CN106221089A - A kind of politef waterproofing membrane and preparation method thereof - Google Patents
A kind of politef waterproofing membrane and preparation method thereof Download PDFInfo
- Publication number
- CN106221089A CN106221089A CN201610754400.0A CN201610754400A CN106221089A CN 106221089 A CN106221089 A CN 106221089A CN 201610754400 A CN201610754400 A CN 201610754400A CN 106221089 A CN106221089 A CN 106221089A
- Authority
- CN
- China
- Prior art keywords
- mentioned
- minute
- politef
- stirred
- joined
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of politef waterproofing membrane, it is made up of the raw material of following weight parts: mannitol 34, butyl acrylate 46, Dodecyl trimethyl ammonium chloride 12, politef 100 130, ten difluoro heptyl propyl trimethoxy silicanes 0.5 2, cellulose phosphate 47, DAA 35, calcium palmitate 12, dialkyl group is to biphenol 0.6 1, 2 mercapto benzimidazoles 0.7 1, β hydroxyalkyl amide 0.8 1, APP 23, azodiisobutyronitrile 0.1 0.2, dimethylformamide 80 90, montmorillonite powder 56, aphthenic acids lithium 0.1 0.2.The membrane waterproofing of the present invention is good, and surface toughness is good, and combination property is superior.
Description
Technical field
The present invention relates to waterproofing membrane technical field, particularly relate to a kind of politef waterproofing membrane and preparation side thereof
Method.
Background technology
The anti-thin film of politef is that a kind of fluorine that employs replaces the synthetic macromolecule of all hydrogen atoms in polyethylene
Material.This material has antiacid alkali resistant, the feature of anti-various organic solvents, is practically insoluble in all of solvent.Meanwhile, waterproof
Ventilated membrane has resistant to elevated temperatures feature, and its coefficient of friction is extremely low, so after lubrication can being made, also become easy clean pot and
The preferable coating of water pipe internal layer;
Waterproof ventilated membrane is in a lot of sector applications widely: modern society's automotive operation is universal, can meet in transportation
To different weather and road conditions.Car light is externally exposed in environment all the time, and cloud, sleet, mince in road surface and dirt all can affect
The illumination of car light, thus affect the degree of safety of the driving process of vehicle.The rapid drawdown of external temperature can cause the decline of internal pressure,
Make equipment easily suck pollutant and increase fogging, ultimately cause car light fault.Waterproof ventilated membrane can provide persistently to car light
Protection, from the intrusion of external moisture, dust, greasy dirt and other dirts.The airing function that product is unique simultaneously is along with pressure
Change carries out respiratory exchange, thus reduces the pressure on sealing member, extends the service life of product.In terms of sensor device:
Waterproof and breathable product can effectively resist adverse effect produced by the pressure reduction that variations in temperature causes.Use the waterproof ventilated membrane can be
Rapid equalisation housing external and internal pressure when ambient temperature and pressure change, in gas sensor and electrochemical sensor, waterproof
Gas product can prevent dust, dirt or liquid from invading sensing head.Meanwhile, waterproof ventilated membrane can allow gas pass through thin film immediately, from
And guarantee that sensor response speed keeps constant, prevent measurement result from mistake occurring and postpones.Communication equipment aspect out of doors: family
After outer communication equipment is mounted with waterproof ventilated membrane product, apparatus casing will no longer be constituted by the pressure reduction caused due to variations in temperature
Negative effect because waterproof and breathable product can when ambient temperature and pressure change rapid equalisation housing external and internal pressure;
But the functional comparison of conventional waterproof ventilated membrane is single, and have add the raw materials such as poisonous plasticizer, environmental protection
Property is poor, and the range of ventilated membrane is less, and some impact strengths are low, is easily damaged, and some resistances to ag(e)ing are poor, service life
Short, therefore, the waterproofing membrane of research higher performance just seems particularly necessary.
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of politef waterproofing membrane and system thereof
Preparation Method.
The present invention is achieved by the following technical solutions:
A kind of politef waterproofing membrane, it is made up of the raw material of following weight parts:
Mannitol 3-4, butyl acrylate 4-6, Dodecyl trimethyl ammonium chloride 1-2, politef 100-130, ten
Difluoro heptyl propyl trimethoxy silicane 0.5-2, cellulose phosphate 4-7, DAA 3-5, calcium palmitate 1-2, dialkyl group pair
Biphenol 0.6-1,2-mercapto benzimidazole 0.7-1, beta-hydroxy alkylamide 0.8-1, APP 2-3, azodiisobutyronitrile
0.1-0.2, dimethylformamide 80-90, montmorillonite powder 5-6, aphthenic acids lithium 0.1-0.2.
The preparation method of a kind of described politef waterproofing membrane, comprises the following steps:
(1) above-mentioned cellulose phosphate is joined in its weight 27-30 times, 35-40% ethanol solution, at 60-70
Insulated and stirred 30-40 minute at DEG C, adds 2-mercapto benzimidazole, and stirring, to room temperature, obtains fiber dispersion;
(2) above-mentioned Dodecyl trimethyl ammonium chloride being joined in the deionized water of its weight 10-14 times, stirring is all
Even, add beta-hydroxy alkylamide, insulated and stirred 6-10 minute at 80-90 DEG C, add above-mentioned mannitol, stirring, to room temperature, obtains
Amide dispersion liquid;
(3) above-mentioned montmorillonite powder is joined in the sodium hydroxide solution that concentration is 4-6% and soak 1-2 hour, filter, will
Precipitation washing 3-4 time, mixes with calcium palmitate, DAA, preheats 3-5 minute, join amide dispersion liquid at 70-80 DEG C
In, 100-200 rev/min is stirred 30-40 minute, adds above-mentioned fiber dispersion, and 300-400 rev/min is stirred 7-10 minute, mistake
Filter, will be vacuum dried 1-2 hour at being deposited in 40-50 DEG C, obtains pretreatment powder;
(4) biphenol is joined in dimethylformamide by above-mentioned dialkyl group, stir, add above-mentioned pretreatment powder
Material, ultrasonic 3-5 minute, is passed through nitrogen, adds butyl acrylate, azodiisobutyronitrile, ten difluoro heptyl propyl trimethoxy silicon
Alkane, insulated and stirred 4-5 hour at 75-80 DEG C, add APP, precipitation dehydrated alcohol, to room temperature, sucking filtration, is washed by stirring
3-4 time, it is vacuum dried 30-40 minute at 80-90 DEG C, obtains fluorinated modified material;
(5) above-mentioned fluorinated modified material is mixed with remaining each raw material, stir, through film blow molding machine blow molding,
Obtain described thin film.
The invention have the advantage that
Montmorillonite powder is processed by the present invention by beta-hydroxy alkylamide, is then blended with cellulose phosphate, effectively improves
The surface strength of blend composition and toughness, modified finally by ten difluoro heptyl propyl trimethoxy silicanes, improve it with many
The compatibility between polymers and the hydrophobicity of finished surface, the membrane waterproofing of the present invention is good, and surface toughness is good, combination property
Superior.
Detailed description of the invention
A kind of politef waterproofing membrane, it is made up of the raw material of following weight parts:
Mannitol 3, butyl acrylate 4, Dodecyl trimethyl ammonium chloride 1, politef 100, ten difluoro heptyl third
Base trimethoxy silane 0.5, cellulose phosphate 4, DAA 3, calcium palmitate 1, dialkyl group are to biphenol 0.6,2-mercapto
Benzimidazole 0.7, beta-hydroxy alkylamide 0.8, APP 2, azodiisobutyronitrile 0.1, dimethylformamide 80, montmorillonite powder
5, aphthenic acids lithium 0.1.
The preparation method of a kind of described politef waterproofing membrane, comprises the following steps:
(1) above-mentioned cellulose phosphate is joined in its weight 27 times, the ethanol solution of 35%, be incubated at 60 DEG C and stir
Mixing 30 minutes, add 2-mercapto benzimidazole, stirring, to room temperature, obtains fiber dispersion;
(2) above-mentioned Dodecyl trimethyl ammonium chloride is joined in the deionized water of its weight 10 times, stir, add
Enter beta-hydroxy alkylamide, insulated and stirred 6 minutes at 80 DEG C, add above-mentioned mannitol, stirring, to room temperature, obtains amide dispersion liquid;
(3) above-mentioned montmorillonite powder is joined in the sodium hydroxide solution that concentration is 4% and soak 1 hour, filter, will precipitation
Wash 3 times, mix with calcium palmitate, DAA, preheat 3 minutes at 70 DEG C, join in amide dispersion liquid, 100 revs/min
Stirring 30 minutes, add above-mentioned fiber dispersion, 300 revs/min are stirred 7 minutes, filter, and will be deposited at 40 DEG C vacuum drying 1
Hour, obtain pretreatment powder;
(4) biphenol is joined in dimethylformamide by above-mentioned dialkyl group, stir, add above-mentioned pretreatment powder
Material, ultrasonic 3 minutes, is passed through nitrogen, adds butyl acrylate, azodiisobutyronitrile, ten difluoro heptyl propyl trimethoxy silicanes,
Insulated and stirred 4 hours at 75 DEG C, add APP, and precipitation dehydrated alcohol, to room temperature, sucking filtration, is washed 3 times, 80 by stirring
It is vacuum dried 30 minutes at DEG C, obtains fluorinated modified material;
(5) above-mentioned fluorinated modified material is mixed with remaining each raw material, stir, through film blow molding machine blow molding,
Obtain described thin film.
Performance test:
Air transmission coefficient (ml/min/1PSI): 400;
Aqueous vapor conductivity (g/24h): 0.2058.
Claims (2)
1. a politef waterproofing membrane, it is characterised in that it is made up of the raw material of following weight parts:
Mannitol 3-4, butyl acrylate 4-6, Dodecyl trimethyl ammonium chloride 1-2, politef 100-130, ten difluoros
Heptyl propyl trimethoxy silicane 0.5-2, cellulose phosphate 4-7, DAA 3-5, calcium palmitate 1-2, dialkyl group are to hexichol
Phenol 0.6-1,2-mercapto benzimidazole 0.7-1, beta-hydroxy alkylamide 0.8-1, APP 2-3, azodiisobutyronitrile 0.1-
0.2, dimethylformamide 80-90, montmorillonite powder 5-6, aphthenic acids lithium 0.1-0.2.
2. the preparation method of a politef waterproofing membrane as claimed in claim 1, it is characterised in that include following step
Rapid:
(1) above-mentioned cellulose phosphate is joined in its weight 27-30 times, 35-40% ethanol solution, at 60-70 DEG C
Insulated and stirred 30-40 minute, adds 2-mercapto benzimidazole, and stirring, to room temperature, obtains fiber dispersion;
(2) above-mentioned Dodecyl trimethyl ammonium chloride is joined in the deionized water of its weight 10-14 times, stir, add
Enter beta-hydroxy alkylamide, insulated and stirred 6-10 minute at 80-90 DEG C, add above-mentioned mannitol, stirring, to room temperature, obtains amide and divides
Dissipate liquid;
(3) above-mentioned montmorillonite powder is joined in the sodium hydroxide solution that concentration is 4-6% and soak 1-2 hour, filter, will precipitation
Wash 3-4 time, mix with calcium palmitate, DAA, preheat 3-5 minute at 70-80 DEG C, join in amide dispersion liquid,
100-200 rev/min is stirred 30-40 minute, adds above-mentioned fiber dispersion, and 300-400 rev/min is stirred 7-10 minute, filters, will
It is vacuum dried 1-2 hour at being deposited in 40-50 DEG C, obtains pretreatment powder;
(4) biphenol is joined in dimethylformamide by above-mentioned dialkyl group, stirs, add above-mentioned pretreatment powder,
Ultrasonic 3-5 minute, it is passed through nitrogen, adds butyl acrylate, azodiisobutyronitrile, ten difluoro heptyl propyl trimethoxy silicanes,
Insulated and stirred 4-5 hour at 75-80 DEG C, adds APP, and precipitation dehydrated alcohol, to room temperature, sucking filtration, is washed 3-4 by stirring
Secondary, it is vacuum dried 30-40 minute at 80-90 DEG C, obtains fluorinated modified material;
(5) above-mentioned fluorinated modified material is mixed with remaining each raw material, stir, through film blow molding machine blow molding, to obtain final product
Described thin film.