CN106329338A - Electric power cabinet with antibacterial effect - Google Patents
Electric power cabinet with antibacterial effect Download PDFInfo
- Publication number
- CN106329338A CN106329338A CN201610795627.XA CN201610795627A CN106329338A CN 106329338 A CN106329338 A CN 106329338A CN 201610795627 A CN201610795627 A CN 201610795627A CN 106329338 A CN106329338 A CN 106329338A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- electric power
- power cabinet
- resin
- cabinet body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an electric power cabinet with an antibacterial effect, which comprises an electric power cabinet body, an LED lamp, a voltmeter, guide wheels, a drying agent box, a thermometer, a humidity sensor and a cooling fan, wherein the LED lamp is arranged at the top part of the electric power cabinet body, the guide wheels are arranged at the bottom part of the electric power cabinet body, the voltmeter, the thermometer and the drying agent box are arranged inside the electric power cabinet body, the humidity sensor is arranged at the inner wall of the side surface of the electric power cabinet body, and the cooling fan is arranged at the inner wall of the top part of the electric power cabinet body.
Description
Technical field
The application relates to electric power cabinet field, particularly relates to a kind of electric power cabinet with antibacterial effect.
Background technology
Electric power cabinet is a kind of widely used power system final stage device, use relatively decentralized in duty ratio, loop is less
Occasion.
Due to electric power cabinet application extensive, its cabinet surfaces externally and internally have a large amount of antibacterial exist, due to current electric power cabinet one
As not there is autonomous sterilizing function, the personal safety of operator is caused the biggest hidden danger by it.
Summary of the invention
It is desirable to provide a kind of electric power cabinet with antibacterial effect, to solve problem set forth above.
Embodiments of the invention provide a kind of electric power cabinet with antibacterial effect, including electric power cabinet body, LED,
Voltmeter, directive wheel, desiccant case, thermometer, humidity sensor, heat emission fan, described electric power cabinet bodies top is provided with LED,
Electric power cabinet body bottom portion is provided with directive wheel, and electric power cabinet body interior is provided with voltmeter, thermometer, desiccant case, electric power cabinet body
Side inner walls is provided with humidity sensor, and electric power cabinet bodies top inwall is provided with heat emission fan, and described electric power cabinet body surfaces externally and internally sets
There is antibacterial resin.
The technical scheme that embodiments of the invention provide can include following beneficial effect:
The present invention is provided with anti-biotic material at electric power cabinet body surfaces externally and internally, antibacterial resin solidify to form, and it is to large intestine bar
Bacterium and staphylococcus glucose bacterium have obvious bactericidal effect, simultaneously because the use of additive, the variable color effect of this antibacterial resin
The most inconspicuous, thus solve problem set forth above.
Aspect and advantage that the application adds will part be given in the following description, and part will become from the following description
Obtain substantially, or recognized by the practice of the application.It should be appreciated that above general description and details hereinafter only describe
It is exemplary and explanatory, the application can not be limited.
Accompanying drawing explanation
The invention will be further described to utilize accompanying drawing, but the embodiment in accompanying drawing does not constitute any limit to the present invention
System, for those of ordinary skill in the art, on the premise of not paying creative work, it is also possible to obtain according to the following drawings
Other accompanying drawing.
Fig. 1 is the structural representation of electric power cabinet of the present invention.
Fig. 2 is the Making programme figure of antibacterial resin of the present invention.
Detailed description of the invention
Here will illustrate exemplary embodiment in detail, its example represents in the accompanying drawings.Explained below relates to
During accompanying drawing, unless otherwise indicated, the same numbers in different accompanying drawings represents same or analogous key element.Following exemplary embodiment
Described in embodiment do not represent all embodiments consistent with the present invention.On the contrary, they are only with the most appended
The example of the apparatus and method that some aspects that described in detail in claims, the present invention are consistent.
In productive life, ubiquitous due to harmful levels of pathogens, the health of people is caused the biggest threat by it.Utilize sterilization
Anti-biotic material suppresses and kills the growth of noxious bacteria, breeding is the effective way preventing spread of germs.Currently, anti-biotic material is
Through be widely used in the daily production of people with in life, be such as applied to plastic product with in sanitary ware.
Anti-biotic material is a kind of new material to microorganism with the powerful ability of killing or rejection ability, the most extensively should
In people's daily life with industrial and agricultural development, at present, anti-biotic material is more refers to that adding certain antibiotic substance resists
Microbial inoculum, so that material has suppression or kills the ability of the microorganism being attached to its surface self, such as anti-bacteria ceramic, antibacterial
Metal, anti-bacterial fibre, antibiotic plastic etc..
Antibacterial is generally divided into organic antibacterial agent and inorganic antiseptic.Organic antibacterial agent is with organic acid, phenols, quaternary ammonium
The Organic substances such as salt are the antibacterial of antimicrobial component, and inorganic antiseptic is mainly by resisting that the metals itself such as silver, copper, zinc have
Bacterium ability, by methods such as physical absorption or ion exchanges, is fixed on surface or the hole of porous material by metals such as silver, copper, zinc
In road, it is then added in goods obtain the material with antibiotic property.Wherein, organic antibacterial agent can effectively suppress to have and falls ill
Bacterium, mycete result from breeding, instant effect, but the shortcoming such as existence and stability is poor, easily decompose, persistency is poor, toxicity is big, for a long time
Use harmful；Inorganic antiseptic is the emphasis of research at present, has the advantages such as hypotoxicity, thermostability, persistency, is fine
The antibacterial kinds of life product suitable such as dimension, plastics, building materials.
Additionally, zeolite is the crystalline aluminosilicate of a kind of alkali metal or alkaline-earth metal, having another name called molecular sieve, its structure is silicon
The three dimensional skeletal structure that oxygen tetrahedron and aluminum-oxygen tetrahedron share oxygen atom and constitute, has bigger specific surface area, due to bone
Aluminum in frame-oxygen tetrahedron electricity price is uneven, for reaching electrostatic equilibrium, must be in conjunction with the metal cation such as sodium, calcium in structure, its
Can be partially or completely exchanged by other cations so that zeolite has the strongest cation exchange capacity (CEC)；When preparing zeolite antibacterial agent, will boiling
Stone impregnated in solution, the alkali metal in silver ion displacement is zeolite structured or alkaline-earth metal ions, utilizes the antibiotic property of silver ion
Can so that zeolite has antibacterial ability.
But, existing Ag Loaded Zeolite Antimicrobial yet suffers from antibacterial ability to be needed to improve, and anti-tarnishing ability is not strong, stability
The problems such as difference.
Application scenarios one:
Fig. 1 shows a kind of electric power cabinet with antibacterial effect that embodiments herein relates to, including electric power cabinet body
1, LED 2, voltmeter 3, directive wheel 4, desiccant case 5, thermometer 6, humidity sensor 7, heat emission fan 8, described electric power cabinet body
1 top is provided with LED 2, is provided with directive wheel 4 bottom electric power cabinet body 1, and electric power cabinet body 1 is internal is provided with voltmeter 3, thermometer
6, desiccant case 5, electric power cabinet body 1 side inner walls is provided with humidity sensor 7, and electric power cabinet body 1 top inner wall is provided with heat emission fan
8, described electric power cabinet body 1 surfaces externally and internally is provided with antibacterial resin.
The present invention is provided with anti-biotic material at electric power cabinet body surfaces externally and internally, antibacterial resin solidify to form, and it is to large intestine bar
Bacterium and staphylococcus glucose bacterium have obvious bactericidal effect, simultaneously because the use of additive, the variable color effect of this antibacterial resin
The most inconspicuous.
Preferably, described antibacterial resin is first that antibacterial is mixing with resin, it is thus achieved that antibacterial plastic concentrate, then by antibacterial plastic concentrate with
Resin is mixing, obtains described antibacterial resin through techniques such as injection, extrusions.Further, described resin is acrylic resin, institute
Stating antibacterial particle diameter is 4 μm.
Antibacterial and resin twice are mixing, it is possible to ensure that in the antibacterial resin obtained, antibacterial is uniformly dispersed, and then make
This anti-biotic material entirety antibiotic property homogeneous.
Preferably, described antibacterial is for carrying silver zinc copper zeolite antibacterial agent, and in described antibacterial, silver, zinc, the mol ratio of copper are
3:1:2.
Zeolite is owing to having loose structure, and specific surface area is relatively big, and zeolite structured in containing metal cation, have very
Strong cation exchange capacity (CEC), is a kind of natural carrier；Silver ion, zinc ion, copper ion are respectively provided with stronger killing
Bacterium ability, three is mixed in proportion use, and synergism is played in the raising to sterilizing ability.
Preferably, possibly together with ultraviolet absorber and infrared absorbing agents in described antibacterial resin, described ultraviolet absorber is hydroxyl
Base carbonic acid magnalium, described infrared absorbing agents is TiO2、K2Ti6O3And Fe3O4Stuff and other stuff.Described ultraviolet absorber and INFRARED ABSORPTION
Agent mass fraction in antibacterial resin is 0.09%.
Containing silver ion in described antibacterial resin, aging due to the reduction of silver ion and resin, cause this resin variable
Color, long-time after resin can turn yellow color, the application is added with ultraviolet absorber and infrared absorbing agents, described purple in antibacterial resin
Outer absorbent is hydroxy carbonate magnalium, and infrared absorbing agents is TiO2、K2Ti6O3And Fe3O4Stuff and other stuff, ultraviolet absorber and infrared
The interpolation of absorbent so that described antibacterial resin can effectively absorb ultraviolet light and infrared light, it is to avoid the reduction of silver ion, right
Well protection is played in the variable color of antibacterial resin.
Further preferred, such as Fig. 2, the preparation process of described antibacterial timber fat is as follows:
Step one, preparation load silver zinc copper zeolite antibacterial agent:
First, activating zeolite is processed: take in the heat-treatment furnace that zeolite is placed on 400 DEG C, calcine 2h, to remove zeolite pore
The organic impurities of residual in road；
Then take 10g active zeolite, be distributed in 100ml deionized water, be 3.9 with dust technology regulation pH value, at 50 DEG C
Add silver nitrate, zinc nitrate and copper nitrate mixed solution under water-bath and carry out ion exchange, after ion exchange, by solid particle mistake
Filter, separation, then clean to not having NO with deionized water3-Exist, after cleaning, powder body is dried at 120 DEG C 20h, through grinding
The load silver zinc copper zeolite antibacterial agent powder that particle diameter is 4 μm is retained after screening.
Step 2, prepares antibacterial resin:
First, take acrylic resin 5 parts, carry silver zinc copper zeolite antibacterial agent 1 part mixing at 210 DEG C, obtain antibacterial plastic concentrate；
Then, antibacterial plastic concentrate 1 part, acrylic resin 19 parts, ultraviolet absorber hydroxy carbonate magnalium, infrared absorbing agents are taken
TiO2、K2Ti6O3And Fe3O4After stuff and other stuff mix homogeneously mixing, after injection and the technique such as extrusion, obtain antibacterial resin.
Preferably, after the antibacterial resin tabletting after mixing, make resin sheet, after cleaning, bacteria suspension is coated antibacterial tree
Fat surface, cultivates 24h in incubator at 37 DEG C, counting shows that it is 99.88% to 24 hours sterilizing rates of escherichia coli, to gold
24 hours sterilizing rates of Staphylococcus aureus are 99.89%；Simultaneously because ultraviolet absorber and the interpolation of infrared absorbing agents, Jing Guozi
After outer smooth 100h irradiates, the color change of antibacterial resin is inconspicuous.
Application scenarios two:
Fig. 1 shows a kind of electric power cabinet with antibacterial effect that embodiments herein relates to, including electric power cabinet body
1, LED 2, voltmeter 3, directive wheel 4, desiccant case 5, thermometer 6, humidity sensor 7, heat emission fan 8, described electric power cabinet body
1 top is provided with LED 2, is provided with directive wheel 4 bottom electric power cabinet body 1, and electric power cabinet body 1 is internal is provided with voltmeter 3, thermometer
6, desiccant case 5, electric power cabinet body 1 side inner walls is provided with humidity sensor 7, and electric power cabinet body 1 top inner wall is provided with heat emission fan
8, described electric power cabinet body 1 surfaces externally and internally is provided with antibacterial resin.
The present invention is provided with anti-biotic material at electric power cabinet body surfaces externally and internally, antibacterial resin solidify to form, and it is to large intestine bar
Bacterium and staphylococcus glucose bacterium have obvious bactericidal effect, simultaneously because the use of additive, the variable color effect of this antibacterial resin
The most inconspicuous.
Preferably, described antibacterial resin is first that antibacterial is mixing with resin, it is thus achieved that antibacterial plastic concentrate, then by antibacterial plastic concentrate with
Resin is mixing, obtains described antibacterial resin through techniques such as injection, extrusions.Further, described resin is acrylic resin, institute
Stating antibacterial particle diameter is 4 μm.
Antibacterial and resin twice are mixing, it is possible to ensure that in the antibacterial resin obtained, antibacterial is uniformly dispersed, and then make
This anti-biotic material entirety antibiotic property homogeneous.
Preferably, described antibacterial is for carrying silver zinc copper zeolite antibacterial agent, and in described antibacterial, silver, zinc, the mol ratio of copper are
3:1:2.
Zeolite is owing to having loose structure, and specific surface area is relatively big, and zeolite structured in containing metal cation, have very
Strong cation exchange capacity (CEC), is a kind of natural carrier；Silver ion, zinc ion, copper ion are respectively provided with stronger killing
Bacterium ability, three is mixed in proportion use, and synergism is played in the raising to sterilizing ability.
Preferably, possibly together with ultraviolet absorber and infrared absorbing agents in described antibacterial resin, described ultraviolet absorber is hydroxyl
Base carbonic acid magnalium, described infrared absorbing agents is TiO2、K2Ti6O3And Fe3O4Stuff and other stuff.Described ultraviolet absorber and INFRARED ABSORPTION
Agent mass fraction in antibacterial resin is 0.07%.
Containing silver ion in described antibacterial resin, aging due to the reduction of silver ion and resin, cause this resin variable
Color, long-time after resin can turn yellow color, the application is added with ultraviolet absorber and infrared absorbing agents, described purple in antibacterial resin
Outer absorbent is hydroxy carbonate magnalium, and infrared absorbing agents is TiO2、K2Ti6O3And Fe3O4Stuff and other stuff, ultraviolet absorber and infrared
The interpolation of absorbent so that described antibacterial resin can effectively absorb ultraviolet light and infrared light, it is to avoid the reduction of silver ion, right
Well protection is played in the variable color of antibacterial resin.
Further preferred, such as Fig. 2, the preparation process of described antibacterial timber fat is as follows:
Step one, preparation load silver zinc copper zeolite antibacterial agent:
First, activating zeolite is processed: take in the heat-treatment furnace that zeolite is placed on 400 DEG C, calcine 2h, to remove zeolite pore
The organic impurities of residual in road；
Then take 10g active zeolite, be distributed in 100ml deionized water, be 3.9 with dust technology regulation pH value, at 50 DEG C
Add silver nitrate, zinc nitrate and copper nitrate mixed solution under water-bath and carry out ion exchange, after ion exchange, by solid particle mistake
Filter, separation, then clean to not having NO with deionized water3-Exist, after cleaning, powder body is dried at 120 DEG C 20h, through grinding
The load silver zinc copper zeolite antibacterial agent powder that particle diameter is 4 μm is retained after screening.
Step 2, prepares antibacterial resin:
First, take acrylic resin 5 parts, carry silver zinc copper zeolite antibacterial agent 1 part mixing at 210 DEG C, obtain antibacterial plastic concentrate；
Then, antibacterial plastic concentrate 1 part, acrylic resin 19 parts, ultraviolet absorber hydroxy carbonate magnalium, infrared absorbing agents are taken
TiO2、K2Ti6O3And Fe3O4After stuff and other stuff mix homogeneously mixing, after injection and the technique such as extrusion, obtain antibacterial resin.
Preferably, after the antibacterial resin tabletting after mixing, make resin sheet, after cleaning, bacteria suspension is coated antibacterial tree
Fat surface, cultivates 24h in incubator at 37 DEG C, counting shows that it is 99.79% to 24 hours sterilizing rates of escherichia coli, to gold
24 hours sterilizing rates of Staphylococcus aureus are 99.92%；Simultaneously because ultraviolet absorber and the interpolation of infrared absorbing agents, Jing Guozi
After outer smooth 100h irradiates, the color change of antibacterial resin is inconspicuous.
Application scenarios three:
Fig. 1 shows a kind of electric power cabinet with antibacterial effect that embodiments herein relates to, including electric power cabinet body
1, LED 2, voltmeter 3, directive wheel 4, desiccant case 5, thermometer 6, humidity sensor 7, heat emission fan 8, described electric power cabinet body
1 top is provided with LED 2, is provided with directive wheel 4 bottom electric power cabinet body 1, and electric power cabinet body 1 is internal is provided with voltmeter 3, thermometer
6, desiccant case 5, electric power cabinet body 1 side inner walls is provided with humidity sensor 7, and electric power cabinet body 1 top inner wall is provided with heat emission fan
8, described electric power cabinet body 1 surfaces externally and internally is provided with antibacterial resin.
The present invention is provided with anti-biotic material at electric power cabinet body surfaces externally and internally, antibacterial resin solidify to form, and it is to large intestine bar
Bacterium and staphylococcus glucose bacterium have obvious bactericidal effect, simultaneously because the use of additive, the variable color effect of this antibacterial resin
The most inconspicuous.
Preferably, described antibacterial resin is first that antibacterial is mixing with resin, it is thus achieved that antibacterial plastic concentrate, then by antibacterial plastic concentrate with
Resin is mixing, obtains described antibacterial resin through techniques such as injection, extrusions.Further, described resin is acrylic resin, institute
Stating antibacterial particle diameter is 4 μm.
Antibacterial and resin twice are mixing, it is possible to ensure that in the antibacterial resin obtained, antibacterial is uniformly dispersed, and then make
This anti-biotic material entirety antibiotic property homogeneous.
Preferably, described antibacterial is for carrying silver zinc copper zeolite antibacterial agent, and in described antibacterial, silver, zinc, the mol ratio of copper are
3:1:2.
Zeolite is owing to having loose structure, and specific surface area is relatively big, and zeolite structured in containing metal cation, have very
Strong cation exchange capacity (CEC), is a kind of natural carrier；Silver ion, zinc ion, copper ion are respectively provided with stronger killing
Bacterium ability, three is mixed in proportion use, and synergism is played in the raising to sterilizing ability.
Preferably, possibly together with ultraviolet absorber and infrared absorbing agents in described antibacterial resin, described ultraviolet absorber is hydroxyl
Base carbonic acid magnalium, described infrared absorbing agents is TiO2、K2Ti6O3And Fe3O4Stuff and other stuff.Described ultraviolet absorber and INFRARED ABSORPTION
Agent mass fraction in antibacterial resin is 0.08%.
Containing silver ion in described antibacterial resin, aging due to the reduction of silver ion and resin, cause this resin variable
Color, long-time after resin can turn yellow color, the application is added with ultraviolet absorber and infrared absorbing agents, described purple in antibacterial resin
Outer absorbent is hydroxy carbonate magnalium, and infrared absorbing agents is TiO2、K2Ti6O3And Fe3O4Stuff and other stuff, ultraviolet absorber and infrared
The interpolation of absorbent so that described antibacterial resin can effectively absorb ultraviolet light and infrared light, it is to avoid the reduction of silver ion, right
Well protection is played in the variable color of antibacterial resin.
Further preferred, such as Fig. 2, the preparation process of described antibacterial timber fat is as follows:
Step one, preparation load silver zinc copper zeolite antibacterial agent:
First, activating zeolite is processed: take in the heat-treatment furnace that zeolite is placed on 400 DEG C, calcine 2h, to remove zeolite pore
The organic impurities of residual in road；
Then take 10g active zeolite, be distributed in 100ml deionized water, be 3.9 with dust technology regulation pH value, at 50 DEG C
Add silver nitrate, zinc nitrate and copper nitrate mixed solution under water-bath and carry out ion exchange, after ion exchange, by solid particle mistake
Filter, separation, then clean to not having NO with deionized water3-Exist, after cleaning, powder body is dried at 120 DEG C 20h, through grinding
The load silver zinc copper zeolite antibacterial agent powder that particle diameter is 4 μm is retained after screening.
Step 2, prepares antibacterial resin:
First, take acrylic resin 5 parts, carry silver zinc copper zeolite antibacterial agent 1 part mixing at 210 DEG C, obtain antibacterial plastic concentrate；
Then, antibacterial plastic concentrate 1 part, acrylic resin 19 parts, ultraviolet absorber hydroxy carbonate magnalium, infrared absorbing agents are taken
TiO2、K2Ti6O3And Fe3O4After stuff and other stuff mix homogeneously mixing, after injection and the technique such as extrusion, obtain antibacterial resin.
Preferably, after the antibacterial resin tabletting after mixing, make resin sheet, after cleaning, bacteria suspension is coated antibacterial tree
Fat surface, cultivates 24h in incubator at 37 DEG C, counting shows that it is 99.82% to 24 hours sterilizing rates of escherichia coli, to gold
24 hours sterilizing rates of Staphylococcus aureus are 99.83%；Simultaneously because ultraviolet absorber and the interpolation of infrared absorbing agents, Jing Guozi
After outer smooth 100h irradiates, the color change of antibacterial resin is inconspicuous.
Application scenarios four:
Fig. 1 shows a kind of electric power cabinet with antibacterial effect that embodiments herein relates to, including electric power cabinet body
1, LED 2, voltmeter 3, directive wheel 4, desiccant case 5, thermometer 6, humidity sensor 7, heat emission fan 8, described electric power cabinet body
1 top is provided with LED 2, is provided with directive wheel 4 bottom electric power cabinet body 1, and electric power cabinet body 1 is internal is provided with voltmeter 3, thermometer
6, desiccant case 5, electric power cabinet body 1 side inner walls is provided with humidity sensor 7, and electric power cabinet body 1 top inner wall is provided with heat emission fan
8, described electric power cabinet body 1 surfaces externally and internally is provided with antibacterial resin.
The present invention is provided with anti-biotic material at electric power cabinet body surfaces externally and internally, antibacterial resin solidify to form, and it is to large intestine bar
Bacterium and staphylococcus glucose bacterium have obvious bactericidal effect, simultaneously because the use of additive, the variable color effect of this antibacterial resin
The most inconspicuous.
Preferably, described antibacterial resin is first that antibacterial is mixing with resin, it is thus achieved that antibacterial plastic concentrate, then by antibacterial plastic concentrate with
Resin is mixing, obtains described antibacterial resin through techniques such as injection, extrusions.Further, described resin is acrylic resin, institute
Stating antibacterial particle diameter is 4 μm.
Antibacterial and resin twice are mixing, it is possible to ensure that in the antibacterial resin obtained, antibacterial is uniformly dispersed, and then make
This anti-biotic material entirety antibiotic property homogeneous.
Preferably, described antibacterial is for carrying silver zinc copper zeolite antibacterial agent, and in described antibacterial, silver, zinc, the mol ratio of copper are
3:1:2.
Zeolite is owing to having loose structure, and specific surface area is relatively big, and zeolite structured in containing metal cation, have very
Strong cation exchange capacity (CEC), is a kind of natural carrier；Silver ion, zinc ion, copper ion are respectively provided with stronger killing
Bacterium ability, three is mixed in proportion use, and synergism is played in the raising to sterilizing ability.
Preferably, possibly together with ultraviolet absorber and infrared absorbing agents in described antibacterial resin, described ultraviolet absorber is hydroxyl
Base carbonic acid magnalium, described infrared absorbing agents is TiO2、K2Ti6O3And Fe3O4Stuff and other stuff.Described ultraviolet absorber and INFRARED ABSORPTION
Agent mass fraction in antibacterial resin is 0.06%.
Containing silver ion in described antibacterial resin, aging due to the reduction of silver ion and resin, cause this resin variable
Color, long-time after resin can turn yellow color, the application is added with ultraviolet absorber and infrared absorbing agents, described purple in antibacterial resin
Outer absorbent is hydroxy carbonate magnalium, and infrared absorbing agents is TiO2、K2Ti6O3And Fe3O4Stuff and other stuff, ultraviolet absorber and infrared
The interpolation of absorbent so that described antibacterial resin can effectively absorb ultraviolet light and infrared light, it is to avoid the reduction of silver ion, right
Well protection is played in the variable color of antibacterial resin.
Further preferred, such as Fig. 2, the preparation process of described antibacterial timber fat is as follows:
Step one, preparation load silver zinc copper zeolite antibacterial agent:
First, activating zeolite is processed: take in the heat-treatment furnace that zeolite is placed on 400 DEG C, calcine 2h, to remove zeolite pore
The organic impurities of residual in road；
Then take 10g active zeolite, be distributed in 100ml deionized water, be 3.9 with dust technology regulation pH value, at 50 DEG C
Add silver nitrate, zinc nitrate and copper nitrate mixed solution under water-bath and carry out ion exchange, after ion exchange, by solid particle mistake
Filter, separation, then clean to not having NO with deionized water3-Exist, after cleaning, powder body is dried at 120 DEG C 20h, through grinding
The load silver zinc copper zeolite antibacterial agent powder that particle diameter is 4 μm is retained after screening.
Step 2, prepares antibacterial resin:
First, take acrylic resin 5 parts, carry silver zinc copper zeolite antibacterial agent 1 part mixing at 210 DEG C, obtain antibacterial plastic concentrate；
Then, antibacterial plastic concentrate 1 part, acrylic resin 19 parts, ultraviolet absorber hydroxy carbonate magnalium, infrared absorbing agents are taken
TiO2、K2Ti6O3And Fe3O4After stuff and other stuff mix homogeneously mixing, after injection and the technique such as extrusion, obtain antibacterial resin.
Preferably, after the antibacterial resin tabletting after mixing, make resin sheet, after cleaning, bacteria suspension is coated antibacterial tree
Fat surface, cultivates 24h in incubator at 37 DEG C, counting shows that it is 99.64% to 24 hours sterilizing rates of escherichia coli, to gold
24 hours sterilizing rates of Staphylococcus aureus are 99.57%；Simultaneously because ultraviolet absorber and the interpolation of infrared absorbing agents, Jing Guozi
After outer smooth 100h irradiates, the color change of antibacterial resin is inconspicuous.
Application scenarios five:
Fig. 1 shows a kind of electric power cabinet with antibacterial effect that embodiments herein relates to, including electric power cabinet body
1, LED 2, voltmeter 3, directive wheel 4, desiccant case 5, thermometer 6, humidity sensor 7, heat emission fan 8, described electric power cabinet body
1 top is provided with LED 2, is provided with directive wheel 4 bottom electric power cabinet body 1, and electric power cabinet body 1 is internal is provided with voltmeter 3, thermometer
6, desiccant case 5, electric power cabinet body 1 side inner walls is provided with humidity sensor 7, and electric power cabinet body 1 top inner wall is provided with heat emission fan
8, described electric power cabinet body 1 surfaces externally and internally is provided with antibacterial resin.
The present invention is provided with anti-biotic material at electric power cabinet body surfaces externally and internally, antibacterial resin solidify to form, and it is to large intestine bar
Bacterium and staphylococcus glucose bacterium have obvious bactericidal effect, simultaneously because the use of additive, the variable color effect of this antibacterial resin
The most inconspicuous.
Preferably, described antibacterial resin is first that antibacterial is mixing with resin, it is thus achieved that antibacterial plastic concentrate, then by antibacterial plastic concentrate with
Resin is mixing, obtains described antibacterial resin through techniques such as injection, extrusions.Further, described resin is acrylic resin, institute
Stating antibacterial particle diameter is 4 μm.
Antibacterial and resin twice are mixing, it is possible to ensure that in the antibacterial resin obtained, antibacterial is uniformly dispersed, and then make
This anti-biotic material entirety antibiotic property homogeneous.
Preferably, described antibacterial is for carrying silver zinc copper zeolite antibacterial agent, and in described antibacterial, silver, zinc, the mol ratio of copper are
3:1:2.
Zeolite is owing to having loose structure, and specific surface area is relatively big, and zeolite structured in containing metal cation, have very
Strong cation exchange capacity (CEC), is a kind of natural carrier；Silver ion, zinc ion, copper ion are respectively provided with stronger killing
Bacterium ability, three is mixed in proportion use, and synergism is played in the raising to sterilizing ability.
Preferably, possibly together with ultraviolet absorber and infrared absorbing agents in described antibacterial resin, described ultraviolet absorber is hydroxyl
Base carbonic acid magnalium, described infrared absorbing agents is TiO2、K2Ti6O3And Fe3O4Stuff and other stuff.Described ultraviolet absorber and INFRARED ABSORPTION
Agent mass fraction in antibacterial resin is 0.05%.
Containing silver ion in described antibacterial resin, aging due to the reduction of silver ion and resin, cause this resin variable
Color, long-time after resin can turn yellow color, the application is added with ultraviolet absorber and infrared absorbing agents, described purple in antibacterial resin
Outer absorbent is hydroxy carbonate magnalium, and infrared absorbing agents is TiO2、K2Ti6O3And Fe3O4Stuff and other stuff, ultraviolet absorber and infrared
The interpolation of absorbent so that described antibacterial resin can effectively absorb ultraviolet light and infrared light, it is to avoid the reduction of silver ion, right
Well protection is played in the variable color of antibacterial resin.
Further preferred, such as Fig. 2, the preparation process of described antibacterial timber fat is as follows:
Step one, preparation load silver zinc copper zeolite antibacterial agent:
First, activating zeolite is processed: take in the heat-treatment furnace that zeolite is placed on 400 DEG C, calcine 2h, to remove zeolite pore
The organic impurities of residual in road；
Then take 10g active zeolite, be distributed in 100ml deionized water, be 3.9 with dust technology regulation pH value, at 50 DEG C
Add silver nitrate, zinc nitrate and copper nitrate mixed solution under water-bath and carry out ion exchange, after ion exchange, by solid particle mistake
Filter, separation, then clean to not having NO with deionized water3-Exist, after cleaning, powder body is dried at 120 DEG C 20h, through grinding
The load silver zinc copper zeolite antibacterial agent powder that particle diameter is 4 μm is retained after screening.
Step 2, prepares antibacterial resin:
First, take acrylic resin 5 parts, carry silver zinc copper zeolite antibacterial agent 1 part mixing at 210 DEG C, obtain antibacterial plastic concentrate；
Then, antibacterial plastic concentrate 1 part, acrylic resin 19 parts, ultraviolet absorber hydroxy carbonate magnalium, infrared absorbing agents are taken
TiO2、K2Ti6O3And Fe3O4After stuff and other stuff mix homogeneously mixing, after injection and the technique such as extrusion, obtain antibacterial resin.
Preferably, after the antibacterial resin tabletting after mixing, make resin sheet, after cleaning, bacteria suspension is coated antibacterial tree
Fat surface, cultivates 24h in incubator at 37 DEG C, counting shows that it is 99.51% to 24 hours sterilizing rates of escherichia coli, to gold
24 hours sterilizing rates of Staphylococcus aureus are 99.48%；Simultaneously because ultraviolet absorber and the interpolation of infrared absorbing agents, Jing Guozi
After outer smooth 100h irradiates, the color change of antibacterial resin is inconspicuous.
It should be appreciated that the invention is not limited in precision architecture described above and illustrated in the accompanying drawings, and
And various modifications and changes can carried out without departing from the scope.The scope of the present invention is only limited by appended claim.
Claims (2)
1. there is an electric power cabinet for antibacterial effect, including electric power cabinet body, LED, voltmeter, directive wheel, desiccant case, temperature
Degree meter, humidity sensor, heat emission fan, it is characterised in that described electric power cabinet bodies top is provided with LED, electric power cabinet body bottom portion
Being provided with directive wheel, electric power cabinet body interior is provided with voltmeter, thermometer, desiccant case, and electric power cabinet body side inner walls is provided with wet
Degree sensor, electric power cabinet bodies top inwall is provided with heat emission fan.
Electric power cabinet the most according to claim 1, it is characterised in that described electric power cabinet body surfaces externally and internally is provided with antibacterial tree
Fat.