CN106243945A - A kind of polish lacquer being sprayed on racket - Google Patents

A kind of polish lacquer being sprayed on racket Download PDF

Info

Publication number
CN106243945A
CN106243945A CN201610766252.4A CN201610766252A CN106243945A CN 106243945 A CN106243945 A CN 106243945A CN 201610766252 A CN201610766252 A CN 201610766252A CN 106243945 A CN106243945 A CN 106243945A
Authority
CN
China
Prior art keywords
parts
resin
racket
styrene
sprayed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610766252.4A
Other languages
Chinese (zh)
Inventor
仇素文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Hanwen Sports Ltd By Share Ltd
Original Assignee
Anhui Hanwen Sports Ltd By Share Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Hanwen Sports Ltd By Share Ltd filed Critical Anhui Hanwen Sports Ltd By Share Ltd
Priority to CN201610766252.4A priority Critical patent/CN106243945A/en
Publication of CN106243945A publication Critical patent/CN106243945A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of polish lacquer being sprayed on racket, made by with raw material: alkyd resin, carbomer resin, diallyl isophthalate resin, 2,5 difluorobenzene ethylene styrene butyl acrylate things, modified plant ash, calcium oxide, 3 diethyl amino propylamines, dimethacrylate, 2 heptanone, glycidyl methacrylate, styrene.Coating of the present invention has the effect of excellence in terms of color inhibition, weather resistance, and touch feeling is good, resistance to hand perspiration, has high light feature, can be used as the Special spray coating coating of racket.

Description

A kind of polish lacquer being sprayed on racket
Technical field
The present invention relates to a kind of polish lacquer being sprayed on racket, belong to technical field of coatings.
Background technology
Shuttlecock is the motion that indoor, an outdoor are taken into account.According to the number participated in, singles and doubles can be divided into, and Emerging 3V3 rule.Racket is made up of the joint of face, dabber, handle and frame with dabber.The length of one racket is not More than 680 person of outstanding talent's rice, wherein racket handle and ball rapping bar length are less than 41 centimetres, a length of 28 centimetres of frame, a width of 23 centimetres, with The development of science and technology, the side that the development of racket is increasingly lighter towards weight, frame is increasingly harder, dabber elasticity is become better and better To development.The paint of joining being currently used for racket easily makes paint film xanthochromia aging, adhesive force occurs along with the passage of the time of use The shortcomings such as difference, loss of gloss, eclipsed, obfuscation.
Summary of the invention
For overcoming above-mentioned deficiency, present invention aim at providing a kind of polish lacquer being sprayed on racket, i.e. have Water-fast, chemical resistance good, the advantage of resistance to hand perspiration, meanwhile, also there is high shine characteristics, and this characteristic persistent period be long.
The solution of the present invention is as follows: a kind of polish lacquer being sprayed on racket, is made up of following raw material:
Alkyd resin 110-130 part, carbomer resin 30-60 part, diallyl isophthalate resin 20-28 part, 2,5-difluoro Styrene-styrene-butyl acrylate thing 15-20 part, modified plant ash 10-20 part, calcium oxide 5-8 part, 3-diethylamine Base propylamine 6-10 part, dimethacrylate 5-14 part, 2-heptanone 8-16 part, glycidyl methacrylate 1- 5 parts, styrene 8-18 part;
Described modified plant ash is prepared by following methods:
Plant ash 12-18g is joined immersion 2-3h in nano silicon aqueous solution, then uses deionized water filtration washing For neutrality;Place into sodium hydroxide solution and soak 4-5h, then be washed with deionized to neutrality;Then at 480-490 DEG C Calcining 2-3 h, lowers the temperature, pulverizes;Then add to benzene diacrylate 0.3-0.8g, ethyl cellulose 0.3-0.6 g, three Acetoxyl group vinyl silanes 0.1-0.3 g, attapulgite clay 4-8g mix, and are heated to 210-220 DEG C, and heat time heating time is 20- 30min, lowers the temperature, pulverizes, to obtain final product.
Further, it is made up of following raw material:
Alkyd resin 120 parts, carbomer resin 45 parts, diallyl isophthalate resin 22 parts, 2,5-difluorobenzene ethylene-benzene second Alkene-butyl acrylate thing 18 parts, modified plant ash 13 parts, calcium oxide 6 parts, 3-diethyl amino propylamine 7 parts, diethylene glycol two Methacrylate 9 parts, 2-heptanone 12 parts, glycidyl methacrylate 4 parts, styrene 12 parts.
Further, it is made up of following raw material:
Alkyd resin 126 parts, carbomer resin 36 parts, diallyl isophthalate resin 26 parts, 2,5-difluorobenzene ethylene-benzene second Alkene-butyl acrylate thing 16 parts, modified plant ash 18 parts, calcium oxide 5 parts, 3-diethyl amino propylamine 8 parts, diethylene glycol two Methacrylate 11 parts, 2-heptanone 96 parts, glycidyl methacrylate 3 parts, styrene 10 parts.
The production method of the polish lacquer being sprayed on racket: just alkyd resin, carbomer resin, isophthalic acid Diallyl phthalate resin, 2,5-difluorobenzene ethylene-stryene-butyl acrylate thing are 600-800 rev/min of lower mixed at high speed 10-15min;Add except cinnamic clout is at 900-1100 rev/min of lower mixed at high speed 30-40 min;Add benzene second Alkene, mixes 5-10 min under 400-500 rev/min, to obtain final product.
Coating of the present invention has the effect of excellence in terms of color inhibition, weather resistance, and touch feeling is good, and resistance to hand perspiration has High light feature, can be used as the Special spray coating coating of racket.
Detailed description of the invention
Below in conjunction with embodiment, the present invention will be further described.
The preparation of modified plant ash:
Plant ash 12-18g is joined immersion 2-3h in nano silicon aqueous solution, then uses deionized water filtration washing For neutrality;Place into sodium hydroxide solution and soak 4-5h, then be washed with deionized to neutrality;Then at 480-490 DEG C Calcining 2-3 h, lowers the temperature, pulverizes;Then add to benzene diacrylate 0.3-0.8g, ethyl cellulose 0.3-0.6 g, three Acetoxyl group vinyl silanes 0.1-0.3 g, attapulgite clay 4-8g mix, and are heated to 210-220 DEG C, and heat time heating time is 20- 30min, lowers the temperature, pulverizes, to obtain final product.
Embodiment 1
A kind of polish lacquer being sprayed on racket, is made up of following raw material:
Alkyd resin 120 parts, carbomer resin 45 parts, diallyl isophthalate resin 22 parts, 2,5-difluorobenzene ethylene-benzene second Alkene-butyl acrylate thing 18 parts, modified plant ash 13 parts, calcium oxide 6 parts, 3-diethyl amino propylamine 7 parts, diethylene glycol two Methacrylate 9 parts, 2-heptanone 12 parts, glycidyl methacrylate 4 parts, styrene 12 parts.
The production method of the polish lacquer being sprayed on racket: just alkyd resin, carbomer resin, isophthalic acid Diallyl phthalate resin, 2,5-difluorobenzene ethylene-stryene-butyl acrylate thing are 600-800 rev/min of lower mixed at high speed 10-15min;Add except cinnamic clout is at 900-1100 rev/min of lower mixed at high speed 30-40 min;Add benzene second Alkene, mixes 5-10 min under 400-500 rev/min, to obtain final product.
Embodiment 2
A kind of polish lacquer being sprayed on racket, is made up of following raw material:
Alkyd resin 126 parts, carbomer resin 36 parts, diallyl isophthalate resin 26 parts, 2,5-difluorobenzene ethylene-benzene second Alkene-butyl acrylate thing 16 parts, modified plant ash 18 parts, calcium oxide 5 parts, 3-diethyl amino propylamine 8 parts, diethylene glycol two Methacrylate 11 parts, 2-heptanone 96 parts, glycidyl methacrylate 3 parts, styrene 10 parts.
Production method is with embodiment 1.
Embodiment 3
A kind of polish lacquer being sprayed on racket, is made up of following raw material:
Alkyd resin 128 parts, carbomer resin 34 parts, diallyl isophthalate resin 25 parts, 2,5-difluorobenzene ethylene-benzene second Alkene-butyl acrylate thing 17 parts, modified vegetation 18 parts, calcium oxide 6 parts, 3-diethyl amino propylamine 9 parts, diethylene glycol diformazan Base acrylate 7 parts, 2-heptanone 12 parts, glycidyl methacrylate 3 parts, styrene 15 parts;
Production method is with embodiment 1.
Comparative example 1
It is with at embodiment 1 difference, does not contains modified plant ash.
The polish lacquer being sprayed at above-described embodiment 1-3, comparative example 1 gained on racket is tested, and result is such as Shown in following table.
Embodiment 1 Embodiment 2 Embodiment 3 Comparative example 1 Common polish lacquer
Finish fineness (μm) 18 15 16 28 42±5
60 ° of gloss (100%, 48h) 99.9 99.5 99.8 91 81±3
Covering power Preferably Preferably Preferably Preferably Typically
Although the detailed description of the invention to the present invention gives detailed description and illustrates above, but it should be noted that We can carry out various equivalence according to the conception of the present invention to above-mentioned embodiment and change and amendment, and function produced by it is made With still without departing from description contained spiritual time, all should be within protection scope of the present invention.

Claims (4)

1. the polish lacquer being sprayed on racket, it is characterised in that be made up of following raw material:
Alkyd resin 110-130 part, carbomer resin 30-60 part, diallyl isophthalate resin 20-28 part, 2,5-difluoro Styrene-styrene-butyl acrylate thing 15-20 part, modified plant ash 10-20 part, calcium oxide 5-8 part, 3-diethylamine Base propylamine 6-10 part, dimethacrylate 5-14 part, 2-heptanone 8-16 part, glycidyl methacrylate 1- 5 parts, styrene 8-18 part;
Described modified plant ash is prepared by following methods:
Plant ash 12-18g is joined immersion 2-3h in nano silicon aqueous solution, then uses deionized water filtration washing For neutrality;Place into sodium hydroxide solution and soak 4-5h, then be washed with deionized to neutrality;Then at 480-490 DEG C Calcining 2-3 h, lowers the temperature, pulverizes;Then add to benzene diacrylate 0.3-0.8g, ethyl cellulose 0.3-0.6 g, three Acetoxyl group vinyl silanes 0.1-0.3 g, attapulgite clay 4-8g mix, and are heated to 210-220 DEG C, and heat time heating time is 20- 30min, lowers the temperature, pulverizes, to obtain final product.
A kind of polish lacquer being sprayed on racket the most according to claim 1, it is characterised in that by following weight portion Raw material is made:
Alkyd resin 120 parts, carbomer resin 45 parts, diallyl isophthalate resin 22 parts, 2,5-difluorobenzene ethylene-benzene second Alkene-butyl acrylate thing 18 parts, modified plant ash 13 parts, calcium oxide 6 parts, 3-diethyl amino propylamine 7 parts, diethylene glycol two Methacrylate 9 parts, 2-heptanone 12 parts, glycidyl methacrylate 4 parts, styrene 12 parts.
A kind of polish lacquer being sprayed on racket the most according to claim 1, it is characterised in that by following weight portion Raw material is made:
Alkyd resin 126 parts, carbomer resin 36 parts, diallyl isophthalate resin 26 parts, 2,5-difluorobenzene ethylene-benzene second Alkene-butyl acrylate thing 16 parts, modified plant ash 18 parts, calcium oxide 5 parts, 3-diethyl amino propylamine 8 parts, diethylene glycol two Methacrylate 11 parts, 2-heptanone 96 parts, glycidyl methacrylate 3 parts, styrene 10 parts.
4. according to the production method of the arbitrary described polish lacquer being sprayed on racket of claim 1-3, it is characterised in that Step is as follows:
By alkyd resin, carbomer resin, diallyl isophthalate resin, 2,5-difluorobenzene ethylene-stryene-acrylic acid fourth Ester polymer is 600-800 rev/min of lower mixed at high speed 10-15min;Add except cinnamic clout 900-1100 turn/ Minute lower mixed at high speed 30-40 min;Add styrene, under 400-500 rev/min, mix 5-10 min, to obtain final product.
CN201610766252.4A 2016-08-30 2016-08-30 A kind of polish lacquer being sprayed on racket Pending CN106243945A (en)