CN106316122A - 一种钧瓷釉料 - Google Patents

一种钧瓷釉料 Download PDF

Info

Publication number
CN106316122A
CN106316122A CN201610680524.9A CN201610680524A CN106316122A CN 106316122 A CN106316122 A CN 106316122A CN 201610680524 A CN201610680524 A CN 201610680524A CN 106316122 A CN106316122 A CN 106316122A
Authority
CN
China
Prior art keywords
glaze
copper
oxide
raw material
pottery
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610680524.9A
Other languages
English (en)
Inventor
温书强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610680524.9A priority Critical patent/CN106316122A/zh
Publication of CN106316122A publication Critical patent/CN106316122A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种钧瓷釉料，它是由下列重量百分比的原料制备而成的：长石45﹪，方解石10﹪，铜矿石10﹪，滑石粉10﹪，木炭粉15﹪，氧化铜9.5﹪，氧化锡0.5﹪，对传统配方进行重新量化，自然原料配合作用，在高温熔融作用下，会产生釉色整体色彩多样变化的独特艺术效果，具有很好的社会和经济效益。

Description

一种钧瓷釉料
技术领域
本发明涉及钧瓷领域，具体涉及一种钧瓷釉料。
背景技术
陶瓷的发展与人类的进步有着密切而久远的联系，它是人类文明的时代标志。陶瓷中的钧瓷，经理了唐、宋、元、明、清的岁月洗礼，形成了独特的艺术表现形式，钧窑有着极美的色彩，釉在窑中变化万千，并具有自然美感，今天仍为各地瓷窑所继承和仿效，并不断创新，使钧窑这枝绚丽的花朵重放异彩。
河南禹州的钧窑为北方青瓷窑系，目前仍然有着很大的成就，一般采用柴、煤、炭和天然气烧制，不同的烧制工艺产生的釉色变化也不同。外部是釉料在经过高温熔融时产生绚丽的色彩斑斓变化，原因主要在釉料的配方，这是影响钧瓷成品外色的重要因素，同时也是造成钧瓷入窑一色，出窑万彩的关键因素。
因此，本发明生产一种原料纯正，配比新颖，成品色彩绚丽的钧瓷釉料，具有广泛的市场前景。
发明内容
针对现有技术的不足，本发明提供一种原料纯正，配比新颖，成品色彩绚丽的钧瓷釉料，用来解决现有技术中的缺陷。
本发明的技术方案是这样实现：一种钧瓷釉料，它是由下列重量百分比的原料制备而成的：长石44﹪至46﹪，方解石9﹪至11﹪，铜矿石9﹪至11﹪，滑石粉9﹪至11﹪，木炭粉14﹪至16﹪，氧化铜9.4﹪至9.6﹪，氧化锡0.4﹪至0.6﹪。
它是由下列重量百分比的原料制备而成的：长石45﹪，方解石10﹪，铜矿石10﹪，滑石粉10﹪，木炭粉15﹪，氧化铜9.5﹪，氧化锡0.5﹪。
本发明具有如下的积极效果：本发明对传统配方进行重新量化，自然原料配合相互作用，与化学原料在高温熔融作用下，会产生釉色整体色彩多样变化的独特艺术效果，具有很好的社会和经济效益。
具体实施方式
实施例1：一种钧瓷釉料，它是由下列重量百分比的原料制备而成的: 长石45﹪，方解石10﹪，铜矿石10﹪，滑石粉10﹪，木炭粉15﹪，氧化铜9.5﹪，氧化锡0.5﹪。
本发明对传统配方进行重新量化，自然原料配合相互作用，与化学原料在高温熔融作用下，会产生釉色整体色彩多样变化的独特艺术效果，具有很好的社会和经济效益。
实施例2：一种钧瓷釉料，它是由下列重量百分比的原料制备而成的: 长石46﹪，方解石9﹪，铜矿石11﹪，滑石粉9﹪，木炭粉15﹪，氧化铜9.5﹪，氧化锡0.5﹪。
本发明对传统配方进行重新量化，自然原料配合相互作用，与化学原料在高温熔融作用下，会产生釉色整体色彩多样变化的独特艺术效果，具有很好的社会和经济效益。
长石属于硅酸盐矿物盐，其内部含量为钾元素、钠元素和钙元素等，分为黄色、白色和红色等，是釉料的主要成分，主要对于釉料的形成起到重要作用。禹州分布有众多矿藏。
方解石主要降低釉料熔融温度，增加釉色的光泽度和透明度，防治釉面龟裂和堆积，用量不能过多，否则会导致釉面析晶失透，造成温度变窄，变化过少，并引起釉面吸烟。
铜矿石是最主要的铜矿石矿物，一般由Cu,Fe,S三种元素组成，理论组成（%）Cu34.56, Fe 30.52, S 34.92，理论化学式为CuFeS2。
滑石粉是天然含水硅酸镁矿物，是助熔料，可降低釉料的熔融温度和降低膨胀系数，促进胎釉中间层的形成，并增加乳浊性。
木炭粉主要补充钙元素和磷元素，有良好的助熔性，起到电解质作用，提高釉料的高温粘合度，同时具有乳浊作用和对釉料的分相作用。
氧化铜是一种铜的黑色氧化物，略显两性，稍有吸湿性。相对分子质量为79.545，密度为6.3～6.9 g/cm3，熔点1326℃。不溶于水和乙醇，溶于酸、氯化铵及氰化钾溶液，氨溶液中缓慢溶解，能与强碱反应。氧化铜主要用于制人造丝、陶瓷、釉及搪瓷、电池、石油脱硫剂、杀虫剂，也供制氢、催化剂、绿色玻璃等用。
氧化锡为白色、淡黄色或淡灰色四方、六方或斜方晶系粉末。熔点1630℃。
上述天然原料与化工原料配合使用，在高温熔融作用下，会产生釉色整体色彩多样变化的独特艺术效果，具有很好的社会和经济效益。

Claims (2)

1.一种钧瓷釉料，其特征在于，它是由下列重量百分比的原料制备而成的：长石44﹪至46﹪，方解石9﹪至11﹪，铜矿石9﹪至11﹪，滑石粉9﹪至11﹪，木炭粉14﹪至16﹪，氧化铜9.4﹪至9.6﹪，氧化锡0.4﹪至0.6﹪。
2.根据权利要求1所述的钧瓷釉料，其特征在于，它是由下列重量百分比的原料制备而成的：长石45﹪，方解石10﹪，铜矿石10﹪，滑石粉10﹪，木炭粉15﹪，氧化铜9.5﹪，氧化锡0.5﹪。
CN201610680524.9A 2016-08-18 2016-08-18 一种钧瓷釉料 Pending CN106316122A (zh)