CN106316100A - Silicate glass plate for debugging screen - Google Patents
Silicate glass plate for debugging screen Download PDFInfo
- Publication number
- CN106316100A CN106316100A CN201510381699.5A CN201510381699A CN106316100A CN 106316100 A CN106316100 A CN 106316100A CN 201510381699 A CN201510381699 A CN 201510381699A CN 106316100 A CN106316100 A CN 106316100A
- Authority
- CN
- China
- Prior art keywords
- glass plate
- temperature
- silica glass
- silicate
- total amount
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a silicate glass plate for debugging a screen. The silicate glass plate is characterized by being prepared from the following raw material ingredients in percentage by weight: 30% to 32% of quartz sand, 9% to 11% of sodium carbonate, 2% to 5% of dolomite, 1% to 3% of calcite, 1% to 3% of fluorite, 1% to 3% of lepidolite, 1% to 3% of chrome ore powder, 20% to 40% of silicate, 10% to 25% of calcium silicate, 5% to 12% of silicon dioxide and 1% to 6% of nickel sesquioxide. The strength and hardness properties of the silicate glass plate prepared by the formula are similar to those of silicon cell panels, so that the problem of waste during the debugging of screens, back field aluminum slurry, back silver and front silver can be avoided; and the product is simple to produce and low in cost and is environmentally friendly and sanitary, and thus the popularization is facilitated.
Description
Technical field
The present invention relates to a kind of debugging web plate silica glass plate, belong to technical field of solar batteries.
Background technology
Solar energy is a kind of green energy resource, because it is pollution-free, inexhaustible, not by advantages such as resource advantage are limited
Increasingly it is subject to people's attention, so solaode arises at the historic moment.Crystal silicon solar batteries is a kind of energy
Enough devices responded luminous energy and can convert light energy into electric energy, it can utilize photovoltaic effect by luminous energy
Be converted to electric energy.But during manufacturing back field aluminum paste, the back of the body silver, positive silver paste, web plate, it is required for printing
Debugging, is all to carry out debugging test with expensive silion cell plate when printing debugging test, and an examination is exactly several
Ten, hundreds of, or even an a few thousand sheets, be very waste.
Summary of the invention
The primary and foremost purpose of the present invention is, overcomes problems of the prior art, it is provided that a kind of debugging web plate
Use silica glass plate.
For solving above technical problem, a kind of debugging web plate silica glass plate provided by the present invention, its feature exists
In: raw material components and the weight content of described silica glass plate are as follows: quartz sand 30%-32%, sodium carbonate
9%-11%, dolomite 2-5%, calcite 1-3%, fluorite 1-3%, lepidolite 1-3%, chromite ore fine 1-3%,
Silicate 20-40%, calcium silicates 10-25%, silicon dioxide 5-12%, nickel sesquioxide 1-6%, respectively
The percetage by weight sum of component is 100%.Step (1) described silica glass plate consists of: quartz sand,
Sodium carbonate, dolomite, calcite, fluorite, lepidolite, chromite ore fine, silicate, calcium silicates, dioxy
SiClx, nickel sesquioxide are mixed even;Step (2) feeds the mixture into fusing stove, using coal burning
The coal gas of 550 DEG C obtained sends into fusing stove, sealing combustion by gas transmission equipment, makes the temperature of compound
Reach 1530 DEG C-1540 DEG C, keep this temperature 18-24 hour, make compound reach molten condition, obtain
The blackish green glass melt of ash;Glass melt is sent into forming machine by step (3), makes certain specification
Silica glass plate;Annealing is sent into conveyer when glass plate is naturally cooling to about 600 DEG C by step (4)
Case, first adjusts the temperature in annelaing pot to about 550 DEG C, maintains 20 minutes, then temperature is adjusted to 400 DEG C of left sides
The right side, maintains 20 minutes, the most progressively lowers the temperature, cool the temperature to 150 DEG C, now anneal in 60 minutes
Complete, grey blackish green glass plate is sent in air, naturally cools to room temperature in atmosphere, obtain finished product.
It is an advantage of the current invention that and overcome the problem that there is waste in existing operation, it is provided that a kind of debugging web plate silicon
Glass plate, the performance of the silica glass plate intensity hardness made is similar to silion cell plate, size and silion cell
Plate is the same, and the cost of every silica glass plate only needs 0.5 yuan, and silion cell plate cost is at 15 yuan, silica glass plate
Nontoxic pollution-free in manufacture process, conservation of nature environment, and silion cell plate has injury to human body the Nature,
Mei Jia enterprise can save 500 blocks of silion cell plates average every day during experimental debugging, and the whole world is not said,
In Jiu, state-owned more than 300 produce solar silicon wafers and slurry, can save nearly 20,000 silion cell plates every day, just
Price does not say that the harm that the Nature is caused by the silion cell plate of annual saving is well imagined.
Detailed description of the invention
Embodiment one
By account for real estate quartz sand that total amount is 30%, account for sodium carbonate that total amount is 10%, account for total amount be 4% white
Marble, account for calcite that total amount is 2%, account for fluorite that total amount is 1%, account for lepidolite that total amount is 0.8%,
Account for chromite ore fine that total amount is 0.6%, account for total amount be 30% silicate, to account for total amount be 10% calcium silicates, accounts for total amount
Be 8% silicon dioxide, to account for total amount be 2% nickel sesquioxide even blend;Feed the mixture into fusing stove,
Send into fusing stove, sealing combustion with the coal gas of 550 DEG C of coal burning acquisition by gas transmission equipment, make compound
Temperature reach 1530 DEG C-1540 DEG C, keep this temperature 18-24 hour, make compound reach molten condition,
Obtain grey blackish green glass melt;Glass melt is sent into forming machine, makes the silica glass of certain specification
Plate;Annelaing pot is sent into conveyer, in first adjusting annelaing pot when silica glass plate is naturally cooling to about 600 DEG C
Temperature, to about 550 DEG C, maintains 20 minutes;Again temperature is adjusted to about 400 DEG C, maintains 20 minutes;So
After progressively lower the temperature, in 60 minute, cool the temperature to 150 DEG C, now anneal complete, by grey blackish green silicon glass
Glass plate is sent in air, naturally cools to room temperature in atmosphere, obtains finished product.
Embodiment 2
Real estate quartz sand that total amount is 31% will be accounted for, account for sodium carbonate that total amount is 10%, account for total amount and be
The dolomite of 4%, account for calcite that total amount is 2%, account for fluorite that total amount is 1%, account for the lithium that total amount is 0.8%
Muscovitum, account for chromite ore fine that total amount is 0.6%, account for total amount be 30% silicate, account for total amount and be 12% calcium silicates,
Account for total amount be 7% silicon dioxide, to account for total amount be 1% nickel sesquioxide even blend;Feed the mixture into fusing
Stove, sends into fusing stove, sealing combustion the coal gas of 550 DEG C obtained with coal burning by gas transmission equipment, makes
The temperature of compound reaches 1530 DEG C-1540 DEG C, keeps this temperature 18-24 hour, makes compound reach melted
State, obtains grey blackish green glass melt;Glass melt is sent into forming machine, makes certain specification
Silica glass plate;Send into annelaing pot with conveyer when silica glass plate is naturally cooling to about 600 DEG C, first adjust annealing
Temperature in case, to about 550 DEG C, maintains 20 minutes;Again temperature is adjusted to about 400 DEG C, maintains 20 points
Clock;The most progressively lower the temperature, in 60 minutes, cool the temperature to 150 DEG C, now anneal complete, ash is blackish green
Color silica glass plate is sent in air, naturally cools to room temperature in atmosphere, obtains finished product.
Embodiment 3
Real estate quartz sand that total amount is 32% will be accounted for, account for sodium carbonate that total amount is 9%, account for total amount and be
The dolomite of 4%, account for calcite that total amount is 2%, account for fluorite that total amount is 1%, account for the lithium that total amount is 0.8%
Muscovitum, account for chromite ore fine that total amount is 0.6%, account for total amount be 25% silicate, account for total amount and be 15% calcium silicates,
Account for total amount be 9% silicon dioxide, to account for total amount be 1% nickel sesquioxide even blend;Feed the mixture into fusing
Stove, sends into fusing stove, sealing combustion the coal gas of 550 DEG C obtained with coal burning by gas transmission equipment, makes
The temperature of compound reaches 1530 DEG C-1540 DEG C, keeps this temperature 18-24 hour, makes compound reach melted
State, obtains grey blackish green glass melt;Glass melt is sent into forming machine, makes certain specification
Silica glass plate;Send into annelaing pot with conveyer when silica glass plate is naturally cooling to about 600 DEG C, first adjust annealing
Temperature in case, to about 550 DEG C, maintains 20 minutes;Again temperature is adjusted to about 400 DEG C, maintains 20 points
Clock;The most progressively lower the temperature, in 60 minutes, cool the temperature to 150 DEG C, now anneal complete, ash is blackish green
Color silica glass plate is sent in air, naturally cools to room temperature in atmosphere, obtains finished product.
The intensity hardness that the method that thus goes up obtains is similar to the silica glass plate of silion cell plate, can manufacture back surface field
During aluminium paste, the back of the body silver, positive silver paste, web plate, debugging printing uses, cost-effective, protects environment.
Claims (2)
1. a debugging web plate silica glass plate, it is characterised in that: the raw material components of described silica glass plate
And weight content is as follows: quartz sand 30%-32%, sodium carbonate 9%-11%, dolomite 2-5%,
Calcite 1-3%, fluorite 1-3%, lepidolite 1-3%, chromite ore fine 1-3%, silicate 20-40%,
Calcium silicates 10-25%, silicon dioxide 5-12%, nickel sesquioxide 1-6%, the most each component
Percetage by weight sum is 100%.
A kind of debugging web plate silica glass plate the most according to claim 1, it is characterised in that: step
Suddenly (1) described silica glass plate consists of: quartz sand, sodium carbonate, dolomite, calcite,
Fluorite, lepidolite, chromite ore fine, silicate, calcium silicates, silicon dioxide, nickel sesquioxide
It is mixed even;Step (2) feeds the mixture into fusing stove, 550 obtained with coal burning
DEG C coal gas by gas transmission equipment send into fusing stove, sealing combustion, make the temperature of compound reach
To 1530 DEG C-1540 DEG C, keep this temperature 18-24 hour, make compound reach molten condition,
Obtain grey blackish green glass melt;Glass melt is sent into forming machine by step (3),
Make the silica glass plate of certain specification;Glass plate is naturally cooling to 600 DEG C of left sides by step (4)
Send into annelaing pot with conveyer time right, first adjust the temperature in annelaing pot to about 550 DEG C, tie up
Hold 20 minutes, then temperature be adjusted to about 400 DEG C, maintain 20 minutes, the most progressively lower the temperature,
In 60 minutes, cool the temperature to 150 DEG C, now anneal complete, by grey blackish green glass plate
Send in air, naturally cool to room temperature in atmosphere, obtain finished product.