CN106278716A - A kind of cold-resistant oxygen supplement coated fertilizer - Google Patents

Abstract

The invention discloses a kind of cold-resistant oxygen supplement coated fertilizer, be prepared by the raw materials in: carboxymethyl cellulose 23, Glycine max (L.) Merr. 44 48, Semen Citri Reticulatae powder 14 16, chitosan 12, lignin sulfonic acid zinc 23, potassium chloride 46, calcium-base bentonite 56, carbamide 89,30% hydrogenperoxide steam generator 12 14, Laxogenin powder 23, butyl acrylate 0.5 0.7, sodium dihydrogen phosphate dry powder 23, nano zine oxide 0.9 1.1, water are appropriate；Fertilizer of the present invention is added by the pelletize of fermentation powder, can effectively reduce interstices of soil, reduce air flow property thus completely cut off the entrance of cold air, the interpolation of the material such as carboxymethyl cellulose simultaneously can regulate and control the water content of soil, avoid the absorption freezing under low temperature environment to affect root system to nutrient because soil water-containing is more, accelerate the nutrition accumulation of crop under cold conditions, improve resistance, improve the yield of crop under low temperature.

Description

A kind of cold-resistant oxygen supplement coated fertilizer

Technical field

The present invention relates to technical field of fertilizers, particularly relate to a kind of cold-resistant oxygen supplement coated fertilizer.

Background technology

Along with global climate is abnormal, some areas heavy rain, flood frequently occur, because of improper irrigation or draining the most not The factor such as good often results in crop arable land hydrops waterlogging, makes soil be in waterflooding state, and under flooding condition, in soil, gas is forced Discharge, easily cause oxygen in soil not enough.And oxygen is that root system of plant breathing is necessary, long term hypoxia can make plant cell Electron transmission is obstructed, and active oxygen accumulates in a large number, and membrane structure and function are destroyed, and even there will be crop mortality. Under Hypoxia Stress, root system accumulates the noxious substances such as a large amount of ethanol, lactic acid, and root system metabolism disorder, aerobic respiration is suppressed and causes Energy supply lacks, and the impact absorption to nutrient, waterflooding causes the minimizing of root system oxygen supply, also can cause plant leaf blade pore Closing, stomatal conductance reduces, and in turn results in net photosynthetic rate, the reduction of photochemistry quantum efficiency, and in blade, total leaf is green simultaneously Element and Chlorophyll-a Content decline, and cause the minimizing of plant growth and total biomass, affect greatly crop yield.For Case above, common solution is chesson or enriches oxygenating agent, and the former amount of labour is relatively big, latter increases production Cost, is all not carried out preferable economic benefit.

Research shows, under waterflooding anoxia condition, in plant cell, proline content is exponentially increased, and remains thin with this The turgescence of born of the same parents, protective enzyme and membranous system escape injury, and proline can be alleviated to a certain extent as a kind of osmotic adjustment The anoxia injury effect to cell membrane.Laxogenin is structurally similar to Study on Brassinosteroids, and obtains into This is the cheapest compared with brassinosteroid, Laxogenin can induce soluble sugar in plant, soluble protein, Proline long-pending Tired, Premeabilisation of cells regulating power can be strengthened under waterflooding anoxia condition, make cell maintain a constant turgescence, thus maintain The physiological and biochemical activities relevant with turgescence such as cell growth, stomatal opening and photosynthesis are smoothed out.And Laxogenin Polyradical can be removed by improving oxidase system activity, reduce autoxidation rate, and then reduce membrane lipid The integrity of extent of peroxidation, protecting film structure and macromolecular substances structure, and then keep the stability of cell to carry with vigor Its anoxia resistance high.Meet water after being meanwhile blended with hydrogen peroxide by carbamide and can slowly release the feature of oxygen, by upper State in the preparation being applied to fertilizer, soil epiliminion dissolved oxygen amount can be improved, increase the active o content in the soil liquid, think root The oxygen needed for providing is breathed by system, can prevent again the adverse effect to crop under waterflooding anoxia condition, and then improve crop yield, Increase planting benefit.

The application for a patent for invention of Publication No. 104045386A discloses a kind of hyperoxic plant organic fertilizer, this fertilizer Material is made up of the raw material of following parts by weight: bean cake 20-40 part, cottonseed meal 10-20 part, sugar slag 5-10 part, silicon dioxide 4-8 Part, coal humic acid 5-10 part, manioc waste 20-30 part, shale 7-14 part, plant ash 4-8 part, plant mushroom waste soil 20-30 Part, maltose residues 5-10 part, Semen Maydis grit 5-10 part, Ramulus et folium taxi cuspidatae 3-9 part, Os Sus domestica powder 7-12 part, bulls powder 8-14 part.This invention fertilizer Nutrient content is higher, and fertilizer efficiency is very fast, but is not effectively improved the oxygen content of soil plough horizon, also cannot for unfavorable conditions such as waterflooding Improve the repellence of crop, and without the raising of notable surcharge, limit the use of fertilizer.

Summary of the invention

The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of cold-resistant oxygen supplement coated fertilizer.

The present invention is achieved by the following technical solutions:

A kind of cold-resistant oxygen supplement coated fertilizer, is prepared by the raw materials in: carboxymethyl cellulose 2-3, Glycine max (L.) Merr. 44-48, Semen Citri Reticulatae powder 14-16, chitosan 1-2, lignin sulfonic acid zinc 2-3, potassium chloride 4-6, calcium-base bentonite 5-6, carbamide 8-9,30% peroxide Change hydrogen solution 12-14, Laxogenin powder 2-3, butyl acrylate 0.5-0.7, sodium dihydrogen phosphate dry powder 2-3, nano oxidized Zinc 0.9-1.1, water are appropriate.

Specifically comprising the following steps that of described cold-resistant oxygen supplement coated fertilizer preparation method

(1) Glycine max (L.) Merr., the mixing of Semen Citri Reticulatae powder are placed in fermentation vat, control the 44-that water content is fermentation heap maximum water holding capacity 48%, in retting fermentation 2-3 week, after having fermented, fermentation material is dried, be ground into siccative standby；

(2) 25-30 times of mixture quality is joined after being mixed with chitosan, lignin sulfonic acid zinc by Laxogenin powder In water, it is heated to 56-58 DEG C, is incubated and is stirred continuously 20-30 minute, be down to room temperature afterwards, then be added thereto to step 1 gained Siccative, soaks and stirs 5-6 hour, filters after completing, and collects filtrate and filtrate respectively, and it is standby for powder that filtrate is dried pulverizing With；

(3) carbamide is put in 30% hydrogenperoxide steam generator, then is added thereto to sodium dihydrogen phosphate dry powder, be warming up to 30-32 DEG C, Reacting 50-60 minute, period is constantly stirred, and has reacted and has been placed on subzero 3-5 DEG C of crystallization, after drying by gained material with Step 2 gained powder, potassium chloride, carboxymethyl cellulose, calcium-base bentonite mixing granulation, obtain nuclear core fertiliser granulates standby；

(4) step 2 gained filtrate is sufficiently mixed with butyl acrylate, nano zine oxide, stirs, obtain coating nutritional solution, Being placed in fluidized bed coating equipment by step 3 gained nuclear core fertiliser granulates, control inlet temperature and be 50-55 DEG C, leaving air temp is 30-35 DEG C, coating nutritional solution flow velocity is 2-2.5 ml/min, and coating nutritional solution is coated uniformly on nuclear core fertiliser granulates table Face, obtains coated fertilizer of the present invention.

The invention have the advantage that

Oxygen supplement coated fertilizer of the present invention passes through the peplos effect release with slow-release oxygen gas, it is ensured that crop root aerobic respiration Be normally carried out, for the various physiological metabolism of plant provide energy, enhance crop cell activities of antioxidant enzymes simultaneously, and reduce nothing Oxygen breathes the noxious substance the produced injury to plant, can maintain stable cellularity to a certain extent, and then improve leaf Sheet activities of antioxidant enzymes, alleviates the accumulated active oxygen injury to plant under waterflooding anoxia condition, has strengthening crop resistance to overhead flooding injury Positive role.

Fertilizer of the present invention is added by the pelletize of fermentation powder, can effectively reduce interstices of soil, reduce air flow property from And completely cutting off the entrance of cold air, the interpolation of the material such as carboxymethyl cellulose simultaneously can regulate and control the water content of soil, it is to avoid low temperature ring Freeze the absorption affecting root system to nutrient under border because soil water-containing is more, accelerate the nutrition accumulation of crop under cold conditions, Improve resistance, improve the yield of crop under low temperature.

Detailed description of the invention

A kind of cold-resistant oxygen supplement coated fertilizer, is made up of the raw material of following weight portion (kg): carboxymethyl cellulose 2, Glycine max (L.) Merr. 44, Semen Citri Reticulatae powder 14, chitosan 1, lignin sulfonic acid zinc 2, potassium chloride 4, calcium-base bentonite 5, carbamide 8,30% hydrogenperoxide steam generator 12, Laxogenin powder 2, butyl acrylate 0.5, sodium dihydrogen phosphate dry powder 2, nano zine oxide 0.9, water are appropriate.

Specifically comprising the following steps that of described cold-resistant oxygen supplement coated fertilizer preparation method

(1) Glycine max (L.) Merr., the mixing of Semen Citri Reticulatae powder being placed in fermentation vat, controlling water content is the 44% of fermentation heap maximum water holding capacity, macerates System fermentation 2 weeks, dries fermentation material after having fermented, is ground into siccative standby；

(2) water of 25 times of mixture qualities is joined with chitosan, lignin sulfonic acid zinc after being mixed by Laxogenin powder In, it is heated to 56 DEG C, is incubated and is stirred continuously 20 minutes, be down to room temperature afterwards, then be added thereto to step 1 gained siccative, leaching Steep and stir 5 hours, filtering after completing, collecting filtrate and filtrate respectively, and it is standby for powder that filtrate is dried pulverizing；

(3) carbamide is put in 30% hydrogenperoxide steam generator, then be added thereto to sodium dihydrogen phosphate dry powder, be warming up to 30 DEG C, reaction 50 minutes, period was constantly stirred, and has reacted and has been placed on subzero 3 DEG C of crystallizations, by gained material and step 2 gained after drying Powder, potassium chloride, carboxymethyl cellulose, calcium-base bentonite mixing granulation, obtain nuclear core fertiliser granulates standby；

(4) step 2 gained filtrate is sufficiently mixed with butyl acrylate, nano zine oxide, stirs, obtain coating nutritional solution, Being placed in fluidized bed coating equipment by step 3 gained nuclear core fertiliser granulates, controlling inlet temperature is 50 DEG C, and leaving air temp is 30 DEG C, coating nutritional solution flow velocity is 2 ml/min, and coating nutritional solution is coated uniformly on nuclear core fertiliser granulates surface, i.e. get Ben Fa Bright coated fertilizer.

In order to further illustrate the using value of the present invention, inventor have selected two pieces of experiments that many Yushan Districts physical features is identical Field plantation Semen Tritici aestivi, one of field uses fertilizer of the present invention as experimental group, and another block uses commercially available common fertilizer conduct Matched group, wheat planting period, two groups of field management were identical, recorded yield, the equal 513kg of experimental group per mu yield, matched group mu after results Produce equal 450kg, it is seen that fertilizer of the present invention has preferable using effect.

Claims (2)

1. a cold-resistant oxygen supplement coated fertilizer, it is characterised in that be prepared by the raw materials in: carboxymethyl cellulose 2-3, Glycine max (L.) Merr. 44-48, Semen Citri Reticulatae powder 14-16, chitosan 1-2, lignin sulfonic acid zinc 2-3, potassium chloride 4-6, calcium-base bentonite 5-6, urine Element 8-9,30% hydrogenperoxide steam generator 12-14, Laxogenin powder 2-3, butyl acrylate 0.5-0.7, sodium dihydrogen phosphate dry powder 2-3, nano zine oxide 0.9-1.1, water are appropriate.

2. according to the cold-resistant oxygen supplement coated fertilizer described in claims 1, it is characterised in that the concrete steps of preparation method are such as Under:

(1) Glycine max (L.) Merr., the mixing of Semen Citri Reticulatae powder are placed in fermentation vat, control the 44-that water content is fermentation heap maximum water holding capacity 48%, in retting fermentation 2-3 week, after having fermented, fermentation material is dried, be ground into siccative standby；

(2) 25-30 times of mixture quality is joined with chitosan, lignin sulfonic acid zinc after being mixed by Laxogenin powder Water in, be heated to 56-58 DEG C, be incubated and be stirred continuously 20-30 minute, be down to room temperature afterwards, then be added thereto to step 1 institute Obtain siccative, soak and stir 5-6 hour, filter after completing, collect filtrate and filtrate respectively, and be powder by filtrate drying pulverizing Standby；

(3) carbamide is put in 30% hydrogenperoxide steam generator, then is added thereto to sodium dihydrogen phosphate dry powder, be warming up to 30-32 DEG C, Reacting 50-60 minute, period is constantly stirred, and has reacted and has been placed on subzero 3-5 DEG C of crystallization, after drying by gained material with Step 2 gained powder, potassium chloride, carboxymethyl cellulose, calcium-base bentonite mixing granulation, obtain nuclear core fertiliser granulates standby；

(4) step 2 gained filtrate is sufficiently mixed with butyl acrylate, nano zine oxide, stirs, obtain coating nutritional solution, Being placed in fluidized bed coating equipment by step 3 gained nuclear core fertiliser granulates, control inlet temperature and be 50-55 DEG C, leaving air temp is 30-35 DEG C, coating nutritional solution flow velocity is 2-2.5 ml/min, and coating nutritional solution is coated uniformly on nuclear core fertiliser granulates table Face, obtains coated fertilizer of the present invention.