CN106219620A - Particle that a kind of industrial waste water purifying processes and preparation method thereof - Google Patents
Particle that a kind of industrial waste water purifying processes and preparation method thereof Download PDFInfo
- Publication number
- CN106219620A CN106219620A CN201610609862.3A CN201610609862A CN106219620A CN 106219620 A CN106219620 A CN 106219620A CN 201610609862 A CN201610609862 A CN 201610609862A CN 106219620 A CN106219620 A CN 106219620A
- Authority
- CN
- China
- Prior art keywords
- parts
- waste water
- particle
- industrial waste
- water purifying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
nullThe invention discloses particle of a kind of industrial waste water purifying process and preparation method thereof，It include following according to weight portion composition composition: 80 parts of coke、Aluminium polychlorid 15 parts、8 parts of ferrous sulfate、NPE 6 parts、Ultra-fine carboxyl nikel powder 15 parts、Disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate 26 parts、Hydrophobic silica 37 parts、6 10 parts of calcium fluoride、Sodium dihydrogen phosphate 0.5 1.5 parts、Alkylphenol polyoxyethylene 0.2 0.6 parts、Polyethylene polyamine 0.8 1.2 parts、Nano titanium oxide 48 parts、Dimethyl methyl acid amide 0.4 0.8 parts、Cobaltous bromide 15 parts、Alkyl phenol formaldehyde resin polyoxyethylene ether 1.2 2.4 parts、Dimethicone 0.7 1.1 parts、26 parts of stearic acid lactic acid fat、Arabic gum 15 25 parts、Nano zine oxide 59 parts、Dimethyl carbonate solvent 20 25 parts.Rationally, preparation method is simple, and raw material is easy to get, it is possible to be suspended in water in instant component preparation, and purification speed is fast, greatly strengthen this Industrial Wastewater Treatment effect, and has advantage nontoxic, harmless, that process sewage is effective.
Description
Technical field
The present invention relates to industrial waste gas purifying technical field, particularly relate to the particle that a kind of industrial waste water purifying processes
And preparation method thereof.
Background technology
Industrial wastewater (industrial wastewater), refers to waste water and the waste liquid discharged in art production process, wherein
Containing the pollutant produced in commercial production materials, intermediate product, side-product and the production process outflowed with water, it is to cause ring
The major reason that environment pollution, particularly water pollute.Effectively administering of industrial wastewater should follow following principle:
The most basic is reform production technology, stops the generation of poisonous and harmful waste water the most in process of production.As with nothing
Poison materials or product replace poisonous materials or product.2. using toxic raw materials and producing poisonous intermediate product and product
In production process, use rational technological process and equipment, and carry out strict operation and supervision, eliminate slip, reduce as far as possible
Number of dropouts.
3. extremely toxic substance waste water is contained, as should be with containing waste water such as some heavy metals, radioactive substance, high-concentration phenol, cyanogen
Other effluent segregations, in order to process and reclaim utility.
4. some flows pollute light waste water such as cooling waste water greatly, should not enter sewer, in order to avoid increasing urban sewage
Road and the load of sewage treatment plant.This kind of waste water should use by appropriately processed Posterior circle in factory.
5. composition and character are similar to the organic wastewater of municipal sewage, such as paper waste, sugar production wastewater, food processing wastewater
Deng, urban sewage system can be entered.Large-scale wastewater treatment plant should be built, the bio-oxidation pond built including treatment in accordance with local conditions, dirt
The treatment facility that reservoir, land treatment system etc. are simple and feasible.Compared with small sewage treatment plant, large-scale wastewater treatment plant can
Significantly reduce capital construction and operating cost, again because of the water yield and water stabilization, it is easy to keep good operation conditions and process effect
Really.
More 6. can be with biodegradable toxic wastewater such as containing phenol, cyanogen waste water, after processing in factory, can be by permissible discharge mark
Standard enters municipal sewage system, sewage treatment plant carry out oxidation degradation process further.
7. contain and be difficult to biodegradable toxic pollutant waste water, should not enter municipal sewage system and transport to sewage disposal
Factory, and individual processing should be carried out.
But, the process of industrial wastewater is due to many industrial wastewater complicated components, and character is changeable, still has some technical problems
It is not fully solved.
The present invention is directed to present situation, propose particle of a kind of industrial waste water purifying process and preparation method thereof, for work
Industry waste water can be suspended in water when processing, and carries out advanced treating, good purification.
Summary of the invention
For overcoming above-mentioned deficiency, the present invention provides particle that a kind of industrial waste water purifying processes and preparation method thereof.
The present invention takes techniques below scheme to realize: the particle that a kind of industrial waste water purifying processes, its bag
Include following according to weight portion composition composition: 80 parts of coke, aluminium polychlorid 15 parts, 8 parts of ferrous sulfate, Nonyl pheno
6 parts of ether, ultra-fine carboxyl nikel powder 1-5 part, disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate 2-6 part, hydrophobic silica 3-7 part, calcium fluoride
6-10 part, sodium dihydrogen phosphate 0.5-1.5 part, alkylphenol polyoxyethylene 0.2-0.6 part, polyethylene polyamine 0.8-1.2 part, nanometer
Titanium dioxide 4-8 part, dimethyl methyl acid amide 0.4-0.8 part, cobaltous bromide 1-5 part, alkyl phenol formaldehyde resin polyoxyethylene ether 1.2-
2.4 parts, dimethicone 0.7-1.1 part, stearic acid lactic acid fat 2-6 part, arabic gum 15-25 part, nano zine oxide 5-9 part,
Dimethyl carbonate solvent 20-25 part.
Further, it include following according to weight portion composition composition: 80 parts of coke, aluminium polychlorid 15 parts, sulphuric acid
Ferrous 8 parts, NPE 6 parts, ultra-fine carboxyl nikel powder 1 part, disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate 2 parts, hydrophobic two
Silicon oxide 3 parts, 6 parts of calcium fluoride, sodium dihydrogen phosphate 0.5 part, alkylphenol polyoxyethylene 0.2 part, polyethylene polyamine 0.8 part, receive
Rice titanium dioxide 4 parts, dimethyl methyl acid amide 0.4 part, cobaltous bromide 1 part, alkyl phenol formaldehyde resin polyoxyethylene ether 1.2 parts, diformazan
Base silicone oil 0.7 part, 2 parts of stearic acid lactic acid fat, arabic gum 15 parts, nano zine oxide 5 parts, dimethyl carbonate solvent 20 parts.
Further, it include following according to weight portion composition composition: 80 parts of coke, aluminium polychlorid 15 parts, sulphuric acid
Ferrous 8 parts, NPE 6 parts, ultra-fine carboxyl nikel powder 3 parts, disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate 4 parts, hydrophobic two
Silicon oxide 5 parts, 8 parts of calcium fluoride, sodium dihydrogen phosphate 1 part, alkylphenol polyoxyethylene 0.4 part, polyethylene polyamine 1 part, nanometer two
Titanium oxide 6 parts, dimethyl methyl acid amide 0.6 part, cobaltous bromide 3 parts, alkyl phenol formaldehyde resin polyoxyethylene ether 1.8 parts, dimethyl-silicon
Oil 0.9 part, 4 parts of stearic acid lactic acid fat, arabic gum 20 parts, nano zine oxide 7 parts, dimethyl carbonate solvent 23 parts.
Further, it include following according to weight portion composition composition: 80 parts of coke, aluminium polychlorid 15 parts, sulphuric acid
Ferrous 8 parts, NPE 6 parts, ultra-fine carboxyl nikel powder 1-5 part, disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate 6 parts, hydrophobic
Silicon dioxide 7 parts, 10 parts of calcium fluoride, sodium dihydrogen phosphate 1.5 parts, alkylphenol polyoxyethylene 0.6 part, polyethylene polyamine 1.2 parts,
Nano titanium oxide 4-8 part, dimethyl methyl acid amide 0.8 part, cobaltous bromide 5 parts, alkyl phenol formaldehyde resin polyoxyethylene ether 2.4 parts,
Dimethicone 1.1 parts, 6 parts of stearic acid lactic acid fat, arabic gum 25 parts, nano zine oxide 9 parts, dimethyl carbonate solvent 25
Part.
The present invention also provides for the preparation method of the particle that a kind of industrial waste water purifying processes, and comprises the following steps:
(1) other components outside coke removal, arabic gum, nano zine oxide, dimethyl carbonate solvent are transported in grinding machine
Pulverizing, fineness of the particles≤0.2 millimeter, obtain mixture A, standby；
(2) coke is transported to pulverizing in grinding machine, fineness of the particles≤0.2 millimeter, obtains coke granule, standby；
(3) mixture A is placed in large beaker, adds dimethyl carbonate solvent and the arabic gum of half amount of 3/4ths amounts,
Being placed on magnetic stirring apparatus by beaker, under room temperature, stirring 2-4h is to being completely dissolved, and obtains mixed liquid B；
(4) by mixture B heating in water bath to 78-88 DEG C, and in mixture B, the coke granule that step (2) prepares, constant temperature are added
0.8-1.2h is to being completely dissolved in stirring, obtains mixed liquor C；
(5) mixed liquor C is cooled to 40-45 DEG C, and in mixture C, adds dimethyl carbonate solvent and the Arab of surplus
Glue, constant temperature stirring 55-65min, to being completely dissolved, obtains mixed liquor D；
(6) mixed liquor D is placed in centrifuge 2-2.6h, obtains the particle semi-finished product that industrial waste water purifying processes；
(7) the particle semi-finished product that above-mentioned prepared industrial waste water purifying processes being placed in baking oven drying, temperature is 115-
125 DEG C, time 5-7h, obtain the particle first product that industrial waste water purifying processes；
(8) the particle first product that industrial waste water purifying obtained above processes is transported to pelletize in comminutor, prepares one
The particle that industrial waste water purifying processes.
The method have the advantages that in sum the present invention is directed to industrial waste gas propose one purify granule and
Preparation technology, rationally, preparation method is simple in component preparation, and raw material is easy to get, preparation method is simple, with low cost, easy to operate when using,
Can be suspended in water and waste water is carried out advanced treating, product stability is good, and between each component, symbiosis coordinates, and synergism, only
Change speed fast, greatly strengthen this Industrial Wastewater Treatment effect, and there is advantage nontoxic, harmless, that process sewage is effective.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below in conjunction with
Detailed description of the invention, is expanded on further the present invention.
Embodiment 1
The particle that a kind of industrial waste water purifying processes, it includes the following composition according to weight portion composition: 80 parts of coke, poly-
Close 15 parts of aluminum chloride, 8 parts of ferrous sulfate, NPE 6 parts, ultra-fine carboxyl nikel powder 1 part, dodecyl diphenyl oxide two
Sodium sulfonate 2 parts, hydrophobic silica 3 parts, 6 parts of calcium fluoride, sodium dihydrogen phosphate 0.5 part, alkylphenol polyoxyethylene 0.2 part, many
Ethylene polyamine 0.8 part, nano titanium oxide 4 parts, dimethyl methyl acid amide 0.4 part, cobaltous bromide 1 part, alkylphenol-formaldehyde resin polyoxy
Vinyl Ether 1.2 parts, dimethicone 0.7 part, 2 parts of stearic acid lactic acid fat, arabic gum 15 parts, nano zine oxide 5 parts, carbonic acid two
Methyl ester solvent 20 parts.
The present invention also provides for the preparation method of the particle that a kind of industrial waste water purifying processes, and comprises the following steps:
(1) other components outside coke removal, arabic gum, nano zine oxide, dimethyl carbonate solvent are transported in grinding machine
Pulverizing, fineness of the particles≤0.2 millimeter, obtain mixture A, standby；
(2) coke is transported to pulverizing in grinding machine, fineness of the particles≤0.2 millimeter, obtains coke granule, standby；
(3) mixture A is placed in large beaker, adds dimethyl carbonate solvent and the arabic gum of half amount of 3/4ths amounts,
Being placed on magnetic stirring apparatus by beaker, under room temperature, stirring 2h is to being completely dissolved, and obtains mixed liquid B；
(4) by mixture B heating in water bath to 78 DEG C, and adding the coke granule that step (2) prepares in mixture B, constant temperature stirs
Mix 0.8h to being completely dissolved, obtain mixed liquor C；
(5) mixed liquor C is cooled to 40 DEG C, and in mixture C, adds dimethyl carbonate solvent and the arabic gum of surplus,
Constant temperature stirring 55min, to being completely dissolved, obtains mixed liquor D；
(6) mixed liquor D is placed in centrifuge 2h, obtains the particle semi-finished product that industrial waste water purifying processes；
(7) the particle semi-finished product that above-mentioned prepared industrial waste water purifying processes being placed in baking oven drying, temperature is 115
DEG C, time 5h, obtain the particle first product that industrial waste water purifying processes；
(8) the particle first product that industrial waste water purifying obtained above processes is transported to pelletize in comminutor, prepares one
The particle that industrial waste water purifying processes.
Embodiment 2
The particle that a kind of industrial waste water purifying processes, it includes the following composition according to weight portion composition: 80 parts of coke, poly-
Close 15 parts of aluminum chloride, 8 parts of ferrous sulfate, NPE 6 parts, ultra-fine carboxyl nikel powder 3 parts, dodecyl diphenyl oxide two
Sodium sulfonate 4 parts, hydrophobic silica 5 parts, 8 parts of calcium fluoride, sodium dihydrogen phosphate 1 part, alkylphenol polyoxyethylene 0.4 part, many second
Alkene polyamines 1 part, nano titanium oxide 6 parts, dimethyl methyl acid amide 0.6 part, cobaltous bromide 3 parts, alkylphenol-formaldehyde resin polyoxyethylene
1.8 parts of ether, dimethicone 0.9 part, 4 parts of stearic acid lactic acid fat, arabic gum 20 parts, nano zine oxide 7 parts, dimethyl carbonate
Solvent 23 parts.
The present invention also provides for the preparation method of the particle that a kind of industrial waste water purifying processes, and comprises the following steps:
(1) other components outside coke removal, arabic gum, nano zine oxide, dimethyl carbonate solvent are transported in grinding machine
Pulverizing, fineness of the particles≤0.2 millimeter, obtain mixture A, standby；
(2) coke is transported to pulverizing in grinding machine, fineness of the particles≤0.2 millimeter, obtains coke granule, standby；
(3) mixture A is placed in large beaker, adds dimethyl carbonate solvent and the arabic gum of half amount of 3/4ths amounts,
Being placed on magnetic stirring apparatus by beaker, under room temperature, stirring 3h is to being completely dissolved, and obtains mixed liquid B；
(4) by mixture B heating in water bath to 83 DEG C, and adding the coke granule that step (2) prepares in mixture B, constant temperature stirs
Mix 1h to being completely dissolved, obtain mixed liquor C；
(5) mixed liquor C is cooled to 43 DEG C, and in mixture C, adds dimethyl carbonate solvent and the arabic gum of surplus,
Constant temperature stirring 60min, to being completely dissolved, obtains mixed liquor D；
(6) mixed liquor D is placed in centrifuge 2-2.6h, obtains the particle semi-finished product that industrial waste water purifying processes；
(7) the particle semi-finished product that above-mentioned prepared industrial waste water purifying processes being placed in baking oven drying, temperature is 120
DEG C, time 6h, obtain the particle first product that industrial waste water purifying processes；
(8) the particle first product that industrial waste water purifying obtained above processes is transported to pelletize in comminutor, prepares one
The particle that industrial waste water purifying processes.
Embodiment 3
The particle that a kind of industrial waste water purifying processes, it includes the following composition according to weight portion composition: 80 parts of coke, poly-
Close 15 parts of aluminum chloride, 8 parts of ferrous sulfate, NPE 6 parts, ultra-fine carboxyl nikel powder 1-5 part, dodecyl diphenyl oxide
Sodium disulfonate 6 parts, hydrophobic silica 7 parts, 10 parts of calcium fluoride, sodium dihydrogen phosphate 1.5 parts, alkylphenol polyoxyethylene 0.6 part,
Polyethylene polyamine 1.2 parts, nano titanium oxide 4-8 part, dimethyl methyl acid amide 0.8 part, cobaltous bromide 5 parts, alkylphenol-formaldehyde resin
Polyoxyethylene ether 2.4 parts, dimethicone 1.1 parts, 6 parts of stearic acid lactic acid fat, arabic gum 25 parts, nano zine oxide 9 parts, carbon
Dimethyl phthalate solvent 25 parts.
The present invention also provides for the preparation method of the particle that a kind of industrial waste water purifying processes, and comprises the following steps:
(1) other components outside coke removal, arabic gum, nano zine oxide, dimethyl carbonate solvent are transported in grinding machine
Pulverizing, fineness of the particles≤0.2 millimeter, obtain mixture A, standby；
(2) coke is transported to pulverizing in grinding machine, fineness of the particles≤0.2 millimeter, obtains coke granule, standby；
(3) mixture A is placed in large beaker, adds dimethyl carbonate solvent and the arabic gum of half amount of 3/4ths amounts,
Being placed on magnetic stirring apparatus by beaker, under room temperature, stirring 4h is to being completely dissolved, and obtains mixed liquid B；
(4) by mixture B heating in water bath to 88 DEG C, and adding the coke granule that step (2) prepares in mixture B, constant temperature stirs
Mix 1.2h to being completely dissolved, obtain mixed liquor C；
(5) mixed liquor C is cooled to 45 DEG C, and in mixture C, adds dimethyl carbonate solvent and the arabic gum of surplus,
Constant temperature stirring 65min, to being completely dissolved, obtains mixed liquor D；
(6) mixed liquor D is placed in centrifuge 2.6h, obtains the particle semi-finished product that industrial waste water purifying processes；
(7) the particle semi-finished product that above-mentioned prepared industrial waste water purifying processes being placed in baking oven drying, temperature is 125
DEG C, time 7h, obtain the particle first product that industrial waste water purifying processes；
(8) the particle first product that industrial waste water purifying obtained above processes is transported to pelletize in comminutor, prepares one
The particle that industrial waste water purifying processes.
The above is embodiments of the invention, therefore all according to the structure described in the present patent application scope, feature and principle institute
The equivalence change done or modification, in the range of being all included in present patent application.
Claims (5)
1. the particle that an industrial waste water purifying processes, it is characterised in that: it includes the following one-tenth according to weight portion composition
Point: 80 parts of coke, aluminium polychlorid 15 parts, 8 parts of ferrous sulfate, NPE 6 parts, ultra-fine carboxyl nikel powder 1-5 part,
Disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate 2-6 part, hydrophobic silica 3-7 part, calcium fluoride 6-10 part, sodium dihydrogen phosphate 0.5-1.5
Part, alkylphenol polyoxyethylene 0.2-0.6 part, polyethylene polyamine 0.8-1.2 part, nano titanium oxide 4-8 part, dimethyl formic acid
Amine 0.4-0.8 part, cobaltous bromide 1-5 part, alkyl phenol formaldehyde resin polyoxyethylene ether 1.2-2.4 part, dimethicone 0.7-1.1
Part, stearic acid lactic acid fat 2-6 part, arabic gum 15-25 part, nano zine oxide 5-9 part, dimethyl carbonate solvent 20-25 part.
The particle that a kind of industrial waste water purifying the most according to claim 1 processes, it is characterised in that: it includes following
According to weight portion composition composition: 80 parts of coke, aluminium polychlorid 15 parts, 8 parts of ferrous sulfate, NPE 6 parts,
Ultra-fine carboxyl nikel powder 1 part, disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate 2 parts, hydrophobic silica 3 parts, 6 parts of calcium fluoride, biphosphate
0.5 part of sodium, alkylphenol polyoxyethylene 0.2 part, polyethylene polyamine 0.8 part, nano titanium oxide 4 parts, dimethyl methyl acid amide 0.4
Part, cobaltous bromide 1 part, alkyl phenol formaldehyde resin polyoxyethylene ether 1.2 parts, dimethicone 0.7 part, 2 parts of stearic acid lactic acid fat, Ah
Draw 15 parts of primary glue, nano zine oxide 5 parts, dimethyl carbonate solvent 20 parts.
The particle that a kind of industrial waste water purifying the most according to claim 1 processes, it is characterised in that: it includes following
According to weight portion composition composition: 80 parts of coke, aluminium polychlorid 15 parts, 8 parts of ferrous sulfate, NPE 6 parts,
Ultra-fine carboxyl nikel powder 3 parts, disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate 4 parts, hydrophobic silica 5 parts, 8 parts of calcium fluoride, biphosphate
1 part of sodium, alkylphenol polyoxyethylene 0.4 part, polyethylene polyamine 1 part, nano titanium oxide 6 parts, dimethyl methyl acid amide 0.6 part,
Cobaltous bromide 3 parts, alkyl phenol formaldehyde resin polyoxyethylene ether 1.8 parts, dimethicone 0.9 part, 4 parts of stearic acid lactic acid fat, I
20 parts of primary glue, nano zine oxide 7 parts, dimethyl carbonate solvent 23 parts.
The particle that a kind of industrial waste water purifying the most according to claim 1 processes, it is characterised in that: it includes following
According to weight portion composition composition: 80 parts of coke, aluminium polychlorid 15 parts, 8 parts of ferrous sulfate, NPE 6 parts,
Ultra-fine carboxyl nikel powder 1-5 part, disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate 6 parts, hydrophobic silica 7 parts, 10 parts of calcium fluoride, di(2-ethylhexyl)phosphate
1.5 parts of hydrogen sodium, alkylphenol polyoxyethylene 0.6 part, polyethylene polyamine 1.2 parts, nano titanium oxide 4-8 part, dimethyl formic acid
Amine 0.8 part, cobaltous bromide 5 parts, alkyl phenol formaldehyde resin polyoxyethylene ether 2.4 parts, dimethicone 1.1 parts, stearic acid lactic acid fat 6
Part, arabic gum 25 parts, nano zine oxide 9 parts, dimethyl carbonate solvent 25 parts.
5. the preparation method of the particle processed according to the arbitrary described a kind of industrial waste water purifying of claim 1-4, it is special
Levy and be: comprise the following steps:
(1) other components outside coke removal, arabic gum, nano zine oxide, dimethyl carbonate solvent are transported in grinding machine
Pulverizing, fineness of the particles≤0.2 millimeter, obtain mixture A, standby；
(2) coke is transported to pulverizing in grinding machine, fineness of the particles≤0.2 millimeter, obtains coke granule, standby；
(3) mixture A is placed in large beaker, adds dimethyl carbonate solvent and the arabic gum of half amount of 3/4ths amounts,
Being placed on magnetic stirring apparatus by beaker, under room temperature, stirring 2-4h is to being completely dissolved, and obtains mixed liquid B；
(4) by mixture B heating in water bath to 78-88 DEG C, and in mixture B, the coke granule that step (2) prepares, constant temperature are added
0.8-1.2h is to being completely dissolved in stirring, obtains mixed liquor C；
(5) mixed liquor C is cooled to 40-45 DEG C, and in mixture C, adds dimethyl carbonate solvent and the Arab of surplus
Glue, constant temperature stirring 55-65min, to being completely dissolved, obtains mixed liquor D；
(6) mixed liquor D is placed in centrifuge 2-2.6h, obtains the particle semi-finished product that industrial waste water purifying processes；
(7) the particle semi-finished product that above-mentioned prepared industrial waste water purifying processes being placed in baking oven drying, temperature is 115-
125 DEG C, time 5-7h, obtain the particle first product that industrial waste water purifying processes；
(8) the particle first product that industrial waste water purifying obtained above processes is transported to pelletize in comminutor, prepares one
The particle that industrial waste water purifying processes.