CN106317464A - 一种高分散性碳酸钙填料性碳酸钙填料及其制备方法 - Google Patents
一种高分散性碳酸钙填料性碳酸钙填料及其制备方法 Download PDFInfo
- Publication number
- CN106317464A CN106317464A CN201510390451.5A CN201510390451A CN106317464A CN 106317464 A CN106317464 A CN 106317464A CN 201510390451 A CN201510390451 A CN 201510390451A CN 106317464 A CN106317464 A CN 106317464A
- Authority
- CN
- China
- Prior art keywords
- parts
- calcium carbonate
- ethylene
- glycerol
- acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高分散性碳酸钙填料及其制备方法,该高分散性碳酸钙填料由以下质量份成分组成:轻质碳酸钙85-100份,煅烧高岭土2-3份、甘油1-2份、聚烯烃弹性体0.8-1份、聚乙烯蜡1-2份、丙烯酸酯3-5份、硬脂酸锌1-1.5份、氧化铬1.5-2份、乙烯-丙烯酸共聚物0.5-1份,其制备方法是将轻质碳酸钙、煅烧高岭土、氧化铬、聚烯烃弹性体混合搅拌,然后加入甘油、聚乙烯蜡、丙烯酸酯和乙烯-丙烯酸共聚物混合搅拌,最后雾喷干燥得到成品。
Description
技术领域
本发明涉及一种碳酸钙,尤其涉及一种高分散性碳酸钙填料及其制备方法。
背景技术
碳酸钙是一类重要的功能性无机填料,具有价格低廉、储量丰富、性能稳定、易加工、无毒等优点,能够显著的改善材料的加工性能、物理性能以及降低生产成本等等,广泛应用于塑料、橡胶、涂料、造纸等领域,但是由于碳酸钙为亲水性化合物,导致在实际应用中存在与高聚物相容性不足,分散性差等缺陷,不能达到满意的填充补强效果,目前市场上主要由两种方式能使其分散性变好,主要是采用物理和化学方法进行处理,一是通过粉碎的方式使其粒径变小,另一种是通过化学改性的方式改变其表面性能,提高其与高聚物的相容性和分散性,然而微细化的碳酸钙容易团聚,其对提高与高聚物的相容性和分散性作用很小,无法满足需要,为此,我们提供一种表面改性的碳酸钙填料的制备方法。
发明内容
本发明的目的针对现有技术中碳酸钙难以直接添加到产品中缺陷,提供一种高分散性碳酸钙填料及其制备方法,该方法制备的改性碳酸钙填料改性效果好,相容性好,添加到塑料中时能均匀分散。
为实现上述目的,本发明采用的技术方案是:一种高分散性碳酸钙填料,由以下质量份成分组成:轻质碳酸钙85-100份,煅烧高岭土2-3份、甘油1-2份、聚烯烃弹性体0.8-1份、聚乙烯蜡1-2份、丙烯酸酯3-5份、硬脂酸锌1-1.5份、氧化铬1.5-2份、乙烯-丙烯酸共聚物0.5-1份。
进一步地,最佳配比由以下质量份成分组成:轻质碳酸钙粉90份,煅烧高岭土2份、甘油1份、聚烯烃弹性体0.8、聚乙烯蜡1.5份、丙烯酸酯4份、硬脂酸锌1份、氧化铬1.7份、乙烯-丙烯酸共聚物0.8份。
进一步地,一种高分散性碳酸钙填料的制备方法,其制备步骤如下:
1)先将轻质碳酸钙、煅烧高岭土、氧化铬、聚烯烃弹性体混合,加入2-3倍水,采用湿法研磨的方法研磨,得到预混料,研磨过程中加入硬脂酸锌;
2)将甘油、聚乙烯蜡、丙烯酸酯和乙烯-丙烯酸共聚物加入到步骤1)得到的预混料,在8000-10000转/min的条件下搅拌20-30min,搅拌温度为60-70℃;
3)将步骤2)搅拌好的物料送入采用湿法研磨的方式进行研磨,然后收集浆料,将浆料采用雾喷法进行干燥,得到成品。
有益效果:本发明的高分散性碳酸钙填料通过在配料中添加聚烯烃弹性体和乙烯-丙烯酸共聚物使其碳酸钙不易团聚,也提高了碳酸钙相容性和分散性,从而使得该碳酸钙填料填充的聚合物材料也具有良好的相容性和分散性,同时选择多种功能的表面活性剂混合,使得其改性效果大大提高。
具体实施方式
实施例1
一种高分散性碳酸钙填料,由以下质量份成分组成:轻质碳酸钙85份,煅烧高岭土2份、甘油1份、聚烯烃弹性体0.8份、聚乙烯蜡1份、丙烯酸酯3份、硬脂酸锌1份、氧化铬1.5份、乙烯-丙烯酸共聚物0.5份,其制备步骤如下:
1)先将轻质碳酸钙、煅烧高岭土、氧化铬、聚烯烃弹性体混合,加入2倍水,采用湿法研磨的方法研磨,得到预混料,研磨过程中加入硬脂酸锌;
2)将甘油、聚乙烯蜡、丙烯酸酯和乙烯-丙烯酸共聚物加入到步骤1)得到的预混料,在8000转/min的条件下搅拌20min,搅拌温度为60℃;
3)将步骤2)搅拌好的物料送入采用湿法研磨的方式进行研磨,然后收集浆料,将浆料采用雾喷法进行干燥,得到成品。
实施例2
一种高分散性碳酸钙填料,由以下质量份成分组成:轻质碳酸钙92份,煅烧高岭土2.5份、甘油1.5份、聚烯烃弹性体0.9份、聚乙烯蜡1.5份、丙烯酸酯4份、硬脂酸锌1.25份、氧化铬1.75份、乙烯-丙烯酸共聚物0.75份,其制备步骤如下:
1)先将轻质碳酸钙、煅烧高岭土、氧化铬、聚烯烃弹性体混合,加入2.5倍水,采用湿法研磨的方法研磨,得到预混料,研磨过程中加入硬脂酸锌;
2)将甘油、聚乙烯蜡、丙烯酸酯和乙烯-丙烯酸共聚物加入到步骤1)得到的预混料,在9000转/min的条件下搅拌25min,搅拌温度为65℃;
3)将步骤2)搅拌好的物料送入采用湿法研磨的方式进行研磨,然后收集浆料,将浆料采用雾喷法进行干燥,得到成品。
实施例3
一种高分散性碳酸钙填料,由以下质量份成分组成:轻质碳酸钙90份,煅烧高岭土2份、甘油1份、聚烯烃弹性体0.8、聚乙烯蜡1.5份、丙烯酸酯4份、硬脂酸锌1份、氧化铬1.7份、乙烯-丙烯酸共聚物0.8份,其制备步骤如下:
1)先将轻质碳酸钙、煅烧高岭土、氧化铬、聚烯烃弹性体混合,加入2.5倍水,采用湿法研磨的方法研磨,得到预混料,研磨过程中加入硬脂酸锌;
2)将甘油、聚乙烯蜡、丙烯酸酯和乙烯-丙烯酸共聚物加入到步骤1)得到的预混料,在9000转/min的条件下搅拌25min,搅拌温度为65℃;
3)将步骤2)搅拌好的物料送入采用湿法研磨的方式进行研磨,然后收集浆料,将浆料采用雾喷法进行干燥,得到成品。
实施例4
一种高分散性碳酸钙填料,由以下质量份成分组成:轻质碳酸钙100份,煅烧高岭土3份、甘油2份、聚烯烃弹性体1份、聚乙烯蜡2份、丙烯酸酯5份、硬脂酸锌1.5份、氧化铬2份、乙烯-丙烯酸共聚物1份,其制备步骤如下:
1)先将轻质碳酸钙、煅烧高岭土、氧化铬、聚烯烃弹性体混合,加入3倍水,采用湿法研磨的方法研磨,得到预混料,研磨过程中加入硬脂酸锌;
2)将甘油、聚乙烯蜡、丙烯酸酯和乙烯-丙烯酸共聚物加入到步骤1)得到的预混料,在10000转/min的条件下搅拌30min,搅拌温度为70℃;
3)将步骤2)搅拌好的物料送入采用湿法研磨的方式进行研磨,然后收集浆料,将浆料采用雾喷法进行干燥,得到成品。
将上述4个实施例制得的成品用与添加到PVC中,实验数据如下表
上面所述的实施例仅仅是对本发明的优选实施方式进行描述,并非对本发明的构思和范围进行限定。在不脱离本发明设计构思的前提下,本领域普通人员对本发明的技术方案做出的各种变型和改进,均应落入到本发明的保护范围。
Claims (3)
1.一种高分散性碳酸钙填料,其特征在于,由以下质量份成分组成:轻质碳酸钙85-100份,煅烧高岭土2-3份、甘油1-2份、聚烯烃弹性体0.8-1份、聚乙烯蜡1-2份、丙烯酸酯3-5份、硬脂酸锌1-1.5份、氧化铬1.5-2份、乙烯-丙烯酸共聚物0.5-1份。
2.如权利要求1所述的高分散性碳酸钙填料,其特征在于,最佳配比由以下质量份成分组成:轻质碳酸钙粉90份,煅烧高岭土2份、甘油1份、聚烯烃弹性体0.8、聚乙烯蜡1.5份、丙烯酸酯4份、硬脂酸锌1份、氧化铬1.7份、乙烯-丙烯酸共聚物0.8份。
3.一种如权利要求1-2任意一项所述的高分散性碳酸钙填料的制备方法,其特征在于,其制备步骤如下:
1)先将轻质碳酸钙、煅烧高岭土、氧化铬、聚烯烃弹性体混合,加入2-3倍水,采用湿法研磨的方法研磨,得到预混料,研磨过程中加入硬脂酸锌;
2)将甘油、聚乙烯蜡、丙烯酸酯和乙烯-丙烯酸共聚物加入到步骤1)得到的预混料,在8000-10000转/min的条件下搅拌20-30min,搅拌温度为60-70℃;
3)将步骤2)搅拌好的物料送入采用湿法研磨的方式进行研磨,然后收集浆料,将浆料采用雾喷法进行干燥,得到成品。