CN107857961A - A kind of outdoor photoactivation medical package film and preparation method thereof - Google Patents
A kind of outdoor photoactivation medical package film and preparation method thereof Download PDFInfo
- Publication number
- CN107857961A CN107857961A CN201711275001.7A CN201711275001A CN107857961A CN 107857961 A CN107857961 A CN 107857961A CN 201711275001 A CN201711275001 A CN 201711275001A CN 107857961 A CN107857961 A CN 107857961A
- Authority
- CN
- China
- Prior art keywords
- stirs
- added
- taken
- photoactivation
- outdoor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of outdoor photoactivation medical package film, it is made up of the raw material of following weight parts:Dibatyl phithalate 46, butyl titanate 40 50, tricalcium silicate 23, rosin 35, dibutyl maleate 24,2 mercaptobenzimidazoles 0.7 1, castor oil acid calcium 12, uvioresistant poly polymer solution 10 14,10 15% ammoniacal liquor 56, polytetrafluoroethylene (PTFE) 110 120, the uvioresistant poly polymer solution and Abietyl modified colloidal sol are blended the present invention, serve the effect of enhancing viscosity, effectively raise the resistance to overturning of packaging film, the uvioresistant poly compound that the present invention adds can effectively improve the resistance effect to ultraviolet, prevent packaging film quick aging.
Description
Technical field
The invention belongs to packaging film field, and in particular to a kind of outdoor photoactivation medical package film and preparation method thereof.
Background technology
Plastic sheeting is the common daily necessities of present people, and plastic sheeting has transparent good, the moist good, heat resistance of resistance
The advantages that excellent, easy to use, cheap, is widely used in all trades and professions, and plastic sheeting in the market is mainly with poly-
Based on the plastic sheetings such as ethene, polytetrafluoroethylene (PTFE), makrolon, but some products occur fold, poor transparency, thickness
Uneven, the problems such as film bubble flake is more, meanwhile, with the gradual enhancing of people's environmental consciousness, the recycling rate of waterused of plastic foil
With regard to more and more higher, therefore, the requirement for its tearing toughness is also just higher.
The content of the invention
In view of the defects and deficiencies of the prior art, the present invention intends to provide a kind of outdoor photoactivation medical package
Film and preparation method thereof.
To achieve the above object, the present invention uses following technical scheme:
A kind of outdoor photoactivation medical package film, it is made up of the raw material of following weight parts:
Dibatyl phithalate 4-6, butyl titanate 40-50, tricalcium silicate 2-3, rosin 3-5, dibutyl maleate 2-
4th, 2-mercaptobenzimidazole 0.7-1, castor oil acid calcium 1-2, uvioresistant poly polymer solution 10-14,10-15% ammoniacal liquor 5-6, poly-
Tetrafluoroethene 110-120.
What described uvioresistant poly polymer solution was made up of the raw material of following weight parts:
Methyl acrylate 17-20, EMA 20-30, BTA 1-2, divinylbenzene 0.1-0.2,
Polyacrylamide 3-4, initiator 0.7-1.
The preparation method of described uvioresistant poly polymer solution, comprises the following steps:
(1) initiator is taken, is added in the deionized water of 20-30 times of its weight, stirs;
(2) BTA is taken, is added in the absolute ethyl alcohol of 4-6 times of its weight, stirs, adds divinyl
Benzene, stir, obtain crosslinker solution;
(3) polyacrylamide is taken, is added in the deionized water of 20-30 times of its weight, stirs;
(4) methyl acrylate, EMA mixing are taken, is added to the deionized water of 10-13 times of compound weight
In, stir, be sent in reactor, be passed through nitrogen, regulation temperature of reaction kettle is 70-75 DEG C, and it is molten that above-mentioned initiator is added dropwise
Liquid, rear insulated and stirred 3-4 hours are added dropwise, add above-mentioned crosslinker solution, rise temperature is 80-85 DEG C, insulated and stirred 40-50
Minute, discharging, mix, stirred to normal temperature with above-mentioned polyacrylamide solution, produce the uvioresistant poly polymer solution.
Described initiator is ammonium persulfate.
A kind of preparation method of outdoor photoactivation medical package film, comprises the following steps:
(1) rosin is taken, is heated and softened, is added in the absolute ethyl alcohol of 5-8 times of its weight, stirs, adds 2- sulfydryls
Benzimidazole, 10-20 minutes are incubated at 70-75 DEG C, obtain rosin alcoholic solution;
(2) butyl titanate is taken, is added in the deionized water of 10-17 times of its weight, stirs, it is molten to add abienol
Liquid, stir, 10-15% ammoniacal liquor is added dropwise, rear stirring reaction 3-4 hours are added dropwise, obtain Abietyl modified colloidal sol;
(3) above-mentioned Abietyl modified colloidal sol is taken, mixes, stirs with uvioresistant poly polymer solution, adds castor oil acid calcium,
The insulated and stirred 10-20 minutes at 90-95 DEG C, filtering, precipitation is washed, 20-30 minutes are dried at 70-75 DEG C of vacuum, are obtained poly-
Polymer modified colloidal sol;
(4) above-mentioned polymer modification colloidal sol is taken, mixes, stirs with remaining each raw material, melt, spin-coating film, produce.
Advantages of the present invention:
Using methyl acrylate, EMA as mix monomer, BTA adulterates the present invention for uvioresistant
Agent, it polymerize under initiator effect, obtains uvioresistant poly polymer solution, the present invention changes the uvioresistant poly polymer solution with rosin
Property colloidal sol blending, serve the effect of enhancing viscosity, effectively raise the resistance to overturning of packaging film, what the present invention added
Uvioresistant poly compound can effectively improve the resistance effect to ultraviolet, prevent packaging film quick aging.
Embodiment
Embodiment 1
A kind of outdoor photoactivation medical package film, it is made up of the raw material of following weight parts:
Dibatyl phithalate 6, butyl titanate 50, tricalcium silicate 3, rosin 5, dibutyl maleate 4,2- sulfydryl benzos
Imidazoles 1, castor oil acid calcium 2, the ammoniacal liquor 6 of uvioresistant poly polymer solution 14,15%, polytetrafluoroethylene (PTFE) 120.
What described uvioresistant poly polymer solution was made up of the raw material of following weight parts:
Methyl acrylate 20, EMA 30, BTA 2, divinylbenzene 0.2, polyacrylamide 4,
Initiator 1.
The preparation method of described uvioresistant poly polymer solution, comprises the following steps:
(1) initiator is taken, is added in the deionized water of 30 times of its weight, stirs;
(2) BTA is taken, is added in the absolute ethyl alcohol of 6 times of its weight, stirs, adds divinylbenzene,
Stir, obtain crosslinker solution;
(3) polyacrylamide is taken, is added in the deionized water of 30 times of its weight, stirs;
(4) methyl acrylate, EMA mixing are taken, is added in the deionized water of 13 times of compound weight,
Stir, be sent in reactor, be passed through nitrogen, regulation temperature of reaction kettle is 75 DEG C, and above-mentioned initiator solution is added dropwise, and is added dropwise
After insulated and stirred 4 hours, add above-mentioned crosslinker solution, rise temperature is 85 DEG C, insulated and stirred 50 minutes, discharging, and upper
Polyacrylamide solution mixing is stated, stirs to normal temperature, produces the uvioresistant poly polymer solution.
Described initiator is ammonium persulfate.
A kind of preparation method of outdoor photoactivation medical package film, comprises the following steps:
(1) rosin is taken, is heated and softened, is added in the absolute ethyl alcohol of 8 times of its weight, stirs, adds 2- sulfydryl benzene
And imidazoles, 20 minutes are incubated at 75 DEG C, obtains rosin alcoholic solution;
(2) butyl titanate is taken, is added in the deionized water of 17 times of its weight, stirs, adds rosin alcoholic solution,
Stir, 15% ammoniacal liquor is added dropwise, rear stirring reaction is added dropwise 4 hours, obtain Abietyl modified colloidal sol;
(3) above-mentioned Abietyl modified colloidal sol is taken, mixes, stirs with uvioresistant poly polymer solution, adds castor oil acid calcium,
Insulated and stirred 20 minutes at 95 DEG C, filtering, precipitation is washed, dried 30 minutes at 75 DEG C of vacuum, obtain polymer modification colloidal sol;
(4) above-mentioned polymer modification colloidal sol is taken, mixes, stirs with remaining each raw material, melt, spin-coating film, produce.
Embodiment 2
A kind of outdoor photoactivation medical package film, it is made up of the raw material of following weight parts:
Dibatyl phithalate 4, butyl titanate 40, tricalcium silicate 2, rosin 3, dibutyl maleate 2,2- sulfydryl benzos
Imidazoles 0.7, castor oil acid calcium 1, the ammoniacal liquor 5 of uvioresistant poly polymer solution 10,10%, polytetrafluoroethylene (PTFE) 110.
What described uvioresistant poly polymer solution was made up of the raw material of following weight parts:
Methyl acrylate 17, EMA 20, BTA 1, divinylbenzene 0.1, polyacrylamide 3,
Initiator 0.7.
The preparation method of described uvioresistant poly polymer solution, comprises the following steps:
(1) initiator is taken, is added in the deionized water of 20 times of its weight, stirs;
(2) BTA is taken, is added in the absolute ethyl alcohol of 4 times of its weight, stirs, adds divinylbenzene,
Stir, obtain crosslinker solution;
(3) polyacrylamide is taken, is added in the deionized water of 20 times of its weight, stirs;
(4) methyl acrylate, EMA mixing are taken, is added in the deionized water of 10 times of compound weight,
Stir, be sent in reactor, be passed through nitrogen, regulation temperature of reaction kettle is 70 DEG C, and above-mentioned initiator solution is added dropwise, and is added dropwise
After insulated and stirred 3 hours, add above-mentioned crosslinker solution, rise temperature is 80 DEG C, insulated and stirred 40 minutes, discharging, and upper
Polyacrylamide solution mixing is stated, stirs to normal temperature, produces the uvioresistant poly polymer solution.
Described initiator is ammonium persulfate.
A kind of preparation method of outdoor photoactivation medical package film, comprises the following steps:
(1) rosin is taken, is heated and softened, is added in the absolute ethyl alcohol of 5 times of its weight, stirs, adds 2- sulfydryl benzene
And imidazoles, 10 minutes are incubated at 70 DEG C, obtains rosin alcoholic solution;
(2) butyl titanate is taken, is added in the deionized water of 10 times of its weight, stirs, adds rosin alcoholic solution,
Stir, 10% ammoniacal liquor is added dropwise, rear stirring reaction is added dropwise 3 hours, obtain Abietyl modified colloidal sol;
(3) above-mentioned Abietyl modified colloidal sol is taken, mixes, stirs with uvioresistant poly polymer solution, adds castor oil acid calcium,
Insulated and stirred 10 minutes at 90 DEG C, filtering, precipitation is washed, dried 20 minutes at 70 DEG C of vacuum, obtain polymer modification colloidal sol;
(4) above-mentioned polymer modification colloidal sol is taken, mixes, stirs with remaining each raw material, melt, spin-coating film, produce.
Performance test:
Tensile strength, Zong/Heng≤40/20MPa;
Elongation at break, Zong/Heng≤400%/500%
Angle tear strength, Zong/Heng≤100kgf/cm/140kgf/cm
Biao Mian Zhang Li≤49 × 10-3N/m。
Claims (5)
1. a kind of outdoor photoactivation medical package film, it is characterised in that it is made up of the raw material of following weight parts:
Dibatyl phithalate 4-6, butyl titanate 40-50, tricalcium silicate 2-3, rosin 3-5, dibutyl maleate 2-4,2-
Mercaptobenzimidazole 0.7-1, castor oil acid calcium 1-2, uvioresistant poly polymer solution 10-14,10-15% ammoniacal liquor 5-6, polytetrafluoro
Ethene 110-120.
A kind of 2. outdoor photoactivation medical package film according to claim 1, it is characterised in that described uvioresistant poly
Polymer solution is made up of the raw material of following weight parts:
Methyl acrylate 17-20, EMA 20-30, BTA 1-2, divinylbenzene 0.1-0.2, poly- third
Acrylamide 3-4, initiator 0.7-1.
A kind of 3. outdoor photoactivation medical package film according to claim 2, it is characterised in that described uvioresistant poly
The preparation method of polymer solution, comprises the following steps:
(1) initiator is taken, is added in the deionized water of 20-30 times of its weight, stirs;
(2) BTA is taken, is added in the absolute ethyl alcohol of 4-6 times of its weight, stirs, divinylbenzene is added, stirs
Mix uniformly, obtain crosslinker solution;
(3) polyacrylamide is taken, is added in the deionized water of 20-30 times of its weight, stirs;
(4) methyl acrylate, EMA mixing are taken, is added in the deionized water of 10-13 times of compound weight, stirs
Mix uniformly, be sent in reactor, be passed through nitrogen, regulation temperature of reaction kettle is 70-75 DEG C, and above-mentioned initiator solution is added dropwise, and is dripped
Insulated and stirred 3-4 hours after adding, above-mentioned crosslinker solution being added, rise temperature is 80-85 DEG C, insulated and stirred 40-50 minutes,
Discharging, mixes with above-mentioned polyacrylamide solution, stirs to normal temperature, produce the uvioresistant poly polymer solution.
A kind of 4. outdoor photoactivation medical package film according to Claims 2 or 3, it is characterised in that described initiation
Agent is ammonium persulfate.
5. a kind of preparation method of the outdoor photoactivation medical package film as described in any in 1-3 such as claim, its feature exist
In comprising the following steps:
(1) rosin is taken, is heated and softened, is added in the absolute ethyl alcohol of 5-8 times of its weight, stirs, adds 2- sulfydryl benzos
Imidazoles, 10-20 minutes are incubated at 70-75 DEG C, obtain rosin alcoholic solution;
(2) butyl titanate is taken, is added in the deionized water of 10-17 times of its weight, stirs, adds rosin alcoholic solution,
Stir, 10-15% ammoniacal liquor is added dropwise, rear stirring reaction 3-4 hours are added dropwise, obtain Abietyl modified colloidal sol;
(3) above-mentioned Abietyl modified colloidal sol is taken, mixes, stirs with uvioresistant poly polymer solution, adds castor oil acid calcium,
Insulated and stirred 10-20 minutes at 90-95 DEG C, filtering, precipitation is washed, 20-30 minutes are dried at 70-75 DEG C of vacuum, must be polymerize
Thing modification sol;
(4) above-mentioned polymer modification colloidal sol is taken, mixes, stirs with remaining each raw material, melt, spin-coating film, produce.