CN106192666A - A kind of permeable mortar and utilize the porous pavement that permeable mortar makes - Google Patents
A kind of permeable mortar and utilize the porous pavement that permeable mortar makes Download PDFInfo
- Publication number
- CN106192666A CN106192666A CN201610576969.2A CN201610576969A CN106192666A CN 106192666 A CN106192666 A CN 106192666A CN 201610576969 A CN201610576969 A CN 201610576969A CN 106192666 A CN106192666 A CN 106192666A
- Authority
- CN
- China
- Prior art keywords
- permeable
- layer
- concrete
- mortar
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of permeable mortar, it is made up of the raw material of following weight portion: coarse sand 50% 70%, white cement 20% 30%, concrete additive 2% 5%, glass fibre 5% 8%, binding agent 10% 15%, reinforcing agent 1% 1.5%, utilize the porous pavement that permeable mortar is made, it is characterized in that, include permeable surface layer, porous base course, metalling, concrete layer and element soil layer the most successively.The present invention utilizes white cement generation chemical reaction to produce bubble, solidified by Lauxite again, form a netted supporting construction, thus realize its water permeability, the permeable pavement structure utilizing permeable mortar to make is simple, water permeability is good, advantageously accounts for urban waterlogging and the sewage poly-problem not dissipated for a long time.
Description
Technical field
The present invention relates to pavement construction technical field, a kind of permeable mortar and utilize that permeable mortar makes permeable
Road surface.
Background technology
Along with socioeconomic high speed development, the paces of urban construction are increasingly faster, and increasing high buildings and large mansions rise sheer from level ground
And rise.But, while people's economic activity, ecological environment is also brought many negative impacts.South China in recent years
Rainwater rolls up, and often results in urban waterlogging phenomenon, earth's surface long-pending flood for a long time, not only causes traffic to be obstructed, the most also gives people
Life is made troubles.
Number of patent application: 201010216430.9 disclose a kind of bubble lightweight concrete bonding agent mortar compositions and execute
Work method, described compositions includes the component of following weight portion: Portland cement 30～50 parts, sulfur aluminum cement 10～30
Part, aluminium potassium sulfate 1～3 parts, terrace mortar latex powder 5～10 parts, Zinc fluosilicate 3～6 parts, prodan 0.5～1.5 parts, silicon
Acid sodium 4～8 parts, calcium hydroxide 5～10 parts, sodium carbonate 3～6 parts, petroleum sodium sulfonate 3～6 parts.This invention shortens lightweight coagulation
The time that soil bankets again, improve the comprcssive strength of lightweight concrete and impervious permeable ability.Above-mentioned application is to be prepared as
Concrete, its reacted cement composition density is high, close structure, it is impossible to reaching permeable performance, the application is due to bubble
Effect struts in mortar so that water permeability is good.
Summary of the invention
It is an object of the invention to overcome the deficiencies in the prior art, it is provided that a kind of permeable mortar and utilize permeable mortar to make
Porous pavement, this permeable mortar utilizes white cement generation chemical reaction to produce bubble, then is solidified by Lauxite, formed
One netted supporting construction, thus realize its water permeability, the permeable pavement structure utilizing permeable mortar to make is simple, permeable
Performance is good, advantageously accounts for urban waterlogging and the sewage poly-problem not dissipated for a long time.
It is an object of the invention to be achieved through the following technical solutions: a kind of permeable mortar, former by following weight portion
Material is made:
Coarse sand 50%-70%, white cement 20%-30%, concrete additive 2%-5%, glass fibre 5%-8%, binding agent 10%-15%,
Reinforcing agent 1%-1.5%.
In the present invention, reinforcing agent includes polyvinyl alcohol, polyvinyl formal, Lauxite, styrene-butadiene latex and VAE breast
Any one in liquid.
In the present invention, any one during concrete additive is quick lime, high Gypsum Fibrosum, lithium carbonate and nitrite.
Utilize the porous pavement that permeable mortar is made, include the most successively permeable surface layer, porous base course, metalling,
Concrete layer and element soil layer；
Described permeable surface layer is laid by permeable mortar and is formed, and the thickness of permeable surface layer is 10mm-15mm；
Described porous base course be aggregate, fine coal ball and cement mortar mutually bond formed alveolate texture layer, the thickness of porous base course
Degree is 30mm-40mm；
Described metalling includes that top coat, hydrophobic layer and bottom surface layer, top coat and hydrophobic layer are the plane that lightweight concrete is laid
Rotating fields, hydrophobic layer is formed by chip ballast laying, and the diameter of chip ballast is less than 10mm, and the thickness of metalling is 60-80mm；
The thickness of described concrete layer is 3mm-5mm, and concrete layer is communicated with the water-permeable pipe of metalling, and water-permeable pipe vertically sets
Putting, the port of water-permeable pipe is provided with drainage screen.
In the present invention, its preparation method comprises the following steps:
A1, ramming flat by ground, arrange concrete bar on ground, in concrete bar, interval is installed some permeable
Pipe, water-permeable pipe termination is wrapped up anti-blocking cloth, then is laid concrete in concrete bar；
A2, concrete surface is floating, after concrete curing, then lay one layer of lightweight concrete the end of as to concrete surface
Surface layer；
A3, until bottom surface layer solidify after, select the uniform chip ballast of diameter and be laid on bottom surface layer as hydrophobic layer, by rubble
Slag surface is flattened by forcing press, then arranges second layer concrete bar on hydrophobic layer；
A4, in second layer concrete bar, lay lightweight concrete as top coat, and with floating rule floating top coat surface,
Remove the anti-blocking cloth of water-permeable pipe termination；
A5, cement mortar is mixed with binding agent, stabilizer, water after uniform stirring, obtain cement mixing slurry, by aggregate, fine coal ball
Put in cement mixing slurry and pull out after stirring, be laid on top coat surface as porous base course；
After a6, the rammer that pressurizes porous base course are flat, re-lay one layer of permeable mortar on porous base course surface, permeable mortar surface is smeared
Flat；
A7, until permeable mortar solidify after, at one layer of epoxy resin layer of permeable mortar surface spraying.
In the present invention, one layer of water-permeable brick of permeable topping laying it is set in.
The invention has the beneficial effects as follows: the present invention by chemical blowing make in permeable mortar formed bubble be linked to be netted
Supporting construction, is advantageously implemented good water penetration；The permeable pavement structure utilizing permeable mortar to make is simple, water permeability
Good, advantageously account for urban waterlogging and the sewage poly-problem not dissipated for a long time.
Accompanying drawing explanation
Fig. 1 is the structural representation of the porous pavement of the present invention；
In figure, the permeable surface layer of 10-, 20-porous base course, 30-metalling, 40-concrete layer, 50-element soil layer.
Detailed description of the invention
Technical scheme is described in further detail below in conjunction with the accompanying drawings, but protection scope of the present invention is not limited to
The following stated.
Embodiment 1:
A kind of permeable mortar, is made up of the raw material of following weight portion:
Coarse sand 50%, white cement 30%, concrete additive 5%, glass fibre 5%, binding agent 15%, reinforcing agent 1%.
The method utilizing this permeable mortar to prepare porous pavement, comprises the following steps:
A1, ramming flat by ground, arrange concrete bar on ground, in concrete bar, interval is installed some permeable
Pipe, water-permeable pipe termination is wrapped up anti-blocking cloth, then is laid concrete in concrete bar；
A2, concrete surface is floating, after concrete curing, then lay one layer of lightweight concrete the end of as to concrete surface
Surface layer；
A3, until bottom surface layer solidify after, select the uniform chip ballast of diameter and be laid on bottom surface layer as hydrophobic layer, by rubble
Slag surface is flattened by forcing press, then arranges second layer concrete bar on hydrophobic layer；
A4, in second layer concrete bar, lay lightweight concrete as top coat, and with floating rule floating top coat surface,
Remove the anti-blocking cloth of water-permeable pipe termination；
A5, cement mortar is mixed with binding agent, stabilizer, water after uniform stirring, obtain cement mixing slurry, by aggregate, fine coal ball
Put in cement mixing slurry and pull out after stirring, be laid on top coat surface as porous base course；
After a6, the rammer that pressurizes porous base course are flat, re-lay one layer of permeable mortar on porous base course surface, permeable mortar surface is smeared
Flat；
A7, until permeable mortar solidify after, at one layer of epoxy resin layer of permeable mortar surface spraying.
Embodiment 2:
A kind of permeable mortar, is made up of the raw material of following weight portion:
Coarse sand 70%, white cement 30%, concrete additive 2%, glass fibre 8%, binding agent 10%, reinforcing agent 1.5%.
The method utilizing this permeable mortar to prepare porous pavement, comprises the following steps:
A1, ramming flat by ground, arrange concrete bar on ground, in concrete bar, interval is installed some permeable
Pipe, water-permeable pipe termination is wrapped up anti-blocking cloth, then is laid concrete in concrete bar；
A2, concrete surface is floating, after concrete curing, then lay one layer of lightweight concrete the end of as to concrete surface
Surface layer；
A3, until bottom surface layer solidify after, select the uniform chip ballast of diameter and be laid on bottom surface layer as hydrophobic layer, by rubble
Slag surface is flattened by forcing press, then arranges second layer concrete bar on hydrophobic layer；
A4, in second layer concrete bar, lay lightweight concrete as top coat, and with floating rule floating top coat surface,
Remove the anti-blocking cloth of water-permeable pipe termination；
A5, cement mortar is mixed with binding agent, stabilizer, water after uniform stirring, obtain cement mixing slurry, by aggregate, fine coal ball
Put in cement mixing slurry and pull out after stirring, be laid on top coat surface as porous base course；
After a6, the rammer that pressurizes porous base course are flat, re-lay one layer of permeable mortar on porous base course surface, permeable mortar surface is smeared
Flat；
A7, until permeable mortar solidify after, at one layer of epoxy resin layer of permeable mortar surface spraying.
Embodiment 3:
A kind of permeable mortar, is made up of the raw material of following weight portion:
Coarse sand 60%, white cement 25%, concrete additive 4%, glass fibre 6%, binding agent 12%, reinforcing agent 1.2%.
The method utilizing this permeable mortar to prepare porous pavement, comprises the following steps:
A1, ramming flat by ground, arrange concrete bar on ground, in concrete bar, interval is installed some permeable
Pipe, water-permeable pipe termination is wrapped up anti-blocking cloth, then is laid concrete in concrete bar；
A2, concrete surface is floating, after concrete curing, then lay one layer of lightweight concrete the end of as to concrete surface
Surface layer；
A3, until bottom surface layer solidify after, select the uniform chip ballast of diameter and be laid on bottom surface layer as hydrophobic layer, by rubble
Slag surface is flattened by forcing press, then arranges second layer concrete bar on hydrophobic layer；
A4, in second layer concrete bar, lay lightweight concrete as top coat, and with floating rule floating top coat surface,
Remove the anti-blocking cloth of water-permeable pipe termination；
A5, cement mortar is mixed with binding agent, stabilizer, water after uniform stirring, obtain cement mixing slurry, by aggregate, fine coal ball
Put in cement mixing slurry and pull out after stirring, be laid on top coat surface as porous base course；
After a6, the rammer that pressurizes porous base course are flat, re-lay one layer of permeable mortar on porous base course surface, permeable mortar surface is smeared
Flat；
A7, until permeable mortar solidify after, at one layer of epoxy resin layer of permeable mortar surface spraying.
The structure of the porous pavement made in above-mentioned several embodiment is: a kind of porous pavement, as it is shown in figure 1, by up to
Under include successively permeable surface layer 10, porous base course 20, metalling 30, concrete layer 40 and element soil layer 50；
Described permeable surface layer 10 is laid by permeable mortar and is formed, and the thickness of permeable surface layer 10 is 10mm-15mm；
Described porous base course 20 be aggregate, fine coal ball and cement mortar mutually bond formed alveolate texture layer, porous base course 20
Thickness be 30mm-40mm；
Described metalling 30 includes that top coat, hydrophobic layer and bottom surface layer, top coat and hydrophobic layer are the flat of lightweight concrete laying
Surface layer structure, hydrophobic layer is formed by chip ballast laying, and the diameter of chip ballast is less than 10mm, and the thickness of metalling 30 is 60-80mm；
The thickness of described concrete layer 40 is 3mm-5mm, and concrete layer 40 is communicated with the water-permeable pipe of metalling, and water-permeable pipe is vertical
Arranging, the port of water-permeable pipe is provided with drainage screen.
Embodiment described above only have expressed the detailed description of the invention of the present invention, and it describes more concrete and detailed, but also
Therefore the restriction to the scope of the claims of the present invention can not be interpreted as.It should be pointed out that, for those of ordinary skill in the art
For, without departing from the inventive concept of the premise, it is also possible to make some deformation and improvement, these broadly fall into the guarantor of the present invention
Protect scope.
Claims (6)
1. a permeable mortar, it is characterised in that be made up of the raw material of following weight portion:
Coarse sand 50%-70%, white cement 20%-30%, concrete additive 2%-5%, glass fibre 5%-8%, binding agent 10%-15%,
Reinforcing agent 1%-1.5%.
A kind of permeable mortar, it is characterised in that reinforcing agent includes that polyvinyl alcohol, polyvinyl alcohol contract
Any one in formaldehyde, Lauxite, styrene-butadiene latex and VAE emulsion.
A kind of permeable mortar, it is characterised in that concrete additive is quick lime, high Gypsum Fibrosum, carbon
Acid lithium and nitrite in any one.
4. one kind utilizes the porous pavement that permeable mortar is made, it is characterised in that include permeable surface layer, permeable the most successively
Basic unit, metalling, concrete layer and element soil layer；
Described permeable surface layer is laid by permeable mortar and is formed, and the thickness of permeable surface layer is 10mm-15mm；
Described porous base course be aggregate, fine coal ball and cement mortar mutually bond formed alveolate texture layer, the thickness of porous base course
Degree is 30mm-40mm；
Described metalling includes that top coat, hydrophobic layer and bottom surface layer, top coat and hydrophobic layer are the plane that lightweight concrete is laid
Rotating fields, hydrophobic layer is formed by chip ballast laying, and the diameter of chip ballast is less than 10mm, and the thickness of metalling is 60-80mm；
The thickness of described concrete layer is 3mm-5mm, and concrete layer is communicated with the water-permeable pipe of metalling, and water-permeable pipe vertically sets
Putting, the port of water-permeable pipe is provided with drainage screen.
A kind of porous pavement utilizing permeable mortar to make, it is characterised in that its preparation method bag
Include following steps:
A1, ramming flat by ground, arrange concrete bar on ground, in concrete bar, interval is installed some permeable
Pipe, water-permeable pipe termination is wrapped up anti-blocking cloth, then is laid concrete in concrete bar；
A2, concrete surface is floating, after concrete curing, then lay one layer of lightweight concrete the end of as to concrete surface
Surface layer；
A3, until bottom surface layer solidify after, select the uniform chip ballast of diameter and be laid on bottom surface layer as hydrophobic layer, by rubble
Slag surface is flattened by forcing press, then arranges second layer concrete bar on hydrophobic layer；
A4, in second layer concrete bar, lay lightweight concrete as top coat, and with floating rule floating top coat surface,
Remove the anti-blocking cloth of water-permeable pipe termination；
A5, cement mortar is mixed with binding agent, stabilizer, water after uniform stirring, obtain cement mixing slurry, by aggregate, fine coal ball
Put in cement mixing slurry and pull out after stirring, be laid on top coat surface as porous base course；
After a6, the rammer that pressurizes porous base course are flat, re-lay one layer of permeable mortar on porous base course surface, permeable mortar surface is smeared
Flat；
A7, until permeable mortar solidify after, at one layer of epoxy resin layer of permeable mortar surface spraying.
A kind of porous pavement utilizing permeable mortar to make, it is characterised in that be set in permeable
Layer lays one layer of water-permeable brick.