CN106194610A - Wind power generator rotor - Google Patents

Wind power generator rotor Download PDF

Info

Publication number
CN106194610A
CN106194610A CN201610777355.0A CN201610777355A CN106194610A CN 106194610 A CN106194610 A CN 106194610A CN 201610777355 A CN201610777355 A CN 201610777355A CN 106194610 A CN106194610 A CN 106194610A
Authority
CN
China
Prior art keywords
weight
parts
weight portion
metallic rotator
axle
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610777355.0A
Other languages
Chinese (zh)
Inventor
邓雪明
邓东来
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU QIANGSHENG POWER EQUIPMENT Co Ltd
Original Assignee
CHANGSHU QIANGSHENG POWER EQUIPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU QIANGSHENG POWER EQUIPMENT Co Ltd filed Critical CHANGSHU QIANGSHENG POWER EQUIPMENT Co Ltd
Priority to CN201610777355.0A priority Critical patent/CN106194610A/en
Publication of CN106194610A publication Critical patent/CN106194610A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of wind power generator rotor, its metallic rotator axle is through Passivation Treatment, Passivation Treatment comprises the steps: 1) 1～2 part of alhpa olefin sodium sulfonate, 1.5 parts of Fatty alcohol polyoxyethylene polyoxypropylene ether, 1.4 parts of methylcellulose, 0.8 part of Mg-high andesite, 0.9 part of cerous nitrate are put in 33 parts of deionized waters successively, stir；2) put into 1.6 parts of ethanolamine, 1.3 part of two nonyl certain herbaceous plants with big flowers base barium sulfonate, 0.7 part of Borax, 1.5 parts of sodium thiosulfate, 1.6 parts of sodium polyacrylate the most successively, continue stirring, to being sufficiently mixed uniformly, prepare inactivating treatment liquid；3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time, after taking-up with pure water clean dry again.Wind power generator rotor of the present invention, its metallic rotator axle is through Passivation Treatment, and performance is good, and surface smoothness is good.

Description

Wind power generator rotor
Technical field
The present invention relates to wind power generator rotor.
Background technology
Existing wind power generator rotor, including metallic rotator axle, but antirust, corrosion-resistant, the abrasion-resistant of metallic rotator axle, anti- Oxidation, heat-resisting, cold-resistant, weather resistance have much room for improvement, and surface smoothness is the most not ideal enough.
Summary of the invention
It is an object of the invention to provide a kind of wind power generator rotor, its metallic rotator axle is through Passivation Treatment, at gold Metal surface forms uniform passivation protection film, has antirust, corrosion-resistant, abrasion-resistant, the antioxidation of excellence, heat-resisting, cold-resistant, weather-proof Performance, and surface smoothness is good.
For achieving the above object, the technical scheme is that a kind of wind power generator rotor of design, it includes that metal turns Sub-axle, this metallic rotator axle is through Passivation Treatment, and described Passivation Treatment comprises the steps:
1) by 1～2 weight portion alpha-olefin sodium sulfonates, 1.5 parts by weight of fatty alcohol polyoxyethylene poly-oxygen propylene aethers, 1.4 weight Part methylcellulose, 0.8 weight portion Mg-high andesite, 0.9 parts by weight of cerium nitrate put in 33 parts by weight of deionized water successively, and stirring is all Even；
2) put into the most successively 1.6 parts by weight of ethanol amine, 1.3 weight portion two nonyl certain herbaceous plants with big flowers base barium sulfonates, 0.7 weight portion Borax, 1.5 Weight portion sodium thiosulfate, 1.6 parts by weight of polypropylene acid sodium, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid；
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time, Clean with pure water after taking-up and dry again.
Preferably, wind power generator rotor, it includes metallic rotator axle, and this metallic rotator axle is through Passivation Treatment, described Passivation Treatment comprises the steps:
1) by 1 weight portion alpha-olefin sodium sulfonate, 1.5 parts by weight of fatty alcohol polyoxyethylene poly-oxygen propylene aethers, 1.4 weight portion first Base cellulose, 0.8 weight portion Mg-high andesite, 0.9 parts by weight of cerium nitrate put in 33 parts by weight of deionized water successively, stir；
2) put into the most successively 1.6 parts by weight of ethanol amine, 1.3 weight portion two nonyl certain herbaceous plants with big flowers base barium sulfonates, 0.7 weight portion Borax, 1.5 Weight portion sodium thiosulfate, 1.6 parts by weight of polypropylene acid sodium, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid；
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time, Clean with pure water after taking-up and dry again.
Preferably, wind power generator rotor, it includes metallic rotator axle, and this metallic rotator axle is through Passivation Treatment, described Passivation Treatment comprises the steps:
1) by 2 weight portion alpha-olefin sodium sulfonates, 1.5 parts by weight of fatty alcohol polyoxyethylene poly-oxygen propylene aethers, 1.4 weight portion first Base cellulose, 0.8 weight portion Mg-high andesite, 0.9 parts by weight of cerium nitrate put in 33 parts by weight of deionized water successively, stir；
2) put into the most successively 1.6 parts by weight of ethanol amine, 1.3 weight portion two nonyl certain herbaceous plants with big flowers base barium sulfonates, 0.7 weight portion Borax, 1.5 Weight portion sodium thiosulfate, 1.6 parts by weight of polypropylene acid sodium, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid；
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time, Clean with pure water after taking-up and dry again.
Preferably, wind power generator rotor, it includes metallic rotator axle, and this metallic rotator axle is through Passivation Treatment, described Passivation Treatment comprises the steps:
1) by 1.2 weight portion alpha-olefin sodium sulfonates, 1.5 parts by weight of fatty alcohol polyoxyethylene poly-oxygen propylene aethers, 1.4 weight portions Methylcellulose, 0.8 weight portion Mg-high andesite, 0.9 parts by weight of cerium nitrate put in 33 parts by weight of deionized water successively, and stirring is all Even；
2) put into the most successively 1.6 parts by weight of ethanol amine, 1.3 weight portion two nonyl certain herbaceous plants with big flowers base barium sulfonates, 0.7 weight portion Borax, 1.5 Weight portion sodium thiosulfate, 1.6 parts by weight of polypropylene acid sodium, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid；
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time, Clean with pure water after taking-up and dry again.
Advantages of the present invention and having the beneficial effects that: providing a kind of wind power generator rotor, its metallic rotator axle is through blunt Change processes, and forms uniform passivation protection film in metal surface, has antirust, corrosion-resistant, abrasion-resistant, the antioxidation of excellence, resistance to Heat, cold-resistant, weather resistance, and surface smoothness is good.
Performance and the purposes of " inactivating treatment liquid " are determined by its component and proportioning, and in " inactivating treatment liquid " not Can influence each other with component, component and proportioning thereof can determine the final performance of " inactivating treatment liquid ", such as fruit component and proportioning thereof not Mutually coordinated, that single component is brought beneficial effect, even can be eliminated by other components abatement, the when of serious, and different groups Split-phase is conflicted mutually, does not has whole synthesis effect, produces negative interaction and substandard products.The present invention is by a large amount of creative works, repeatedly Checking, obtains optimal component and the proportioning of " inactivating treatment liquid " so that multiple components combine, mutually coordinated and produce Forward comprehensive effect.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.Following example are only used for more Add and clearly demonstrate technical scheme, and can not limit the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Wind power generator rotor, it includes metallic rotator axle, this metallic rotator axle through Passivation Treatment, described Passivation Treatment Comprise the steps:
1) by 1～2 weight portion alpha-olefin sodium sulfonates, 1.5 parts by weight of fatty alcohol polyoxyethylene poly-oxygen propylene aethers, 1.4 weight Part methylcellulose, 0.8 weight portion Mg-high andesite, 0.9 parts by weight of cerium nitrate put in 33 parts by weight of deionized water successively, and stirring is all Even；
2) put into the most successively 1.6 parts by weight of ethanol amine, 1.3 weight portion two nonyl certain herbaceous plants with big flowers base barium sulfonates, 0.7 weight portion Borax, 1.5 Weight portion sodium thiosulfate, 1.6 parts by weight of polypropylene acid sodium, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid；
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time, Clean with pure water after taking-up and dry again.
Embodiment 2
Wind power generator rotor, it includes metallic rotator axle, this metallic rotator axle through Passivation Treatment, described Passivation Treatment Comprise the steps:
1) by 1 weight portion alpha-olefin sodium sulfonate, 1.5 parts by weight of fatty alcohol polyoxyethylene poly-oxygen propylene aethers, 1.4 weight portion first Base cellulose, 0.8 weight portion Mg-high andesite, 0.9 parts by weight of cerium nitrate put in 33 parts by weight of deionized water successively, stir；
2) put into the most successively 1.6 parts by weight of ethanol amine, 1.3 weight portion two nonyl certain herbaceous plants with big flowers base barium sulfonates, 0.7 weight portion Borax, 1.5 Weight portion sodium thiosulfate, 1.6 parts by weight of polypropylene acid sodium, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid；
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time, Clean with pure water after taking-up and dry again.
Embodiment 3
Wind power generator rotor, it includes metallic rotator axle, this metallic rotator axle through Passivation Treatment, described Passivation Treatment Comprise the steps:
1) by 2 weight portion alpha-olefin sodium sulfonates, 1.5 parts by weight of fatty alcohol polyoxyethylene poly-oxygen propylene aethers, 1.4 weight portion first Base cellulose, 0.8 weight portion Mg-high andesite, 0.9 parts by weight of cerium nitrate put in 33 parts by weight of deionized water successively, stir；
2) put into the most successively 1.6 parts by weight of ethanol amine, 1.3 weight portion two nonyl certain herbaceous plants with big flowers base barium sulfonates, 0.7 weight portion Borax, 1.5 Weight portion sodium thiosulfate, 1.6 parts by weight of polypropylene acid sodium, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid；
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time, Clean with pure water after taking-up and dry again.
Embodiment 4
Wind power generator rotor, it includes metallic rotator axle, this metallic rotator axle through Passivation Treatment, described Passivation Treatment Comprise the steps:
1) by 1.2 weight portion alpha-olefin sodium sulfonates, 1.5 parts by weight of fatty alcohol polyoxyethylene poly-oxygen propylene aethers, 1.4 weight portions Methylcellulose, 0.8 weight portion Mg-high andesite, 0.9 parts by weight of cerium nitrate put in 33 parts by weight of deionized water successively, and stirring is all Even；
2) put into the most successively 1.6 parts by weight of ethanol amine, 1.3 weight portion two nonyl certain herbaceous plants with big flowers base barium sulfonates, 0.7 weight portion Borax, 1.5 Weight portion sodium thiosulfate, 1.6 parts by weight of polypropylene acid sodium, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid；
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time, Clean with pure water after taking-up and dry again.
In the various embodiments described above, the metallic rotator axle of wind power generator rotor is through Passivation Treatment, in metal surface shape Uniformly passivation protection film, has antirust, corrosion-resistant, abrasion-resistant, the antioxidation of excellence, heat-resisting, cold-resistant, weather resistance, and Surface smoothness is good.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art For Yuan, on the premise of without departing from the technology of the present invention principle, it is also possible to make some improvements and modifications, these improvements and modifications Also should be regarded as protection scope of the present invention.

Claims (4)

1. wind power generator rotor, it is characterised in that it includes metallic rotator axle, this metallic rotator axle is through Passivation Treatment, institute State Passivation Treatment to comprise the steps:
1) by 1～2 weight portion alpha-olefin sodium sulfonates, 1.5 parts by weight of fatty alcohol polyoxyethylene poly-oxygen propylene aethers, 1.4 weight portion first Base cellulose, 0.8 weight portion Mg-high andesite, 0.9 parts by weight of cerium nitrate put in 33 parts by weight of deionized water successively, stir；
2) 1.6 parts by weight of ethanol amine, 1.3 weight portion two nonyl certain herbaceous plants with big flowers base barium sulfonates, 0.7 weight portion Borax, 1.5 weight are put into the most successively Part sodium thiosulfate, 1.6 parts by weight of polypropylene acid sodium, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid；
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time, take out Clean with pure water afterwards and dry again.
Wind power generator rotor the most according to claim 1, it is characterised in that it includes metallic rotator axle, this metal turns Sub-axle is through Passivation Treatment, and described Passivation Treatment comprises the steps:
1) by 1 weight portion alpha-olefin sodium sulfonate, 1.5 parts by weight of fatty alcohol polyoxyethylene poly-oxygen propylene aethers, 1.4 weight portion methyl fibres Dimension element, 0.8 weight portion Mg-high andesite, 0.9 parts by weight of cerium nitrate put in 33 parts by weight of deionized water successively, stir；
2) 1.6 parts by weight of ethanol amine, 1.3 weight portion two nonyl certain herbaceous plants with big flowers base barium sulfonates, 0.7 weight portion Borax, 1.5 weight are put into the most successively Part sodium thiosulfate, 1.6 parts by weight of polypropylene acid sodium, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid；
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time, take out Clean with pure water afterwards and dry again.
Wind power generator rotor the most according to claim 1, it is characterised in that it includes metallic rotator axle, this metal turns Sub-axle is through Passivation Treatment, and described Passivation Treatment comprises the steps:
1) by 2 weight portion alpha-olefin sodium sulfonates, 1.5 parts by weight of fatty alcohol polyoxyethylene poly-oxygen propylene aethers, 1.4 weight portion methyl fibres Dimension element, 0.8 weight portion Mg-high andesite, 0.9 parts by weight of cerium nitrate put in 33 parts by weight of deionized water successively, stir；
2) 1.6 parts by weight of ethanol amine, 1.3 weight portion two nonyl certain herbaceous plants with big flowers base barium sulfonates, 0.7 weight portion Borax, 1.5 weight are put into the most successively Part sodium thiosulfate, 1.6 parts by weight of polypropylene acid sodium, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid；
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time, take out Clean with pure water afterwards and dry again.
Wind power generator rotor the most according to claim 1, it is characterised in that it includes metallic rotator axle, this metal turns Sub-axle is through Passivation Treatment, and described Passivation Treatment comprises the steps:
1) by 1.2 weight portion alpha-olefin sodium sulfonates, 1.5 parts by weight of fatty alcohol polyoxyethylene poly-oxygen propylene aethers, 1.4 weight portion methyl Cellulose, 0.8 weight portion Mg-high andesite, 0.9 parts by weight of cerium nitrate put in 33 parts by weight of deionized water successively, stir；
2) 1.6 parts by weight of ethanol amine, 1.3 weight portion two nonyl certain herbaceous plants with big flowers base barium sulfonates, 0.7 weight portion Borax, 1.5 weight are put into the most successively Part sodium thiosulfate, 1.6 parts by weight of polypropylene acid sodium, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid；
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time, take out Clean with pure water afterwards and dry again.
CN201610777355.0A 2016-08-31 2016-08-31 Wind power generator rotor Pending CN106194610A (en)