CN106336111A - Temperable environment-friendly film-plated decorative glass and manufacturing process - Google Patents
Temperable environment-friendly film-plated decorative glass and manufacturing process Download PDFInfo
- Publication number
- CN106336111A CN106336111A CN201610862008.8A CN201610862008A CN106336111A CN 106336111 A CN106336111 A CN 106336111A CN 201610862008 A CN201610862008 A CN 201610862008A CN 106336111 A CN106336111 A CN 106336111A
- Authority
- CN
- China
- Prior art keywords
- glass
- plated film
- environmental protection
- tempering
- pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to temperable environment-friendly film-plated decorative glass. The temperable environment-friendly film-plated decorative glass comprises a glass body, and is characterized in that notches or bumps are arranged on one side surface of the glass body; a texture pattern is arranged on the surface of one side surface, having the notches or the bumps, of the glass body; the surface of the texture pattern is plated with a metal film. By adopting the structure that the notches or the bumps are arranged on one side surface of the glass body, the texture pattern is arranged on the surface of one side surface, having the notches or the bumps, of the glass body, and the surface of the texture pattern is plated with the metal film, the metal film can achieve shock resistance, ultraviolet protection and radiation protection, the notches or the bumps can achieve pattern decoration, and the notches or the bumps, the tiny texture pattern and the metal film are combined to form slow refraction and reflection, so that another light pollution is not caused on the basis of environment friendliness and energy conversation; meanwhile, through special-angle refraction, seen from different angles, the temperable environment-friendly film-plated decorative glass shows different color changes, so that the decorative effect is further improved. The temperable environment-friendly film-plated decorative glass is very suitable for outdoor or indoor decoration or applied to a curtain wall.
Description
Technical field
The present invention relates to a kind of environmental protection plated film ambetti and its manufacture craft, belong to ambetti preparing technical field.
Background technology
In building decoration engineering, glass is the class ornament materials being most widely used.With the development of building industry, glass
Architectural must use more and more extensive.Glass decoration functions till now from initially single daylighting function, gradually develop
The main flow of non-line generation building.And architectural decorative glass is to be leading with design concept and function, using glass material and artistic skill
Ingeniously, become unified harmonious entirety with decorated building, both enriched art of architecture image, and also can improve utility function,
Economic worth and social value.
Now ambetti general on the market, seldom using having power saving function, and decorative colors arrange by colorant completely
It is rendered into the decorative effect of fixation, its cladding glass, some adopt the coated glass of energy-conservation, can reach certain sheltering coefficient and biography
, to realize energy-saving and environmental protection, but due to being all to adopt plane, easily specular light reflections in hot coefficient, causes alternative light dirty
Dye.
Content of the invention
The present invention be directed to prior art exist problem, provide one kind can tempering environmental protection plated film ambetti, be one kind both
Suitably indoor and outdoor decorate or be used in cladding glass, energy-saving and environmental protection can be realized again, not result in another kind of light pollution
Environmental protection plated film ambetti, will not fade, resistance to decoration, and aesthetic is changeable persistently, can out of doors or interior is decorated or answered
The glass installed for curtain wall.
In order to solve the above problems, the technical solution adopted in the present invention is:
One kind can tempering environmental protection plated film ambetti, including glass body it is characterised in that: described glass body one side
It is provided with recess or salient point, described be provided with recess or the glass body one side surface of salient point is provided with skin texture line chart, skin texture
One or more layers metal film has been plated on line surface.
As the improvement further of technology, described skin texture line is a kind of skin texture line of obtuse angle shape.
As the improvement further of technology, described recess or salient point be one kind be square, triangle, circle, five-pointed star,
Quadrangle or decorative pattern shape.
As the improvement further of technology, the shape of described recess or salient point and quantity are as needed for decoration Pattern Design
Shape or quantity depending on.
As the improvement further of technology, described metal film is a kind of lowe metal film, and its thickness is 40nm
100nm.
As the improvement further of technology, described ambetti is a kind of glass through safety glass process.
One kind can tempering environmental protection plated film ambetti it is characterised in that: production technology, comprise the following steps:
1) one block of suitable plate glass, the wheel of the decorative pattern profile designing are chosen on plate glass one side
Exterior feature, is got ready the mould of decorative pattern, and gets the skin texture line mould being met with pattern, glass size ready, pattern mold is placed on
Plate glass bottom;
2) put into high temperature furnace and high-temperature heating is carried out to glass body and mould, until plate glass one side surface thermosol shape
Become mould pattern, realize recess or the salient point of pattern, molten solid shaping, carry the compacting of pattern one side in vitreum and form skin texture
Line, along with the furnace cooling forms recess or salient point and micro- trunk manages the glass of line;
3) and then using vacuum coating equipment plated film is carried out to vitreum;
4) finally carry out tempering process and form environmental protection plated film ambetti.
Described step 2) high-temperature heating temperature be 650 DEG C -850 DEG C, warm-up time be 10~20 minutes.
Described step 3) with 4) in can exchange step and realize, you can first adopt vacuum again to after the process of vitreum tempering
Coating machine carries out plated film to vitreum, eventually forms environmental protection plated film ambetti.
The invention has the beneficial effects as follows:
Glass one side is provided with recess or salient point, the described glass body one side surface setting being provided with recess or salient point
Skin texture line, skin texture line has plated layer of metal film on surface, and metal film can achieve that shatter-proof, antiultraviolet, anti-good fortune are penetrated, recess or salient point
Pattern decorative can be made, its recess of metal-coated membrane or salient point micro- skin texture line are combined with metal film, form slow refraction, reflection, retain
On the basis of environmental protection, folding energy, do not result in another kind of light pollution, simultaneously this special angle refraction, different angles are taken a fancy to, and can be in
Existing different color change, improves decorative effect further.It is highly suitable for open air or interior to be decorated or be applied to curtain
The glass that wall is installed.
Form meeting variable color, resistance to decoration, aesthetic is changeable persistently, the glass of suitably indoor, open air and curtain wall, and make work
Skill is simple, with low cost, it is easy to accomplish industrialized production.
Brief description
Fig. 1 is the structural reference figure of the present invention;
Fig. 2 is that the lateral parts of the present invention amplify with reference to figure.
Specific embodiment
One kind can tempering environmental protection plated film ambetti, including glass body 1 it is characterised in that: described glass body 1 side
Face is provided with recess or salient point 2, described be provided with recess or the glass body one side surface of salient point 2 is provided with skin texture line figure,
One or more layers metal film 3 has been plated on skin texture line surface.
Described micro- skin texture line is a kind of skin texture line of obtuse angle shape.
Described recess or salient point 2 be one kind be square, triangle, circle, five-pointed star, quadrangle or decorative pattern shape
Shape.
Depending on the shape of described recess or salient point 2 and quantity are shape or quantity as needed for decoration Pattern Design.
Described metal film is a kind of lowe metal film, and its thickness is 40nm 100nm.
Described ambetti is a kind of glass through safety glass process.
One kind can tempering environmental protection plated film ambetti, its production technology, comprise the following steps:
1) one block of suitable plate glass, the wheel of the decorative pattern profile designing are chosen on plate glass one side
Exterior feature, is got ready the mould of decorative pattern, and gets the skin texture line mould being met with pattern, glass size ready, pattern mold is placed on
Plate glass bottom;
2) put into high temperature furnace and high-temperature heating is carried out to glass body and mould, until plate glass one side surface thermosol shape
Become mould pattern, realize recess or the salient point of pattern, molten solid shaping, carry the compacting of pattern one side in vitreum and form skin texture
Line, along with the furnace cooling forms recess or salient point and micro- trunk manages the glass of line;
3) and then using vacuum coating equipment plated film is carried out to vitreum;
4) finally carry out tempering process and form environmental protection plated film ambetti.
Described step 2) high-temperature heating temperature be 650 DEG C -850 DEG C, warm-up time be 10~20 minutes.
Described step 3) with 4) in can exchange step and realize, you can first adopt vacuum again to after the process of vitreum tempering
Coating machine carries out plated film to vitreum, eventually forms environmental protection plated film ambetti.
Embodiment 1
One kind can tempering environmental protection plated film ambetti, including glass body 1 it is characterised in that: described glass body 1 side
Face is provided with recess 2, and the described glass body one side surface being provided with recess 2 is provided with skin texture line, and skin texture line surface is plated
Layer of metal film 3.
Its manufacture craft, comprises the following steps:
Choose 10 millimeters of plate glass of one piece of thickness, the little square grid decorative pattern designing on plate glass one side
The profile of profile, gets the mould of little square grid decorative pattern ready, and get ready meet with pattern, glass size there is skin texture line
Mould, is placed on plate glass bottom pattern mold, puts into high temperature furnace and carries out 700 DEG C of high-temperature heatings 12 to glass body and mould
Minute, until plate glass one side surface thermosol forms mould pattern, realize the little square grid of multiple recesses of pattern, molten solid
Shape, then use micro- skin texture line mould with keeping warm mode, carry the compacting of pattern one side in vitreum and form skin texture line, cold with stove
But form the glass of recess or salient point and skin texture line, then plated film is carried out using vacuum coating equipment, finally carry out tempering and process shape
Become environmental protection plated film ambetti.
Embodiment 2
One kind can tempering environmental protection plated film ambetti, including glass body 1 it is characterised in that: described glass body 1 side
Face is provided with salient point 2, and the described glass body one side surface being provided with salient point 2 is provided with uniformly micro- skin texture line, micro- skin texture line
Double layer of metal film 3 has been plated on surface.
Its manufacture craft, comprises the following steps:
Choose 10 millimeters of plate glass of one piece of thickness, outside the small circular decorative pattern designing on plate glass one side
The profile of shape, gets the mould of small circular decorative pattern ready, and get ready meet with pattern, glass size there is skin texture line mould
Tool, is placed on plate glass bottom pattern mold, puts into high temperature furnace and carry out 10 points of 850 DEG C of high-temperature heatings to glass body and mould
Clock, until plate glass one side surface thermosol forms mould pattern, realizes the small circular of multiple salient points of pattern, molten consolidates into
Shape, then use micro- skin texture line mould with keeping warm mode, carry the compacting of pattern one side in vitreum and form skin texture line, along with the furnace cooling
Form the glass of recess or salient point and skin texture line, then plated film is carried out using vacuum coating equipment, finally carry out tempering process and formed
Environmental protection plated film ambetti.
Embodiment 3
One kind can tempering environmental protection plated film ambetti, including glass body 1 it is characterised in that: described glass body 1 side
Face is provided with recess 2, and the described glass body one side surface being provided with recess 2 is provided with skin texture line, and skin texture line surface is plated
Layer of metal film 3.
Its manufacture craft, comprises the following steps:
Choose 10 millimeters of plate glass of one piece of thickness, the little square grid decorative pattern designing on plate glass one side
The profile of profile, is got ready the mould of little square grid decorative pattern, and gets the skin texture line mould being met with pattern, glass size ready
Tool, is placed on plate glass bottom pattern mold, puts into high temperature furnace and carry out 20 points of 650 DEG C of high-temperature heatings to glass body and mould
Clock, until plate glass one side surface thermosol forms mould pattern, realizes the little square grid of multiple recesses of pattern, molten consolidates into
Shape, then use skin texture line mould with keeping warm mode, carry the compacting of pattern one side in vitreum and form skin texture line, along with the furnace cooling shape
Become the glass of recess or salient point and skin texture line, then plated film is carried out using vacuum coating equipment, finally carry out tempering process and form ring
Protect plated film ambetti.
Embodiment 4
One kind can tempering environmental protection plated film ambetti, including glass body 1 it is characterised in that: described glass body 1 side
Face is provided with recess 2, and the described glass body one side surface being provided with recess 2 is provided with skin texture line, and skin texture line surface is plated
Three-layered metal film 3.
Its manufacture craft, comprises the following steps:
Choose 10 millimeters of plate glass of one piece of thickness, the little square grid decorative pattern designing on plate glass one side
The profile of profile, is got ready the mould of little square grid decorative pattern, and gets the skin texture line mould being met with pattern, glass size ready
Tool, is placed on plate glass bottom pattern mold, puts into high temperature furnace and carry out 11 points of 750 DEG C of high-temperature heatings to glass body and mould
Clock, until plate glass one side surface thermosol forms mould pattern, realizes the little square grid of multiple recesses of pattern, molten consolidates into
Shape, then use skin texture line mould with keeping warm mode, carry the compacting of pattern one side in vitreum and form skin texture line, along with the furnace cooling shape
Become the glass of recess or salient point and skin texture line, then using carrying out tempering process, finally carry out vacuum coating equipment and carry out plated film shape
Become environmental protection plated film ambetti.
In the present invention, glass one side is provided with recess or salient point, the described glass body one side being provided with recess or salient point
Surface arranges skin texture line, and skin texture line has plated layer of metal film on surface, and metal film can achieve that shatter-proof, antiultraviolet, anti-good fortune are penetrated, recessed
Mouth or salient point can make pattern decorative, and its recess of metal-coated membrane or salient point micro- skin texture line are combined with metal film, form slow refraction, instead
Penetrate, on the basis of retaining environmental protection, rolling over energy, do not result in another kind of light pollution, simultaneously this special angle refraction, different angles
Take a fancy to, different color change can be presented, improve decorative effect further.Be highly suitable for open air or interior decorated or
It is applied to the glass of curtain wall installation.
Form meeting variable color, resistance to decoration, aesthetic is changeable persistently, the glass of suitably indoor, open air and curtain wall, and make work
Skill is simple, with low cost, it is easy to accomplish industrialized production.
Claims (9)
1. one kind can tempering environmental protection plated film ambetti, including glass body (1) it is characterised in that: described glass body (1)
Side is provided with recess or salient point (2), described is provided with recess or the glass body one side surface of salient point (2) is provided with skin texture line
Figure, skin texture line surface has been plated one or more layers metal film (3).
2. one kind according to claim 1 can tempering environmental protection plated film ambetti it is characterised in that: described skin texture line is
A kind of skin texture line figure of obtuse angle shape.
3. one kind according to claim 1 can tempering environmental protection plated film ambetti it is characterised in that: described recess or convex
Point (2) be one kind be square, triangle, circle, five-pointed star, quadrangle or decorative pattern shape.
4. one kind according to claim 3 can tempering environmental protection plated film ambetti it is characterised in that: described recess or convex
Depending on the shape of point (2) and quantity are shape or quantity as needed for decoration Pattern Design.
5. one kind according to claim 1 can tempering environmental protection plated film ambetti it is characterised in that: described metal film is
A kind of lowe metal film, its thickness is 40nm 100nm.
6. one kind according to claim 1 can tempering environmental protection plated film ambetti it is characterised in that: described ambetti
It is a kind of glass through safety glass process.
7. one kind of arbitrary the claims can tempering environmental protection plated film ambetti it is characterised in that: production technology, including with
Lower step:
1) choose one block of suitable plate glass, the profile of the decorative pattern profile designing on plate glass one side, standby
The mould of good decorative pattern, and get the skin texture line mould meeting with pattern, glass size ready, pattern mold is placed on flat board glass
Glass bottom;
2) put into high temperature furnace and high-temperature heating is carried out to glass body and mould, until plate glass one side surface thermosol forms mould
Tool pattern, realizes recess or the salient point of pattern, molten solid shaping, carries the compacting of pattern one side in vitreum and form skin texture line, with
Stove is cooled into recess or salient point and micro- trunk manages the glass of line;
3) and then using vacuum coating equipment plated film is carried out to vitreum;
4) finally carry out tempering process and form environmental protection plated film ambetti.
8. according to claim 7 a kind of can tempering environmental protection plated film ambetti production technology it is characterised in that: described
Step 2) high-temperature heating temperature be 650 DEG C -850 DEG C, warm-up time be 10~20 minutes.
9. according to claim 7 a kind of can tempering environmental protection plated film ambetti production technology it is characterised in that: described
Step 3) with 4) and in can exchange step and realize, you can first to adopting vacuum coating equipment after the process of vitreum tempering again to glass
Body carries out plated film, eventually forms environmental protection plated film ambetti.