CN106280426A - A kind of false proof characters cut in intaglio laser marking injection PP Pipe Compound and preparation method thereof - Google Patents
A kind of false proof characters cut in intaglio laser marking injection PP Pipe Compound and preparation method thereof Download PDFInfo
- Publication number
- CN106280426A CN106280426A CN201610832722.2A CN201610832722A CN106280426A CN 106280426 A CN106280426 A CN 106280426A CN 201610832722 A CN201610832722 A CN 201610832722A CN 106280426 A CN106280426 A CN 106280426A
- Authority
- CN
- China
- Prior art keywords
- intaglio
- characters cut
- injection
- false proof
- pipe compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of false proof characters cut in intaglio laser marking injection PP Pipe Compound and preparation method thereof, be made up of the raw material of following mass percentage content: PA6,50 99%；GF, 0 50%；Red phosphorus microcapsule, 0.1 2%；Other modified additives, surplus.It is original in production procedure with production equipment that the present invention does not change plastic, does not change plastic key property.Only in the operation of last Laser Jet, automatically form rare characters cut in intaglio bar code at product surface.So that goods are difficult to counterfeit.Characters cut in intaglio code is formed in moulded products surface laser stamp by the injection PP Pipe Compound of the present invention；There is retrospective, exclusiveness, economy.There is extraordinary antifalsification.
Description
Technical field
The present invention relates to a kind of false proof characters cut in intaglio laser marking injection PP Pipe Compound, be specifically related to a kind of false proof characters cut in intaglio laser marking
Injection PP Pipe Compound and preparation method thereof, belongs to modifying plastics field.
Background technology
Along with modified plastics product is applying the every aspect at industrial product in a large number, each plastic manufacturer has by force
Strong false proof demand.Existing it is up in bar code be that the figure of plane is the most imitated in Laser Jet technology, so that plastics
Goods are the most counterfeit, and consumer and manufacturer are brought huge loss.Market in urgent need one has trackability, exclusive
Property, the anti-counterfeiting technology of economy.The present invention is not damaging plastics on the premise of key property and processing mode, for city in technology
Field provides a kind of product surface false proof characters cut in intaglio laser marking PP Pipe Compound with retrospective, exclusiveness, economy.
Summary of the invention
It is an object of the invention to the present situation for existing Laser Jet injection molding material, it is provided that a kind of false proof characters cut in intaglio laser marking is molded
PP Pipe Compound and preparation method thereof,
For reaching above-mentioned purpose, present invention provide the technical scheme that
A kind of false proof characters cut in intaglio laser marking injection PP Pipe Compound, is made up of the raw material of following mass percentage content:
Wherein, other modified additives can be modified additive generally in the art, will not enumerate.
The present invention also provides for the preparation method of above-mentioned false proof characters cut in intaglio laser marking injection PP Pipe Compound, adds work step including following
Rapid:
(1) according to formula proportion mixing raw material or feed respectively, or raw material is divided several groups of mixing；
(2) mix through twin-screw extrusion unit, shear granulation.
The process equipment used is injection machine, extruder, blow moulding machine.
The present invention provides a kind of laser marking to be molded false proof characters cut in intaglio code, uses above-mentioned false proof characters cut in intaglio laser marking injection specially
Materials injection mo(u)lding, carries out stamp by laser marker to plastic.
Beneficial effect:
Existing plastic anti-counterfeiting technology mainly uses Laser Jet, such as: the water pot of automobile.Owing to it adds
Value height, copys easily, and Laser Jet is the most easily copied, and consumer is difficult to whether resolution is genuine part, is badly in need of one and has reality
By the more preferable anti-counterfeiting technology of property.
It is original in production procedure with production equipment that the present invention does not change plastic, does not change plastic basic nature
Energy.Only in the operation of last Laser Jet, automatically form rare characters cut in intaglio bar code at product surface.So that goods are difficult to
Counterfeit.Characters cut in intaglio code is formed in moulded products surface laser stamp by the injection PP Pipe Compound of the present invention；Have retrospective, exclusiveness,
Economy, has extraordinary antifalsification.
Detailed description of the invention
Below in conjunction with specific embodiment, the invention will be further described.
Embodiment 1
(1) basic components:
(2) according to above-mentioned mixing, through double screw extruder extruding pelletization, packing；
(3) injection mo(u)lding type door handle；
(4) directly false proof characters cut in intaglio bar code is formed by laser marker stamp at door handle inner surface.
Embodiment 2
(1) basic components
(2) according to above-mentioned mixing, through double screw extruder extruding pelletization, packing；
(3) injection mo(u)lding type phone housing；
(4) false proof characters cut in intaglio bar code is formed in phone housing inner surface Direct Laser stamp；
Embodiment 3
(1) basic components
(2) according to above-mentioned mixing, through double screw extruder extruding pelletization, packing；
(3) injection mo(u)lding type electric appliance casing；
(4) false proof characters cut in intaglio bar code is formed in electric appliance casing inner surface Direct Laser stamp.
Embodiment 4
(1) basic components
(2) according to above-mentioned mixing, through double screw extruder extruding pelletization, packing；
(3) injection mo(u)lding type electronic equipment casing；
(4) false proof characters cut in intaglio bar code is formed in electronic equipment outer surface Direct Laser stamp.
The above, be only presently preferred embodiments of the present invention, and the present invention not makees any pro forma restriction, any ripe
Know professional and technical personnel, in the range of without departing from technical solution of the present invention, according to the technical spirit of the present invention, to above real
Execute any simple amendment, equivalent and improvement etc. that example made, all still fall within technical solution of the present invention protection domain it
In.
Claims (4)
1. a false proof characters cut in intaglio laser marking injection PP Pipe Compound, it is characterised in that: by the raw material group of following mass percentage content
Become:
2. the preparation method of the false proof characters cut in intaglio laser marking injection PP Pipe Compound described in claim 1, it is characterised in that: include following
Procedure of processing:
(1) according to formula proportion mixing raw material or feed respectively, or raw material is divided several groups of mixing；
(2) mix through twin-screw extrusion unit, shear granulation.
The preparation method of false proof characters cut in intaglio laser marking the most as claimed in claim 2 injection PP Pipe Compound, it is characterised in that: employing
Process equipment is injection machine, extruder, blow moulding machine.
4. a laser marking is molded false proof characters cut in intaglio code, it is characterised in that: use the false proof characters cut in intaglio laser described in claim 1 to beat
Mark moulds PP Pipe Compound injection mo(u)lding, by laser marker, plastic is carried out stamp.