CN106281096A - A kind of environment friendly heat resistant rupture pressure disc - Google Patents
A kind of environment friendly heat resistant rupture pressure disc Download PDFInfo
- Publication number
- CN106281096A CN106281096A CN201610841919.2A CN201610841919A CN106281096A CN 106281096 A CN106281096 A CN 106281096A CN 201610841919 A CN201610841919 A CN 201610841919A CN 106281096 A CN106281096 A CN 106281096A
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- pressure disc
- rupture pressure
- heat resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of environment friendly heat resistant rupture pressure disc, it includes anti-scratching wearproof layer, safety anti-explosive layer, UV-absorbing layer, pet vector layer, pressure-sensitive adhesive layer and release film layer successively；The raw material of described anti-scratching wearproof layer, in parts by weight, including following components: emulsion acrylic resin 30 50 parts, isobutyl etherificate amino resin emulsion 25 36 parts, the wood fiber 26 parts, succinic anhydrides 0.5 1.3 parts, nanocrystalline 13 parts of Rhizoma amorphophalli powder, vermiculite power 24 parts, dispersant 0.1 0.5 parts, deionized water 10 15 parts.The raw material of described safety anti-explosive layer, in parts by weight, including following components: fluorine-carbon modified polyacrylic resin emulsion 20 40 parts, polyflon 5 11 parts, acryl-modified silicone resin resin 6 10 parts, Nano titanium nitride 23 parts, anhydrous sorbitol monocarboxylate 38 parts, hollow silica nanoparticle 14 parts, cross-linking agent 0.8 1 parts, 35 parts of firming agent, deionized water 8 12 parts.This rupture pressure disc anti-scratching wearproof is good, and anti-ultraviolet property is excellent, and explosion-proof performance is good, and each layer adhesion is strong, and safety transparent is high temperature resistant.
Description
Technical field:
The present invention relates to film applications, be specifically related to a kind of environment friendly heat resistant rupture pressure disc.
Background technology:
Along with the quickening of Urbanization in China, increasing skyscraper is rised sheer from level ground.Modern building design in order to
Strengthen the daylighting effect of building, view effect and elevation of building aesthetic effect, more use glass structure.Open type flooring
Design, glass ceiling and large area are landed the application of glass and are gradually come into fashion.But, these designs are bringing U.S. simultaneously,
Also many worries are brought to us.Such as: the energy waste problem that the use of large-area glass brings；Fragility material during glass
Material, can be easily by stress broken generation fragment.Although the broken formation of safety glass is without the granule of wedge angle, but under external force,
Easily splash and cause personal injury；On the other hand, health problem that too much ultraviolet irradiation brings etc..
Along with highlighting of Global Greenhouse Effect and energy problem, people, while paying close attention to life level of comfort, also begin to
Focus more on the environmental protection in room and energy-conservation.The appearance of safety anti-explosive film, provides a new approach for dissolving of these problems.
Safety anti-explosive film is flexible material.Pad pasting can not increase the intensity of glass, it is also not possible to the extraneous stress of opposing.It its effect be
After glass itself is broken, prevents fragment from splashing by bonding glass fragment and hurt sb.'s feelings.Therefore safety anti-explosive film needs excellence
Shock resistance and resistance to elevated temperatures.
Summary of the invention:
It is an object of the invention to provide a kind of environment friendly heat resistant rupture pressure disc, its explosion-proof performance is good, and resistance to elevated temperatures is excellent, anti-
Impact property is good.
For achieving the above object, the present invention is by the following technical solutions:
A kind of environment friendly heat resistant rupture pressure disc, this rupture pressure disc includes anti-scratching wearproof layer, safety anti-explosive layer, ultra-violet absorption successively
Layer, pet vector layer, pressure-sensitive adhesive layer and release film layer；
Wherein, the raw material of described anti-scratching wearproof layer, in parts by weight, including following components:
Emulsion acrylic resin 30-50 part,
Isobutyl etherificate amino resin emulsion 25-36 part,
Wood fiber 2-6 part, succinic anhydrides 0.5-1.3 part,
SKGM nanocrystalline 1-3 part, vermiculite power 2-4 part,
Dispersant 0.1-0.5 part, deionized water 10-15 part；
The raw material of described safety anti-explosive layer, in parts by weight, including following components:
Fluorine-carbon modified polyacrylic resin emulsion 20-40 part,
Polyflon 5-11 part,
Acryl-modified silicone resin resin 6-10 part,
Nano titanium nitride 2-3 part,
Anhydrous sorbitol monocarboxylate's 3-8 part,
Hollow silica nanoparticle 1-4 part,
Cross-linking agent 0.8-1 part, firming agent 3-5 part, deionized water 8-12 part.
Preferred as technique scheme, the raw material of described anti-scratching wearproof layer, in parts by weight, including following components:
Emulsion acrylic resin 50 parts,
Isobutyl etherificate amino resin emulsion 25 parts,
The wood fiber 5.5 parts, succinic anhydrides 1.1 parts,
Nanocrystalline 3 parts of SKGM, vermiculite power 2 parts,
Dispersant 0.35 part, deionized water 12 parts；
The raw material of described safety anti-explosive layer, in parts by weight, including following components:
Fluorine-carbon modified polyacrylic resin emulsion 35 parts,
Polyflon 10 parts,
Acryl-modified silicone resin resin 8 parts,
Nano titanium nitride 2.3 parts,
Anhydrous sorbitol monocarboxylate 7 parts,
Hollow silica nanoparticle 2 parts,
Cross-linking agent 1 part, 4 parts of firming agent, deionized water 10 parts.
Preferred as technique scheme, the preparation method of UV-absorbing layer, comprise the following steps:
Titanium tetrachloride is added drop-wise in the mixed liquor of dehydrated alcohol and glacial acetic acid, ultrasonic 1-2h under 800-1000W power, super
It is heated to reflux 4-7h at mixed liquor after sound 60-80 DEG C, obtains Nano sol, PET film is immersed in Nano sol, dipping
5-10h, then takes out 40-45 DEG C of drying, is finally putting in electromagnetic oven, be warming up to 180-260 DEG C with the speed of 10-20 DEG C/min
And it is incubated 2-3h, and then stopping heat supply, cooling is taken out, is obtained scribbling the thin film of UV-absorbing layer.
Preferred as technique scheme, the raw material of described pressure-sensitive adhesive layer, in parts by weight, including following components:
Silicones 30-40 part, silicone rubber 10-20 part,
Silane crosslinker 1-3 part, diluent 15-20 part,
Konjac glucomannan 5-10 part, catalyst 0.5-1.5 part.
Preferred as technique scheme, described dispersant is the mixture of potassium citrate and linoleic acid sodium, the two matter
Amount ratio is 1:1.
Preferred as technique scheme, described cross-linking agent is titanate esters cross-linking agent, aluminate coupling agent, silane coupled
One or more mixing in agent.
Preferred as technique scheme, described catalyst is the mixing of organotin catalysts and metal composite carboxylate
Thing, the two mass ratio is 1:(0.05-0.08).
The method have the advantages that
It is nanocrystalline that the present invention adds appropriate SKGM in the anti-scratching wearproof layer of rupture pressure disc, and uses succinic anhydrides to enter
Row modification, the anti-scratching wearproof coating film excellent performance prepared, shock resistance is good, and tearing toughness is big, and rationally adds dispersion
Agent, vermiculite power so that prepared anti-scratching wearproof layer Stability of Slurry is good, resistance to elevated temperatures is excellent；
The present invention uses one-step method to prepare UV-absorbing layer, and prepared UV-absorbing layer can be coated in PET uniformly
Substrate surface, anti-ultraviolet property is excellent；
The safety anti-explosive film resistance to elevated temperatures that the present invention provides is good, and excellent shock resistance has good anti-scratching wearproof
Performance, transparency is high, nontoxic, safety and environmental protection.
Detailed description of the invention:
In order to be better understood from the present invention, below by embodiment, the present invention is further described, and embodiment is served only for solving
Release the present invention, the present invention will not be constituted any restriction.
Embodiment 1
A kind of environment friendly heat resistant rupture pressure disc, this rupture pressure disc includes anti-scratching wearproof layer, safety anti-explosive layer, ultra-violet absorption successively
Layer, pet vector layer, pressure-sensitive adhesive layer and release film layer；
Wherein, the raw material of described anti-scratching wearproof layer, in parts by weight, including following components:
Emulsion acrylic resin 30 parts, isobutyl etherificate amino resin emulsion 25 parts,
The wood fiber 2 parts, succinic anhydrides 0.5 part, nanocrystalline 1 part of SKGM,
Vermiculite power 2 parts, dispersant 0.1 part, deionized water 10 parts；
Wherein, dispersant is the mixture of potassium citrate and linoleic acid sodium, and the two mass ratio is 1:1；
The raw material of described safety anti-explosive layer, in parts by weight, including following components:
Fluorine-carbon modified polyacrylic resin emulsion 20 parts, polyflon 5 parts,
Acryl-modified silicone resin resin 6 parts, Nano titanium nitride 2 parts,
Anhydrous sorbitol monocarboxylate 3 parts, hollow silica nanoparticle 1 part,
Cross-linking agent 0.8 part, 3 parts of firming agent, deionized water 8 parts；
Wherein, described cross-linking agent is titanate esters cross-linking agent；
The raw material of described pressure-sensitive adhesive layer, in parts by weight, including following components:
Silicones 30 parts, 10 parts of silicone rubber, silane crosslinker 1 part,
Diluent 15 parts, Konjac glucomannan 5 parts, catalyst 0.5 part；
Wherein, described catalyst is the mixture of organotin catalysts and metal composite carboxylate, and the two mass ratio is 1:
0.05。
The preparation method of UV-absorbing layer is: be added drop-wise to by titanium tetrachloride in the mixed liquor of dehydrated alcohol and glacial acetic acid,
Ultrasonic 1h under 800W power, ultrasonic after mixed liquor 60 DEG C at be heated to reflux 4h, obtain Nano sol, PET film be immersed in
In Nano sol, impregnate 5h, then take out 40-45 DEG C of drying, be finally putting in electromagnetic oven, be warming up to the speed of 10 DEG C/min
180 DEG C and be incubated 2h, then stopping heat supply, cooling is taken out, is obtained scribbling the thin film of UV-absorbing layer.
Embodiment 2
A kind of environment friendly heat resistant rupture pressure disc, this rupture pressure disc includes anti-scratching wearproof layer, safety anti-explosive layer, ultra-violet absorption successively
Layer, pet vector layer, pressure-sensitive adhesive layer and release film layer；
Wherein, the raw material of described anti-scratching wearproof layer, in parts by weight, including following components:
Emulsion acrylic resin 50 parts, isobutyl etherificate amino resin emulsion 36 parts,
The wood fiber 6 parts, succinic anhydrides 1.3 parts, nanocrystalline 3 parts of SKGM,
Vermiculite power 4 parts, dispersant 0.5 part, deionized water 15 parts；
Wherein, dispersant is the mixture of potassium citrate and linoleic acid sodium, and the two mass ratio is 1:1；
The raw material of described safety anti-explosive layer, in parts by weight, including following components:
Fluorine-carbon modified polyacrylic resin emulsion 40 parts, polyflon 11 parts,
Acryl-modified silicone resin resin 10 parts, Nano titanium nitride 3 parts,
Anhydrous sorbitol monocarboxylate 8 parts, hollow silica nanoparticle 4 parts,
Cross-linking agent 1 part, 5 parts of firming agent, deionized water 12 parts；
Wherein, described cross-linking agent is aluminate coupling agent；
The raw material of described pressure-sensitive adhesive layer, in parts by weight, including following components:
Silicones 40 parts, 20 parts of silicone rubber, silane crosslinker 3 parts,
Diluent 20 parts, Konjac glucomannan 10 parts, catalyst 1.5 parts；
Wherein, described catalyst is the mixture of organotin catalysts and metal composite carboxylate, and the two mass ratio is 1:
0.08。
The preparation method of UV-absorbing layer is: be added drop-wise to by titanium tetrachloride in the mixed liquor of dehydrated alcohol and glacial acetic acid,
Ultrasonic 2h under 1000W power, ultrasonic after mixed liquor 80 DEG C at be heated to reflux 7h, obtain Nano sol, PET film be immersed in
In Nano sol, impregnate 10h, then take out 40-45 DEG C of drying, be finally putting in electromagnetic oven, heat up with the speed of 20 DEG C/min
To 260 DEG C and be incubated 3h, then stopping heat supply, cooling is taken out, is obtained scribbling the thin film of UV-absorbing layer.
Embodiment 3
A kind of environment friendly heat resistant rupture pressure disc, this rupture pressure disc includes anti-scratching wearproof layer, safety anti-explosive layer, ultra-violet absorption successively
Layer, pet vector layer, pressure-sensitive adhesive layer and release film layer；
Wherein, the raw material of described anti-scratching wearproof layer, in parts by weight, including following components:
Emulsion acrylic resin 35 parts, isobutyl etherificate amino resin emulsion 28 parts,
The wood fiber 3 parts, succinic anhydrides 0.7 part, nanocrystalline 1.5 parts of SKGM,
Vermiculite power 2.5 parts, dispersant 0.2 part, deionized water 11 parts；
Wherein, dispersant is the mixture of potassium citrate and linoleic acid sodium, and the two mass ratio is 1:1；
The raw material of described safety anti-explosive layer, in parts by weight, including following components:
Fluorine-carbon modified polyacrylic resin emulsion 25 parts, polyflon 7 parts,
Acryl-modified silicone resin resin 7 parts, Nano titanium nitride 2.2 parts,
Anhydrous sorbitol monocarboxylate 4 parts, hollow silica nanoparticle 2 parts,
Cross-linking agent 0.85 part, 3.5 parts of firming agent, deionized water 9 parts；
Wherein, described cross-linking agent is silane coupler；
The raw material of described pressure-sensitive adhesive layer, in parts by weight, including following components:
Silicones 32 parts, 13 parts of silicone rubber, silane crosslinker 1.5 parts,
Diluent 16 parts, Konjac glucomannan 6 parts, catalyst 0.7 part；
Wherein, described catalyst is the mixture of organotin catalysts and metal composite carboxylate, and the two mass ratio is 1:
0.06。
The preparation method of UV-absorbing layer is: be added drop-wise to by titanium tetrachloride in the mixed liquor of dehydrated alcohol and glacial acetic acid,
Ultrasonic 1.2h under 850W power, ultrasonic after mixed liquor 65 DEG C at be heated to reflux 5h, obtain Nano sol, by PET film immerse
In Nano sol, impregnate 6h, then take out 40-45 DEG C of drying, be finally putting in electromagnetic oven, heat up with the speed of 12 DEG C/min
To 200 DEG C and be incubated 2.2h, then stopping heat supply, cooling is taken out, is obtained scribbling the thin film of UV-absorbing layer.
Embodiment 4
A kind of environment friendly heat resistant rupture pressure disc, this rupture pressure disc includes anti-scratching wearproof layer, safety anti-explosive layer, ultra-violet absorption successively
Layer, pet vector layer, pressure-sensitive adhesive layer and release film layer；
Wherein, the raw material of described anti-scratching wearproof layer, in parts by weight, including following components:
Emulsion acrylic resin 40 parts, isobutyl etherificate amino resin emulsion 31 parts,
The wood fiber 4 parts, succinic anhydrides 0.9 part, nanocrystalline 2 parts of SKGM,
Vermiculite power 3.5 parts, dispersant 0.3 part, deionized water 12 parts；
Wherein, dispersant is the mixture of potassium citrate and linoleic acid sodium, and the two mass ratio is 1:1；
The raw material of described safety anti-explosive layer, in parts by weight, including following components:
Fluorine-carbon modified polyacrylic resin emulsion 30 parts, polyflon 9 parts,
Acryl-modified silicone resin resin 8 parts, Nano titanium nitride 2.4 parts,
Anhydrous sorbitol monocarboxylate 5 parts, hollow silica nanoparticle 3 parts,
Cross-linking agent 0.9 part, 4 parts of firming agent, deionized water 10 parts；
Wherein, described cross-linking agent is the mixture of titanate esters cross-linking agent, aluminate coupling agent；
The raw material of described pressure-sensitive adhesive layer, in parts by weight, including following components:
Silicones 34 parts, 16 parts of silicone rubber, silane crosslinker 2 parts,
Diluent 17 parts, Konjac glucomannan 7 parts, catalyst 0.9 part；
Wherein, described catalyst is the mixture of organotin catalysts and metal composite carboxylate, and the two mass ratio is 1:
0.07。
The preparation method of UV-absorbing layer is: be added drop-wise to by titanium tetrachloride in the mixed liquor of dehydrated alcohol and glacial acetic acid,
Ultrasonic 1.4h under 900W power, ultrasonic after mixed liquor 70 DEG C at be heated to reflux 6h, obtain Nano sol, by PET film immerse
In Nano sol, impregnate 7h, then take out 40-45 DEG C of drying, be finally putting in electromagnetic oven, heat up with the speed of 14 DEG C/min
To 220 DEG C and be incubated 2.4h, then stopping heat supply, cooling is taken out, is obtained scribbling the thin film of UV-absorbing layer.
Embodiment 5
A kind of environment friendly heat resistant rupture pressure disc, this rupture pressure disc includes anti-scratching wearproof layer, safety anti-explosive layer, ultra-violet absorption successively
Layer, pet vector layer, pressure-sensitive adhesive layer and release film layer；
Wherein, the raw material of described anti-scratching wearproof layer, in parts by weight, including following components:
Emulsion acrylic resin 45 parts, isobutyl etherificate amino resin emulsion 34 parts,
The wood fiber 5 parts, succinic anhydrides 1.1 parts, nanocrystalline 2.5 parts of SKGM,
Vermiculite power 3 parts, dispersant 0.4 part, deionized water 14 parts；
Wherein, dispersant is the mixture of potassium citrate and linoleic acid sodium, and the two mass ratio is 1:1；
The raw material of described safety anti-explosive layer, in parts by weight, including following components:
Fluorine-carbon modified polyacrylic resin emulsion 35 parts, polyflon 10 parts,
Acryl-modified silicone resin resin 9 parts, Nano titanium nitride 2.6 parts,
Anhydrous sorbitol monocarboxylate 7 parts, hollow silica nanoparticle 3.5 parts,
Cross-linking agent 0.95 part, 4.5 parts of firming agent, deionized water 11 parts；
Wherein, described cross-linking agent is the mixture of aluminate coupling agent, silane coupler；
The raw material of described pressure-sensitive adhesive layer, in parts by weight, including following components:
Silicones 36 parts, 18 parts of silicone rubber, silane crosslinker 2.5 parts,
Diluent 18 parts, Konjac glucomannan 8 parts, catalyst 1.3 parts；
Wherein, described catalyst is the mixture of organotin catalysts and metal composite carboxylate, and the two mass ratio is 1:
0.075。
The preparation method of UV-absorbing layer is: be added drop-wise to by titanium tetrachloride in the mixed liquor of dehydrated alcohol and glacial acetic acid,
Ultrasonic 1.6h under 900W power, ultrasonic after mixed liquor 75 DEG C at be heated to reflux 6h, obtain Nano sol, by PET film immerse
In Nano sol, impregnate 9h, then take out 40-45 DEG C of drying, be finally putting in electromagnetic oven, heat up with the speed of 16 DEG C/min
To 240 DEG C and be incubated 2.6h, then stopping heat supply, cooling is taken out, is obtained scribbling the thin film of UV-absorbing layer.
Claims (7)
1. an environment friendly heat resistant rupture pressure disc, it is characterised in that this rupture pressure disc include successively anti-scratching wearproof layer, safety anti-explosive layer,
UV-absorbing layer, pet vector layer, pressure-sensitive adhesive layer and release film layer；
Wherein, the raw material of described anti-scratching wearproof layer, in parts by weight, including following components:
Emulsion acrylic resin 30-50 part,
Isobutyl etherificate amino resin emulsion 25-36 part,
Wood fiber 2-6 part, succinic anhydrides 0.5-1.3 part,
SKGM nanocrystalline 1-3 part, vermiculite power 2-4 part,
Dispersant 0.1-0.5 part, deionized water 10-15 part.
The raw material of described safety anti-explosive layer, in parts by weight, including following components:
Fluorine-carbon modified polyacrylic resin emulsion 20-40 part,
Polyflon 5-11 part,
Acryl-modified silicone resin resin 6-10 part,
Nano titanium nitride 2-3 part,
Anhydrous sorbitol monocarboxylate's 3-8 part,
Hollow silica nanoparticle 1-4 part,
Cross-linking agent 0.8-1 part, firming agent 3-5 part, deionized water 8-12 part.
2. a kind of environment friendly heat resistant rupture pressure disc as claimed in claim 1, it is characterised in that the raw material of described anti-scratching wearproof layer,
In parts by weight, including following components:
Emulsion acrylic resin 50 parts,
Isobutyl etherificate amino resin emulsion 25 parts,
The wood fiber 5.5 parts, succinic anhydrides 1.1 parts,
Nanocrystalline 3 parts of SKGM, vermiculite power 2 parts,
Dispersant 0.35 part, deionized water 12 parts；
The raw material of described safety anti-explosive layer, in parts by weight, including following components:
Fluorine-carbon modified polyacrylic resin emulsion 35 parts,
Polyflon 10 parts,
Acryl-modified silicone resin resin 8 parts,
Nano titanium nitride 2.3 parts,
Anhydrous sorbitol monocarboxylate 7 parts,
Hollow silica nanoparticle 2 parts,
Cross-linking agent 1 part, 4 parts of firming agent, deionized water 10 parts.
3. a kind of environment friendly heat resistant rupture pressure disc as claimed in claim 1, it is characterised in that the preparation side of UV-absorbing layer
Method, comprises the following steps:
Titanium tetrachloride is added drop-wise in the mixed liquor of dehydrated alcohol and glacial acetic acid, ultrasonic 1-2h under 800-1000W power, ultrasonic after
Mixed liquor 60-80 DEG C at be heated to reflux 4-7h, obtain Nano sol, PET film be immersed in Nano sol, impregnate 5-
10h, then takes out 40-45 DEG C of drying, is finally putting in electromagnetic oven, be warming up to 180-260 DEG C also with the speed of 10-20 DEG C/min
Insulation 2-3h, then stops heat supply, and cooling is taken out, obtained scribbling the thin film of UV-absorbing layer.
4. a kind of environment friendly heat resistant rupture pressure disc as claimed in claim 1, it is characterised in that the raw material of described pressure-sensitive adhesive layer, with
Weight portion meter, including following components:
Silicones 30-40 part, silicone rubber 10-20 part,
Silane crosslinker 1-3 part, diluent 15-20 part,
Konjac glucomannan 5-10 part, catalyst 0.5-1.5 part.
5. environment friendly heat resistant rupture pressure disc as claimed in claim 1 a kind of, it is characterised in that described dispersant be potassium citrate with
The mixture of linoleic acid sodium, the two mass ratio is 1:1.
6. a kind of environment friendly heat resistant rupture pressure disc as claimed in claim 1, it is characterised in that described cross-linking agent is titanate esters crosslinking
One or more mixing in agent, aluminate coupling agent, silane coupler.
7. a kind of environment friendly heat resistant rupture pressure disc as claimed in claim 4, it is characterised in that described catalyst is organotin catalyzed
Agent and the mixture of metal composite carboxylate, the two mass ratio is 1:(0.05-0.08).