CN106195785A - Colour correction optical thin film - Google Patents
Colour correction optical thin film Download PDFInfo
- Publication number
- CN106195785A CN106195785A CN201610678085.8A CN201610678085A CN106195785A CN 106195785 A CN106195785 A CN 106195785A CN 201610678085 A CN201610678085 A CN 201610678085A CN 106195785 A CN106195785 A CN 106195785A
- Authority
- CN
- China
- Prior art keywords
- layer
- color correcting
- resin
- optical thin
- correction optical
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Colour correction optical thin film, including color correcting layer, described color correcting layer is made up of thermosetting resin, UV resin, red light emitting substance, green luminescent material, blue light-emitting substances;The two sides of described color correcting layer is compounded with the upper barrier layer for preventing color correcting layer from aoxidizing, lower barrier layer respectively.The present invention uses color correcting layer and this color correcting layer to include red light emitting substance, green luminescent material, blue light-emitting substances, during use, colour correction optical thin film by the present invention is placed in the top of upper diffusion barrier, make the light that LED sends after the colour correction optical thin film of optical film assembly and the present invention, can show the redness of distinctness, green, blue color, therefore display effect is apparent.
Description
Technical field
The present invention relates to a kind of colour correction optical thin film.
Background technology
Optical film assembly is widely used in the fields such as television set, display, notebook computer, mobile phone display screen.Blooming
Assembly generally comprises the upper diffusion barrier of from top to bottom stacking, increment film, lower diffusion barrier, light guide plate, reflectance coating composition.Prior art
In its display resolution effect of optical pellicle need promote.
Summary of the invention
In order to overcome the above-mentioned deficiency of existing optical pellicle, the present invention provides a kind of colour correction optical thin film, its
With existing optical pellicle with the use of it can be made to show the redness of distinctness, green, blue color, thus improve display
Definition.
The present invention solves the technical scheme of its technical problem: colour correction optical thin film, including color correcting layer, described
Color correcting layer be made up of thermosetting resin, UV resin, red light emitting substance, green luminescent material, blue light-emitting substances;
The two sides of described color correcting layer is compounded with the upper barrier layer for preventing color correcting layer from aoxidizing, lower barrier layer respectively.
Further, described red light emitting substance is red azo compounds, and described green luminescent material is green even
Nitrogen compound, described blue light-emitting substances is blue azo-compound;Or: described red light emitting substance is red quinones
Compound, described green luminescent material is green quinones, and described blue light-emitting substances is blue quinones;
Or: described red light emitting substance is red light quantum point, and described green luminescent material is green light quantum point, described blueness
Luminescent substance is blue light quantum point.
Further, described thermosetting resin: UV resin: red light emitting substance: green luminescent material: blue light-emitting substances
Mass ratio be 5 ~ 20:5 ~ 20:1:1:1.
Further, described upper barrier layer, between lower barrier layer and color correcting layer compound in an inert atmosphere
Complete.
Further, described upper barrier layer, lower barrier layer all include basic unit and are coated on the coating layer of described basic unit one side,
Described color correcting layer is sandwiched between two-layer coating layer;
Described coating layer is mixing glue, and described mixing glue is by solvent, acrylic resin, polyurethane resin, asphalt mixtures modified by epoxy resin
Fat, light trigger, organic filler form;
Color correcting layer is sandwiched between two-layer mixing glue after being applied in described basic unit by described mixing glue, then exists
Dry 60 seconds ~ 180 seconds at 50 DEG C ~ 130 DEG C, after drying, carry out UV cured again.
Further, described organic filler is PMMA particle or PBMA particle or PU particle or nylon particle or PET particle.
Or: described upper barrier layer, lower barrier layer all include basic unit and are coated on the coating layer of described basic unit one side, institute
The color correcting layer stated is sandwiched between two-layer coating layer;
Described coating layer is mixing glue, and described mixing glue is by solvent, acrylic resin, polyurethane resin, asphalt mixtures modified by epoxy resin
Fat, light trigger, inorganic particulate form;
Color correcting layer is sandwiched between two-layer mixing glue after being applied in described basic unit by described mixing glue, then exists
Dry 60 seconds ~ 180 seconds at 50 DEG C ~ 130 DEG C, after drying, carry out UV cured again.
Further, described inorganic particulate is SiO2Particle or Al2O3Particle.
Further, described basic unit is thickness PET film between 10 microns to 250 microns or PC film.
The beneficial effects of the present invention is: use color correcting layer and this color correcting layer include red light emitting substance,
Green luminescent material, blue light-emitting substances, during use, colour correction optical thin film by the present invention is placed in the top of upper diffusion barrier,
Make the light that LED sends after the colour correction optical thin film of optical film assembly and the present invention, the redness, green of distinctness can be shown
Color, blue color, therefore display effect is apparent.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the present invention is described in further detail.
Embodiment one
Colour correction optical thin film, including color correcting layer, described color correcting layer is by thermosetting resin, UV resin, redness
Luminescent substance, green luminescent material, blue light-emitting substances form.In the present embodiment, described red light emitting substance is red even
Nitrogen compound, described green luminescent material is green azo-compound, and described blue light-emitting substances is blue azo compounds
Thing.Thermosetting resin can use thermosetting phenolic resin, or Lauxite, or melamine resin, or epoxy resin, or
Thermocurable polyimide, or the thermosetting resin such as furane resins, in the present embodiment, described thermosetting resin: UV resin: red
Luminescent substance: green luminescent material: the mass ratio of blue light-emitting substances is 10:10:1:1:1.
The two sides of described color correcting layer is compounded with the upper barrier layer for preventing color correcting layer from aoxidizing, lower obstruct respectively
Layer, thermosetting resin and UV resin are used for being formed composite joint between upper barrier layer, lower barrier layer, so that upper barrier layer,
Color correcting layer, lower barrier layer shape are integral.
In the present embodiment, described upper barrier layer, lower barrier layer all include basic unit and are coated on the painting of described basic unit one side
Layer of cloth, described color correcting layer is sandwiched between two-layer coating layer, basic unit use the PET film between 10 microns to 250 microns or
PC film.
Described coating layer is mixing glue, and described mixing glue is by solvent, acrylic resin, polyurethane resin, ring
Epoxy resins, light trigger, organic filler form, and organic filler can use PMMA particle, or PBMA particle, or PU particle, or Buddhist nun
Dragon particle, or PET particle.Solvent can be selected for butanone, or toluene, or butyl acetate, or Ketohexamethylene, solvent, acrylic resin, poly-
Proportionate relationship between urethane resin, epoxy resin, light trigger, organic filler can arbitrarily configure, but in order to reach preferable
Blocks moisture, the effect of oxygen, and take into account optical property, configure above-mentioned mixing glue as follows: in each liter of solvent
Add acrylic resin, polyurethane resin, epoxy resin, light trigger, organic filler gross mass 500g, wherein acrylic acid tree
Fat: polyurethane resin: epoxy resin: light trigger: the mass ratio of organic filler is 10:3:2:1:0.5.
Color correcting layer is sandwiched between two-layer mixing glue, so after being applied in described basic unit by described mixing glue
After at 100 DEG C dry 90 seconds, carry out UV cured after drying again, i.e. complete barrier layer, lower barrier layer, color correcting layer
Between compound.Described upper barrier layer, being combined between lower barrier layer and color correcting layer complete in an inert atmosphere.
Color correcting layer includes red light emitting substance, green luminescent material, blue light-emitting substances, by color school during use
Positive optical thin film is placed in the top of diffusion barrier, makes light that LED sends through the colour correction light of optical film assembly and the present invention
After learning thin film, can show the redness of distinctness, green, blue color, therefore display effect is apparent.
Color correcting layer is sandwiched between two-layer mixing glue, the most again certain after being applied in basic unit by mixing glue
Carrying out the drying of certain drying time at a temperature of drying, embodiment two ~ embodiment nine is thermosetting with the difference of embodiment one
Resin: UV resin: red light emitting substance: green luminescent material: the mass ratio of blue light-emitting substances, and dry temperature and drying
Time difference, remaining embodiment is identical with embodiment one.Thermosetting resin: UV resin: red light emitting substance: green
Stimulative substance: the mass ratio of blue light-emitting substances is referred to as color correcting layer each constituent mass ratio in the following table.
Embodiment | Color correcting layer each constituent mass ratio | Dry temperature (DEG C) | Drying time (second) |
Embodiment two | 5:15:1:1:1 | 50 | 70 |
Embodiment three | 8:5:1:1:1 | 90 | 120 |
Embodiment four | 20:7:1:1:1 | 60 | 170 |
Embodiment five | 15:18:1:1:1 | 120 | 60 |
Embodiment six | 17:20:1:1:1 | 70 | 180 |
Embodiment seven | 6:19:1:1:1 | 130 | 100 |
Embodiment eight | 12:13:1:1:1 | 110 | 150 |
Embodiment nine | 18:17:1:1:1 | 80 | 130 |
Embodiment ten
Colour correction optical thin film, including color correcting layer, described color correcting layer is by thermosetting resin, UV resin, redness
Luminescent substance, green luminescent material, blue light-emitting substances form.In the present embodiment, described red light emitting substance is red even
Nitrogen compound, described green luminescent material is green azo-compound, and described blue light-emitting substances is blue azo compounds
Thing.Thermosetting resin can use thermosetting phenolic resin, or Lauxite, or melamine resin, or epoxy resin, or
Thermocurable polyimide, or the thermosetting resin such as furane resins, in the present embodiment, described thermosetting resin: UV resin: red
Luminescent substance: green luminescent material: the mass ratio of blue light-emitting substances is 10:10:1:1:1.
The two sides of described color correcting layer is compounded with the upper barrier layer for preventing color correcting layer from aoxidizing, lower obstruct respectively
Layer, thermosetting resin and UV resin are used for being formed composite joint between upper barrier layer, lower barrier layer, so that upper barrier layer,
Color correcting layer, lower barrier layer shape are integral.
In the present embodiment, described upper barrier layer, lower barrier layer all include basic unit and are coated on the painting of described basic unit one side
Layer of cloth, described color correcting layer is sandwiched between two-layer coating layer, basic unit use the PET film between 10 microns to 250 microns or
PC film.
Described coating layer is mixing glue, and described mixing glue is by solvent, acrylic resin, polyurethane resin, ring
Epoxy resins, light trigger, inorganic particulate form, and inorganic particulate can use SiO2Particle or Al2O3Particle.Solvent can be selected for butanone,
Or toluene, or butyl acetate, or Ketohexamethylene, solvent, acrylic resin, polyurethane resin, epoxy resin, light trigger, inorganic
Proportionate relationship between particle can arbitrarily configure, but in order to reach the effect of preferable blocks moisture, oxygen, and take into account optical
Can, configure above-mentioned mixing glue as follows: each liter of solvent adds acrylic resin, polyurethane resin, asphalt mixtures modified by epoxy resin
Fat, light trigger, inorganic particulate gross mass 500g, wherein acrylic resin: polyurethane resin: epoxy resin: light trigger: nothing
The mass ratio of machine particle is 10:3:2:1:0.5.
Color correcting layer is sandwiched between two-layer mixing glue, so after being applied in described basic unit by described mixing glue
After at 100 DEG C dry 90 seconds, carry out UV cured after drying again, i.e. complete barrier layer, lower barrier layer, color correcting layer
Between compound.Described upper barrier layer, being combined between lower barrier layer and color correcting layer complete in an inert atmosphere.
Color correcting layer is sandwiched between two-layer mixing glue, the most again certain after being applied in basic unit by mixing glue
Carrying out the drying of certain drying time at a temperature of drying, embodiment 11 ~ embodiment 18 is heat with the difference of embodiment ten
Thermosetting resin: UV resin: red light emitting substance: green luminescent material: the mass ratio of blue light-emitting substances, and dry temperature and
Drying time difference, remaining embodiment is identical with embodiment ten.Thermosetting resin: UV resin: red light emitting substance: green
Color luminescent substance: the mass ratio of blue light-emitting substances is referred to as color correcting layer each constituent mass ratio in the following table.
Embodiment | Color correcting layer each constituent mass ratio | Dry temperature (DEG C) | Drying time (second) |
Embodiment 11 | 5:15:1:1:1 | 50 | 70 |
Embodiment 12 | 8:5:1:1:1 | 90 | 120 |
Embodiment 13 | 20:7:1:1:1 | 60 | 170 |
Embodiment 14 | 15:18:1:1:1 | 120 | 60 |
Embodiment 15 | 17:20:1:1:1 | 70 | 180 |
Embodiment 16 | 6:19:1:1:1 | 130 | 100 |
Embodiment 17 | 12:13:1:1:1 | 110 | 150 |
Embodiment 18 | 18:17:1:1:1 | 80 | 130 |
Embodiment 19
Colour correction optical thin film, including color correcting layer, described color correcting layer is by thermosetting resin, UV resin, redness
Luminescent substance, green luminescent material, blue light-emitting substances form.In the present embodiment, described red light emitting substance is red quinone
Compounds, described green luminescent material is green quinones, and described blue light-emitting substances is blue quinones chemical combination
Thing.Thermosetting resin can use thermosetting phenolic resin, or Lauxite, or melamine resin, or epoxy resin, or
Thermocurable polyimide, or the thermosetting resin such as furane resins, in the present embodiment, described thermosetting resin: UV resin: red
Luminescent substance: green luminescent material: the mass ratio of blue light-emitting substances is 10:10:1:1:1.
The two sides of described color correcting layer is compounded with the upper barrier layer for preventing color correcting layer from aoxidizing, lower obstruct respectively
Layer, thermosetting resin and UV resin are used for being formed composite joint between upper barrier layer, lower barrier layer, so that upper barrier layer,
Color correcting layer, lower barrier layer shape are integral.
In the present embodiment, described upper barrier layer, lower barrier layer all include basic unit and are coated on the painting of described basic unit one side
Layer of cloth, described color correcting layer is sandwiched between two-layer coating layer, basic unit use the PET film between 10 microns to 250 microns or
PC film.
Described coating layer is mixing glue, and described mixing glue is by solvent, acrylic resin, polyurethane resin, ring
Epoxy resins, light trigger, organic filler form, and organic filler can use PMMA particle, or PBMA particle, or PU particle, or Buddhist nun
Dragon particle, or PET particle.Solvent can be selected for butanone, or toluene, or butyl acetate, or Ketohexamethylene, solvent, acrylic resin, poly-
Proportionate relationship between urethane resin, epoxy resin, light trigger, organic filler can arbitrarily configure, but in order to reach preferable
Blocks moisture, the effect of oxygen, and take into account optical property, configure above-mentioned mixing glue as follows: in each liter of solvent
Add acrylic resin, polyurethane resin, epoxy resin, light trigger, organic filler gross mass 500g, wherein acrylic acid tree
Fat: polyurethane resin: epoxy resin: light trigger: the mass ratio of organic filler is 10:3:2:1:0.5.
Color correcting layer is sandwiched between two-layer mixing glue, so after being applied in described basic unit by described mixing glue
After at 100 DEG C dry 90 seconds, carry out UV cured after drying again, i.e. complete barrier layer, lower barrier layer, color correcting layer
Between compound.Described upper barrier layer, being combined between lower barrier layer and color correcting layer complete in an inert atmosphere.
Color correcting layer is sandwiched between two-layer mixing glue, the most again certain after being applied in basic unit by mixing glue
Carrying out the drying of certain drying time at a temperature of drying, embodiment 20 ~ embodiment 27 exists with the difference of embodiment 19
In thermosetting resin: UV resin: red light emitting substance: green luminescent material: the mass ratio of blue light-emitting substances, and dry temperature
Degree and drying time difference, remaining embodiment is identical with embodiment 19.Thermosetting resin: UV resin: emitting red light
Material: green luminescent material: the mass ratio of blue light-emitting substances is referred to as color correcting layer each constituent mass ratio in the following table.
Embodiment | Color correcting layer each constituent mass ratio | Dry temperature (DEG C) | Drying time (second) |
Embodiment 20 | 5:15:1:1:1 | 50 | 70 |
Embodiment 21 | 8:5:1:1:1 | 90 | 120 |
Embodiment 22 | 20:7:1:1:1 | 60 | 170 |
Embodiment 23 | 15:18:1:1:1 | 120 | 60 |
Embodiment 24 | 17:20:1:1:1 | 70 | 180 |
Embodiment 25 | 6:19:1:1:1 | 130 | 100 |
Embodiment 26 | 12:13:1:1:1 | 110 | 150 |
Embodiment 27 | 18:17:1:1:1 | 80 | 130 |
Embodiment 28
Colour correction optical thin film, including color correcting layer, described color correcting layer is by thermosetting resin, UV resin, redness
Luminescent substance, green luminescent material, blue light-emitting substances form.In the present embodiment, described red light emitting substance is red quinone
Compounds, described green luminescent material is green quinones, and described blue light-emitting substances is blue quinones chemical combination
Thing.Thermosetting resin can use thermosetting phenolic resin, or Lauxite, or melamine resin, or epoxy resin, or
Thermocurable polyimide, or the thermosetting resin such as furane resins, in the present embodiment, described thermosetting resin: UV resin: red
Luminescent substance: green luminescent material: the mass ratio of blue light-emitting substances is 10:10:1:1:1.
The two sides of described color correcting layer is compounded with the upper barrier layer for preventing color correcting layer from aoxidizing, lower obstruct respectively
Layer, thermosetting resin and UV resin are used for being formed composite joint between upper barrier layer, lower barrier layer, so that upper barrier layer,
Color correcting layer, lower barrier layer shape are integral.
In the present embodiment, described upper barrier layer, lower barrier layer all include basic unit and are coated on the painting of described basic unit one side
Layer of cloth, described color correcting layer is sandwiched between two-layer coating layer, basic unit use the PET film between 10 microns to 250 microns or
PC film.
Described coating layer is mixing glue, and described mixing glue is by solvent, acrylic resin, polyurethane resin, ring
Epoxy resins, light trigger, inorganic particulate form, and inorganic particulate can use SiO2Particle or Al2O3Particle.Solvent can be selected for butanone,
Or toluene, or butyl acetate, or Ketohexamethylene, solvent, acrylic resin, polyurethane resin, epoxy resin, light trigger, inorganic
Proportionate relationship between particle can arbitrarily configure, but in order to reach the effect of preferable blocks moisture, oxygen, and take into account optical
Can, configure above-mentioned mixing glue as follows: each liter of solvent adds acrylic resin, polyurethane resin, asphalt mixtures modified by epoxy resin
Fat, light trigger, inorganic particulate gross mass 500g, wherein acrylic resin: polyurethane resin: epoxy resin: light trigger: nothing
The mass ratio of machine particle is 10:3:2:1:0.5.
Color correcting layer is sandwiched between two-layer mixing glue, so after being applied in described basic unit by described mixing glue
After at 100 DEG C dry 90 seconds, carry out UV cured after drying again, i.e. complete barrier layer, lower barrier layer, color correcting layer
Between compound.Described upper barrier layer, being combined between lower barrier layer and color correcting layer complete in an inert atmosphere.
Color correcting layer is sandwiched between two-layer mixing glue, the most again certain after being applied in basic unit by mixing glue
The drying of certain drying time, embodiment 29 ~ embodiment 36 and the district of embodiment 28 is carried out at a temperature of drying
It is not thermosetting resin: UV resin: red light emitting substance: green luminescent material: the mass ratio of blue light-emitting substances, and dries
Dry temperature and drying time difference, remaining embodiment is identical with embodiment 28.Thermosetting resin: UV resin: red
Color luminescent substance: green luminescent material: the mass ratio of blue light-emitting substances is referred to as color correcting layer each component matter in the following table
Amount ratio.
Embodiment | Color correcting layer each constituent mass ratio | Dry temperature (DEG C) | Drying time (second) |
Embodiment 29 | 5:15:1:1:1 | 50 | 70 |
Embodiment 30 | 8:5:1:1:1 | 90 | 120 |
Embodiment 31 | 20:7:1:1:1 | 60 | 170 |
Embodiment 32 | 15:18:1:1:1 | 120 | 60 |
Embodiment 33 | 17:20:1:1:1 | 70 | 180 |
Embodiment 34 | 6:19:1:1:1 | 130 | 100 |
Embodiment 35 | 12:13:1:1:1 | 110 | 150 |
Embodiment 36 | 18:17:1:1:1 | 80 | 130 |
Embodiment 37
Colour correction optical thin film, including color correcting layer, described color correcting layer is by thermosetting resin, UV resin, redness
Luminescent substance, green luminescent material, blue light-emitting substances form.In the present embodiment, described red light emitting substance is HONGGUANG amount
Sub-, described green luminescent material is green light quantum point, and described blue light-emitting substances is blue light quantum point.Thermosetting resin
Thermosetting phenolic resin, or Lauxite, or melamine resin, or epoxy resin can be used, or thermosetting polyamides is sub-
Amine, or the thermosetting resin such as furane resins, in the present embodiment, described thermosetting resin: UV resin: red light emitting substance: green
Color luminescent substance: the mass ratio of blue light-emitting substances is 10:10:1:1:1.
The two sides of described color correcting layer is compounded with the upper barrier layer for preventing color correcting layer from aoxidizing, lower obstruct respectively
Layer, thermosetting resin and UV resin are used for being formed composite joint between upper barrier layer, lower barrier layer, so that upper barrier layer,
Color correcting layer, lower barrier layer shape are integral.
In the present embodiment, described upper barrier layer, lower barrier layer all include basic unit and are coated on the painting of described basic unit one side
Layer of cloth, described color correcting layer is sandwiched between two-layer coating layer, basic unit use the PET film between 10 microns to 250 microns or
PC film.
Described coating layer is mixing glue, and described mixing glue is by solvent, acrylic resin, polyurethane resin, ring
Epoxy resins, light trigger, organic filler form, and organic filler can use PMMA particle, or PBMA particle, or PU particle, or Buddhist nun
Dragon particle, or PET particle.Solvent can be selected for butanone, or toluene, or butyl acetate, or Ketohexamethylene, solvent, acrylic resin, poly-
Proportionate relationship between urethane resin, epoxy resin, light trigger, organic filler can arbitrarily configure, but in order to reach preferable
Blocks moisture, the effect of oxygen, and take into account optical property, configure above-mentioned mixing glue as follows: in each liter of solvent
Add acrylic resin, polyurethane resin, epoxy resin, light trigger, organic filler gross mass 500g, wherein acrylic acid tree
Fat: polyurethane resin: epoxy resin: light trigger: the mass ratio of organic filler is 10:3:2:1:0.5.
Color correcting layer is sandwiched between two-layer mixing glue, so after being applied in described basic unit by described mixing glue
After at 100 DEG C dry 90 seconds, carry out UV cured after drying again, i.e. complete barrier layer, lower barrier layer, color correcting layer
Between compound.Described upper barrier layer, being combined between lower barrier layer and color correcting layer complete in an inert atmosphere.
Color correcting layer is sandwiched between two-layer mixing glue, the most again certain after being applied in basic unit by mixing glue
The drying of certain drying time, embodiment 38 ~ embodiment 45 and the district of embodiment 37 is carried out at a temperature of drying
It is not thermosetting resin: UV resin: red light emitting substance: green luminescent material: the mass ratio of blue light-emitting substances, and dries
Dry temperature and drying time difference, remaining embodiment is identical with embodiment 37.Thermosetting resin: UV resin: red
Color luminescent substance: green luminescent material: the mass ratio of blue light-emitting substances is referred to as color correcting layer each component matter in the following table
Amount ratio.
Embodiment | Color correcting layer each constituent mass ratio | Dry temperature (DEG C) | Drying time (second) |
Embodiment 38 | 5:15:1:1:1 | 50 | 70 |
Embodiment 39 | 8:5:1:1:1 | 90 | 120 |
Embodiment 40 | 20:7:1:1:1 | 60 | 170 |
Embodiment 41 | 15:18:1:1:1 | 120 | 60 |
Embodiment 42 | 17:20:1:1:1 | 70 | 180 |
Embodiment 43 | 6:19:1:1:1 | 130 | 100 |
Embodiment 44 | 12:13:1:1:1 | 110 | 150 |
Embodiment 45 | 18:17:1:1:1 | 80 | 130 |
Embodiment 46
Colour correction optical thin film, including color correcting layer, described color correcting layer is by thermosetting resin, UV resin, redness
Luminescent substance, green luminescent material, blue light-emitting substances form.In the present embodiment, described red light emitting substance is HONGGUANG amount
Sub-, described green luminescent material is green light quantum point, and described blue light-emitting substances is blue light quantum point.Thermosetting resin
Thermosetting phenolic resin, or Lauxite, or melamine resin, or epoxy resin can be used, or thermosetting polyamides is sub-
Amine, or the thermosetting resin such as furane resins, in the present embodiment, described thermosetting resin: UV resin: red light emitting substance: green
Color luminescent substance: the mass ratio of blue light-emitting substances is 10:10:1:1:1.
The two sides of described color correcting layer is compounded with the upper barrier layer for preventing color correcting layer from aoxidizing, lower obstruct respectively
Layer, thermosetting resin and UV resin are used for being formed composite joint between upper barrier layer, lower barrier layer, so that upper barrier layer,
Color correcting layer, lower barrier layer shape are integral.
In the present embodiment, described upper barrier layer, lower barrier layer all include basic unit and are coated on the painting of described basic unit one side
Layer of cloth, described color correcting layer is sandwiched between two-layer coating layer, basic unit use the PET film between 10 microns to 250 microns or
PC film.
Described coating layer is mixing glue, and described mixing glue is by solvent, acrylic resin, polyurethane resin, ring
Epoxy resins, light trigger, inorganic particulate form, and inorganic particulate can use SiO2Particle or Al2O3Particle.Solvent can be selected for butanone,
Or toluene, or butyl acetate, or Ketohexamethylene, solvent, acrylic resin, polyurethane resin, epoxy resin, light trigger, inorganic
Proportionate relationship between particle can arbitrarily configure, but in order to reach the effect of preferable blocks moisture, oxygen, and take into account optical
Can, configure above-mentioned mixing glue as follows: each liter of solvent adds acrylic resin, polyurethane resin, asphalt mixtures modified by epoxy resin
Fat, light trigger, inorganic particulate gross mass 500g, wherein acrylic resin: polyurethane resin: epoxy resin: light trigger: nothing
The mass ratio of machine particle is 10:3:2:1:0.5.
Color correcting layer is sandwiched between two-layer mixing glue, so after being applied in described basic unit by described mixing glue
After at 100 DEG C dry 90 seconds, carry out UV cured after drying again, i.e. complete barrier layer, lower barrier layer, color correcting layer
Between compound.Described upper barrier layer, being combined between lower barrier layer and color correcting layer complete in an inert atmosphere.
Color correcting layer is sandwiched between two-layer mixing glue, the most again certain after being applied in basic unit by mixing glue
The drying of certain drying time, embodiment 47 ~ embodiment 54 and the district of embodiment 46 is carried out at a temperature of drying
It is not thermosetting resin: UV resin: red light emitting substance: green luminescent material: the mass ratio of blue light-emitting substances, and dries
Dry temperature and drying time difference, remaining embodiment is identical with embodiment 46.Thermosetting resin: UV resin: red
Color luminescent substance: green luminescent material: the mass ratio of blue light-emitting substances is referred to as color correcting layer each component matter in the following table
Amount ratio.
Embodiment | Color correcting layer each constituent mass ratio | Dry temperature (DEG C) | Drying time (second) |
Embodiment 47 | 5:15:1:1:1 | 50 | 70 |
Embodiment 48 | 8:5:1:1:1 | 90 | 120 |
Embodiment 49 | 20:7:1:1:1 | 60 | 170 |
Embodiment 50 | 15:18:1:1:1 | 120 | 60 |
Embodiment 51 | 17:20:1:1:1 | 70 | 180 |
Embodiment 52 | 6:19:1:1:1 | 130 | 100 |
Embodiment 53 | 12:13:1:1:1 | 110 | 150 |
Embodiment 54 | 18:17:1:1:1 | 80 | 130 |
Claims (12)
1. colour correction optical thin film, it is characterised in that include color correcting layer, described color correcting layer by thermosetting resin,
UV resin, red light emitting substance, green luminescent material, blue light-emitting substances form;
The two sides of described color correcting layer is compounded with the upper barrier layer for preventing color correcting layer from aoxidizing, lower barrier layer respectively.
2. colour correction optical thin film as claimed in claim 1, it is characterised in that: described red light emitting substance is red even
Nitrogen compound, described green luminescent material is green azo-compound, and described blue light-emitting substances is blue azo compounds
Thing.
3. colour correction optical thin film as claimed in claim 1, it is characterised in that: described red light emitting substance is red quinone
Compounds, described green luminescent material is green quinones, and described blue light-emitting substances is blue quinones chemical combination
Thing.
4. colour correction optical thin film as claimed in claim 1, it is characterised in that: described red light emitting substance is HONGGUANG amount
Sub-, described green luminescent material is green light quantum point, and described blue light-emitting substances is blue light quantum point.
5. the colour correction optical thin film as described in one of claim 2 ~ 4, it is characterised in that: described thermosetting resin: UV
Resin: red light emitting substance: green luminescent material: the mass ratio of blue light-emitting substances is 5 ~ 20:5 ~ 20:1:1:1.
6. the colour correction optical thin film as described in one of claim 1 ~ 4, it is characterised in that: described upper barrier layer, lower resistance
Being combined between interlayer and color correcting layer completes in an inert atmosphere.
7. the colour correction optical thin film as described in one of claim 1 ~ 4, it is characterised in that: described upper barrier layer, lower resistance
Interlayer all include basic unit and be coated on described basic unit one side coating layer, described color correcting layer be sandwiched in two-layer coating layer it
Between;
Described coating layer is mixing glue, and described mixing glue is by solvent, acrylic resin, polyurethane resin, asphalt mixtures modified by epoxy resin
Fat, light trigger, organic filler form;
Color correcting layer is sandwiched between two-layer mixing glue after being applied in described basic unit by described mixing glue, then exists
Dry 60 seconds ~ 180 seconds at 50 DEG C ~ 130 DEG C, after drying, carry out UV cured again.
8. colour correction optical thin film as claimed in claim 7, it is characterised in that: described organic filler be PMMA particle or
PBMA particle or PU particle or nylon particle or PET particle.
9. the colour correction optical thin film as described in one of claim 1 ~ 4, it is characterised in that: described upper barrier layer, lower resistance
Interlayer all include basic unit and be coated on described basic unit one side coating layer, described color correcting layer be sandwiched in two-layer coating layer it
Between;
Described coating layer is mixing glue, and described mixing glue is by solvent, acrylic resin, polyurethane resin, asphalt mixtures modified by epoxy resin
Fat, light trigger, inorganic particulate form;
Color correcting layer is sandwiched between two-layer mixing glue after being applied in described basic unit by described mixing glue, then exists
Dry 60 seconds ~ 180 seconds at 50 DEG C ~ 130 DEG C, after drying, carry out UV cured again.
10. colour correction optical thin film as claimed in claim 9, it is characterised in that: described inorganic particulate is SiO2Particle or
Al2O3Particle.
11. colour correction optical thin films as claimed in claim 7, it is characterised in that: described basic unit is that thickness is at 10 microns
PET film between 250 microns or PC film.
12. colour correction optical thin films as claimed in claim 9, it is characterised in that: described basic unit is that thickness is at 10 microns
PET film between 250 microns or PC film.