CN106283380A - The logical rope of pin that pin leads to the weaving method of rope and the method is weaved into - Google Patents
The logical rope of pin that pin leads to the weaving method of rope and the method is weaved into Download PDFInfo
- Publication number
- CN106283380A CN106283380A CN201510247309.5A CN201510247309A CN106283380A CN 106283380 A CN106283380 A CN 106283380A CN 201510247309 A CN201510247309 A CN 201510247309A CN 106283380 A CN106283380 A CN 106283380A
- Authority
- CN
- China
- Prior art keywords
- paper
- vexed
- paper roll
- rope
- pin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides the logical rope of pin that a kind of pin leads to the weaving method of rope and the method is weaved into, belong to textile technology field.The method includes: tubular paper roll is carried out separation, obtains treating vexed paper roll;To treat that vexed paper roll is dipped in paper softener, and make paper softener not treat vexed paper roll, and further take out and treat vexed paper roll after soaking, after placing in being placed in confined space, obtain vexed rear paper roll;Vexed rear paper roll is woven, obtains the logical rope of pin.The little paper roll (treating vexed paper roll) obtained after tubular paper roll (the biggest paper disc or paper roll) separation is dipped in paper softener by the method, and is placed in confined space, to realize vexed paper effect.Obtain after vexed paper vexed after paper roll, its pliability and resistance to draw performance to be substantially improved, can be directly used in the braiding that pin leads to rope, eliminate coil paper yarn commonly used in the prior art operation, thus realize saving time, energy consumption and operate effect easily, improve pin and lead to the braid efficiency of rope.
Description
Technical field
The present invention relates to textile technology field, lead to the braiding of rope in particular to a kind of pin
The logical rope of the pin that method and the method are weaved into.
Background technology
It is first to be organized pitch of the laps again through fast stringed set various raw materials by knitting needle that pin leads to rope, connects
Novel product form, can weave diversified in specifications according to number, the arrangement mode of knitting needle
Circle, the hollow or product of flat shape, finely from 1mm to 8mm.
Prepare pin to lead to the material of rope and can use cotton yarn, polypropylene staple fibre spun yarn, Polyester Yarns, mercerized cotton, Buddhist nun
Dragon, artificial silk etc., this pin logical rope quality is soft, has good ductility, has certain elasticity.
Typically can also be as ribbon, the raw material that rope band produces, it is usually used in cored, such as primary and secondary
Band, the cored of sennit.Pin leads to the speed of production the most typically circle rope of rope wants fast, production efficiency
The most of a relatively high, therefore, it is widely used in recent years, as common in being applied to more
Chinese knot hangs the fields such as fringe, clothing, footwear material and package packing supplies.
Concrete, in the related, during preparing the logical rope of pin, mainly include point
Paper, coil paper yarn and braiding operation.Wherein, in the operation of separation, big paper disc is split
For having the little paper disc of one fixed width;Owing to paper toughness and the Nai La degree of this little paper disc are non-
The most limited, therefore, this little paper disc needs (will the narrow thin paper of little paper disc by coil paper yarn
Be twisted circular cord) after weave again, to meet the intensity need during crochet needle leads to rope
Ask.
But, in the operation of coil paper yarn, holding time is longer, operates relatively complicated, and
Need the most large-scale operation equipment;Therefore add pin and lead to the energy consumption in rope preparation process,
And reduce braid efficiency.
In view of this, the special proposition present invention.
Summary of the invention
It is an object of the invention to provide a kind of pin and lead to the weaving method of rope, this weaving method will
Little paper roll (the treating vexed paper roll) leaching obtained after tubular paper roll (the biggest paper disc or paper roll) separation
In or directly spray paper softener, and placed in confined space, to realize
Vexed paper effect.Obtain after vexed paper vexed after paper roll, its pliability and resistance to draw performance big
Width promotes so that it is can be directly used in the braiding that pin leads to rope, eliminates in prior art normal
The operation of coil paper yarn, thus realize saving time, energy consumption and operate effect easily,
Improve pin and lead to the braid efficiency of rope.
Another object of the present invention is to the logical rope of pin providing above-mentioned weaving method to make, with
Realize its application in fields such as clothing, footwear material and package packing supplies.
The logical rope of this pin that the present invention provides is the logical rope of papery pin, with traditional terylene or Buddhist nun
Dragon pin leads to rope to be compared, on the one hand, its waste products is prone to be decomposed, thus has preferable ring
Guaranteed cost;On the other hand, this papery pin leads to the also very easy realization weight of the waste product after rope uses
Multiple utilization, has the effect economized on resources.
In order to realize the above-mentioned purpose of the present invention, spy by the following technical solutions:
The invention provides a kind of pin and lead to the weaving method of rope, including: will obtain after separation
The paper disc arrived soaks through paper softener or sprays, after standing in airtight space
Directly weave, obtain the logical rope of pin.
In paper fiber molecule chain, typically can contain multiple hydroxyls, and be straight chain type macromole,
Having the strongest molecular separating force and hydrogen bond between its chain, degree of crystallinity is higher, for being rigidly connected,
Therefore it is highly susceptible to being pulled off.But after being soaked by paper softener, softening agent adheres to
In the surface of paper roll, stand at closed environment and (prevent softening agent generation qualitative change, and lose
Go ins and outs) during, softening agent is fully infiltrated into inside paper roll, and paper softener exists
Nonpolar isolating membrane is formed, so that strand occurs mutually the most under stress between fiber
Sliding and motion, and add pliability and the Nai La performance of paper so that it is it is difficult to be pulled off,
And can be directly used in the braiding that pin leads to rope.Therefore, the method eliminates the behaviour of coil paper yarn
Make, thus saved time cost, improve pin and lead to the braid efficiency of rope.
Preferably, in order to reach superior technique effect so that whole weaving method can be fast
Speed is implemented effectively, above-mentioned weaving method, specifically can comprise the following steps that
1), tubular paper roll is carried out separation, obtain treating vexed paper roll;
2), treat that vexed paper roll is dipped in paper softener by described, and make paper softener not have
Described treat vexed paper roll, further take out and treat vexed paper roll after soaking, be placed in confined space
Place so that paper softener permeates, and obtains vexed rear paper roll;
It is said that in general, (make paper softener fully soak to realize preferable osmotic effect
Enter in paper roll), preferred standing time is 2-12 hour.
Wherein, in described paper softener, in terms of volume parts, including by dimethyl-silicon
Oxygen alkane mixed methylcyclosiloxane, N-β-(aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane mixing
Become silicon crude oil complex 2-4 part and fatty alcohol-polyoxyethylene ether 1-2 part;
3), described vexed rear paper roll is woven, obtain the logical rope of pin.
Preferably, in step 2) in, the composition of paper softener used has been carried out spy
Fixed selection, by dimethyl siloxane mixed methylcyclosiloxane, N-β-(aminoethyl)-γ-aminopropyl
Methyl dimethoxysilane is mixed into silicon crude oil complex 2-4 part and fatty alcohol-polyoxyethylene ether
1-2 part.
Dimethyl siloxane mixed methylcyclosiloxane is from one or more line styles, ring-type and chain siloxanes
Set out, under catalyst action, made by reactions such as balance, addition or condensations, its property
Matter is relatively stable, it is easy to N-β-(aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane
Mixture, and N-β-(aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane is difunctional idol
Connection agent, after its functional group is bonded on silicone oil skeleton, can improve organosilicon (molecule) and exist
The degree of orientation on fiber, adds the affinity to fiber, gives the super softness of fiber, cunning
Refreshing, pendency, antistatic, the washable effect such as wrinkle resistant;Fatty alcohol-polyoxyethylene ether as auxiliary agent,
There is emulsifying and osmosis, so that paper softener permeates the most comprehensive in paper.
Optionally, in step 2) in, in described silicon crude oil complex, dimethyl siloxane
Mixed methylcyclosiloxane and the volume ratio of N-β-(aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane
It is 1: (1-4).
When dimethyl siloxane mixed methylcyclosiloxane and N-β-(aminoethyl)-γ-aminopropyltriethoxy two
The volume ratio of methoxy silane is 1: time (1-4), and each component of softening agent is more easy to realize mixing
Effect, and due to N-β-(aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane content
More, therefore there is preferably softening and increasing and rub effect.
Optionally, in step 2) in, in terms of volume parts, in described paper softener also
Including water 3-54 part.
For the most narrower little paper roll, its softening agent that need not the biggest concentration can realize
Increase soft increasing and slide effect, therefore to cost-effective, by its dilute.
Optionally, in step 2) in, in described silicon crude oil complex, dimethyl siloxane
Mixed methylcyclosiloxane and the volume ratio of N-β-(aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane
It is 1: 1;And described standing time is 2 hours.
When dimethyl siloxane mixed methylcyclosiloxane and N-β-(aminoethyl)-γ-aminopropyltriethoxy two
When the volume ratio of methoxy silane is 1: 1, more meet the increasing of the less paper roll of some width
Soft, and after soaking, it is not necessary to stand the too long of time (about 2 hours),
Realize the effect being impregnated with completely, further increasing pin and lead to the braid efficiency of rope.
Optionally, in step 2) in, the time of described immersion is the 1-60 second.
Owing to paper softener is organic materials, it has certain viscosity;In the mistake soaked
Cheng Zhong, will treat that vexed paper roll should not immerse the time oversize, to prevent paper softener infiltration capacity mistake
Big thus can not be absorbed by paper roll completely.Therefore, the time of immersion is preferably the 1-60 second.
Optionally, in step 1) in, the operation of described separation uses separation machine to carry out.
By separation machine, quickly and efficiently parent roll official form for filing a lawsuit volume can be cut into and multiple have
The little paper roll of given dimensional, facilitates the operation of follow-up vexed paper to carry out in order.
Optionally, in step 1) in, described in treat that the width of vexed paper roll is 2-25 millimeter.
Treat that the required specification that the width of vexed paper roll leads to rope according to pin selects, it is however generally that,
Treat that vexed paper roll is set between 2-25 millimeter, if width is too big, then can affect bating effect,
Make to soften insufficient, it is impossible to effectively realize strengthening the effect of vexed rear paper roll pulling force, if width
The least, during braiding, paper slip is weak to draw, and is easily pulled off.
Optionally, in step 1) in, described in treat that the width of vexed paper roll is 2-10 millimeter.
The logical rope of the pin that described weaving method is weaved into.
Compared with prior art, the invention have the benefit that
(1), the little paper roll (treating vexed paper roll) obtained after separation is dipped in or soft with paper
Soft dose of sprinkling, and it is interior to realize vexed paper effect to be subsequently placed at confined space.After vexed paper
The vexed rear paper roll obtained, its pliability and resistance to draw performance to be substantially improved, and become soft
Smooth, it is easy to change shape so that it is can be directly used for, in the braiding that pin leads to rope, eliminating
Coil paper yarn (paper slip is rolled into cord) commonly used in the prior art operates, thus realizes saving
The effects such as the convenience of time, reduction energy consumption and raising operation, improve pin and lead to the volume of rope
Knit efficiency.
(2) operation and coil paper yarn of the prior art and the operation of the immersion before it, are soaked
Compare, have easy to operation, and time saving and energy saving effect.
(3), paper softener formed by specific material combination, organosilicon can be effectively improved
(molecule) degree of orientation on fiber, adds the affinity to fiber, gives paper fiber
Super softness, smooth, pendency, antistatic, the washable effect such as wrinkle resistant.
Accompanying drawing explanation
In order to be illustrated more clearly that the embodiment of the present invention or technical scheme of the prior art, with
Lower the accompanying drawing used required in embodiment or description of the prior art will be briefly described.
Fig. 1 leads to the flow chart of the weaving method of rope for the pin that the present invention provides.
Detailed description of the invention
Below in conjunction with embodiment, embodiment of the present invention are described in detail, but this
Skilled person is it will be appreciated that the following example is merely to illustrate the present invention, and should not regard
For limiting the scope of the present invention.Unreceipted actual conditions person in embodiment, according to normal condition
Or the condition of manufacturer's suggestion is carried out.Agents useful for same or instrument unreceipted production firm person, all
For the conventional products that can be obtained by commercially available purchase.
Refer to Fig. 1, the pin that the present invention provides leads to the weaving method of rope, comprises the following steps:
Step 101: tubular paper roll is carried out separation, obtains treating vexed paper roll;
Preferably, in this step, in order to improve the efficiency of separation operation, separation machine is used
Carry out separation, and the specification of tubular paper roll not particularly restricted, after separation, obtain
Treat that the width general control of vexed paper roll is between 2-25 millimeter.And for its basic weight also without specific
Limit.
Step 102: treat that vexed paper roll is dipped in paper softener by described, and make paper soft
Agent treated vexed paper roll described in not having, further take out through immersion after treat vexed paper roll, be placed in airtight
Place in space so that paper softener permeates, and obtains vexed rear paper roll;
Wherein, in described paper softener, in terms of volume parts, including by dimethyl-silicon
Oxygen alkane mixed methylcyclosiloxane, N-β-(aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane mixing
Become silicon crude oil complex 2-4 part and fatty alcohol-polyoxyethylene ether 1-2 part;
It is furthermore preferred that in described silicon crude oil complex, dimethyl siloxane mixed methylcyclosiloxane and N-
The volume ratio of β-(aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane is 1: 1-4;Have
The silicon crude oil complex of this proportioning, each component of softening agent is more easy to realize Blending Efficiency of Blending, and
Owing to N-β-(aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane content is more, therefore
There is preferably softening and increasing and rub effect.
For some large-sized paper rolls, softening agent can be with water mixture, as in said ratio
On the basis of, water 3-54 part can be added.
Additionally, it is preferred that, in described silicon crude oil complex, dimethyl siloxane mixed methylcyclosiloxane
It is 1: 1 with the volume ratio of N-β-(aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane;
And described standing time is 2 hours.The softening agent with this proportioning more meets some width
Less paper roll increases soft, and after soaking, it is not necessary to stand the too long of time (2
Hour) effect that is impregnated with completely can be realized, improve pin and lead to the braid efficiency of rope.
Additionally, due to paper softener is organic materials, it has certain viscosity, adheres to
Power is stronger;Therefore, during soaking, treat that vexed paper roll should not immerse the long time, with
Prevent paper softener infiltration capacity excessive thus can not be absorbed by paper roll completely.The time soaked
It is preferably the 1-60 second;And less for width, and the more loose paper roll of ratio, directly use paper
Open softening agent to spray.
Step 103: woven by described vexed rear paper roll, obtains the logical rope of pin.
The pin of the method employing routine of braiding leads to rope method to be carried out, due to conventional braiding process
All use cord, and in this programme, slice paper weaves, can so adjusting knitting needle accordingly
Realize preferably weave effect.
It follows that combine above content, the weaving method that the pin of the present invention leads to rope is enumerated
Embodiment in detail below.
Embodiment 1
S11: utilize separation machine to carry out separation tubular paper roll, obtaining width is 6 millimeters
Treat vexed paper roll;
S12: will treat that vexed paper roll is dipped in paper softener, and make paper softener not have institute
State and treat vexed paper roll 2 seconds, further take out through immersion after treat vexed paper roll, be placed in confined space
Interior placement 2 hours;Obtain vexed rear paper roll;
Wherein, in described paper softener, in terms of volume parts, including by dimethyl-silicon
Oxygen alkane mixed methylcyclosiloxane, N-β-(aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane mixing
Become silicon crude oil complex 2 parts and fatty alcohol-polyoxyethylene ether 1 part;Described silicon crude oil complex
In, dimethyl siloxane mixed methylcyclosiloxane and N-β-(aminoethyl)-γ-aminopropyltriethoxy diformazan
The volume ratio of TMOS is 1: 1.
S13: woven by described vexed rear paper roll, obtains the logical rope of pin.
Embodiment 2
S21: utilize separation machine to carry out separation tubular paper roll, obtaining width is 8 millimeters
Treat vexed paper roll;
S22: will treat that vexed paper roll is dipped in paper softener, and make paper softener not have institute
State and treat vexed paper roll 3 seconds, further take out through immersion after treat vexed paper roll, be placed in confined space
Interior placement 3 hours;Obtain vexed rear paper roll;
Wherein, in described paper softener, in terms of volume parts, including by dimethyl-silicon
Oxygen alkane mixed methylcyclosiloxane, N-β-(aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane mixing
Become silicon crude oil complex 2 parts, fatty alcohol-polyoxyethylene ether 1 part and 15 parts of water;Described silicon is former
In oil complex, dimethyl siloxane mixed methylcyclosiloxane and N-β-(aminoethyl)-γ-aminopropyl
The volume ratio of methyl dimethoxysilane is 1: 2.
S23: woven by described vexed rear paper roll, obtains the logical rope of pin.
Embodiment 3
S31: utilize separation machine to carry out separation tubular paper roll, obtaining width is 4 millimeters
Treat vexed paper roll;
S32: will treat that vexed paper roll is dipped in paper softener, and make paper softener not have institute
State and treat vexed paper roll 2 seconds, further take out through immersion after treat vexed paper roll, be placed in confined space
Interior placement 2 hours;Obtain vexed rear paper roll;
Wherein, in described paper softener, in terms of volume parts, including by dimethyl-silicon
Oxygen alkane mixed methylcyclosiloxane, N-β-(aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane mixing
Become silicon crude oil complex 2 parts, fatty alcohol-polyoxyethylene ether 1 part and 7 parts of water;Described silicon is former
In oil complex, dimethyl siloxane mixed methylcyclosiloxane and N-β-(aminoethyl)-γ-aminopropyl
The volume ratio of methyl dimethoxysilane is 1: 1.
S33: woven by described vexed rear paper roll, obtains the logical rope of pin.
Embodiment 4
S41: utilize separation machine to carry out separation tubular paper roll, obtaining width is 12 millimeters
Treat vexed paper roll;
S42: will treat that vexed paper roll is dipped in paper softener, and make paper softener not have institute
State and treat vexed paper roll 5 seconds, further take out through immersion after treat vexed paper roll, be placed in confined space
Interior placement 6 hours;Obtain vexed rear paper roll;
Wherein, in described paper softener, in terms of volume parts, including by dimethyl-silicon
Oxygen alkane mixed methylcyclosiloxane, N-β-(aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane mixing
Become silicon crude oil complex 2 parts, fatty alcohol-polyoxyethylene ether 1 part and 27 parts of water;Described silicon is former
In oil complex, dimethyl siloxane mixed methylcyclosiloxane and N-β-(aminoethyl)-γ-aminopropyl
The volume ratio of methyl dimethoxysilane is 1: 3.
S43: woven by described vexed rear paper roll, obtains the logical rope of pin.
The weaving method that the pin that various embodiments of the present invention provide leads to rope is equal, different in width vexed after
The tensile strength of paper roll all significantly improves, and becomes a softer and smoother touch, it is easy to change shape,
Can be directly used in the weaving application that pin leads to rope.And, in the operation of vexed paper, time used
Between the shortest, fewer than conventional coil paper yarn operation, and operation facility is easily-controllable, the most effectively carries
Principle of readjustment, restructuring, consolidation and improvement leads to the braid efficiency of rope.
Although illustrate and describing the present invention with specific embodiment, but it will be appreciated that
May be made that without departing from the spirit and scope of the present invention many other change and
Amendment.It is, therefore, intended that include in the following claims belonging in the scope of the invention
All such changes and modifications.
Claims (10)
1. pin leads to the weaving method of rope, it is characterised in that include to obtain after separation
Paper roll soaks through paper softener or sprays, after standing in airtight space directly
Weave, obtain the logical rope of pin.
Pin the most according to claim 1 leads to the weaving method of rope, it is characterised in that tool
Body comprises the following steps:
1), tubular paper roll is carried out separation, obtain treating vexed paper roll;
2), treat that vexed paper roll is dipped in paper softener by described, and make paper softener not have
Described treat vexed paper roll, further take out and treat vexed paper roll after soaking, be placed in confined space
Place so that paper softener permeates, and obtains vexed rear paper roll;
Wherein, in described paper softener, in terms of volume parts, including by dimethyl-silicon
Oxygen alkane mixed methylcyclosiloxane, N-β-(aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane mixing
Become silicon crude oil complex 2-4 part and fatty alcohol-polyoxyethylene ether 1-2 part;
3), described vexed rear paper roll is woven, obtain the logical rope of pin.
Weaving method the most according to claim 2, it is characterised in that in step 2)
In, in described silicon crude oil complex, dimethyl siloxane mixed methylcyclosiloxane and N-β-(ammonia second
Base) volume ratio of-γ-aminopropyltriethoxy dimethoxysilane is 1: (1-4).
Weaving method the most according to claim 3, it is characterised in that in step 2)
In, in terms of volume parts, described paper softener also includes water 3-54 part.
Weaving method the most according to claim 3, it is characterised in that in step 2)
In,
In described silicon crude oil complex, dimethyl siloxane mixed methylcyclosiloxane and N-β-(ammonia second
Base) volume ratio of-γ-aminopropyltriethoxy dimethoxysilane is 1: 1;And described standing time
It it is 2 hours.
Weaving method the most according to claim 4, it is characterised in that in step 2)
In, the time of described immersion is the 1-60 second.
7. according to the weaving method described in any one of claim 1-6, it is characterised in that
Step 1) in, the operation of described separation uses separation machine to carry out.
Weaving method the most according to claim 7, it is characterised in that in step 1)
In, described in treat that the width of vexed paper roll is 2-25 millimeter.
Weaving method the most according to claim 8, it is characterised in that in step 1)
In, described in treat that the width of vexed paper roll is 2-10 millimeter.
10. the logical rope of the pin that the weaving method described in any one of claim 1-9 is weaved into.