CN106283003A - Road indicator - Google Patents
Road indicator Download PDFInfo
- Publication number
- CN106283003A CN106283003A CN201610749563.XA CN201610749563A CN106283003A CN 106283003 A CN106283003 A CN 106283003A CN 201610749563 A CN201610749563 A CN 201610749563A CN 106283003 A CN106283003 A CN 106283003A
- Authority
- CN
- China
- Prior art keywords
- weight
- weight portion
- parts
- main body
- metallic plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of road indicator, its metallic plate main body is through Passivation Treatment, Passivation Treatment comprises the steps: 1) 1~2 weight portion tannic acids, 1.5 weight portion ammonium titanium fluorides, 0.7 parts by weight of phosphoric acid ferrimanganic, 1.1 parts by weight of silica, 4.6 parts by weight of isopropyl alcohol are put in 30 parts by weight of deionized water successively, stir;2) 3.8 parts by weight of polypropylene acid, 0.7 weight portion dodecyl trimethyl ammonium sulfate, 1.1 weight portion 2 aminoethyl 17 alkenyl imidazolines, 1.5 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 4.5 weight portion dihydroxylic alcohols are put into the most successively, continue stirring, to being sufficiently mixed uniformly, prepare inactivating treatment liquid;3) metallic plate main body is inserted inactivating treatment liquid is passivated process, treatment temperature 43 DEG C, process 37 seconds time, after taking-up with pure water clean dry again.Road indicator of the present invention, its metallic plate main body is through Passivation Treatment, and performance is good, and surface smoothness is good.
Description
Technical field
The present invention relates to road indicator.
Background technology
Existing road direction board, including metallic plate main body, but antirust, the abrasion-resistant of metallic plate main body, corrosion-resistant, heat-resisting,
Cold-resistant, weather resistance has much room for improvement, and surface smoothness is the most not ideal enough.
Summary of the invention
It is an object of the invention to provide a kind of road indicator, its metallic plate main body is through Passivation Treatment, at metal watch
Face forms uniform passivation protection film, has antirust, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, the weather resistance of excellence, and surface
Fineness is good.
For achieving the above object, the technical scheme is that a kind of road indicator of design, it includes metallic plate main body,
This metallic plate main body is through Passivation Treatment, and described Passivation Treatment comprises the steps:
1) by 1~2 weight portion tannic acids, 1.5 weight portion ammonium titanium fluorides, 0.7 parts by weight of phosphoric acid ferrimanganic, 1.1 weight portions two
Silicon oxide, 4.6 parts by weight of isopropyl alcohol put in 30 parts by weight of deionized water successively, stir;
2) 3.8 parts by weight of polypropylene acid, 0.7 weight portion dodecyl trimethyl ammonium sulfate, 1.1 weight portions are put into the most successively
2-aminoethyl 17 alkenyl imidazoline, 1.5 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 4.5 weight portion dihydroxylic alcohols, continue stirring, extremely
It is sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic plate main body is inserted inactivating treatment liquid is passivated process, treatment temperature 43 DEG C, process 37 seconds time,
Clean with pure water after taking-up and dry again.
Preferably, road indicator, it includes metallic plate main body, this metallic plate main body through Passivation Treatment, described passivation
Process comprises the steps:
1) by 1 weight portion tannic acid, 1.5 weight portion ammonium titanium fluorides, 0.7 parts by weight of phosphoric acid ferrimanganic, 1.1 weight portion titanium dioxide
Silicon, 4.6 parts by weight of isopropyl alcohol put in 30 parts by weight of deionized water successively, stir;
2) 3.8 parts by weight of polypropylene acid, 0.7 weight portion dodecyl trimethyl ammonium sulfate, 1.1 weight portions are put into the most successively
2-aminoethyl 17 alkenyl imidazoline, 1.5 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 4.5 weight portion dihydroxylic alcohols, continue stirring, extremely
It is sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic plate main body is inserted inactivating treatment liquid is passivated process, treatment temperature 43 DEG C, process 37 seconds time,
Clean with pure water after taking-up and dry again.
Preferably, road indicator, it includes metallic plate main body, this metallic plate main body through Passivation Treatment, described passivation
Process comprises the steps:
1) by 2 weight portion tannic acids, 1.5 weight portion ammonium titanium fluorides, 0.7 parts by weight of phosphoric acid ferrimanganic, 1.1 weight portion titanium dioxide
Silicon, 4.6 parts by weight of isopropyl alcohol put in 30 parts by weight of deionized water successively, stir;
2) 3.8 parts by weight of polypropylene acid, 0.7 weight portion dodecyl trimethyl ammonium sulfate, 1.1 weight portions are put into the most successively
2-aminoethyl 17 alkenyl imidazoline, 1.5 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 4.5 weight portion dihydroxylic alcohols, continue stirring, extremely
It is sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic plate main body is inserted inactivating treatment liquid is passivated process, treatment temperature 43 DEG C, process 37 seconds time,
Clean with pure water after taking-up and dry again.
Preferably, road indicator, it includes metallic plate main body, this metallic plate main body through Passivation Treatment, described passivation
Process comprises the steps:
1) by 1.2 weight portion tannic acids, 1.5 weight portion ammonium titanium fluorides, 0.7 parts by weight of phosphoric acid ferrimanganic, 1.1 weight portion dioxies
SiClx, 4.6 parts by weight of isopropyl alcohol put in 30 parts by weight of deionized water successively, stir;
2) 3.8 parts by weight of polypropylene acid, 0.7 weight portion dodecyl trimethyl ammonium sulfate, 1.1 weight portions are put into the most successively
2-aminoethyl 17 alkenyl imidazoline, 1.5 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 4.5 weight portion dihydroxylic alcohols, continue stirring, extremely
It is sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic plate main body is inserted inactivating treatment liquid is passivated process, treatment temperature 43 DEG C, process 37 seconds time,
Clean with pure water after taking-up and dry again.
Advantages of the present invention and having the beneficial effects that: providing a kind of road indicator, its metallic plate main body is at transpassivation
Reason, forms uniform passivation protection film in metal surface, has antirust, the abrasion-resistant of excellence, corrosion-resistant, heat-resisting, cold-resistant, weather-proof
Performance, and surface smoothness is good.
Performance and the purposes of " inactivating treatment liquid " are determined by its component and proportioning, and in " inactivating treatment liquid " not
Can influence each other with component, component and proportioning thereof can determine the final performance of " inactivating treatment liquid ", such as fruit component and proportioning thereof not
Mutually coordinated, that single component is brought beneficial effect, even can be eliminated by other components abatement, the when of serious, and different groups
Split-phase is conflicted mutually, does not has whole synthesis effect, produces negative interaction and substandard products.The present invention is by a large amount of creative works, repeatedly
Checking, obtains optimal component and the proportioning of " inactivating treatment liquid " so that multiple components combine, mutually coordinated and produce
Forward comprehensive effect.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.Following example are only used for more
Add and clearly demonstrate technical scheme, and can not limit the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Road indicator, it includes metallic plate main body, and this metallic plate main body is through Passivation Treatment, and described Passivation Treatment includes
Following steps:
1) by 1~2 weight portion tannic acids, 1.5 weight portion ammonium titanium fluorides, 0.7 parts by weight of phosphoric acid ferrimanganic, 1.1 weight portions two
Silicon oxide, 4.6 parts by weight of isopropyl alcohol put in 30 parts by weight of deionized water successively, stir;
2) 3.8 parts by weight of polypropylene acid, 0.7 weight portion dodecyl trimethyl ammonium sulfate, 1.1 weight portions are put into the most successively
2-aminoethyl 17 alkenyl imidazoline, 1.5 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 4.5 weight portion dihydroxylic alcohols, continue stirring, extremely
It is sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic plate main body is inserted inactivating treatment liquid is passivated process, treatment temperature 43 DEG C, process 37 seconds time,
Clean with pure water after taking-up and dry again.
Embodiment 2
Road indicator, it includes metallic plate main body, and this metallic plate main body is through Passivation Treatment, and described Passivation Treatment includes
Following steps:
1) by 1 weight portion tannic acid, 1.5 weight portion ammonium titanium fluorides, 0.7 parts by weight of phosphoric acid ferrimanganic, 1.1 weight portion titanium dioxide
Silicon, 4.6 parts by weight of isopropyl alcohol put in 30 parts by weight of deionized water successively, stir;
2) 3.8 parts by weight of polypropylene acid, 0.7 weight portion dodecyl trimethyl ammonium sulfate, 1.1 weight portions are put into the most successively
2-aminoethyl 17 alkenyl imidazoline, 1.5 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 4.5 weight portion dihydroxylic alcohols, continue stirring, extremely
It is sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic plate main body is inserted inactivating treatment liquid is passivated process, treatment temperature 43 DEG C, process 37 seconds time,
Clean with pure water after taking-up and dry again.
Embodiment 3
Road indicator, it includes metallic plate main body, and this metallic plate main body is through Passivation Treatment, and described Passivation Treatment includes
Following steps:
1) by 2 weight portion tannic acids, 1.5 weight portion ammonium titanium fluorides, 0.7 parts by weight of phosphoric acid ferrimanganic, 1.1 weight portion titanium dioxide
Silicon, 4.6 parts by weight of isopropyl alcohol put in 30 parts by weight of deionized water successively, stir;
2) 3.8 parts by weight of polypropylene acid, 0.7 weight portion dodecyl trimethyl ammonium sulfate, 1.1 weight portions are put into the most successively
2-aminoethyl 17 alkenyl imidazoline, 1.5 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 4.5 weight portion dihydroxylic alcohols, continue stirring, extremely
It is sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic plate main body is inserted inactivating treatment liquid is passivated process, treatment temperature 43 DEG C, process 37 seconds time,
Clean with pure water after taking-up and dry again.
Embodiment 4
Road indicator, it includes metallic plate main body, and this metallic plate main body is through Passivation Treatment, and described Passivation Treatment includes
Following steps:
1) by 1.2 weight portion tannic acids, 1.5 weight portion ammonium titanium fluorides, 0.7 parts by weight of phosphoric acid ferrimanganic, 1.1 weight portion dioxies
SiClx, 4.6 parts by weight of isopropyl alcohol put in 30 parts by weight of deionized water successively, stir;
2) 3.8 parts by weight of polypropylene acid, 0.7 weight portion dodecyl trimethyl ammonium sulfate, 1.1 weight portions are put into the most successively
2-aminoethyl 17 alkenyl imidazoline, 1.5 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 4.5 weight portion dihydroxylic alcohols, continue stirring, extremely
It is sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic plate main body is inserted inactivating treatment liquid is passivated process, treatment temperature 43 DEG C, process 37 seconds time,
Clean with pure water after taking-up and dry again.
In the various embodiments described above, the metallic plate main body of road indicator, through Passivation Treatment, is formed all in metal surface
Even passivation protection film, has antirust, abrasion-resistant, corrosion-resistant, heat-resisting, cold-resistant, the weather resistance of excellence, and surface smoothness
Good.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For Yuan, on the premise of without departing from the technology of the present invention principle, it is also possible to make some improvements and modifications, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. road indicator, it is characterised in that it includes metallic plate main body, this metallic plate main body is through Passivation Treatment, described blunt
Change processes and comprises the steps:
1) by 1~2 weight portion tannic acids, 1.5 weight portion ammonium titanium fluorides, 0.7 parts by weight of phosphoric acid ferrimanganic, 1.1 weight portion titanium dioxide
Silicon, 4.6 parts by weight of isopropyl alcohol put in 30 parts by weight of deionized water successively, stir;
2) 3.8 parts by weight of polypropylene acid, 0.7 weight portion dodecyl trimethyl ammonium sulfate, 1.1 weight portion 2-ammonia are put into the most successively
Ethyl 17 alkenyl imidazoline, 1.5 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 4.5 weight portion dihydroxylic alcohols, continue stirring, to fully
Mix homogeneously, prepares inactivating treatment liquid;
3) metallic plate main body is inserted inactivating treatment liquid is passivated process, treatment temperature 43 DEG C, process 37 seconds time, take out
Clean with pure water afterwards and dry again.
Road indicator the most according to claim 1, it is characterised in that it includes metallic plate main body, this metallic plate main body
Through Passivation Treatment, described Passivation Treatment comprises the steps:
1) by 1 weight portion tannic acid, 1.5 weight portion ammonium titanium fluorides, 0.7 parts by weight of phosphoric acid ferrimanganic, 1.1 parts by weight of silica,
4.6 parts by weight of isopropyl alcohol put in 30 parts by weight of deionized water successively, stir;
2) 3.8 parts by weight of polypropylene acid, 0.7 weight portion dodecyl trimethyl ammonium sulfate, 1.1 weight portion 2-ammonia are put into the most successively
Ethyl 17 alkenyl imidazoline, 1.5 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 4.5 weight portion dihydroxylic alcohols, continue stirring, to fully
Mix homogeneously, prepares inactivating treatment liquid;
3) metallic plate main body is inserted inactivating treatment liquid is passivated process, treatment temperature 43 DEG C, process 37 seconds time, take out
Clean with pure water afterwards and dry again.
Road indicator the most according to claim 1, it is characterised in that it includes metallic plate main body, this metallic plate main body
Through Passivation Treatment, described Passivation Treatment comprises the steps:
1) by 2 weight portion tannic acids, 1.5 weight portion ammonium titanium fluorides, 0.7 parts by weight of phosphoric acid ferrimanganic, 1.1 parts by weight of silica,
4.6 parts by weight of isopropyl alcohol put in 30 parts by weight of deionized water successively, stir;
2) 3.8 parts by weight of polypropylene acid, 0.7 weight portion dodecyl trimethyl ammonium sulfate, 1.1 weight portion 2-ammonia are put into the most successively
Ethyl 17 alkenyl imidazoline, 1.5 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 4.5 weight portion dihydroxylic alcohols, continue stirring, to fully
Mix homogeneously, prepares inactivating treatment liquid;
3) metallic plate main body is inserted inactivating treatment liquid is passivated process, treatment temperature 43 DEG C, process 37 seconds time, take out
Clean with pure water afterwards and dry again.
Road indicator the most according to claim 1, it is characterised in that it includes metallic plate main body, this metallic plate main body
Through Passivation Treatment, described Passivation Treatment comprises the steps:
1) by 1.2 weight portion tannic acids, 1.5 weight portion ammonium titanium fluorides, 0.7 parts by weight of phosphoric acid ferrimanganic, 1.1 weight portion titanium dioxide
Silicon, 4.6 parts by weight of isopropyl alcohol put in 30 parts by weight of deionized water successively, stir;
2) 3.8 parts by weight of polypropylene acid, 0.7 weight portion dodecyl trimethyl ammonium sulfate, 1.1 weight portion 2-ammonia are put into the most successively
Ethyl 17 alkenyl imidazoline, 1.5 weight portion oleoyl methylamine ethyl sulfonic acid sodium, 4.5 weight portion dihydroxylic alcohols, continue stirring, to fully
Mix homogeneously, prepares inactivating treatment liquid;
3) metallic plate main body is inserted inactivating treatment liquid is passivated process, treatment temperature 43 DEG C, process 37 seconds time, take out
Clean with pure water afterwards and dry again.