CN106319942A - Post-finishing process for bamboo fiber knitted fabric - Google Patents

Post-finishing process for bamboo fiber knitted fabric Download PDF

Info

Publication number
CN106319942A
CN106319942A CN201610687991.4A CN201610687991A CN106319942A CN 106319942 A CN106319942 A CN 106319942A CN 201610687991 A CN201610687991 A CN 201610687991A CN 106319942 A CN106319942 A CN 106319942A
Authority
CN
China
Prior art keywords
weight
parts
fabric
dressing liquid
successively
Prior art date
Application number
CN201610687991.4A
Other languages
Chinese (zh)
Inventor
许良宏
Original Assignee
常熟市大正纺织制版有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 常熟市大正纺织制版有限公司 filed Critical 常熟市大正纺织制版有限公司
Priority to CN201610687991.4A priority Critical patent/CN106319942A/en
Publication of CN106319942A publication Critical patent/CN106319942A/en

Abstract

The invention discloses a post-finishing process for bamboo fiber knitted fabric. The post-finishing process comprises the following steps: 1) sequentially feeding 1-2 parts by weight of sodium pentachlorophenolate, 0.9 part by weight of alkyl sulfonate, 1.3 parts by weight of ammonium dihydrogen phosphate, 2.3 parts by weight of fatty acid triglyceride and 4.1 parts by weight of ethylene glycol monostearate into 57 parts by weight of deionized water, and stirring uniformly; 2) sequentially feeding 2.9 parts by weight of gamma-epoxypropyl ether trimethoxysilane, 0.9 part by weight of imidazoline, 1.3 parts by weight of methylene biguanide, 4.1 parts by weight of hexabutyl peroxybenzoate and 1.2 parts by weight of fatty acyl diethanol amine, continuing to stir until fully mixing evenly to prepare finishing liquid; and 3) and then padding the fabric in the finishing liquid, and taking out the fabric for drying at constant temperature. The finished fabric has good performance and soft hand feel.

Description

The postfinishing process of bamboo fiber knitting fabric
Technical field
The present invention relates to the postfinishing process of bamboo fiber knitting fabric.
Background technology
Crease-resistant, wear-resisting, the mildew-resistant of existing fabric, mothproof, antibacterial, fire-retardant, antistatic, performance washable, shrinkproof all need to be carried Height, and feel is the most soft.
Summary of the invention
It is an object of the invention to provide the postfinishing process of a kind of bamboo fiber knitting fabric, the fabric after it arranges has Excellent crease-resistant, wear-resisting, mildew-resistant, mothproof, antibacterial, fire-retardant, antistatic, performance washable, shrinkproof, and soft.
For achieving the above object, the technical scheme is that the postfinishing process designing a kind of bamboo fiber knitting fabric, Comprise the steps:
1) by 1~2 weight portion penta sodium pentachlorophenates, 0.9 weight portion alkylsulfonate, 1.3 parts by weight of phosphoric acid ammonium dihydrogens, 2.3 weights Amount part fatty acid triglycercide, 4.1 weight portion ethylene glycol monostearates put in 57 parts by weight of deionized water successively, and stirring is all Even;
2) put into the most successively 2.9 weight portion γ-glycidyl ether trimethoxy silane, 0.9 weight portion imidazoline, 1.3 Weight portion methylene biguanide, 4.1 weight portion perbenzoic acid six butyl esters, 1.2 parts by weight of fatty acyl diethanolamine, continue to stir Mix, to being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
Preferably, the postfinishing process of bamboo fiber knitting fabric, comprise the steps:
1) by 1 weight portion penta sodium pentachlorophenate, 0.9 weight portion alkylsulfonate, 1.3 parts by weight of phosphoric acid ammonium dihydrogens, 2.3 weight portions Fatty acid triglycercide, 4.1 weight portion ethylene glycol monostearates put in 57 parts by weight of deionized water successively, stir;
2) put into the most successively 2.9 weight portion γ-glycidyl ether trimethoxy silane, 0.9 weight portion imidazoline, 1.3 Weight portion methylene biguanide, 4.1 weight portion perbenzoic acid six butyl esters, 1.2 parts by weight of fatty acyl diethanolamine, continue to stir Mix, to being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
Preferably, the postfinishing process of bamboo fiber knitting fabric, comprise the steps:
1) by 2 weight portion penta sodium pentachlorophenates, 0.9 weight portion alkylsulfonate, 1.3 parts by weight of phosphoric acid ammonium dihydrogens, 2.3 weight portions Fatty acid triglycercide, 4.1 weight portion ethylene glycol monostearates put in 57 parts by weight of deionized water successively, stir;
2) put into the most successively 2.9 weight portion γ-glycidyl ether trimethoxy silane, 0.9 weight portion imidazoline, 1.3 Weight portion methylene biguanide, 4.1 weight portion perbenzoic acid six butyl esters, 1.2 parts by weight of fatty acyl diethanolamine, continue to stir Mix, to being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
Preferably, the postfinishing process of bamboo fiber knitting fabric, comprise the steps:
1) by 1.2 weight portion penta sodium pentachlorophenates, 0.9 weight portion alkylsulfonate, 1.3 parts by weight of phosphoric acid ammonium dihydrogens, 2.3 weight Part fatty acid triglycercide, 4.1 weight portion ethylene glycol monostearates put in 57 parts by weight of deionized water successively, and stirring is all Even;
2) put into the most successively 2.9 weight portion γ-glycidyl ether trimethoxy silane, 0.9 weight portion imidazoline, 1.3 Weight portion methylene biguanide, 4.1 weight portion perbenzoic acid six butyl esters, 1.2 parts by weight of fatty acyl diethanolamine, continue to stir Mix, to being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
Advantages of the present invention and having the beneficial effects that: provide the postfinishing process of a kind of bamboo fiber knitting fabric, it arranges After fabric there is crease-resistant, wear-resisting, the mildew-resistant of excellence, mothproof, antibacterial, fire-retardant, antistatic, performance washable, shrinkproof, and feel is soft Soft.
Performance and the purposes of " dressing liquid " are determined by its component and proportioning, and the different component meeting in " dressing liquid " Influencing each other, component and proportioning thereof can determine the final performance of " dressing liquid ", as the most mutually coordinated in fruit component and proportioning thereof, single The beneficial effect that component is brought, even can be eliminated by other components abatement, and the when of serious, different component is mutually conflicted, and rises Less than whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains " arranging Liquid " optimal component and proportioning so that multiple components combine, mutually coordinated and produce forward comprehensive effect.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.Following example are only used for more Add and clearly demonstrate technical scheme, and can not limit the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
The postfinishing process of bamboo fiber knitting fabric, comprises the steps:
1) by 1~2 weight portion penta sodium pentachlorophenates, 0.9 weight portion alkylsulfonate, 1.3 parts by weight of phosphoric acid ammonium dihydrogens, 2.3 weights Amount part fatty acid triglycercide, 4.1 weight portion ethylene glycol monostearates put in 57 parts by weight of deionized water successively, and stirring is all Even;
2) put into the most successively 2.9 weight portion γ-glycidyl ether trimethoxy silane, 0.9 weight portion imidazoline, 1.3 Weight portion methylene biguanide, 4.1 weight portion perbenzoic acid six butyl esters, 1.2 parts by weight of fatty acyl diethanolamine, continue to stir Mix, to being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
Embodiment 2
The postfinishing process of bamboo fiber knitting fabric, comprises the steps:
1) by 1 weight portion penta sodium pentachlorophenate, 0.9 weight portion alkylsulfonate, 1.3 parts by weight of phosphoric acid ammonium dihydrogens, 2.3 weight portions Fatty acid triglycercide, 4.1 weight portion ethylene glycol monostearates put in 57 parts by weight of deionized water successively, stir;
2) put into the most successively 2.9 weight portion γ-glycidyl ether trimethoxy silane, 0.9 weight portion imidazoline, 1.3 Weight portion methylene biguanide, 4.1 weight portion perbenzoic acid six butyl esters, 1.2 parts by weight of fatty acyl diethanolamine, continue to stir Mix, to being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
Embodiment 3
The postfinishing process of bamboo fiber knitting fabric, comprises the steps:
1) by 2 weight portion penta sodium pentachlorophenates, 0.9 weight portion alkylsulfonate, 1.3 parts by weight of phosphoric acid ammonium dihydrogens, 2.3 weight portions Fatty acid triglycercide, 4.1 weight portion ethylene glycol monostearates put in 57 parts by weight of deionized water successively, stir;
2) put into the most successively 2.9 weight portion γ-glycidyl ether trimethoxy silane, 0.9 weight portion imidazoline, 1.3 Weight portion methylene biguanide, 4.1 weight portion perbenzoic acid six butyl esters, 1.2 parts by weight of fatty acyl diethanolamine, continue to stir Mix, to being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
Embodiment 4
The postfinishing process of bamboo fiber knitting fabric, comprises the steps:
1) by 1.2 weight portion penta sodium pentachlorophenates, 0.9 weight portion alkylsulfonate, 1.3 parts by weight of phosphoric acid ammonium dihydrogens, 2.3 weight Part fatty acid triglycercide, 4.1 weight portion ethylene glycol monostearates put in 57 parts by weight of deionized water successively, and stirring is all Even;
2) put into the most successively 2.9 weight portion γ-glycidyl ether trimethoxy silane, 0.9 weight portion imidazoline, 1.3 Weight portion methylene biguanide, 4.1 weight portion perbenzoic acid six butyl esters, 1.2 parts by weight of fatty acyl diethanolamine, continue to stir Mix, to being sufficiently mixed uniformly, prepare dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
Fabric after the various embodiments described above arrange, has crease-resistant, wear-resisting, the mildew-resistant of excellence, mothproof, antibacterial, fire-retardant, anti- Electrostatic, performance washable, shrinkproof, and soft.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art For Yuan, on the premise of without departing from the technology of the present invention principle, it is also possible to make some improvements and modifications, these improvements and modifications Also should be regarded as protection scope of the present invention.

Claims (4)

1. the postfinishing process of bamboo fiber knitting fabric, it is characterised in that comprise the steps:
1) by 1~2 weight portion penta sodium pentachlorophenates, 0.9 weight portion alkylsulfonate, 1.3 parts by weight of phosphoric acid ammonium dihydrogens, 2.3 weight portions Fatty acid triglycercide, 4.1 weight portion ethylene glycol monostearates put in 57 parts by weight of deionized water successively, stir;
2) 2.9 weight portion γ-glycidyl ether trimethoxy silane, 0.9 weight portion imidazoline, 1.3 weight are put into the most successively Part methylene biguanide, 4.1 weight portion perbenzoic acid six butyl esters, 1.2 parts by weight of fatty acyl diethanolamine, continue stirring, extremely It is sufficiently mixed uniformly, prepares dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
The postfinishing process of bamboo fiber knitting fabric the most according to claim 1, it is characterised in that comprise the steps:
1) by 1 weight portion penta sodium pentachlorophenate, 0.9 weight portion alkylsulfonate, 1.3 parts by weight of phosphoric acid ammonium dihydrogens, 2.3 parts by weight of fatty Acid glycerol three ester, 4.1 weight portion ethylene glycol monostearates put in 57 parts by weight of deionized water successively, stir;
2) 2.9 weight portion γ-glycidyl ether trimethoxy silane, 0.9 weight portion imidazoline, 1.3 weight are put into the most successively Part methylene biguanide, 4.1 weight portion perbenzoic acid six butyl esters, 1.2 parts by weight of fatty acyl diethanolamine, continue stirring, extremely It is sufficiently mixed uniformly, prepares dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
The postfinishing process of bamboo fiber knitting fabric the most according to claim 1, it is characterised in that comprise the steps:
1) by 2 weight portion penta sodium pentachlorophenates, 0.9 weight portion alkylsulfonate, 1.3 parts by weight of phosphoric acid ammonium dihydrogens, 2.3 parts by weight of fatty Acid glycerol three ester, 4.1 weight portion ethylene glycol monostearates put in 57 parts by weight of deionized water successively, stir;
2) 2.9 weight portion γ-glycidyl ether trimethoxy silane, 0.9 weight portion imidazoline, 1.3 weight are put into the most successively Part methylene biguanide, 4.1 weight portion perbenzoic acid six butyl esters, 1.2 parts by weight of fatty acyl diethanolamine, continue stirring, extremely It is sufficiently mixed uniformly, prepares dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
The postfinishing process of bamboo fiber knitting fabric the most according to claim 1, it is characterised in that comprise the steps:
1) by 1.2 weight portion penta sodium pentachlorophenates, 0.9 weight portion alkylsulfonate, 1.3 parts by weight of phosphoric acid ammonium dihydrogens, 2.3 weight portion fat Fat acid glycerol three ester, 4.1 weight portion ethylene glycol monostearates put in 57 parts by weight of deionized water successively, stir;
2) 2.9 weight portion γ-glycidyl ether trimethoxy silane, 0.9 weight portion imidazoline, 1.3 weight are put into the most successively Part methylene biguanide, 4.1 weight portion perbenzoic acid six butyl esters, 1.2 parts by weight of fatty acyl diethanolamine, continue stirring, extremely It is sufficiently mixed uniformly, prepares dressing liquid;
3) fabric is padded in dressing liquid process, constant temperature drying after taking-up again.
CN201610687991.4A 2016-08-19 2016-08-19 Post-finishing process for bamboo fiber knitted fabric CN106319942A (en)