CN106221620A - A kind of cold-resistant modified polyvinyl chloride adhesive and preparation method thereof - Google Patents
A kind of cold-resistant modified polyvinyl chloride adhesive and preparation method thereof Download PDFInfo
- Publication number
- CN106221620A CN106221620A CN201610604628.1A CN201610604628A CN106221620A CN 106221620 A CN106221620 A CN 106221620A CN 201610604628 A CN201610604628 A CN 201610604628A CN 106221620 A CN106221620 A CN 106221620A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyvinyl chloride
- cold
- modified polyvinyl
- coupling agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of cold-resistant modified polyvinyl chloride adhesive and preparation method thereof, this adhesive is prepared from by the raw material of following weight portion: superchlorinated polyvinyl chloride resin 13 17 parts, 1,2 dichloroethanes 59 66 parts, nano-calcium carbonate 35 parts, triethyl citrate 11 17 parts, dehydroabietic acid 20 ester 6 14 parts, neoprene latex 7 17 parts, alkylphenol polyoxyethylene 25 parts, nano silicon 10 15 parts, heat filling 10 20 parts, infrared external reflection titanium dioxide 0.7 5.3 parts, light stabilizer 0.2 1 parts, coupling agent 0.1 0.2 parts.Gained adhesive of the present invention has excellent weatherability, tolerance to cold and toughness, and comprehensive strength is higher.
Description
Technical field
The present invention relates to field of material preparation, be specifically related to a kind of cold-resistant modified polyvinyl chloride adhesive and preparation side thereof
Method.
Background technology
Polyvinyl chloride film adhesive is applicable to bonding and the repairing of polyvinyl chloride product, and following PVC water channel, handrail are viscous
Connect, pre-fixing of electroplating bath, but existing polyvinyl chloride film adhesive has that weatherability is poor, tolerance to cold is low, toughness is low, comprehensive
The shortcomings such as intensity is low, greatly limit its range of application.
Summary of the invention
For solving the problems referred to above, the invention provides a kind of cold-resistant modified polyvinyl chloride adhesive and preparation method thereof, institute
Obtaining adhesive and have excellent weatherability, tolerance to cold and toughness, comprehensive strength is higher.
For achieving the above object, the technical scheme that the present invention takes is:
A kind of cold-resistant modified polyvinyl chloride adhesive, is prepared from by the raw material of following weight portion:
Superchlorinated polyvinyl chloride resin 13-17 part, 1,2-dichloroethanes 59-66 part, nano-calcium carbonate 3-5 part, triethyl citrate
11-17 part, dehydroabietic acid 20 ester 6-14 part, neoprene latex 7-17 part, alkylphenol polyoxyethylene 2-5 part, nanometer titanium dioxide
Silicon 10-15 part, heat filling 10-20 part, infrared external reflection titanium dioxide 0.7-5.3 part, light stabilizer 0.2-1 part, coupling agent
0.1-0.2 part.
Preferably, the raw material of following weight portion it is prepared from:
Superchlorinated polyvinyl chloride resin 15 parts, 1,2-dichloroethanes 62.5 parts, nano-calcium carbonate 4 parts, triethyl citrate 14 parts, de-
Hydrogen abietic acid 20 ester 10 parts, neoprene latex 12 parts, alkylphenol polyoxyethylene 3.5 parts, nano silicon 12.5 parts, heat conduction are filled out
Expect 15 parts, infrared external reflection titanium dioxide 3 parts, light stabilizer 0.6 part, coupling agent 0.15 part.
Wherein, described heat filling is that magnesium oxide, aluminium hydroxide, boron nitride, aluminium nitride in mass ratio 1: 2: 3: 1 mixes institute
, the particle diameter of described heat filling is more than 98% in 0.5um-2.0um, purity.
Wherein, described light stabilizer be salicylate, benzophenone, triazines, benzotriazole UV absorbent with
And one or more mixture in hindered amines free radical scavenger.
Wherein, described infrared external reflection titanium dioxide particle diameter is 1100nm-1600nm, TiO2Content is 80%-90%, table
Roll cover SiO2With Al2O3Content be 10-20%.
Wherein, described coupling agent is that silane coupler, titanate coupling agent in mass ratio 1: 1 mixes gained.
The preparation method of above-mentioned a kind of cold-resistant modified polyvinyl chloride adhesive, comprises the steps:
S1, formula as described in claim 1-6 weigh each component;
S2, by the nano silicon weighed by supersonic oscillations equipment be scattered in pure water formation nanometer titanium dioxide
Silicon particle dispersion;
S3, step S2 gained dispersion liquid is injected double screw extruder by liquid feeding pump, with superchlorinated polyvinyl chloride resin altogether
Mixed, it is heated to water and all evaporates, obtain mixture;
S4, mixture is placed in homogenizer, adds 1 weighed, 2-dichloroethanes, nano-calcium carbonate, citric acid
Triethyl, dehydroabietic acid 20 ester, neoprene latex, alkylphenol polyoxyethylene, heat filling, infrared external reflection titanium dioxide, light
Stabilizer, coupling agent, stir 10-30min, discharging, is heated to 80 DEG C~during 95 DEG C of temperature, is kept stirring for 25~45min, then
Stop heating, naturally cool to room temperature, to obtain final product.
The method have the advantages that
By triethyl citrate, the synergism of dehydroabietic acid 20 ester, greatly strengthen the tolerance to cold of binding agent;Logical
Cross the interpolation of alkylphenol polyoxyethylene so that the binding agent corrosion resistance of gained improves;The interpolation of nano silicon so that
The binding agent of gained can keep excellent toughness during life-time service all the time;Use infrared external reflection titanium dioxide, Ke Yi great
The visible ray of amplitude reflection sunlight and infrared part energy, the collaborative contribution of the heat release of heat filling, can make relatively in addition
The surface temperature of binding agent is greatly reduced, is greatly improved its weatherability.
Detailed description of the invention
In order to make objects and advantages of the present invention clearer, below in conjunction with embodiment, the present invention is carried out further
Describe in detail.Should be appreciated that specific embodiment described herein, only in order to explain the present invention, is not used to limit this
Bright.
Heat filling used in following example is magnesium oxide, aluminium hydroxide, boron nitride, aluminium nitride in mass ratio 1:
2: 3: 1 mixing gained, the particle diameter of described heat filling is more than 98% in 0.5um-2.0um, purity;Described light stabilizer is water
One in poplar acid esters, benzophenone, triazines, the UV absorbent of benzotriazole and hindered amines free radical scavenger or
Multiple mixture;Described infrared external reflection titanium dioxide particle diameter is 1100nm-1600nm, TiO2Content is 80%-90%, surface
Clad SiO2With Al2O3Content be 10-20%;Described coupling agent is silane coupler, titanate coupling agent in mass ratio 1:
1 mixing gained.
Embodiment 1
A kind of cold-resistant modified polyvinyl chloride adhesive, is prepared from by the raw material of following weight portion:
Superchlorinated polyvinyl chloride resin 13 parts, 1,2-dichloroethanes 59 parts, nano-calcium carbonate 3 parts, triethyl citrate 11 parts, dehydrogenation
Abietic acid 20 ester 6 parts, neoprene latex 7 parts, alkylphenol polyoxyethylene 2 parts, nano silicon 10 parts, heat filling 10 parts,
Infrared external reflection titanium dioxide 0.7 part, light stabilizer 0.2 part, coupling agent 0.1 part.
Embodiment 2
A kind of cold-resistant modified polyvinyl chloride adhesive, is prepared from by the raw material of following weight portion:
Superchlorinated polyvinyl chloride resin 15 parts, 1,2-dichloroethanes 62.5 parts, nano-calcium carbonate 4 parts, triethyl citrate 14 parts, de-
Hydrogen abietic acid 20 ester 10 parts, neoprene latex 12 parts, alkylphenol polyoxyethylene 3.5 parts, nano silicon 12.5 parts, heat conduction are filled out
Expect 15 parts, infrared external reflection titanium dioxide 3 parts, light stabilizer 0.6 part, coupling agent 0.15 part.
Embodiment 3
A kind of cold-resistant modified polyvinyl chloride adhesive, is prepared from by the raw material of following weight portion:
Superchlorinated polyvinyl chloride resin 17 parts, 1,2-dichloroethanes 66 parts, nano-calcium carbonate 5 parts, triethyl citrate 17 parts, dehydrogenation
Abietic acid 20 ester 14 parts, neoprene latex 17 parts, alkylphenol polyoxyethylene 5 parts, nano silicon 15 parts, heat filling 20
Part, infrared external reflection titanium dioxide 5.3 parts, light stabilizer 1 part, coupling agent 0.2 part.
The embodiment of the present invention additionally provides the preparation method of a kind of cold-resistant modified polyvinyl chloride adhesive, including walking as follows
Rapid:
S1, formula as described in claim 1-6 weigh each component;
S2, by the nano silicon weighed by supersonic oscillations equipment be scattered in pure water formation nanometer titanium dioxide
Silicon particle dispersion;
S3, step S2 gained dispersion liquid is injected double screw extruder by liquid feeding pump, with superchlorinated polyvinyl chloride resin altogether
Mixed, it is heated to water and all evaporates, obtain mixture;
S4, mixture is placed in homogenizer, adds 1 weighed, 2-dichloroethanes, nano-calcium carbonate, citric acid
Triethyl, dehydroabietic acid 20 ester, neoprene latex, alkylphenol polyoxyethylene, heat filling, infrared external reflection titanium dioxide, light
Stabilizer, coupling agent, stir 10-30min, discharging, is heated to 80 DEG C~during 95 DEG C of temperature, is kept stirring for 25~45min, then
Stop heating, naturally cool to room temperature, to obtain final product.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For Yuan, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications also should
It is considered as protection scope of the present invention.
Claims (7)
1. a cold-resistant modified polyvinyl chloride adhesive, it is characterised in that be prepared from by the raw material of following weight portion:
Superchlorinated polyvinyl chloride resin 13-17 part, 1,2-dichloroethanes 59-66 part, nano-calcium carbonate 3-5 part, triethyl citrate 11-17
Part, dehydroabietic acid 20 ester 6-14 part, neoprene latex 7-17 part, alkylphenol polyoxyethylene 2-5 part, nano silicon 10-
15 parts, heat filling 10-20 part, infrared external reflection titanium dioxide 0.7-5.3 part, light stabilizer 0.2-1 part, coupling agent 0.1-0.2
Part.
2. modified polyvinyl chloride adhesive as claimed in claim 1 a kind of cold-resistant, it is characterised in that former by following weight portion
Material is prepared from:
Superchlorinated polyvinyl chloride resin 15 parts, 1,2-dichloroethanes 62.5 parts, nano-calcium carbonate 4 parts, triethyl citrate 14 parts, dehydrogenation fir
Acid 20 ester 10 parts, neoprene latex 12 parts, alkylphenol polyoxyethylene 3.5 parts, nano silicon 12.5 parts, heat filling 15
Part, infrared external reflection titanium dioxide 3 parts, light stabilizer 0.6 part, coupling agent 0.15 part.
3. a kind of cold-resistant modified polyvinyl chloride adhesive as claimed in claim 1, it is characterised in that described heat filling is oxygen
Changing magnesium, aluminium hydroxide, boron nitride, aluminium nitride in mass ratio 1: 2: 3: 1 and mix gained, the particle diameter of described heat filling is at 0.5um-
2.0um, purity is more than 98%.
4. a kind of cold-resistant modified polyvinyl chloride adhesive as claimed in claim 1, it is characterised in that described light stabilizer is
One in salicylate, benzophenone, triazines, the UV absorbent of benzotriazole and hindered amines free radical scavenger
Or multiple mixture.
5. a kind of cold-resistant modified polyvinyl chloride adhesive as claimed in claim 1, it is characterised in that described infrared external reflection two
Titanium oxide particle diameter is 1100nm-1600nm, TiO2Content is 80%-90%, surface coating layer SiO2With Al2O3Content be 10-
20%.
6. a kind of cold-resistant modified polyvinyl chloride adhesive as claimed in claim 1, it is characterised in that described coupling agent is silane
Coupling agent, titanate coupling agent in mass ratio 1: 1 mixes gained.
7. the preparation method of a kind of cold-resistant modified polyvinyl chloride adhesive as described in any one of claim 1-6, its feature exists
In, comprise the steps:
S1, formula as described in claim 1-6 weigh each component;
S2, by the nano silicon weighed by supersonic oscillations equipment be scattered in pure water formation nano silicon grain
Sub-dispersion liquid;
S3, by step S2 gained dispersion liquid by liquid feeding pump inject double screw extruder, with superchlorinated polyvinyl chloride resin be blended, add
Heat is all evaporated to water, obtains mixture;
S4, mixture is placed in homogenizer, adds 1 weighed, 2-dichloroethanes, nano-calcium carbonate, Fructus Citri Limoniae triethylenetetraminehexaacetic acid
Ester, dehydroabietic acid 20 ester, fluorine fourth latex, alkylphenol polyoxyethylene, heat filling, infrared external reflection titanium dioxide, light are stable
Agent, coupling agent, stir 10-30min, discharging, is heated to 80 DEG C~during 95 DEG C of temperature, is kept stirring for 25~45min, then stops
Heating, naturally cools to room temperature, to obtain final product.