CN106316240A - Reinforced light-reflecting heat-insulating polymer cement waterproof paint - Google Patents
Reinforced light-reflecting heat-insulating polymer cement waterproof paint Download PDFInfo
- Publication number
- CN106316240A CN106316240A CN201610617723.5A CN201610617723A CN106316240A CN 106316240 A CN106316240 A CN 106316240A CN 201610617723 A CN201610617723 A CN 201610617723A CN 106316240 A CN106316240 A CN 106316240A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterproof paint
- powder
- auxiliary agent
- inorganic powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses reinforced light-reflecting heat-insulating polymer cement waterproof paint. The polymer cement waterproof paint is prepared from, by weight, 60-70 parts of cement-based polymer emulsion, 35-45 parts of inorganic powder, 0.42-0.51 part of reinforced fiber, 3.7-4.55 parts of auxiliary and 8-15 parts of water. The inorganic powder comprises 20-23 parts of Portland cement, 12-15 parts of light-reflecting quartz powder and 3-7 parts of glass bead light reflecting powder; the auxiliary comprises 1.2-1.3 parts of coalescing agent, 0.3-0.5 part of stabilizer, 1.8-2 parts of plasticizer, 0.15-0.3 part of dispersant, 0.2-0.3 part of defoaming agent and 0.05-0.15 part of preservative. A small amount of acrylic reinforced fiber is added, the anti-cracking performance of a waterproof paint coating is improved, the light-reflecting quartz powder and the glass bead light reflecting powder are used in combination to achieve the efficient light reflecting effect, and the light reflecting performance is greatly improved to achieve the purpose of reducing indoor temperature by reducing the temperature of a roof or a building surface.
Description
[technical field]
The present invention relates to the technical field of building water-proof paint, particularly to a kind of enhancement mode reflection and heat insulation polymer cement
Water-repellent paint.
[background technology]
Polymer cement waterproof paint not only has the strongest water resistance, also has the strongest tensile property.Using
During can form one layer of fluid-tight thin film, effectively avoid permeable phenomenon of leaking, so building in recent years
Build and finishing has obtained large-scale application, not only can use polymer cement in the decoration that pond, kitchen, roofing etc. are indoor
Water-repellent paint, building outer layer it also can mix use with other cement mortar material.
At present, the function of polymer cement waterproof paint is the most single, has a waterproof adhesive performance, and the effect of heat insulation reflecting
The most relatively low, and the painting of inner corner trim thickness is easy to crack, especially under summer high temperature environment, daylight irradiates for a long time, can make Indoor environment
Temperature raises rapidly, and the ventilation effect of indoor is poor, causes radiating effect the best, adds the use of air-conditioning, and power consumption is serious,
Health and environment have been endangered.And the temperature of indoor is reduced by the temperature reducing roof or building surface
Degree, is the most practicable effective solution, in order to solve the problems referred to above, it is necessary to proposes a kind of enhancement mode reflection and heat insulation and gathers
Compound cement waterproof paint.
[summary of the invention]
It is an object of the invention to overcome above-mentioned the deficiencies in the prior art, it is provided that a kind of enhancement mode reflection and heat insulation polymer water
Mud water-repellent paint, it aims to solve the problem that in prior art, the effect of the heat insulation reflecting of polymer cement waterproof paint is relatively low, easy to crack
Technical problem.
For achieving the above object, the present invention proposes a kind of enhancement mode reflection and heat insulation polymer cement waterproof paint, by with
The raw material of lower parts by weight is prepared from: cement-based polymers emulsion 60～70 parts, inorganic powder 35～45 parts, reinforcing fiber
0.42～0.51 part, auxiliary agent 3.7～4.55 parts, water 8～15 parts, described inorganic powder includes portland cement 20～23 parts,
Reflective silica flour 12～15 parts, glass microsphere light-reflecting powder 3～7 parts, described auxiliary agent includes coalescents 1.2～1.3 parts, stable
Agent 0.3～0.5 part, plasticizer 1.8～2 parts, dispersant 0.15～0.3 part, defoamer 0.2～0.3 part, preservative 0.05～
0.15 part.
As preferably, the raw material of following parts by weight it is prepared from: cement-based polymers emulsion 60 parts, inorganic powder
35, reinforcing fiber 0.42 part, auxiliary agent 3.7 parts, 8 parts of water, described inorganic powder includes portland cement 20 parts, reflective silica flour
12 parts, 3 parts of glass microsphere light-reflecting powder, described auxiliary agent includes coalescents 1.2 parts, stabilizer 0.3 part, plasticizer 1.8 parts, divides
Powder 0.15 part, defoamer 0.2 part, preservative 0.05 part.
As preferably, the raw material of following parts by weight it is prepared from: cement-based polymers emulsion 65 parts, inorganic powder 40
Part, reinforcing fiber 0.465 part, auxiliary agent 4.125 parts, 11.5 parts of water, described inorganic powder includes portland cement 21.5 parts, instead
Light silica flour 13.5 parts, 5 parts of glass microsphere light-reflecting powder, described auxiliary agent includes coalescents 1.25 parts, stabilizer 0.4 part, increases
Mould agent 1.9 parts, dispersant 0.225 part, defoamer 0.25 part, preservative 0.1 part.
As preferably, the raw material of following parts by weight it is prepared from: cement-based polymers emulsion 70 parts, inorganic powder 45
Part, reinforcing fiber 0.51 part, auxiliary agent 4.55 parts, 15 parts of water, described inorganic powder includes portland cement 23 parts, reflective quartz
15 parts of powder, 7 parts of glass microsphere light-reflecting powder, described auxiliary agent includes coalescents 1.3 parts, stabilizer 0.5 part, plasticizer 2 parts, divides
Powder 0.3 part, defoamer 0.3 part, preservative 0.15 part.
As preferably, described reinforcing fiber is acrylic fiber, a length of 2～3mm.
As preferably, described reflective silica flour is that micrometer level porous konilite plates high refractive index metal oxide nanometer
Material.
As preferably, described coalescents is Lauryl Alcohol ester, and stabilizer is lignocellulose stabilizer, and plasticizer is
DEDB plasticizer, dispersant is the mixture of stearmide and higher alcohol, and defoamer is polysiloxane-based defoamer, and preservative is
Kathon LX preservative.
Beneficial effects of the present invention: compared with prior art, a kind of enhancement mode reflection and heat insulation polymer that the present invention provides
Cement waterproof paint, promotes the anti-cracking performance of water-repellent paint coating, solves by adding a small amount of acrylic acid reinforcing fiber
Polymer cement waterproof paint inner corner trim thickness is coated with problem easy to crack, and micrometer level porous konilite plates high refractive index metal oxide
The reflective silica flour of nano material is used in combination with glass microsphere light-reflecting powder, reaches the most reflective effect, and reflective function is significantly
Promote, thus the temperature reducing roof or building surface reduces the purpose of indoor temperature.
Inventive feature and advantage will be described in detail by embodiment.
[detailed description of the invention]
For making the object, technical solutions and advantages of the present invention of greater clarity, below by embodiment, the present invention is entered
Row further describes.However, it should be understood that specific embodiment described herein is only in order to explain the present invention, and need not
In limiting the scope of the present invention.Additionally, in the following description, eliminate the description to known features and technology, so that avoid need not
Idea of the invention is obscured in strategic point.
The embodiment of the present invention provides a kind of enhancement mode reflection and heat insulation polymer cement waterproof paint, by following parts by weight
Raw material is prepared from: cement-based polymers emulsion 60～70 parts, inorganic powder 35～45 parts, reinforcing fiber 0.42～0.51 part,
Auxiliary agent 3.7～4.55 parts, water 8～15 parts, described inorganic powder includes portland cement 20～23 parts, reflective silica flour 12～
15 parts, glass microsphere light-reflecting powder 3～7 parts, described auxiliary agent includes coalescents 1.2～1.3 parts, stabilizer 0.3～0.5 part,
Plasticizer 1.8～2 parts, dispersant 0.15～0.3 part, defoamer 0.2～0.3 part, preservative 0.05～0.15 part.
Wherein, described reinforcing fiber is acrylic fiber, a length of 2～3mm.Waterproof painting is promoted by acrylic fiber
The anti-cracking performance of material coating, solves polymer cement waterproof paint inner corner trim thickness and is coated with problem easy to crack.
Further, described reflective silica flour is that micrometer level porous konilite plates high refractive index metal oxide nanometer
Material.The present invention uses micrometer level porous konilite to plate reflective silica flour and the tool of high refractive index metal oxide nano material
There is the high refractive index glass micro pearl reflective powder dual function of light weight, low heat conduction, higher intensity, good chemical stability, instead
Optical property is greatly promoted, and reaches the effect of reflection and heat insulation.
Further, described coalescents is Lauryl Alcohol ester, and stabilizer is lignocellulose stabilizer, plasticizer
For DEDB plasticizer, dispersant is the mixture of stearmide and higher alcohol, and defoamer is polysiloxane-based defoamer, preservative
For Kathon LX preservative.
Embodiment one,
A kind of enhancement mode reflection and heat insulation polymer cement waterproof paint, is prepared from by the raw material of following parts by weight: water
Mud based polyalcohol emulsion 60 parts, inorganic powder 35, reinforcing fiber 0.42 part, auxiliary agent 3.7 parts, 8 parts of water, described inorganic powder bag
Including portland cement 20 parts, reflective silica flour 12 parts, 3 parts of glass microsphere light-reflecting powder, described auxiliary agent includes coalescents 1.2
Part, stabilizer 0.3 part, plasticizer 1.8 parts, dispersant 0.15 part, defoamer 0.2 part, preservative 0.05 part.
Embodiment two,
A kind of enhancement mode reflection and heat insulation polymer cement waterproof paint, is prepared from by the raw material of following parts by weight: water
Mud based polyalcohol emulsion 65 parts, inorganic powder 40 parts, reinforcing fiber 0.465 part, auxiliary agent 4.125 parts, 11.5 parts of water, described nothing
Machine powder includes portland cement 21.5 parts, reflective silica flour 13.5 parts, and 5 parts of glass microsphere light-reflecting powder, described auxiliary agent includes
Coalescents 1.25 parts, stabilizer 0.4 part, plasticizer 1.9 parts, dispersant 0.225 part, defoamer 0.25 part, preservative 0.1
Part.
Embodiment three,
A kind of enhancement mode reflection and heat insulation polymer cement waterproof paint, is prepared from by the raw material of following parts by weight: water
Mud based polyalcohol emulsion 70 parts, inorganic powder 45 parts, reinforcing fiber 0.51 part, auxiliary agent 4.55 parts, 15 parts of water, described inorganic powder
Material includes portland cement 23 parts, reflective silica flour 15 parts, and 7 parts of glass microsphere light-reflecting powder, described auxiliary agent includes coalescents
1.3 parts, stabilizer 0.5 part, plasticizer 2 parts, dispersant 0.3 part, defoamer 0.3 part, preservative 0.15 part.
A kind of enhancement mode reflection and heat insulation polymer cement waterproof paint that the present invention provides, by adding a small amount of acrylic acid
Reinforcing fiber promotes the anti-cracking performance of water-repellent paint coating, solves polymer cement waterproof paint inner corner trim thickness and is coated with easy to crack
Problem, micrometer level porous konilite plates reflective silica flour and the glass microsphere light-reflecting of high refractive index metal oxide nano material
Powder is used in combination, and reaches the most reflective effect, and reflective function is greatly promoted, thus reduces roof or building surface
Temperature reduce the purpose of temperature of indoor.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all essences in the present invention
Any amendment, equivalent or the improvement etc. made within god and principle, should be included within the scope of the present invention.
Claims (7)
1. an enhancement mode reflection and heat insulation polymer cement waterproof paint, it is characterised in that: by the raw material system of following parts by weight
For forming: cement-based polymers emulsion 60～70 parts, inorganic powder 35～45 parts, reinforcing fiber 0.42～0.51 part, auxiliary agent 3.7
～4.55 parts, water 8～15 parts, described inorganic powder includes portland cement 20～23 parts, reflective silica flour 12～15 parts, glass
The reflective powder of glass microballon 3～7 parts, described auxiliary agent includes coalescents 1.2～1.3 parts, stabilizer 0.3～0.5 part, plasticizer
1.8～2 parts, dispersant 0.15～0.3 part, defoamer 0.2～0.3 part, preservative 0.05～0.15 part.
2. a kind of enhancement mode reflection and heat insulation polymer cement waterproof paint as claimed in claim 1, it is characterised in that: by following
The raw material of parts by weight is prepared from: cement-based polymers emulsion 60 parts, inorganic powder 35, reinforcing fiber 0.42 part, auxiliary agent 3.7
Part, 8 parts of water, described inorganic powder includes portland cement 20 parts, reflective silica flour 12 parts, 3 parts of glass microsphere light-reflecting powder, institute
The auxiliary agent stated includes coalescents 1.2 parts, stabilizer 0.3 part, plasticizer 1.8 parts, dispersant 0.15 part, defoamer 0.2 part, prevents
Rotten agent 0.05 part.
3. a kind of enhancement mode reflection and heat insulation polymer cement waterproof paint as claimed in claim 1, it is characterised in that: by following
The raw material of parts by weight is prepared from: cement-based polymers emulsion 65 parts, inorganic powder 40 parts, reinforcing fiber 0.465 part, auxiliary agent
4.125 parts, 11.5 parts of water, described inorganic powder includes portland cement 21.5 parts, reflective silica flour 13.5 parts, glass microballoon
5 parts of reflective powder, described auxiliary agent includes coalescents 1.25 parts, stabilizer 0.4 part, plasticizer 1.9 parts, dispersant 0.225 part,
Defoamer 0.25 part, preservative 0.1 part.
4. a kind of enhancement mode reflection and heat insulation polymer cement waterproof paint as claimed in claim 1, it is characterised in that: by following
The raw material of parts by weight is prepared from: cement-based polymers emulsion 70 parts, inorganic powder 45 parts, reinforcing fiber 0.51 part, auxiliary agent
4.55 parts, 15 parts of water, described inorganic powder includes portland cement 23 parts, reflective silica flour 15 parts, glass microsphere light-reflecting powder 7
Part, described auxiliary agent includes coalescents 1.3 parts, stabilizer 0.5 part, plasticizer 2 parts, dispersant 0.3 part, defoamer 0.3 part,
Preservative 0.15 part.
5. a kind of enhancement mode reflection and heat insulation polymer cement waterproof paint as described in any one in Claims 1-4, it is special
Levy and be: described reinforcing fiber is acrylic fiber, a length of 2～3mm.
6. a kind of enhancement mode reflection and heat insulation polymer cement waterproof paint as described in any one in Claims 1-4, it is special
Levy and be: described reflective silica flour is that micrometer level porous konilite plates high refractive index metal oxide nano material.
7. a kind of enhancement mode reflection and heat insulation polymer cement waterproof paint as described in any one in Claims 1-4, it is special
Levying and be: described coalescents is Lauryl Alcohol ester, stabilizer is lignocellulose stabilizer, and plasticizer is DEDB plasticising
Agent, dispersant is the mixture of stearmide and higher alcohol, and defoamer is polysiloxane-based defoamer, and preservative is Kathon
LX preservative.