CN106316114A - Lead-free glass with high clarification - Google Patents
Lead-free glass with high clarification Download PDFInfo
- Publication number
- CN106316114A CN106316114A CN201610711922.2A CN201610711922A CN106316114A CN 106316114 A CN106316114 A CN 106316114A CN 201610711922 A CN201610711922 A CN 201610711922A CN 106316114 A CN106316114 A CN 106316114A
- Authority
- CN
- China
- Prior art keywords
- content
- agent
- coloured glaze
- quartz sand
- barium sulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses lead-free glass with high clarification. The glass comprises quartz sand, fluxing agent, clarifying agent, coloring agent and curing agent. The fluxing agent is potassium nitrate and sodium nitrate. The clarifying agent is barium sulfate. The coloring agent is copper oxide, titanium dioxide and ferric oxide. The lead-free glass is prepared from, by weight percentage, 45%- 55% of quartz sand, 4%- 8% of potassium nitrate, 2%- 7% of sodium nitrate,10%- -15% of barium sulfate, 5%- 10% of copper oxide,10%- 15% of titanium dioxide, 3%- 5% of ferric oxide, and 2%- 5% of curing agent. Through the above way, the method adopts lead-free formula, conforming to requirements of environment protection. The clarifying agent is barium sulfate which replaces expensive ceric oxide. The proportion of raw material ingredients is optimized, to make glass be featured in short clarifying time and low softening point as well as have low cost.
Description
Technical field
The present invention relates to coloured glaze field, particularly relate to a kind of unleaded high clarification coloured glaze.
Background technology
Coloured glaze is a kind of silicate product, has a long history, and its quality is glittering and translucent, bright and glittering, changes irregularly magnificent,
Fully demonstrate the exquisiteness of Asians, fine and smooth and implicit, be a kind of important decoration element, coloured glaze be mainly composed of titanium dioxide
Silicon, aluminium oxide, flux lead oxide and pigment etc..
Colored glaze product manufacturing process is complicated, yield rate is low, the molding of colored glaze product and quality in addition to controlling preparation technology,
Depending primarily on the formula components of coloured glaze, coloured glaze composition is low with softening point, a length of good characteristic of material property, and softening point, material property are main
Depending on kind and the proportioning thereof of coloured glaze formula components, existing coloured glaze formula is in order to improve ratio of briquetting and the product of colored glaze product
Matter, is all added with lead oxide in its composition, and along with environmental protection requirement is more come with high by people, various countries have formulated harmful substance
The standard limited, it is stipulated that in glass container, lead Cmax is 0.1%, is therefore the direction of coloured glaze Future Development without lead composition.
Summary of the invention
The technical problem that present invention mainly solves is to provide a kind of unleaded high clarification coloured glaze, it is possible to solves existing coloured glaze and exists
Defect.
For solving above-mentioned technical problem, the technical scheme that the present invention uses is: provide a kind of unleaded high clarification coloured glaze,
Described coloured glaze includes: quartz sand, flux, clarifier, coloring agent and firming agent, and described flux is potassium nitrate and sodium nitrate,
Described clarifier is barium sulfate, and described coloring agent is copper oxide, titanium dioxide, iron sesquioxide, calculates in percentage by weight,
The content of described quartz sand is 45%-55%, the content of described potassium nitrate is 4%-8%, the content of described sodium nitrate is 2%-7%, institute
The content stating barium sulfate is 10%-15%, the content of described copper oxide is 5%-10%, the content of described titanium dioxide is 10%-15%,
The content of described iron sesquioxide is 3%-5%, the content of described firming agent is 2%-5%.
In a preferred embodiment of the present invention, the particle size range of described quartz sand is 0.02-0.08mm.
In a preferred embodiment of the present invention, the softening point of described coloured glaze is 460-510 DEG C.
In a preferred embodiment of the present invention, the settling time of described coloured glaze is 2-3h.
The invention has the beneficial effects as follows: the present invention uses lead-free recipe, meet environmental requirement, clarifier uses barium sulfate to replace
The ceria that generation is expensive, and optimize the proportioning of each material composition, make this coloured glaze have settling time is short, softening point is low spy
Point, simultaneously low cost.
Detailed description of the invention
Below presently preferred embodiments of the present invention is described in detail so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that thus protection scope of the present invention is made apparent clear and definite defining.
The embodiment of the present invention includes:
Embodiment one:
A kind of unleaded high clarification coloured glaze, described coloured glaze includes: quartz sand, flux, clarifier, coloring agent and firming agent, described
Flux is potassium nitrate and sodium nitrate, and described clarifier is barium sulfate, and described coloring agent is copper oxide, titanium dioxide, three oxidations
Two ferrum, calculate in percentage by weight, and the content of described quartz sand is 45%, the content of described potassium nitrate is 8%, described sodium nitrate
Content be 7%, the content of described barium sulfate be 15%, the content of described copper oxide be 8%, the content of described titanium dioxide be
12%, the content of described iron sesquioxide be 3%, the content of described firming agent be 2%.
Wherein, the particle size range of described quartz sand is 0.02mm.
The softening point of described coloured glaze is 460 DEG C, and settling time is 2h.
Embodiment two:
A kind of unleaded high clarification coloured glaze, described coloured glaze includes: quartz sand, flux, clarifier, coloring agent and firming agent, described
Flux is potassium nitrate and sodium nitrate, and described clarifier is barium sulfate, and described coloring agent is copper oxide, titanium dioxide, three oxidations
Two ferrum, calculate in percentage by weight, and the content of described quartz sand is 50%, the content of described potassium nitrate is 4%, described sodium nitrate
Content be 4%, the content of described barium sulfate be 12%, the content of described copper oxide be 10%, the content of described titanium dioxide be
10%, the content of described iron sesquioxide be 5%, the content of described firming agent be 5%.
Wherein, the particle size range of described quartz sand is 0.06mm.
The softening point of described coloured glaze is 480 DEG C, and settling time is 2.5h.
Embodiment three:
A kind of unleaded high clarification coloured glaze, described coloured glaze includes: quartz sand, flux, clarifier, coloring agent and firming agent, described
Flux is potassium nitrate and sodium nitrate, and described clarifier is barium sulfate, and described coloring agent is copper oxide, titanium dioxide, three oxidations
Two ferrum, calculate in percentage by weight, and the content of described quartz sand is 55%, the content of described potassium nitrate is 5%, described sodium nitrate
Content be 2%, the content of described barium sulfate be 10%, the content of described copper oxide be 5%, the content of described titanium dioxide be
15%, the content of described iron sesquioxide be 5%, the content of described firming agent be 3%.
Wherein, the particle size range of described quartz sand is 0.08mm.
The softening point of described coloured glaze is 510 DEG C, and settling time is 3h.
Present invention is disclosed a kind of unleaded high clarification coloured glaze, use lead-free recipe, meet environmental requirement, clarifier uses sulfur
The ceria that acid barium replacement is expensive, and optimize the proportioning of each material composition, settling time is short, softening point is low to make this coloured glaze have
Feature, low cost simultaneously.
The foregoing is only embodiments of the invention, not thereby limit the scope of the claims of the present invention, every utilize this
Equivalent structure or equivalence flow process that bright description is made convert, or are directly or indirectly used in other relevant technology necks
Territory, is the most in like manner included in the scope of patent protection of the present invention.
Claims (4)
1. a unleaded high clarification coloured glaze, it is characterised in that described coloured glaze includes: quartz sand, flux, clarifier, coloring agent
And firming agent, described flux is potassium nitrate and sodium nitrate, and described clarifier is barium sulfate, described coloring agent be copper oxide, two
Titanium oxide, iron sesquioxide, calculate in percentage by weight, and the content of described quartz sand is 45%-55%, the containing of described potassium nitrate
Amount is 4%-8%, the content of described sodium nitrate is 2%-7%, the content of described barium sulfate is 10%-15%, the content of described copper oxide
For the content of 5%-10%, described titanium dioxide be 10%-15%, the content of described iron sesquioxide be 3%-5%, described firming agent
Content be 2%-5%.
Unleaded high clarification coloured glaze the most according to claim 1, it is characterised in that the particle size range of described quartz sand is
0.02-0.08mm。
Unleaded high clarification coloured glaze the most according to claim 1, it is characterised in that the softening point of described coloured glaze is 460-510
℃。
Unleaded high clarification coloured glaze the most according to claim 1, it is characterised in that the settling time of described coloured glaze is 2-3h.