CN106283657A - The postfinishing process of wool knitting fabrics - Google Patents
The postfinishing process of wool knitting fabrics Download PDFInfo
- Publication number
- CN106283657A CN106283657A CN201610693052.0A CN201610693052A CN106283657A CN 106283657 A CN106283657 A CN 106283657A CN 201610693052 A CN201610693052 A CN 201610693052A CN 106283657 A CN106283657 A CN 106283657A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- weight portion
- dressing liquid
- successively
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the postfinishing process of a kind of wool knitting fabrics, comprise the steps: 1) by 1~2 part by weight of boric acid zinc, 1.7 weight portion imidazolines, 0.9 weight portion encapsulated red phosphorus, 1.4 weight portion N, N bis-(amido-ethyl) methyl quaternary ammonium, 2.9 parts by weight of polyoxyethylene sorbitan fatty acid esters put in 48 parts by weight of deionized water successively, stir;2) 2.3 weight portion sodium hexameta phosphate, 3.5 parts by weight maleic anhydride modified poly ethylenes, 4.1 weight portion NPEs, 3.1 weight parts of methacrylic acid diethylamino ethyl esters, 1.1 parts by weight of maleic list sodium are put into the most successively, continue stirring, to being sufficiently mixed uniformly, prepare dressing liquid;3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.Fabric performance after the present invention arranges is good and soft.
Description
Technical field
The present invention relates to the postfinishing process of wool knitting fabrics.
Background technology
Crease-resistant, wear-resisting, the mildew-resistant of existing fabric, mothproof, antibacterial, fire-retardant, antistatic, performance washable, shrinkproof all need to be carried
Height, and feel is the most soft.
Summary of the invention
It is an object of the invention to provide the postfinishing process of a kind of wool knitting fabrics, the fabric after it arranges has excellent
Different crease-resistant, wear-resisting, mildew-resistant, mothproof, antibacterial, fire-retardant, antistatic, performance washable, shrinkproof, and soft.
For achieving the above object, the technical scheme is that the postfinishing process designing a kind of wool knitting fabrics, bag
Include following steps:
1) by 1~2 part by weight of boric acid zinc, 1.7 weight portion imidazolines, 0.9 weight portion encapsulated red phosphorus, 1.4 weight portion N, N-
Two (amido-ethyl)-methyl quaternary ammoniums, 2.9 parts by weight of polyoxyethylene sorbitan fatty acid esters put into 48 weight portions successively
In deionized water, stir;
2) 2.3 weight portion sodium hexameta phosphate, 3.5 parts by weight maleic anhydride modified poly ethylenes, 4.1 weight portions are put into the most successively
NPE, 3.1 weight parts of methacrylic acid diethylamino ethyl esters, 1.1 parts by weight of maleic list sodium, continue to stir
Mix, to being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
Preferably, the postfinishing process of wool knitting fabrics, comprise the steps:
1) by 1 part by weight of boric acid zinc, 1.7 weight portion imidazolines, 0.9 weight portion encapsulated red phosphorus, 1.4 weight portion N, N-bis-
(amido-ethyl)-methyl quaternary ammonium, 2.9 parts by weight of polyoxyethylene sorbitan fatty acid esters put into 48 weight portions successively and go
In ionized water, stir;
2) 2.3 weight portion sodium hexameta phosphate, 3.5 parts by weight maleic anhydride modified poly ethylenes, 4.1 weight portions are put into the most successively
NPE, 3.1 weight parts of methacrylic acid diethylamino ethyl esters, 1.1 parts by weight of maleic list sodium, continue to stir
Mix, to being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
Preferably, the postfinishing process of wool knitting fabrics, comprise the steps:
1) by 2 part by weight of boric acid zinc, 1.7 weight portion imidazolines, 0.9 weight portion encapsulated red phosphorus, 1.4 weight portion N, N-bis-
(amido-ethyl)-methyl quaternary ammonium, 2.9 parts by weight of polyoxyethylene sorbitan fatty acid esters put into 48 weight portions successively and go
In ionized water, stir;
2) 2.3 weight portion sodium hexameta phosphate, 3.5 parts by weight maleic anhydride modified poly ethylenes, 4.1 weight portions are put into the most successively
NPE, 3.1 weight parts of methacrylic acid diethylamino ethyl esters, 1.1 parts by weight of maleic list sodium, continue to stir
Mix, to being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
Preferably, the postfinishing process of wool knitting fabrics, comprise the steps:
1) by 1.2 part by weight of boric acid zinc, 1.7 weight portion imidazolines, 0.9 weight portion encapsulated red phosphorus, 1.4 weight portion N, N-bis-
(amido-ethyl)-methyl quaternary ammonium, 2.9 parts by weight of polyoxyethylene sorbitan fatty acid esters put into 48 weight portions successively and go
In ionized water, stir;
2) 2.3 weight portion sodium hexameta phosphate, 3.5 parts by weight maleic anhydride modified poly ethylenes, 4.1 weight portions are put into the most successively
NPE, 3.1 weight parts of methacrylic acid diethylamino ethyl esters, 1.1 parts by weight of maleic list sodium, continue to stir
Mix, to being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
Advantages of the present invention and having the beneficial effects that: provide the postfinishing process of a kind of wool knitting fabrics, after it arranges
Fabric there is crease-resistant, wear-resisting, the mildew-resistant of excellence, mothproof, antibacterial, fire-retardant, antistatic, performance washable, shrinkproof, and feel is soft
Soft.
Performance and the purposes of " dressing liquid " are determined by its component and proportioning, and the different component meeting in " dressing liquid "
Influencing each other, component and proportioning thereof can determine the final performance of " dressing liquid ", as the most mutually coordinated in fruit component and proportioning thereof, single
The beneficial effect that component is brought, even can be eliminated by other components abatement, and the when of serious, different component is mutually conflicted, and rises
Less than whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains " arranging
Liquid " optimal component and proportioning so that multiple components combine, mutually coordinated and produce forward comprehensive effect.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.Following example are only used for more
Add and clearly demonstrate technical scheme, and can not limit the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
The postfinishing process of wool knitting fabrics, comprises the steps:
1) by 1~2 part by weight of boric acid zinc, 1.7 weight portion imidazolines, 0.9 weight portion encapsulated red phosphorus, 1.4 weight portion N, N-
Two (amido-ethyl)-methyl quaternary ammoniums, 2.9 parts by weight of polyoxyethylene sorbitan fatty acid esters put into 48 weight portions successively
In deionized water, stir;
2) 2.3 weight portion sodium hexameta phosphate, 3.5 parts by weight maleic anhydride modified poly ethylenes, 4.1 weight portions are put into the most successively
NPE, 3.1 weight parts of methacrylic acid diethylamino ethyl esters, 1.1 parts by weight of maleic list sodium, continue to stir
Mix, to being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
Embodiment 2
The postfinishing process of wool knitting fabrics, comprises the steps:
1) by 1 part by weight of boric acid zinc, 1.7 weight portion imidazolines, 0.9 weight portion encapsulated red phosphorus, 1.4 weight portion N, N-bis-
(amido-ethyl)-methyl quaternary ammonium, 2.9 parts by weight of polyoxyethylene sorbitan fatty acid esters put into 48 weight portions successively and go
In ionized water, stir;
2) 2.3 weight portion sodium hexameta phosphate, 3.5 parts by weight maleic anhydride modified poly ethylenes, 4.1 weight portions are put into the most successively
NPE, 3.1 weight parts of methacrylic acid diethylamino ethyl esters, 1.1 parts by weight of maleic list sodium, continue to stir
Mix, to being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
Embodiment 3
The postfinishing process of wool knitting fabrics, comprises the steps:
1) by 2 part by weight of boric acid zinc, 1.7 weight portion imidazolines, 0.9 weight portion encapsulated red phosphorus, 1.4 weight portion N, N-bis-
(amido-ethyl)-methyl quaternary ammonium, 2.9 parts by weight of polyoxyethylene sorbitan fatty acid esters put into 48 weight portions successively and go
In ionized water, stir;
2) 2.3 weight portion sodium hexameta phosphate, 3.5 parts by weight maleic anhydride modified poly ethylenes, 4.1 weight portions are put into the most successively
NPE, 3.1 weight parts of methacrylic acid diethylamino ethyl esters, 1.1 parts by weight of maleic list sodium, continue to stir
Mix, to being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
Embodiment 4
The postfinishing process of wool knitting fabrics, comprises the steps:
1) by 1.2 part by weight of boric acid zinc, 1.7 weight portion imidazolines, 0.9 weight portion encapsulated red phosphorus, 1.4 weight portion N, N-bis-
(amido-ethyl)-methyl quaternary ammonium, 2.9 parts by weight of polyoxyethylene sorbitan fatty acid esters put into 48 weight portions successively and go
In ionized water, stir;
2) 2.3 weight portion sodium hexameta phosphate, 3.5 parts by weight maleic anhydride modified poly ethylenes, 4.1 weight portions are put into the most successively
NPE, 3.1 weight parts of methacrylic acid diethylamino ethyl esters, 1.1 parts by weight of maleic list sodium, continue to stir
Mix, to being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
Fabric after the various embodiments described above arrange, has crease-resistant, wear-resisting, the mildew-resistant of excellence, mothproof, antibacterial, fire-retardant, anti-
Electrostatic, performance washable, shrinkproof, and soft.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For Yuan, on the premise of without departing from the technology of the present invention principle, it is also possible to make some improvements and modifications, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. the postfinishing process of wool knitting fabrics, it is characterised in that comprise the steps:
1) by 1~2 part by weight of boric acid zinc, 1.7 weight portion imidazolines, 0.9 weight portion encapsulated red phosphorus, 1.4 weight portion N, N-bis-(acyl
Amido ethyl)-methyl quaternary ammonium, 2.9 parts by weight of polyoxyethylene sorbitan fatty acid esters put into successively 48 weight portions go from
In sub-water, stir;
2) 2.3 weight portion sodium hexameta phosphate, 3.5 parts by weight maleic anhydride modified poly ethylenes, 4.1 weight portion nonyls are put into the most successively
Phenol polyethenoxy ether, 3.1 weight parts of methacrylic acid diethylamino ethyl esters, 1.1 parts by weight of maleic list sodium, continue stirring,
To being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
The postfinishing process of wool knitting fabrics the most according to claim 1, it is characterised in that comprise the steps:
1) by 1 part by weight of boric acid zinc, 1.7 weight portion imidazolines, 0.9 weight portion encapsulated red phosphorus, 1.4 weight portion N, N-bis-(amide
Base ethyl)-methyl quaternary ammonium, 2.9 parts by weight of polyoxyethylene sorbitan fatty acid esters put into 48 weight portion deionizations successively
In water, stir;
2) 2.3 weight portion sodium hexameta phosphate, 3.5 parts by weight maleic anhydride modified poly ethylenes, 4.1 weight portion nonyls are put into the most successively
Phenol polyethenoxy ether, 3.1 weight parts of methacrylic acid diethylamino ethyl esters, 1.1 parts by weight of maleic list sodium, continue stirring,
To being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
The postfinishing process of wool knitting fabrics the most according to claim 1, it is characterised in that comprise the steps:
1) by 2 part by weight of boric acid zinc, 1.7 weight portion imidazolines, 0.9 weight portion encapsulated red phosphorus, 1.4 weight portion N, N-bis-(amide
Base ethyl)-methyl quaternary ammonium, 2.9 parts by weight of polyoxyethylene sorbitan fatty acid esters put into 48 weight portion deionizations successively
In water, stir;
2) 2.3 weight portion sodium hexameta phosphate, 3.5 parts by weight maleic anhydride modified poly ethylenes, 4.1 weight portion nonyls are put into the most successively
Phenol polyethenoxy ether, 3.1 weight parts of methacrylic acid diethylamino ethyl esters, 1.1 parts by weight of maleic list sodium, continue stirring,
To being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
The postfinishing process of wool knitting fabrics the most according to claim 1, it is characterised in that comprise the steps:
1) by 1.2 part by weight of boric acid zinc, 1.7 weight portion imidazolines, 0.9 weight portion encapsulated red phosphorus, 1.4 weight portion N, N-bis-(acyl
Amido ethyl)-methyl quaternary ammonium, 2.9 parts by weight of polyoxyethylene sorbitan fatty acid esters put into successively 48 weight portions go from
In sub-water, stir;
2) 2.3 weight portion sodium hexameta phosphate, 3.5 parts by weight maleic anhydride modified poly ethylenes, 4.1 weight portion nonyls are put into the most successively
Phenol polyethenoxy ether, 3.1 weight parts of methacrylic acid diethylamino ethyl esters, 1.1 parts by weight of maleic list sodium, continue stirring,
To being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.