CN106280285A - A kind of flame retardant type glass flake plasticine - Google Patents

A kind of flame retardant type glass flake plasticine Download PDF

Info

Publication number
CN106280285A
CN106280285A CN201610767555.8A CN201610767555A CN106280285A CN 106280285 A CN106280285 A CN 106280285A CN 201610767555 A CN201610767555 A CN 201610767555A CN 106280285 A CN106280285 A CN 106280285A
Authority
CN
China
Prior art keywords
glass flake
flame retardant
retardant type
type glass
flake plasticine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610767555.8A
Other languages
Chinese (zh)
Other versions
CN106280285B (en
Inventor
贺朝铸
周文清
温韬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhan Bo Qi Palace Environmental Protection Coltd
Original Assignee
Wuhan Bo Qi Palace Environmental Protection Coltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan Bo Qi Palace Environmental Protection Coltd filed Critical Wuhan Bo Qi Palace Environmental Protection Coltd
Priority to CN201610767555.8A priority Critical patent/CN106280285B/en
Publication of CN106280285A publication Critical patent/CN106280285A/en
Application granted granted Critical
Publication of CN106280285B publication Critical patent/CN106280285B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of flame retardant type glass flake plasticine, its raw material is as follows: flame retardant type epoxy vinyl ester resin 20 25 parts, glass flake 10 15 parts, 58 parts of firming agent, fire retardant 10 13 parts, carbon forming agent 58 parts, fire resistance fibre 23 parts, binding agent 12 parts.The present invention is compared with Conventional glass flake mortar, and mechanical property and the heat resistance of anti-flammability glass flake plasticine are constant, but oxygen index (OI) improves, and flame propagation velocity is slack-off, has self-extinguishment.

Description

A kind of flame retardant type glass flake plasticine
Technical field
The present invention relates to glass flake plasticine technical field, be specially a kind of flame retardant type glass flake plasticine.
Background technology
Occur repeatedly in the phenomenon built or be burned off by glass flakes anticorrosion in built power plant's absorption tower antiseptic project. Outwardly, cause due to administrative reasons such as crossed constructions.Essential problem is that glass flake plasticine does not has fire resistance, Oxygen index (OI) is too low, and burning velocity is too fast, and once overdoing does not has self-extinguishment, easily causes large area to overdo, and causes and focuses on safe thing Therefore.
The matrix resin of current glass flake plasticine is commonly used vinyl ester resin and is had superior corrosion resistance, and good Manufacturability.In addition to resin, glass flake, firming agent, accelerator, pigment and function additive etc. are the required of glass flake plasticine Component.Flat scale is overlapping arranged in parallel in resin, interlocks up and down, forms unique shielding construction.Be widely used in acid, The various chemical attack medium such as alkali, salt.This product can be used for desulphurization plant, inner wall of stack, pasted with ceramic veneer sheet, ceramic foam vitreous Brick.
Flame retardant type glass flake plasticine is the fire-retardant upgrade version on the basis of Conventional glass flake mortar, with Conventional glass Flake mortar is compared, and mechanical property and the heat resistance of anti-flammability glass flake plasticine are constant, but oxygen index (OI) improves, and flame passes Broadcast and slow, there is self-extinguishment.
Summary of the invention
It is an object of the invention to provide a kind of flame retardant type glass flake plasticine, to solve proposition in above-mentioned background technology Problem.
For achieving the above object, the present invention provides following technical scheme:
A kind of flame retardant type glass flake plasticine, its raw material is as follows: flame retardant type epoxy vinyl ester resin 20-25 Part, glass flake 10-15 part, firming agent 5-8 part, fire retardant 10-13 part, carbon forming agent 5-8 part, fire resistance fibre 2-3 part, binding agent 1-2 part.
Preferably, described binding agent is celluloid.
Preferably, described firming agent is that methyl ethyl ketone peroxide forms than for 2:1 proportioning according to composition by weight with cobalt octoate liquid.
Preferably, described carbon forming agent is corn starch, and powder particle mesh number is between 800-1000.
Preferably, described fire retardant is that magnesium hydroxide forms than for 1:1 proportioning according to composition by weight with aluminium hydroxide, and all For powder, powder mesh number is between 700-900.
Preferably, described fire resistance fibre is TDE fire-retardant high-strength polyvinyl.
Preferably, described binding agent is polyvinyl alcohol.
Preferably, described anti-flammability glass flake plasticine reaches B1 level, leading indicator: burn rate: 21W/S, oxygen index (OI): 31.7, tensile strength: 26MPa, comprcssive strength: 86MPa, bending strength 42MPa, impact strength 1.5MPa.
Preferably, the production equipment of described glass flake plasticine is evacuation five axle planet homogenizer.
Compared with prior art, the invention has the beneficial effects as follows: the present invention compared with Conventional glass flake mortar, anti-flammability Mechanical property and the heat resistance of glass flake plasticine are constant, but oxygen index (OI) improves, and flame propagation velocity is slack-off, has self-extinguishment Property.
Detailed description of the invention
In order to make the purpose of the present invention, technical scheme and advantage clearer, below in conjunction with specific embodiment, to this Invention is further elaborated.Should be appreciated that specific embodiment described herein only in order to explain the present invention, not For limiting the present invention.
Embodiment 1
A kind of flame retardant type glass flake plasticine, its raw material is as follows: flame retardant type epoxy vinyl ester resin 20 parts, Glass flake 10 parts, 5 parts of firming agent, fire retardant 10 parts, carbon forming agent 5 parts, fire resistance fibre 2 parts, binding agent 1 part.
Described binding agent is celluloid.
Described firming agent is that methyl ethyl ketone peroxide forms than for 2:1 proportioning according to composition by weight with cobalt octoate liquid.
Described carbon forming agent is corn starch, and powder particle mesh number is between 800-1000.
Described fire retardant is that magnesium hydroxide forms than for 1:1 proportioning according to composition by weight with aluminium hydroxide, and is powder Shape, powder mesh number is between 700-900.
Described fire resistance fibre is TDE fire-retardant high-strength polyvinyl.
Described binding agent is polyvinyl alcohol.
Described anti-flammability glass flake plasticine reaches B1 level, leading indicator: burn rate: 21W/S, oxygen index (OI): 31.7, anti- Tensile strength: 26MPa, comprcssive strength: 86MPa, bending strength 42MPa, impact strength 1.5MPa.
The production equipment of described glass flake plasticine is evacuation five axle planet homogenizer.
Embodiment 2
A kind of flame retardant type glass flake plasticine, its raw material is as follows: flame retardant type epoxy vinyl ester resin 23 parts, Glass flake 13 parts, 6 parts of firming agent, fire retardant 12 parts, carbon forming agent 6 parts, fire resistance fibre 2.5 parts, binding agent 1.5 parts.
Described binding agent is celluloid.
Described firming agent is that methyl ethyl ketone peroxide forms than for 2:1 proportioning according to composition by weight with cobalt octoate liquid.
Described carbon forming agent is corn starch, and powder particle mesh number is between 800-1000.
Described fire retardant is that magnesium hydroxide forms than for 1:1 proportioning according to composition by weight with aluminium hydroxide, and is powder Shape, powder mesh number is between 700-900.
Described fire resistance fibre is TDE fire-retardant high-strength polyvinyl.
Described binding agent is polyvinyl alcohol.
Described anti-flammability glass flake plasticine reaches B1 level, leading indicator: burn rate: 21W/S, oxygen index (OI): 31.7, anti- Tensile strength: 26MPa, comprcssive strength: 86MPa, bending strength 42MPa, impact strength 1.5MPa.
The production equipment of described glass flake plasticine is evacuation five axle planet homogenizer.
Embodiment 3
A kind of flame retardant type glass flake plasticine, its raw material is as follows: flame retardant type epoxy vinyl ester resin 25 parts, Glass flake 15 parts, 8 parts of firming agent, fire retardant 13 parts, carbon forming agent 8 parts, fire resistance fibre 3 parts, binding agent 2 parts.
Described binding agent is celluloid.
Described firming agent is that methyl ethyl ketone peroxide forms than for 2:1 proportioning according to composition by weight with cobalt octoate liquid.
Described carbon forming agent is corn starch, and powder particle mesh number is between 800-1000.
Described fire retardant is that magnesium hydroxide forms than for 1:1 proportioning according to composition by weight with aluminium hydroxide, and is powder Shape, powder mesh number is between 700-900.
Described fire resistance fibre is TDE fire-retardant high-strength polyvinyl.
Described binding agent is polyvinyl alcohol.
Described anti-flammability glass flake plasticine reaches B1 level, leading indicator: burn rate: 21W/S, oxygen index (OI): 31.7, anti- Tensile strength: 26MPa, comprcssive strength: 86MPa, bending strength 42MPa, impact strength 1.5MPa.
The production equipment of described glass flake plasticine is evacuation five axle planet homogenizer.
The present invention is compared with Conventional glass flake mortar, and the mechanical property of anti-flammability glass flake plasticine and heat resistance are not Becoming, but oxygen index (OI) improves, flame propagation velocity is slack-off, has self-extinguishment.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention is not limited thereto, Any those familiar with the art in the technical scope that the invention discloses, according to technical scheme and Inventive concept equivalent or change in addition, all should contain within protection scope of the present invention.

Claims (9)

1. a flame retardant type glass flake plasticine, it is characterised in that: its raw material is as follows: flame retardant type epoxy vinyl ester Resin 20-25 part, glass flake 10-15 part, firming agent 5-8 part, fire retardant 10-13 part, carbon forming agent 5-8 part, fire resistance fibre 2-3 Part, binding agent 1-2 part.
A kind of flame retardant type glass flake plasticine the most according to claim 1, it is characterised in that: described binding agent is that nitric acid is fine Dimension element.
A kind of flame retardant type glass flake plasticine the most according to claim 1, it is characterised in that: described firming agent is peroxidating Butanone forms than for 2:1 proportioning according to composition by weight with cobalt octoate liquid.
A kind of flame retardant type glass flake plasticine the most according to claim 1, it is characterised in that: described carbon forming agent is that Semen Maydis forms sediment Powder, and powder particle mesh number is between 800-1000.
A kind of flame retardant type glass flake plasticine the most according to claim 1, it is characterised in that: described fire retardant is hydroxide Magnesium forms than for 1:1 proportioning according to composition by weight with aluminium hydroxide, and is powder, and powder mesh number is between 700-900.
A kind of flame retardant type glass flake plasticine the most according to claim 1, it is characterised in that: described fire resistance fibre is ten bromines Diphenylethane fire-retardant high-strength polyvinyl.
A kind of flame retardant type glass flake plasticine the most according to claim 1, it is characterised in that: described binding agent is polyethylene Alcohol.
A kind of flame retardant type glass flake plasticine the most according to claim 1, it is characterised in that: described anti-flammability glass flake Clay reaches B1 level, leading indicator: burn rate: 21W/S, oxygen index (OI): 31.7, tensile strength: 26MPa, comprcssive strength: 86MPa, bending strength 42MPa, impact strength 1.5MPa.
A kind of flame retardant type glass flake plasticine the most according to claim 1, it is characterised in that: described glass flake plasticine Production equipment is evacuation five axle planet homogenizer.
CN201610767555.8A 2016-08-30 2016-08-30 A kind of flame retardant type glass flake plasticine Active CN106280285B (en)