CN106282989A - Rotor - Google Patents
Rotor Download PDFInfo
- Publication number
- CN106282989A CN106282989A CN201610770780.7A CN201610770780A CN106282989A CN 106282989 A CN106282989 A CN 106282989A CN 201610770780 A CN201610770780 A CN 201610770780A CN 106282989 A CN106282989 A CN 106282989A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- parts
- weight
- metallic rotator
- rotator axle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of rotor, its metallic rotator axle is through Passivation Treatment, Passivation Treatment comprises the steps: 1) 1~2 part of lignosulfonates, 1.2 parts of succinic acid alkyl ester sulfonate sodium, 1.8 parts of hydroxypropyl celluloses, 5.8 parts of organic phospho acids, 4.8 parts of citric acids are put in 33 parts of deionized waters successively, stir;2) put into 0.8 part of titanium dioxide, 0.6 part of potassium hydroxide, 3.6 parts of acrylic acid, 1.1 parts of calcium silicates, 1.8 parts of natrium carbonicum calcinatums the most successively, continue stirring, to being sufficiently mixed uniformly, prepare inactivating treatment liquid;3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time, after taking-up with pure water clean dry again.Rotor of the present invention, its metallic rotator axle is through Passivation Treatment, and performance is good, and surface smoothness is good.
Description
Technical field
The present invention relates to rotor.
Background technology
Existing rotor, including metallic rotator axle, but antirust, corrosion-resistant, abrasion-resistant, the antioxidation of metallic rotator axle,
Heat-resisting, cold-resistant, weather resistance has much room for improvement, and surface smoothness is the most not ideal enough.
Summary of the invention
It is an object of the invention to provide a kind of rotor, its metallic rotator axle is through Passivation Treatment, in metal surface
Form uniform passivation protection film, there is antirust, corrosion-resistant, abrasion-resistant, the antioxidation of excellence, heat-resisting, cold-resistant, weather resistance,
And surface smoothness is good.
For achieving the above object, the technical scheme is that a kind of rotor of design, it includes metallic rotator axle, should
Metallic rotator axle is through Passivation Treatment, and described Passivation Treatment comprises the steps:
1) by 1~2 weight portion lignosulfonates, 1.2 weight portion succinic acid alkyl ester sulfonate sodium, 1.8 weight portion hydroxypropyls
Base cellulose, 5.8 weight portion organic phospho acids, 4.8 parts by weight of lemon acid put in 33 parts by weight of deionized water successively, and stirring is all
Even;
2) 0.8 weight portion titanium dioxide, 0.6 weight portion potassium hydroxide, 3.6 parts by weight of acrylic acid, 1.1 weight are put into the most successively
Part calcium silicates, 1.8 weight portion natrium carbonicum calcinatums, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time,
Clean with pure water after taking-up and dry again.
Preferably, rotor, it includes metallic rotator axle, and this metallic rotator axle is through Passivation Treatment, at described passivation
Reason comprises the steps:
1) by 1 weight portion lignosulfonates, 1.2 weight portion succinic acid alkyl ester sulfonate sodium, 1.8 weight portion hydroxypropyls fibres
Dimension element, 5.8 weight portion organic phospho acids, 4.8 parts by weight of lemon acid put in 33 parts by weight of deionized water successively, stir;
2) 0.8 weight portion titanium dioxide, 0.6 weight portion potassium hydroxide, 3.6 parts by weight of acrylic acid, 1.1 weight are put into the most successively
Part calcium silicates, 1.8 weight portion natrium carbonicum calcinatums, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time,
Clean with pure water after taking-up and dry again.
Preferably, rotor, it includes metallic rotator axle, and this metallic rotator axle is through Passivation Treatment, at described passivation
Reason comprises the steps:
1) by 2 weight portion lignosulfonates, 1.2 weight portion succinic acid alkyl ester sulfonate sodium, 1.8 weight portion hydroxypropyls fibres
Dimension element, 5.8 weight portion organic phospho acids, 4.8 parts by weight of lemon acid put in 33 parts by weight of deionized water successively, stir;
2) 0.8 weight portion titanium dioxide, 0.6 weight portion potassium hydroxide, 3.6 parts by weight of acrylic acid, 1.1 weight are put into the most successively
Part calcium silicates, 1.8 weight portion natrium carbonicum calcinatums, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time,
Clean with pure water after taking-up and dry again.
Preferably, rotor, it includes metallic rotator axle, and this metallic rotator axle is through Passivation Treatment, at described passivation
Reason comprises the steps:
1) by 1.2 weight portion lignosulfonates, 1.2 weight portion succinic acid alkyl ester sulfonate sodium, 1.8 weight portion hydroxypropyls
Cellulose, 5.8 weight portion organic phospho acids, 4.8 parts by weight of lemon acid put in 33 parts by weight of deionized water successively, stir;
2) 0.8 weight portion titanium dioxide, 0.6 weight portion potassium hydroxide, 3.6 parts by weight of acrylic acid, 1.1 weight are put into the most successively
Part calcium silicates, 1.8 weight portion natrium carbonicum calcinatums, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time,
Clean with pure water after taking-up and dry again.
Advantages of the present invention and having the beneficial effects that: a kind of rotor is provided, its metallic rotator axle through Passivation Treatment,
Form uniform passivation protection film in metal surface, have excellence antirust, corrosion-resistant, abrasion-resistant, antioxidation, heat-resisting, cold-resistant,
Weather resistance, and surface smoothness is good.
Performance and the purposes of " inactivating treatment liquid " are determined by its component and proportioning, and in " inactivating treatment liquid " not
Can influence each other with component, component and proportioning thereof can determine the final performance of " inactivating treatment liquid ", such as fruit component and proportioning thereof not
Mutually coordinated, that single component is brought beneficial effect, even can be eliminated by other components abatement, the when of serious, and different groups
Split-phase is conflicted mutually, does not has whole synthesis effect, produces negative interaction and substandard products.The present invention is by a large amount of creative works, repeatedly
Checking, obtains optimal component and the proportioning of " inactivating treatment liquid " so that multiple components combine, mutually coordinated and produce
Forward comprehensive effect.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.Following example are only used for more
Add and clearly demonstrate technical scheme, and can not limit the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Rotor, it includes metallic rotator axle, this metallic rotator axle through Passivation Treatment, described Passivation Treatment include as
Lower step:
1) by 1~2 weight portion lignosulfonates, 1.2 weight portion succinic acid alkyl ester sulfonate sodium, 1.8 weight portion hydroxypropyls
Base cellulose, 5.8 weight portion organic phospho acids, 4.8 parts by weight of lemon acid put in 33 parts by weight of deionized water successively, and stirring is all
Even;
2) 0.8 weight portion titanium dioxide, 0.6 weight portion potassium hydroxide, 3.6 parts by weight of acrylic acid, 1.1 weight are put into the most successively
Part calcium silicates, 1.8 weight portion natrium carbonicum calcinatums, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time,
Clean with pure water after taking-up and dry again.
Embodiment 2
Rotor, it includes metallic rotator axle, this metallic rotator axle through Passivation Treatment, described Passivation Treatment include as
Lower step:
1) by 1 weight portion lignosulfonates, 1.2 weight portion succinic acid alkyl ester sulfonate sodium, 1.8 weight portion hydroxypropyls fibres
Dimension element, 5.8 weight portion organic phospho acids, 4.8 parts by weight of lemon acid put in 33 parts by weight of deionized water successively, stir;
2) 0.8 weight portion titanium dioxide, 0.6 weight portion potassium hydroxide, 3.6 parts by weight of acrylic acid, 1.1 weight are put into the most successively
Part calcium silicates, 1.8 weight portion natrium carbonicum calcinatums, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time,
Clean with pure water after taking-up and dry again.
Embodiment 3
Rotor, it includes metallic rotator axle, this metallic rotator axle through Passivation Treatment, described Passivation Treatment include as
Lower step:
1) by 2 weight portion lignosulfonates, 1.2 weight portion succinic acid alkyl ester sulfonate sodium, 1.8 weight portion hydroxypropyls fibres
Dimension element, 5.8 weight portion organic phospho acids, 4.8 parts by weight of lemon acid put in 33 parts by weight of deionized water successively, stir;
2) 0.8 weight portion titanium dioxide, 0.6 weight portion potassium hydroxide, 3.6 parts by weight of acrylic acid, 1.1 weight are put into the most successively
Part calcium silicates, 1.8 weight portion natrium carbonicum calcinatums, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time,
Clean with pure water after taking-up and dry again.
Embodiment 4
Rotor, it includes metallic rotator axle, this metallic rotator axle through Passivation Treatment, described Passivation Treatment include as
Lower step:
1) by 1.2 weight portion lignosulfonates, 1.2 weight portion succinic acid alkyl ester sulfonate sodium, 1.8 weight portion hydroxypropyls
Cellulose, 5.8 weight portion organic phospho acids, 4.8 parts by weight of lemon acid put in 33 parts by weight of deionized water successively, stir;
2) 0.8 weight portion titanium dioxide, 0.6 weight portion potassium hydroxide, 3.6 parts by weight of acrylic acid, 1.1 weight are put into the most successively
Part calcium silicates, 1.8 weight portion natrium carbonicum calcinatums, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time,
Clean with pure water after taking-up and dry again.
In the various embodiments described above, the metallic rotator axle of rotor, through Passivation Treatment, is formed uniformly in metal surface
Passivation protection film, there is antirust, corrosion-resistant, abrasion-resistant, the antioxidation of excellence, heat-resisting, cold-resistant, weather resistance, and surface light
Cleanliness is good.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For Yuan, on the premise of without departing from the technology of the present invention principle, it is also possible to make some improvements and modifications, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. rotor, it is characterised in that it includes metallic rotator axle, this metallic rotator axle through Passivation Treatment, described passivation
Process comprises the steps:
1) by 1~2 weight portion lignosulfonates, 1.2 weight portion succinic acid alkyl ester sulfonate sodium, 1.8 weight portion hydroxypropyls fibres
Dimension element, 5.8 weight portion organic phospho acids, 4.8 parts by weight of lemon acid put in 33 parts by weight of deionized water successively, stir;
2) 0.8 weight portion titanium dioxide, 0.6 weight portion potassium hydroxide, 3.6 parts by weight of acrylic acid, 1.1 weight portion silicon are put into the most successively
Acid calcium, 1.8 weight portion natrium carbonicum calcinatums, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time, take out
Clean with pure water afterwards and dry again.
Rotor the most according to claim 1, it is characterised in that it includes metallic rotator axle, this metallic rotator axle warp
Transpassivation processes, and described Passivation Treatment comprises the steps:
1) by 1 weight portion lignosulfonates, 1.2 weight portion succinic acid alkyl ester sulfonate sodium, 1.8 weight portion hydroxy propyl celluloses
Element, 5.8 weight portion organic phospho acids, 4.8 parts by weight of lemon acid put in 33 parts by weight of deionized water successively, stir;
2) 0.8 weight portion titanium dioxide, 0.6 weight portion potassium hydroxide, 3.6 parts by weight of acrylic acid, 1.1 weight portion silicon are put into the most successively
Acid calcium, 1.8 weight portion natrium carbonicum calcinatums, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time, take out
Clean with pure water afterwards and dry again.
Rotor the most according to claim 1, it is characterised in that it includes metallic rotator axle, this metallic rotator axle warp
Transpassivation processes, and described Passivation Treatment comprises the steps:
1) by 2 weight portion lignosulfonates, 1.2 weight portion succinic acid alkyl ester sulfonate sodium, 1.8 weight portion hydroxy propyl celluloses
Element, 5.8 weight portion organic phospho acids, 4.8 parts by weight of lemon acid put in 33 parts by weight of deionized water successively, stir;
2) 0.8 weight portion titanium dioxide, 0.6 weight portion potassium hydroxide, 3.6 parts by weight of acrylic acid, 1.1 weight portion silicon are put into the most successively
Acid calcium, 1.8 weight portion natrium carbonicum calcinatums, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time, take out
Clean with pure water afterwards and dry again.
Rotor the most according to claim 1, it is characterised in that it includes metallic rotator axle, this metallic rotator axle warp
Transpassivation processes, and described Passivation Treatment comprises the steps:
1) by 1.2 weight portion lignosulfonates, 1.2 weight portion succinic acid alkyl ester sulfonate sodium, 1.8 weight portion hydroxy propyl celluloses
Element, 5.8 weight portion organic phospho acids, 4.8 parts by weight of lemon acid put in 33 parts by weight of deionized water successively, stir;
2) 0.8 weight portion titanium dioxide, 0.6 weight portion potassium hydroxide, 3.6 parts by weight of acrylic acid, 1.1 weight portion silicon are put into the most successively
Acid calcium, 1.8 weight portion natrium carbonicum calcinatums, continue stirring, to being sufficiently mixed uniformly, prepares inactivating treatment liquid;
3) metallic rotator axle is inserted inactivating treatment liquid is passivated process, treatment temperature 45 DEG C, process 35 seconds time, take out
Clean with pure water afterwards and dry again.