CN106432985A - PVC (polyvinyl chloride) cable material formulation - Google Patents
PVC (polyvinyl chloride) cable material formulation Download PDFInfo
- Publication number
- CN106432985A CN106432985A CN201611051531.9A CN201611051531A CN106432985A CN 106432985 A CN106432985 A CN 106432985A CN 201611051531 A CN201611051531 A CN 201611051531A CN 106432985 A CN106432985 A CN 106432985A
- Authority
- CN
- China
- Prior art keywords
- parts
- nano
- modification
- cable material
- weight portion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a PVC (polyvinyl chloride) cable material formulation. The PVC cable material formulation comprises, by weight, 30-40 parts of polyvinyl chloride, 10-15 parts of high-pressure polyethylene, 8-12 parts of DOP (dioctylphthalate) materials, 2-3 parts of sodium stearate, 5-6 parts of 2,6-tert-butyl-4-methylphenol, 11-18 parts of polyisobutene, 2-5 parts of chlorinated paraffin, 1-5 parts of ethylene acrylic acid grafted maleic anhydride, 1-4 parts of ethylene-propylene-diene rubber, 2-6 parts of a coupling agent, 2-4 parts of modified chitosan, 1-3 parts of nano barium sulfate, 3-8 parts of isocyanate, 8-12 parts of an antioxidant, 5-10 parts of an anti-smoke agent, 5-8 parts of a fire retardant and 6-8 parts of modified filler. The cable material which is prepared from PVC serving as a main material matched with other auxiliary materials and the filler is free of lead, safe and environment friendly, and high machining performance and convenience and labor saving in cutting are realized. In addition, compared with normal cable materials, the PVC cable material has the advantage that diamagnetic performance, waterproof performance, high temperature resistance and chemical corrosion resistance are all improved evidently. The PVC cable material further has advantages of reasonability in material section, flame retardation, low smoke, zero halogen, long service life and the like.
Description
Technical field
The present invention relates to CABLE MATERIALS technical field, specifically a kind of PVC cable material formula.
Background technology
At present, with scientific and technical progress, cable has become the thing that people's everyday life be unable to do without, common on the market
Cable, price is directly proportional to quality, and the better price of function is also higher, cost performance very low it is simply that because of that, function is strong
Greatly, the rational CABLE MATERIALS of cost gets more and more and is accepted by cable industry.
Content of the invention
It is an object of the invention to provide a kind of PVC cable material formula, to solve the problems, such as to propose in above-mentioned background technology.
For achieving the above object, the present invention provides following technical scheme：
A kind of PVC cable material formula, is made up of the following raw material according to weight portion：Polrvinyl chloride 30-40 part, the poly- second of high pressure
Alkene 10-15 part, DOP material 8-12 part, sodium stearate 2-3 part, 2,6- three-level butyl -4- methylphenol 5-6 part, polyisobutylene
11-18 part, chlorinated paraffin 2-5 part, ethylene acrylic grafted maleic anhydride 1-5 part, ethylene propylene diene rubber 1-4 part, coupling agent 2-6
Part, modification of chitosan 2-4 part, nano barium sulfate 1-3 part, isocyanates 3-8 part, antioxidant 8-12 part, antismoke agent 5-10 part, resistance
Combustion agent 5-8 part, Modification material 6-8 part；
Described Modification material is made up of the raw material of following weight portion：3,5- three-level butyl -4- hydroxy phenyl 5-8 parts,
Alumen 1-2 part, vegetable oil 3-4 part, Magnetitum 3-5 part, hexamethylenetetramine 3-5 part, Firebrake ZB 1-3 part, nano-aluminum hydroxide
2.5-4.5 part, polyphosphoric acids aluminum 2-4 part, nano titanium oxide 4-6 part, nano antimony tin oxide powder body 4-9 part, mica powder 5-7
Part, Pulvis Talci 3-5 part, calcinated argil 5-10 part, Kaolin 5-12 part, Calcium Carbonate 5-8 part, ten four carbon alcohols ester 3-7 parts, Graphene
2-4 part, thio-2 acid dibasic acid esters 2-4 part.
A kind of PVC cable material formula, is made up of the following raw material according to weight portion：35 parts of polrvinyl chloride, polyethylene from high pressure process
13 parts, 10 parts of DOP material, 2.5 parts of sodium stearate, 5.5 parts of 2,6- three-level butyl -4- methylphenol, 15 parts of polyisobutylene, chlorination
3 parts of paraffin, 3 parts of ethylene acrylic grafted maleic anhydride, 2 parts of ethylene propylene diene rubber, 4 parts of coupling agent, 3 parts of modification of chitosan, receive
2 parts of nano-barium sulfate, 5 parts of isocyanates, 10 parts of antioxidant, 8 parts of antismoke agent, 6 parts of fire retardant, 7 parts of Modification material；
Described Modification material is made up of the raw material of following weight portion：3,5- 6 parts of three-level butyl -4- hydroxy phenyls, bright
1.5 parts of vitriol, 3.5 parts of vegetable oil, 4 parts of Magnetitum, 4 parts of hexamethylenetetramine, 2 parts of Firebrake ZB, 3.5 parts of nano-aluminum hydroxide, poly
3 parts of aluminum phosphate, 5 parts of nano titanium oxide, 7 parts of nano antimony tin oxide powder body, 6 parts of mica powder, 4 parts of Pulvis Talci, calcinated argil 8
Part, 9 parts of Kaolin, 6 parts of Calcium Carbonate, 5 parts of ten four carbon alcohols ester, 3 parts of Graphene, 3 parts of thio-2 acid dibasic acid esters.
A kind of PVC cable material formula, is made up of the following raw material according to weight portion：30 parts of polrvinyl chloride, polyethylene from high pressure process
10 parts, 8 parts of DOP material, 2 parts of sodium stearate, 5 parts of 2,6- three-level butyl -4- methylphenol, 11 parts of polyisobutylene, chlorinated paraffin 2
Part, 1 part of ethylene acrylic grafted maleic anhydride, 1 part of ethylene propylene diene rubber, 2 parts of coupling agent, modification of chitosan 2 part, nanometer sulphuric acid
1 part of barium, 3 parts of isocyanates, 8 parts of antioxidant, 5 parts of antismoke agent, 5 parts of fire retardant, 6 parts of Modification material；
Described Modification material is made up of the raw material of following weight portion：3,5- 5 parts of three-level butyl -4- hydroxy phenyls, bright
1 part of vitriol, 3 parts of vegetable oil, 3 parts of Magnetitum, 3 parts of hexamethylenetetramine, 1 part of Firebrake ZB, 2.5 parts of nano-aluminum hydroxide, polyphosphoric acids
2 parts of aluminum, 4 parts of nano titanium oxide, 4 parts of nano antimony tin oxide powder body, 5 parts of mica powder, 3 parts of Pulvis Talci, 5 parts of calcinated argil, height
5 parts of ridge soil, 5 parts of Calcium Carbonate, 3 parts of ten four carbon alcohols ester, 2 parts of Graphene, 2 parts of thio-2 acid dibasic acid esters.
A kind of PVC cable material formula, is made up of the following raw material according to weight portion：40 parts of polrvinyl chloride, polyethylene from high pressure process
15 parts, 12 parts of DOP material, 3 parts of sodium stearate, 6 parts of 2,6- three-level butyl -4- methylphenol, 18 parts of polyisobutylene, chlorinated paraffin
5 parts, 5 parts of ethylene acrylic grafted maleic anhydride, 4 parts of ethylene propylene diene rubber, 6 parts of coupling agent, 4 parts of modification of chitosan, nano-sulfur
3 parts of sour barium, 8 parts of isocyanates, 12 parts of antioxidant, 10 parts of antismoke agent, 8 parts of fire retardant, 8 parts of Modification material；
Described Modification material is made up of the raw material of following weight portion：3,5- 8 parts of three-level butyl -4- hydroxy phenyls, bright
2 parts of vitriol, 4 parts of vegetable oil, 5 parts of Magnetitum, 5 parts of hexamethylenetetramine, 3 parts of Firebrake ZB, 4.5 parts of nano-aluminum hydroxide, polyphosphoric acids
4 parts of aluminum, 6 parts of nano titanium oxide, 9 parts of nano antimony tin oxide powder body, 7 parts of mica powder, 5 parts of Pulvis Talci, 10 parts of calcinated argil, height
12 parts of ridge soil, 8 parts of Calcium Carbonate, 7 parts of ten four carbon alcohols ester, 4 parts of Graphene, 4 parts of thio-2 acid dibasic acid esters.
Described coupling agent is methyl hydroxyethylcellulose.
Described antioxidant is 1010 and 168 according to 2：1 ratio compounds.
Described fire retardant is selected from one of antimony oxide, magnesium hydroxide.
Compared with prior art, the invention has the beneficial effects as follows：
CABLE MATERIALS of the present invention, with PVC as major ingredient, coordinates other adjuvants and inserts, and composition is not leaded, safety and environmental protection so that
Machining property is good, and cutting facilitates leicht fallen D/A, and diamagnetic performance, water resistance, resistance to elevated temperatures, resistance to chemical corrosion
All it is obviously improved than common cable material, its tensile property and ageing resistace lift more than 50% than common cable material, biological fall
Solution cycle is short, low production cost, economic worth is high, and prospect is very wide.Have that material selection is reasonable, fire-retardant simultaneously, low smoke and zero halogen,
The advantages of long service life, emergency case is occurring, the material of generation is harmless to human body, natural environment.
Specific embodiment
Embodiment 1
A kind of PVC cable material formula, is made up of the following raw material according to weight portion：35 parts of polrvinyl chloride, polyethylene from high pressure process
13 parts, 10 parts of DOP material, 2.5 parts of sodium stearate, 5.5 parts of 2,6- three-level butyl -4- methylphenol, 15 parts of polyisobutylene, chlorination
3 parts of paraffin, 3 parts of ethylene acrylic grafted maleic anhydride, 2 parts of ethylene propylene diene rubber, 4 parts of coupling agent, 3 parts of modification of chitosan, receive
2 parts of nano-barium sulfate, 5 parts of isocyanates, 10 parts of antioxidant, 8 parts of antismoke agent, 6 parts of fire retardant, 7 parts of Modification material；
Described Modification material is made up of the raw material of following weight portion：3,5- 6 parts of three-level butyl -4- hydroxy phenyls, bright
1.5 parts of vitriol, 3.5 parts of vegetable oil, 4 parts of Magnetitum, 4 parts of hexamethylenetetramine, 2 parts of Firebrake ZB, 3.5 parts of nano-aluminum hydroxide, poly
3 parts of aluminum phosphate, 5 parts of nano titanium oxide, 7 parts of nano antimony tin oxide powder body, 6 parts of mica powder, 4 parts of Pulvis Talci, calcinated argil 8
Part, 9 parts of Kaolin, 6 parts of Calcium Carbonate, 5 parts of ten four carbon alcohols ester, 3 parts of Graphene, 3 parts of thio-2 acid dibasic acid esters.
Described coupling agent is methyl hydroxyethylcellulose.
Described antioxidant is 1010 and 168 according to 2：1 ratio compounds.
Described fire retardant is selected from one of antimony oxide, magnesium hydroxide.
Embodiment 2
A kind of PVC cable material formula, is made up of the following raw material according to weight portion：30 parts of polrvinyl chloride, polyethylene from high pressure process
10 parts, 8 parts of DOP material, 2 parts of sodium stearate, 5 parts of 2,6- three-level butyl -4- methylphenol, 11 parts of polyisobutylene, chlorinated paraffin 2
Part, 1 part of ethylene acrylic grafted maleic anhydride, 1 part of ethylene propylene diene rubber, 2 parts of coupling agent, modification of chitosan 2 part, nanometer sulphuric acid
1 part of barium, 3 parts of isocyanates, 8 parts of antioxidant, 5 parts of antismoke agent, 5 parts of fire retardant, 6 parts of Modification material；
Described Modification material is made up of the raw material of following weight portion：3,5- 5 parts of three-level butyl -4- hydroxy phenyls, bright
1 part of vitriol, 3 parts of vegetable oil, 3 parts of Magnetitum, 3 parts of hexamethylenetetramine, 1 part of Firebrake ZB, 2.5 parts of nano-aluminum hydroxide, polyphosphoric acids
2 parts of aluminum, 4 parts of nano titanium oxide, 4 parts of nano antimony tin oxide powder body, 5 parts of mica powder, 3 parts of Pulvis Talci, 5 parts of calcinated argil, height
5 parts of ridge soil, 5 parts of Calcium Carbonate, 3 parts of ten four carbon alcohols ester, 2 parts of Graphene, 2 parts of thio-2 acid dibasic acid esters.
Described coupling agent is methyl hydroxyethylcellulose.
Described antioxidant is 1010 and 168 according to 2：1 ratio compounds.
Described fire retardant is selected from one of antimony oxide, magnesium hydroxide.
Embodiment 3
A kind of PVC cable material formula, is made up of the following raw material according to weight portion：40 parts of polrvinyl chloride, polyethylene from high pressure process
15 parts, 12 parts of DOP material, 3 parts of sodium stearate, 6 parts of 2,6- three-level butyl -4- methylphenol, 18 parts of polyisobutylene, chlorinated paraffin
5 parts, 5 parts of ethylene acrylic grafted maleic anhydride, 4 parts of ethylene propylene diene rubber, 6 parts of coupling agent, 4 parts of modification of chitosan, nano-sulfur
3 parts of sour barium, 8 parts of isocyanates, 12 parts of antioxidant, 10 parts of antismoke agent, 8 parts of fire retardant, 8 parts of Modification material；
Described Modification material is made up of the raw material of following weight portion：3,5- 8 parts of three-level butyl -4- hydroxy phenyls, bright
2 parts of vitriol, 4 parts of vegetable oil, 5 parts of Magnetitum, 5 parts of hexamethylenetetramine, 3 parts of Firebrake ZB, 4.5 parts of nano-aluminum hydroxide, polyphosphoric acids
4 parts of aluminum, 6 parts of nano titanium oxide, 9 parts of nano antimony tin oxide powder body, 7 parts of mica powder, 5 parts of Pulvis Talci, 10 parts of calcinated argil, height
12 parts of ridge soil, 8 parts of Calcium Carbonate, 7 parts of ten four carbon alcohols ester, 4 parts of Graphene, 4 parts of thio-2 acid dibasic acid esters.
Described coupling agent is methyl hydroxyethylcellulose.
Described antioxidant is 1010 and 168 according to 2：1 ratio compounds.
Described fire retardant is selected from one of antimony oxide, magnesium hydroxide.
Claims (7)
1. a kind of PVC cable material formula is it is characterised in that be made up of the following raw material according to weight portion：Polrvinyl chloride 30-40
Part, polyethylene from high pressure process 10-15 part, DOP material 8-12 part, sodium stearate 2-3 part, 2,6- three-level butyl -4- methylphenol 5-6
Part, polyisobutylene 11-18 part, chlorinated paraffin 2-5 part, ethylene acrylic grafted maleic anhydride 1-5 part, ethylene propylene diene rubber 1-4
Part, coupling agent 2-6 part, modification of chitosan 2-4 part, nano barium sulfate 1-3 part, isocyanates 3-8 part, antioxidant 8-12 part, disappear
Fumicants 5-10 part, fire retardant 5-8 part, Modification material 6-8 part；
Described Modification material is made up of the raw material of following weight portion：3,5- three-level butyl -4- hydroxy phenyl 5-8 parts, Alumen
1-2 part, vegetable oil 3-4 part, Magnetitum 3-5 part, hexamethylenetetramine 3-5 part, Firebrake ZB 1-3 part, nano-aluminum hydroxide 2.5-4.5
Part, polyphosphoric acids aluminum 2-4 part, nano titanium oxide 4-6 part, nano antimony tin oxide powder body 4-9 part, mica powder 5-7 part, Pulvis Talci
3-5 part, calcinated argil 5-10 part, Kaolin 5-12 part, Calcium Carbonate 5-8 part, ten four carbon alcohols ester 3-7 parts, Graphene 2-4 part, sulfur
For dipropyl acid diester 2-4 part.
2. PVC cable material formula according to claim 1 is it is characterised in that be made up of the following raw material according to weight portion：
35 parts of polrvinyl chloride, 13 parts of polyethylene from high pressure process, 10 parts of DOP material, 2.5 parts of sodium stearate, 2,6- three-level butyl -4- methylphenol
5.5 parts, 15 parts of polyisobutylene, 3 parts of chlorinated paraffin, 3 parts of ethylene acrylic grafted maleic anhydride, 2 parts of ethylene propylene diene rubber, be coupled
4 parts of agent, 3 parts of modification of chitosan, 2 parts of nano barium sulfate, 5 parts of isocyanates, 10 parts of antioxidant, 8 parts of antismoke agent, 6 parts of fire retardant,
7 parts of Modification material；
Described Modification material is made up of the raw material of following weight portion：3,5- 6 parts of three-level butyl -4- hydroxy phenyls, Alumen 1.5
Part, 3.5 parts of vegetable oil, 4 parts of Magnetitum, 4 parts of hexamethylenetetramine, 2 parts of Firebrake ZB, 3.5 parts of nano-aluminum hydroxide, polyphosphoric acids aluminum
3 parts, 5 parts of nano titanium oxide, 7 parts of nano antimony tin oxide powder body, 6 parts of mica powder, 4 parts of Pulvis Talci, 8 parts of calcinated argil, kaolinite
9 parts of soil, 6 parts of Calcium Carbonate, 5 parts of ten four carbon alcohols ester, 3 parts of Graphene, 3 parts of thio-2 acid dibasic acid esters.
3. PVC cable material formula according to claim 1 is it is characterised in that be made up of the following raw material according to weight portion：
30 parts of polrvinyl chloride, 10 parts of polyethylene from high pressure process, 8 parts of DOP material, 2 parts of sodium stearate, 2,6- three-level butyl -4- methylphenol 5
Part, 11 parts of polyisobutylene, 2 parts of chlorinated paraffin, 1 part of ethylene acrylic grafted maleic anhydride, 1 part of ethylene propylene diene rubber, coupling agent 2
Part, 2 parts of modification of chitosan, 1 part of nano barium sulfate, 3 parts of isocyanates, 8 parts of antioxidant, 5 parts of antismoke agent, 5 parts of fire retardant, modification
6 parts of inserts；
Described Modification material is made up of the raw material of following weight portion：3,5- 5 parts of three-level butyl -4- hydroxy phenyls, Alumen 1
Part, 3 parts of vegetable oil, 3 parts of Magnetitum, 3 parts of hexamethylenetetramine, 1 part of Firebrake ZB, 2.5 parts of nano-aluminum hydroxide, polyphosphoric acids aluminum 2
Part, 4 parts of nano titanium oxide, 4 parts of nano antimony tin oxide powder body, 5 parts of mica powder, 3 parts of Pulvis Talci, 5 parts of calcinated argil, Kaolin
5 parts, 5 parts of Calcium Carbonate, 3 parts of ten four carbon alcohols ester, 2 parts of Graphene, 2 parts of thio-2 acid dibasic acid esters.
4. PVC cable material formula according to claim 1 is it is characterised in that be made up of the following raw material according to weight portion：
40 parts of polrvinyl chloride, 15 parts of polyethylene from high pressure process, 12 parts of DOP material, 3 parts of sodium stearate, 2,6- three-level butyl -4- methylphenol 6
Part, 18 parts of polyisobutylene, 5 parts of chlorinated paraffin, 5 parts of ethylene acrylic grafted maleic anhydride, 4 parts of ethylene propylene diene rubber, coupling agent 6
Part, 4 parts of modification of chitosan, 3 parts of nano barium sulfate, 8 parts of isocyanates, 12 parts of antioxidant, 10 parts of antismoke agent, 8 parts of fire retardant, change
8 parts of inserts of property；
Described Modification material is made up of the raw material of following weight portion：3,5- 8 parts of three-level butyl -4- hydroxy phenyls, Alumen 2
Part, 4 parts of vegetable oil, 5 parts of Magnetitum, 5 parts of hexamethylenetetramine, 3 parts of Firebrake ZB, 4.5 parts of nano-aluminum hydroxide, polyphosphoric acids aluminum 4
Part, 6 parts of nano titanium oxide, 9 parts of nano antimony tin oxide powder body, 7 parts of mica powder, 5 parts of Pulvis Talci, 10 parts of calcinated argil, kaolinite
12 parts of soil, 8 parts of Calcium Carbonate, 7 parts of ten four carbon alcohols ester, 4 parts of Graphene, 4 parts of thio-2 acid dibasic acid esters.
5. PVC cable material formula according to claim 1 is it is characterised in that described coupling agent is dimethyl hydroxyethyl fibre
Dimension element.
6. PVC cable material formula according to claim 1 it is characterised in that described antioxidant be 1010 and 168 according to
2：1 ratio compounds.
7. PVC cable material formula according to claim 1 is it is characterised in that described fire retardant is selected from antimony oxide, hydrogen
One of magnesium oxide.