described nucleator is one of polyolefin elastomer poe, Sodium Benzoate.
Further, described antioxidant is pentaerythritol ester, thio-2 acid dibasic acid esters, or
The mixture of the two.
A kind of preparation method of pet master batch, comprises the following steps:
Above-mentioned material is prepared in proportion compound;
The compound preparing is added high-speed mixer, mixer rotating speed controls 760~1400
Rev/min, incorporation time is 8~20 minutes, and mixing temperature is maintained at 95~170 degrees Celsius;
Again well-mixed material is entered melt blending in dual-screw-stem machine, melt temperature controls
260~270 degrees Celsius, screw speed is 150~400 revs/min;
Obtain pet of the present invention after the shearing of screw rod, mixing, granulation, drying
Master batch.
The positive effect of the present invention: in technical solution of the present invention, add appropriate dehydrating agent,
Prevent pet from flake phenomenon occurring, make that thin film strength is higher, CABLE MATERIALS insulating properties more
Good, also make that product surface is smooth, transparency is high, improve the physical property of pet product;
Meanwhile, prevent pet aging to a certain extent, make the service life of pet longer, physics
Characteristic is more preferably.
Specific embodiment
In order that the object, technical solutions and advantages of the present invention become more apparent, with reference to
Specific embodiment and embodiment, are described in further details to the present invention.Here, the present invention
Exemplary embodiment and its illustrate for explaining the present invention, but be not intended as to the present invention's
Limit, any implication suitable with the claims in the present invention and scope are all considered as being included in weighing
In the range of sharp claim.
With reference to embodiment, the present invention will be further explained:
Embodiment 1
At normal temperatures and pressures, by the component pet resin of following weight percentage: 70%, titanium white
Powder: 1%, Chinese wax: 0.5%, gas-phase silica: 5%, polyolefin elastomer poe:9%,
Pentaerythritol ester: after 0.5%, dehydrating agent 1.5% mixes, mixture is put into rotating speed and exists
760 revs/min, mixing temperature be maintained in 95 degrees Celsius of high-speed mixer, incorporation time
For 20 minutes;Then by mixed material put into again melt temperature be 260 degrees Celsius,
Screw speed carries out shearing, kneads for 150 revs/min of double screw extruders, after made again
Grain, it is dried to obtain the pet master batch of the present invention.
Embodiment 2
At normal temperatures and pressures, by the component pet resin of following weight percentage: 82%, three oxygen
Change two iron: 5%, microcrystalline wax: 1.5%, silica: 8%, Sodium Benzoate: 11%,
Pentaerythritol ester: after 1.5%, dehydrating agent 2.5% mixes, mixture is put into rotating speed and exists
1400 revs/min, mixing temperature is maintained in 170 degrees Celsius of high-speed mixer, during mixing
Between be 8 minutes;Then by mixed material put into again melt temperature be 270 degrees Celsius,
Screw speed carries out shearing, kneads for 400 revs/min of double screw extruders, after made again
Grain, it is dried to obtain the pet master batch of the present invention.
Comparative example 1
At normal temperatures and pressures, by the component pet resin of following weight percentage: 60%, cadmium red:
8%th, Chinese wax: 3%, gas-phase silica: 11%, Sodium Benzoate: 15%, pentaerythritol ester:
After 3% mixes, by mixture put into rotating speed 600 revs/min, mixing temperature is maintained at
In 80 degrees Celsius of high-speed mixer, incorporation time is 30 minutes;Then by mixed thing
Material is put into melt temperature again and is 200 degrees Celsius, and screw speed is 100 revs/min of twin-screws
Extruder carries out shearing, kneads, after carry out again granulating, be dried to obtain contrast master batch.
By the master batch of embodiment and comparative example preparation, added in pet resin with 4% amount, squeeze
After going out granulation, the following various characteristics of judgement respectively:
Fish-eye shaped bubble is tested: takes 100 grams of samples to carry out observing whether it has fish-eye shaped bubble to produce
Raw.
Tensile strength is tested: and prepare test bars simultaneously, temperature 100 warm and humid heat Celsius,
Time is to be tested in the case of 2 days, tests its tensile strength after test.
Smoothness is tested: by counterweight that is overlapping for 20 built-in testing pieces and pressing upper 8 kilograms, and 150
Degree Celsius heater box in shelve 1 hour, then take out cooling, and observe after 48 hrs
Peel off difficulty.
Concrete comparing result is as follows:
Contrasted by above table it is found that instant invention overcomes depositing when processing pet master batch
In the situation of fish-eye shaped bubble, and pet master batch is made to have good smoothness, and one
Determine can to prevent that pet's is aging in degree.
Claims (8)
1. a kind of pet master batch, comprises following component and weight content:
Carrier: 70%~82%, colouring agent: 1%~5%, lubricant: 0.5%~1.5%,
Anti-blocking agent: 5%~8%, nucleator: 9%~11%, antioxidant: 0.5%~1.5%,
Dehydrating agent 1.5%~2.5%.
2. pet master batch as claimed in claim 1 and preparation method thereof it is characterised in that:
Described carrier is pet resin.
3. pet master batch as claimed in claim 1 and preparation method thereof it is characterised in that:
Described colouring agent is titanium dioxide, cadmium red, chrome yellow, zinc powder, in di-iron trioxide one
Kind.
4. pet master batch as claimed in claim 1 and preparation method thereof it is characterised in that:
Described lubricant is one of atoleine, microcrystalline wax, Tissuemat E.
5. pet master batch as claimed in claim 1 and preparation method thereof it is characterised in that:
Described anti-blocking agent is one of synthetic silica or gas-phase silica.
6. pet master batch as claimed in claim 1 and preparation method thereof it is characterised in that:
Described nucleator is one of polyolefin elastomer poe, Sodium Benzoate.
7. pet master batch as claimed in claim 1 and preparation method thereof it is characterised in that:
Described antioxidant is pentaerythritol ester, thio-2 acid dibasic acid esters, or the two is mixed
Compound.
8. a kind of preparation method of pet master batch, comprises the following steps:
Above-mentioned material is prepared in proportion compound;
The compound preparing is added high-speed mixer, mixer rotating speed controls 760~1400
Rev/min, incorporation time is 8~20 minutes, and mixing temperature is maintained at 95~170 degrees Celsius;
Again well-mixed material is entered melt blending in dual-screw-stem machine, melt temperature controls
At 260~270 degrees Celsius, screw speed is 150~400 revs/min;
Obtain pet of the present invention after the shearing of screw rod, mixing, granulation, drying
Master batch.