CN106245880A - Super-thin plastic floor - Google Patents
Super-thin plastic floor Download PDFInfo
- Publication number
- CN106245880A CN106245880A CN201610612837.0A CN201610612837A CN106245880A CN 106245880 A CN106245880 A CN 106245880A CN 201610612837 A CN201610612837 A CN 201610612837A CN 106245880 A CN106245880 A CN 106245880A
- Authority
- CN
- China
- Prior art keywords
- bed
- parts
- super
- plastic floor
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of super-thin plastic floor, including initial bed, the middle bed of material, fiberglass layer, printing film and wearing layer, the described middle bed of material includes in first the bed of material in the bed of material and second, described initial bed, the bed of material in first, fiberglass layer, the bed of material, printing film and wearing layer set gradually in second, the described middle bed of material is made up of the raw material of following weight portion: polrvinyl chloride 98 106 parts, DOTP 30 35 parts, calcium-zinc composite stabilizing agent 1 2.2 parts, white carbon black 0.2 0.5 parts, calcium carbonate 450 455 parts.Super-thin plastic floor of the present invention, owing to adding fiberglass layer, and have adjusted the formula of the middle bed of material so that product pliability substantially increases, and shrinkage factor drops to less than 0.08%, and hardness reduces, and for extra-thin product, performance is more preferable.And fiberglass layer is arranged in two-layer between the bed of material, then product does not haves the phenomenon of warpage, and product stability is more preferable, more durable.
Description
Technical field
The present invention relates to plastic floor field, particularly relate to a kind of super-thin plastic floor.
Background technology
Plastic floor i.e. PVC floor, it is mainly composed of pvc material.PVC floor is enriched due to its pattern,
Color is various and is widely used in each side of house and business.Plastic floor is that in the world today, popular one is novel
Light body floor decorative material, also referred to as " light body ground material ", be a kind of product very popular in American-European and Asia Japan and Korea S, fashionable
Abroad, initially entering Chinese market from the beginning of the eighties, big and medium-sized cities the most at home have obtained universal accreditation, use non-
Often extensively, the various fields such as such as indoor family, hospital, school, office building, factory, public place, supermarket, business, stadiums
Institute.
In existing plastic floor, in order to control expansion rate and the shrinkage factor of product, add substantial amounts of inorganic filler (carbonic acid
Calcium), but add substantial amounts of inorganic filler and can bring new problem: and along with the increase of inorganic flavoring agent, the density of product, hardness are also
Meeting is along with increase, and toughness can decline, then the edge of product easily becomes fragile, and easily causes damage during processing and transport
Bad, and it is susceptible to warpage.
Summary of the invention
The invention aims to solve the above-mentioned problems in the prior art, it is provided that a kind of super-thin plastic ground
Plate, adds fiberglass layer in the product, and toughness is preferable, and warpage will not occur.
In order to achieve the above object, the present invention provides a kind of super-thin plastic floor, including initial bed, the middle bed of material, glass
Layer, printing film and wearing layer, the described middle bed of material includes in first the bed of material in the bed of material and second, described initial bed, expects in first
Layer, fiberglass layer, the bed of material, printing film and wearing layer set gradually in second, and the described middle bed of material is by the raw material system of following weight portion
Become: polrvinyl chloride 98-106 part, DOTP 30-35 part, calcium-zinc composite stabilizing agent 1-2.2 part, white carbon black 0.2-0.5
Part, calcium carbonate 450-455 part.
In one embodiment of the invention, the described middle bed of material is made up of the raw material of following weight portion: polrvinyl chloride 98 parts, to benzene
Dioctyl phthalate dioctyl ester 30 parts, calcium-zinc composite stabilizing agent 1 part, white carbon black 0.2 part, calcium carbonate 450 parts.
In one embodiment of the invention, the described middle bed of material is made up of the raw material of following weight portion: polrvinyl chloride 100 parts, right
Dioctyl phthalate 32 parts, calcium-zinc composite stabilizing agent 1.5 parts, white carbon black 0.3 part, calcium carbonate 452 parts.
In one embodiment of the invention, the thickness of described fiberglass layer is 0.2mm-0.6mm.
In one embodiment of the invention, the thickness of described fiberglass layer is 0.3mm.
In one embodiment of the invention, described fiberglass layer is latticed glass fibre.
In one embodiment of the invention, in described first, the bed of material is identical with the thickness of the bed of material in described second.
In one embodiment of the invention, in described first, the thickness of the bed of material is 0.6-0.8mm.
In one embodiment of the invention, in described second, the thickness of the bed of material is 0.6-0.8mm.
Compared with prior art, the technical program provides the benefit that:
Super-thin plastic floor of the present invention, owing to adding fiberglass layer, and have adjusted the formula of the middle bed of material so that product is soft
Toughness substantially increases, and shrinkage factor declines, and hardness reduces, and for extra-thin product, performance is more preferable.And fiberglass layer is arranged on
In two-layer between the bed of material, then product does not haves the phenomenon of warpage, and product stability is more preferable, more durable.
Accompanying drawing explanation
Fig. 1 is the structural representation on super-thin plastic floor of the present invention.
Detailed description of the invention
Below in conjunction with the accompanying drawings, by specific embodiment, technical scheme is carried out clear, complete description.
Refer to shown in Fig. 1, the present invention provides a kind of super-thin plastic floor, including initial bed 1, the middle bed of material, fiberglass layer
3, printing film 5 and wearing layer 6.The described middle bed of material includes in first the bed of material 4, the bed of material 2 and second in first in the bed of material 2 and second
The composition of raw materials of the middle bed of material 4 is identical.The bed of material 4, printing film 5 and in the bed of material 2, fiberglass layer 3, second in described initial bed 1, first
Wearing layer 6 sets gradually.The described middle bed of material is made up of the raw material of following weight portion: polrvinyl chloride 98-106 part, p-phthalic acid
Dioctyl ester 30-35 part, calcium-zinc composite stabilizing agent 1-2.2 part, white carbon black 0.2-0.5 part, calcium carbonate 450-455 part.
The middle bed of material is prepared by the following method: material pvc, DOTP, calcium-zinc composite stabilizing agent
Mix according to aforementioned proportion with white carbon black, add calcium carbonate after mix homogeneously and continue mixing, after mix homogeneously, add closed refining glue
In machine, internal rubber mixer controls temperature and is 170-180 DEG C, discharging after banburying 5 minutes, regulation thickness in open mill
Degree, controls slice temperature and is 40-50 DEG C, rolling out film, the i.e. available middle bed of material.
Stack successively initial bed, the middle bed of material, fiberglass layer, the middle bed of material, printing film and wearing layer and carry out hot pressing be combined, i.e.
Available described super-thin plastic floor.
Owing to this plastic floor adds fiberglass layer, and have adjusted the formula of the middle bed of material so that product pliability substantially increases
Adding, shrinkage factor declines, and hardness reduces, and for extra-thin product, performance is more preferable.The thickness of described fiberglass layer 3 is
0.2mm-0.6mm, it is possible to provide preferably pliability, and reduce product hardness.The bed of material in the bed of material 2 and described second in described first
The thickness of 3 is identical, then fiberglass layer 3 is located between the middle bed of material that two layers of thickness is identical, then product does not haves the phenomenon of warpage.
Embodiment 1
A kind of super-thin plastic floor, including initial bed, the middle bed of material, fiberglass layer, printing film and wearing layer.Described middle material
Layer includes in first the bed of material in the bed of material and second.Described initial bed, the bed of material in first, fiberglass layer, the bed of material, printing film in second
Set gradually with wearing layer.The described middle bed of material is made up of the raw material of following weight portion: polrvinyl chloride 98 parts, p-phthalic acid two is pungent
Ester 30 parts, calcium-zinc composite stabilizing agent 1 part, white carbon black 0.2 part, calcium carbonate 450 parts.The middle bed of material is prepared by the following method: raw material
Polrvinyl chloride, DOTP, calcium-zinc composite stabilizing agent and white carbon black mix according to aforementioned proportion, add after mix homogeneously
Calcium carbonate continues mixing, adds in internal rubber mixer after mix homogeneously, and it is 180 DEG C that internal rubber mixer controls temperature, banburying 5
Discharging after minute, regulates thickness in open mill, and controlling slice temperature is 40 DEG C, rolling out film, i.e. available middle material
Layer.Described fiberglass layer is latticed glass fibre.The thickness of described fiberglass layer is 0.3mm, and in described first, the thickness of the bed of material is
0.6mm, in described second, the thickness of the bed of material is 0.6mm.
Embodiment 2
A kind of super-thin plastic floor, including initial bed, the middle bed of material, fiberglass layer, printing film and wearing layer.Described middle material
Layer includes in first the bed of material in the bed of material and second.Described initial bed, the bed of material in first, fiberglass layer, the bed of material, printing film in second
Set gradually with wearing layer.The described middle bed of material is made up of the raw material of following weight portion: polrvinyl chloride 100 parts, p-phthalic acid two
Monooctyl ester 32 parts, calcium-zinc composite stabilizing agent 1.5 parts, white carbon black 0.3 part, calcium carbonate 452 parts.The middle bed of material uses same as in Example 1
Prepared by method.Described fiberglass layer is latticed glass fibre.The thickness of described fiberglass layer is 0.4mm, the bed of material in described first
Thickness is 0.75mm, and in described second, the thickness of the bed of material is 0.75mm.
Embodiment 3
A kind of super-thin plastic floor, including initial bed, the middle bed of material, fiberglass layer, printing film and wearing layer.Described middle material
Layer includes in first the bed of material in the bed of material and second.Described initial bed, the bed of material in first, fiberglass layer, the bed of material, printing film in second
Set gradually with wearing layer.The described middle bed of material is made up of the raw material of following weight portion: polrvinyl chloride 102 parts, p-phthalic acid two
Monooctyl ester 33 parts, calcium-zinc composite stabilizing agent 1.8 parts, white carbon black 0.3 part, calcium carbonate 453 parts.The middle bed of material uses same as in Example 1
Prepared by method.Described fiberglass layer is latticed glass fibre.The thickness of described fiberglass layer is 0.4mm, the bed of material in described first
Thickness is 0.8mm, and in described second, the thickness of the bed of material is 0.8mm.
Embodiment 4
A kind of super-thin plastic floor, including initial bed, the middle bed of material, fiberglass layer, printing film and wearing layer.Described middle material
Layer includes in first the bed of material in the bed of material and second.Described initial bed, the bed of material in first, fiberglass layer, the bed of material, printing film in second
Set gradually with wearing layer.The described middle bed of material is made up of the raw material of following weight portion: polrvinyl chloride 104 parts, p-phthalic acid two
Monooctyl ester 34 parts, calcium-zinc composite stabilizing agent 2 parts, white carbon black 0.4 part, calcium carbonate 455 parts.The middle bed of material uses side same as in Example 1
Prepared by method.Described fiberglass layer is latticed glass fibre.The thickness of described fiberglass layer is 0.5mm, the thickness of the bed of material in described first
Degree is 0.75mm, and in described second, the thickness of the bed of material is 0.75mm.
Embodiment 5
A kind of super-thin plastic floor, including initial bed, the middle bed of material, fiberglass layer, printing film and wearing layer.Described middle material
Layer includes in first the bed of material in the bed of material and second.Described initial bed, the bed of material in first, fiberglass layer, the bed of material, printing film in second
Set gradually with wearing layer.The described middle bed of material is made up of the raw material of following weight portion: polrvinyl chloride 105 parts, p-phthalic acid two
Monooctyl ester 35 parts, calcium-zinc composite stabilizing agent 2 parts, white carbon black 0.5 part, calcium carbonate 450 parts.The middle bed of material uses side same as in Example 1
Prepared by method.Described fiberglass layer is latticed glass fibre.The thickness of described fiberglass layer is 0.6mm, the thickness of the bed of material in described first
Degree is 0.8mm, and in described second, the thickness of the bed of material is 0.8mm.
Embodiment 6
A kind of super-thin plastic floor, including initial bed, the middle bed of material, fiberglass layer, printing film and wearing layer.Described middle material
Layer includes in first the bed of material in the bed of material and second.Described initial bed, the bed of material in first, fiberglass layer, the bed of material, printing film in second
Set gradually with wearing layer.The described middle bed of material is made up of the raw material of following weight portion: polrvinyl chloride 106 parts, p-phthalic acid two
Monooctyl ester 35 parts, calcium-zinc composite stabilizing agent 2.2 parts, white carbon black 0.5 part, calcium carbonate 455 parts.The middle bed of material uses same as in Example 1
Prepared by method.Described fiberglass layer is latticed glass fibre.The thickness of described fiberglass layer is 0.3mm, the bed of material in described first
Thickness is 0.7mm, and in described second, the thickness of the bed of material is 0.7mm.
The shrinkage factor on super-thin plastic floor, hardness and the pliability of detection embodiment 1-6.
Shrinkage factor: use precision high temperature roaster HQ-WG-550 to be measured.
Hardness: use Shore durometer SLX-D to be measured.
Pliability: use scratch resistance tester RZ-706 to measure pliability, product bends rotating around 4cm cylinder and 2cm cylinder,
Check product crack conditions.
Testing result is as shown in table 1.
Table 1
Existing super-thin plastic floor, is not provided with fiberglass layer in the middle bed of material, the shrinkage factor of product is about 0.1%, hardness
Being about 65HD, pliability is poor, does not ruptures around 4cm cylinder, but ruptures around 2cm cylinder.And as shown in Table 1, the present invention surpasses
Slim plastic floor, for existing super-thin plastic floor, its shrinkage factor is substantially reduced, and hardness reduces, pliability
Also significantly improving, properties of product are more excellent.
Although the present invention is open as above with preferred embodiment, but it is not for limiting the present invention, any this area
Technical staff without departing from the spirit and scope of the present invention, may be by the method for the disclosure above and technology contents to this
Bright technical scheme makes possible variation and amendment, therefore, every content without departing from technical solution of the present invention, according to the present invention
Technical spirit any simple modification, equivalent variations and modification that above example is made, belong to technical solution of the present invention
Protection domain.
Claims (9)
1. a super-thin plastic floor, it is characterised in that include initial bed, the middle bed of material, fiberglass layer, printing film and wear-resisting
Layer, the described middle bed of material includes in first the bed of material in the bed of material and second, described initial bed, the bed of material in first, fiberglass layer, expects in second
Layer, printing film and wearing layer set gradually, and the described middle bed of material is made up of the raw material of following weight portion: polrvinyl chloride 98-106
Part, DOTP 30-35 part, calcium-zinc composite stabilizing agent 1-2.2 part, white carbon black 0.2-0.5 part, calcium carbonate 450-455
Part.
Super-thin plastic floor the most according to claim 1, it is characterised in that former by following weight portion of the described middle bed of material
Material is made: polrvinyl chloride 98 parts, DOTP 30 parts, calcium-zinc composite stabilizing agent 1 part, white carbon black 0.2 part, calcium carbonate
450 parts.
Super-thin plastic floor the most according to claim 1, it is characterised in that former by following weight portion of the described middle bed of material
Material is made: polrvinyl chloride 100 parts, DOTP 32 parts, calcium-zinc composite stabilizing agent 1.5 parts, white carbon black 0.3 part, carbonic acid
Ca45 2 parts.
Super-thin plastic floor the most according to claim 1, it is characterised in that the thickness of described fiberglass layer is 0.2mm-
0.6mm。
Super-thin plastic floor the most according to claim 4, it is characterised in that the thickness of described fiberglass layer is 0.3mm.
Super-thin plastic floor the most according to claim 1, it is characterised in that described fiberglass layer is latticed glass fibers
Dimension.
Super-thin plastic floor the most according to claim 1, it is characterised in that in described first in the bed of material and described second
The thickness of the bed of material is identical.
Super-thin plastic floor the most according to claim 1, it is characterised in that in described first, the thickness of the bed of material is 0.6-
0.8mm。
Super-thin plastic floor the most according to claim 1, it is characterised in that in described second, the thickness of the bed of material is 0.6-
0.8mm。