CN107476165A - A kind of infiltration road surface with air-cleaning function and preparation method thereof - Google Patents
A kind of infiltration road surface with air-cleaning function and preparation method thereof Download PDFInfo
- Publication number
- CN107476165A CN107476165A CN201710610024.2A CN201710610024A CN107476165A CN 107476165 A CN107476165 A CN 107476165A CN 201710610024 A CN201710610024 A CN 201710610024A CN 107476165 A CN107476165 A CN 107476165A
- Authority
- CN
- China
- Prior art keywords
- parts
- road surface
- air
- infiltration
- upper strata
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention provides a kind of infiltration road surface with air-cleaning function and preparation method thereof, and the water seepage road face includes upper strata road surface and underpavement;By weight, the raw material on upper strata road surface includes following component:5 95 parts of coarse aggregate;15 parts of basalt fibre;1 10 parts of high polymer binder;15 parts of colouring agent;15 parts of material for air purification;The raw material of underpavement includes following component:1 20 parts of inorganic adhesive;1 90 parts of coarse aggregate;15 parts of basalt fibre;8 25 parts of water.The clearance that the infiltration road surface 24 hours of the preparation of the present invention of clearance in to(for) formaldehyde reaches more than 65%, PM2.5 reaches the clearance of more than 45%, oxynitrides and reaches more than 90%;The 28 days compression strength in the road surface reaches more than 50MPa, and permeable amount reaches 200L/ (m2Min more than).And technique is simple to operation, cost of material is low, is adapted to industrialized production.
Description
Technical field
The present invention relates to a kind of novel pavement environment-friendly materials, and in particular to a kind of infiltration road surface with air-cleaning function
And preparation method thereof.
Background technology
With the development of urbanization process, the pace of construction in city is accelerated, and the ecological environment in city bears huge pressure.
The earth's surface of modern city is gradually hardened by material water-proof materials such as building and concrete and covered, " the artificial sand formed on ecology
It is unconcerned ".Great negative effect is brought to the ecological environment in city in these fluid-tight road surfaces.Therefore, how in urban construction
Realize that environmental protection attracts people's attention with economic, society harmonious development.City water resource is supplemented, to improving business economic
Benefit, raising are safely, preserving the ecological environment has great economic and social benefit.
At present, have begun to build more infiltration road surfaces to solve the problems, such as city water resource shortage.But existing skill
Infiltration road surface in art use it is mostly be it is single with gathering materials, do not have to or it is few with fine aggregate prepare without sand, celluar concrete.Road
The porosity in face becomes big compared with conventional pav, is easy to seep water.But porosity change causes intensity to be deteriorated greatly, so most of water seepage roads
Face is suitable only for bicycle lane or pavement.Therefore, the water seepage road face for building high intensity has good social effect.The Black Warrior
Rock fiber shows the compatibility better than other reinforcing fibers to cement matrix or stone material as a kind of active material.Cement
As a kind of fragile material, substantial amounts of hole and crack are internally easily formed with surface during cast and maintenance, so as to
Influence every mechanical property of base material.And cement matrix can be significantly reduced using basalt fibre as cement reinforcements
Hole and crack.This is due to that matrix load fibers can prevent the expansion in crack and can absorb the energy of crackle, so that
Every mechanical property of cement matrix is improved.Therefore, it is using the binding of basalt fibre and existing infiltration road surface
It is very important.
Meanwhile also in the presence of a severeer environmental problem, that is, the various motor vehicles travelled on road surface contribute to sky
VOC (the volatile organic of most haze (PM2.5) and various harm inside gas pollutant
Compounds, abbreviation VOC).These gases and particulate pollutant can cause greatly to injure to the body and psychology of people.Therefore,
Certain solution is provided on road surface, the technical research adsorbed and degraded to pollutant within the very first time also right and wrong
It is often important.
Therefore, it is badly in need of providing the technical side of a kind of infiltration road surface with air-cleaning function and its methods for making and using same
Case.
The content of the invention
The purpose of the present invention be overcome it is above-mentioned seep water that pavement strength is low, road surface does not have air purification function in the prior art and
The problem of environmental pollution is serious;It is proposed a kind of infiltration road surface with air-cleaning function and preparation method thereof.
To achieve these goals, the present invention provides following technical scheme:
The embodiment of the present invention provides a kind of infiltration road surface with air-cleaning function, water seepage road face include upper strata road surface with
Underpavement;By weight, the raw material on upper strata road surface includes following component:Coarse aggregate, 5-95 parts (such as 5 parts, 10 parts, 25
Part, 35 parts, 50 parts, 60 parts, 75 parts, 85 parts, the scope between any one or two in 90 parts and 95 parts);Basalt
Fiber, 1-5 parts (such as scope between any one or two in 1 part, 2 parts, 3 parts, 4 parts and 5 parts);Macromolecule bonds
Agent, 1-10 parts (such as any one or two in 1 part, 2 parts, 3 parts, 4 parts, 5 parts, 6 parts, 7 parts, 8 parts, 9 parts and 10 parts it
Between scope);Colouring agent, 1-5 parts (such as the model between any one or two in 1 part, 2 parts, 3 parts, 4 parts and 5 parts
Enclose);Material for air purification, 1-5 parts (such as the model between any one or two in 1 part, 2 parts, 3 parts, 4 parts and 5 parts
Enclose);By weight, the raw material of underpavement includes following component:Inorganic adhesive, 1-20 parts (such as 1 part, 5 parts, 10 parts,
The scope between any one or two in 12 parts, 15 parts, 16 parts, 17 parts, 18 parts, 19 parts and 20 parts);Coarse aggregate, 1-
90 parts (such as between any one or two in 5 parts, 10 parts, 25 parts, 35 parts, 50 parts, 60 parts, 75 parts, 85 parts and 90 parts
Scope);Basalt fibre, 1-5 parts (such as the model between any one or two in 1 part, 2 parts, 3 parts, 4 parts and 5 parts
Enclose);Water, 8-25 parts (such as between any one or two in 8 parts, 10 parts, 15 parts, 18 parts, 20 parts, 24 parts and 25 parts
Scope).
A kind of infiltration road surface with air-cleaning function as described above, it is further preferred that by weight, upper strata
The raw material on road surface includes following component:Coarse aggregate, 20-90 parts (such as 20 parts, 22 parts, 25 parts, 35 parts, 50 parts, 60 parts, 75 parts,
The scope between any one or two in 85 parts and 90 parts);Basalt fibre, 2-5 parts (such as 2 parts, 2.5 parts, 3.5
Part, the scope between any one or two in 4.5 parts and 5 parts);High polymer binder, 4-8 parts (such as 4 parts, 4.5
Part, 5.5 parts, 6.5 parts, the scope between any one or two in 7.5 parts and 8 parts);Colouring agent, 2-4 parts (such as 2
Part, 2.5 parts, 3.5 parts, the scope between any one or two in 3.8 parts and 4 parts);Material for air purification, 3-5 parts
(such as scope between any one or two in 3 parts, 3.5 parts, 4.5 parts and 5 parts);By weight, underpavement
Raw material include following component:Inorganic adhesive, 8-16 parts (such as 8 parts, 8.5 parts, 12 parts, 13 parts, 14 parts, 15 parts, 15.5 parts
Scope between any one or two in 16 parts);Coarse aggregate, 2-85 parts (such as 2 parts, 7 parts, 12 parts, 23 parts, 31
Part, 55 parts, 67 parts, 72 parts, the scope between any one or two in 84 parts and 85 parts);Basalt fibre, 3-4 parts
(such as scope between any one or two in 3 parts, 3.2 parts and 4);Water, 10-20 parts (such as 10 parts, 12 parts, 13
Part, 17 parts, the scope between any one or two in 18 parts and 20 parts).
A kind of infiltration road surface with air-cleaning function as described above, it is further preferred that by weight, upper strata
The raw material on road surface includes following component:Coarse aggregate, 80 parts;Basalt fibre, 2 parts;High polymer binder, 5 parts;Colouring agent, 3
Part;Material for air purification, 5 parts;By weight, the raw material of underpavement includes following component:Inorganic adhesive, 10 parts;Slightly
Gather materials, 82 parts;Basalt fibre, 3 parts;Water, 15 parts.
A kind of infiltration road surface with air-cleaning function as described above, it is further preferred that in the upper strata road surface
Material for air purification include selected from nano titanium oxide, nano zine oxide, MOF materials, activated carbon, molecular sieve, active oxidation
One or more in aluminium, activated carbon fiber and diatomite.
In the present invention, it is necessary to which explanation is metal organic frame (Metal Organic Framework, abbreviation MOF)
Material is a kind of coordination polymer quickly grown nearly ten years, has three-dimensional pore structure, typically using metal ion as connection
Point, organic ligand support Special composition 3D extension, it is the important novel porous material of another class outside zeolite and CNT
Material, all it is widely used in catalysis, energy storage and separation.At present, MOF turns into multiple chemistry such as inorganic chemistry, organic chemistry
The important research direction of branch.
A kind of infiltration road surface with air-cleaning function as described above, it is further preferred that in the upper strata road surface
Material for air purification is included selected from nano titanium oxide, nano zine oxide, MOF materials, activated carbon, molecular sieve, activated alumina
With one or more of the diatomite with;And by weight, the material for air purification includes following component:Nanometer titanium dioxide
Titanium, 20-50 parts (such as any one in 20 parts, 22 parts, 25 parts, 30 parts, 35 parts, 40 parts, 42 parts, 45 parts, 48 parts and 50 parts
Or the scope between two);Nano zine oxide, 10-30 parts (such as 10 parts, 12 parts, 14 parts, 16 parts, 20 parts, 23 parts, 26
Part, the scope between any one or two in 28 parts and 30 parts);MOF materials, 1-5 parts (such as 1 part, 2 parts, 3 parts, 4
Part and 5 parts in any one or two between scope);Activated carbon, 5-10 parts (such as 5 parts, 6 parts, 7 parts, 8 parts, 9 parts
Scope between any one or two in 10 parts);Molecular sieve, 10-25 parts (such as 10 parts, 11 parts, 14 parts, 18 parts,
The scope between any one or two in 20 parts, 22 parts, 24 parts and 25 parts);Activated alumina, 10-20 parts (such as 10
Part, 12 parts, 14 parts, 15 parts, 16 parts, 17 parts, the scope between any one or two in 18 parts and 20 parts);Diatomite,
5-10 parts (such as scope between any one or two in 5 parts, 6 parts, 7 parts, 8 parts, 9 parts and 10 parts).
A kind of infiltration road surface with air-cleaning function as described above, it is further preferred that the nanometer titanium dioxide
Titanium is anatase titanium dioxide carbon dioxide;The particle diameter of the nano titanium oxide, the nano zine oxide and the MOF materials is 20-
50nm (such as any one or two in 20nm, 22nm, 23nm, 25nm, 30nm, 35nm, 40nm, 45nm and 50nm it
Between scope);The activated carbon, activated alumina, activated carbon fiber and diatomaceous particle diameter are respectively less than 30 μm;The molecular sieve
Particle diameter be less than 50 μm;And the molecular sieve is h-mordenite, Hydrogen soap zeolite, dealuminium mordenite and BX type molecular sieves
In one or more;The MOF materials are any one or more in ZIF-8, ZIF-67 and Ni-ZIF-8.
A kind of infiltration road surface with air-cleaning function as described above, it is further preferred that on the upper strata road surface
In, the colouring agent is inorganic pigment;The preferably bright red class inorganic pigment of chrome yellow, molybdenum chromium.The basalt fibre is the short of 5mm
Cut basalt fibre;The high polymer binder is one kind in bisphenol A type epoxy resin, polyurethane resin and acrylic resin
Or a variety of compositions;The particle diameter of the coarse aggregate is 5-9mm (such as any one in 5mm, 6mm, 7mm, 8mm and 9mm or two
Scope between individual);In the underpavement, the inorganic binder is 42.5 grades of portland cements;The basalt is fine
Tie up the chopped basalt fibre for 10mm;The particle diameter of the coarse aggregate be 12-15mm (such as 12mm, 12.5mm, 13mm,
The scope between any one or two in 13.5mm, 14mm, 14.5mm and 15mm).
A kind of infiltration road surface with air-cleaning function as described above, further preferably, the thickness on the upper strata road surface
Spend for 25-45mm (such as any one in 25mm, 26mm, 28mm, 30mm, 35mm, 38mm, 42mm and 45mm or two
Between scope), the porosity on upper strata road surface is 15-20% (such as in 15%, 16%, 17%, 18%, 19% and 20%
Scope between any one or two);The thickness of the underpavement be 50-110mm (such as 50mm, 55mm, 60mm,
The model between any one or two in 65mm, 70mm, 75mm, 80mm, 90mm, 95mm, 100mm, 105mm and 110mm
Enclose), the porosity of underpavement is 20-25% (such as any one in 20%, 21%, 22%, 23%, 24% and 25%
Or the scope between two).
A kind of infiltration road surface with air-cleaning function as described above, it is further preferred that on the upper strata road surface
In, the high polymer binder includes any one in bisphenol A type epoxy resin, polyurethane resin and acrylic resin or more
Kind;Preferably, by weight, the high polymer binder includes following component:Bisphenol A type epoxy resin, 60-80 part (examples
Such as the scope between any one in 60 parts, 65 parts, 68 parts, 70 parts, 75 parts, 79 parts and 80 parts or two);Polyurethane tree
Fat, 10-20 parts (such as between any one or two in 10 parts, 12 parts, 15 parts, 16 parts, 17 parts, 19 parts and 20 parts
Scope);Acrylic resin, 10-20 parts (such as any one in 10 parts, 11 parts, 13 parts, 15 parts, 18 parts, 19 parts and 20 parts
Or the scope between two).
A kind of preparation method on the infiltration road surface with air-cleaning function, the preparation method comprise the following steps:
1) underpavement material is prepared first, and the proportioning of each component in above-mentioned underpavement weighs inorganic adhesive
Mixed after agent, coarse aggregate, basalt fibre and water, and underpavement slurry is uniformly mixing to obtain in puddle mixer, by lower floor road
Fabric slurry is coated uniformly on basic unit road surface (basic unit road surface herein refers to the soil matrix layer under permeable layer) above, coating thickness
For 50-110mm (such as 50mm, 55mm, 60mm, 65mm, 70mm, 75mm, 80mm, 90mm, 95mm, 100mm, 105mm and
The scope between any one or two in 110mm);
2) upper strata ground surface material is then prepared, the proportioning of each component in above-mentioned upper strata road surface weighs each raw material,
Composition is obtained after first material for air purification is well mixed with high polymer binder, then again by said composition and coarse aggregate,
Basalt fibre and colouring agent mixing, and the overlying roaduay fabric slurry that stirred to obtain in puddle mixer, overlying roaduay fabric slurry is uniform
Above the underpavement material in step 1), coating thickness be 25-45mm (such as 25mm, 26mm, 28mm, 30mm,
The scope between any one or two in 35mm, 38mm, 42mm and 45mm).
In a kind of preparation method on the infiltration road surface with air-cleaning function as described above, it is further preferred that
Carried out again using spraying coating process above upper strata ground surface material in step 2) or directly above existing infiltration road surface
Processing;The spraying coating process uses high-pressure airless spraying gun, the spray pressure of high-pressure airless spraying gun for 11-25Mpa (such as 11Mpa,
The scope between any one or two in 12Mpa, 15Mpa, 18Mpa, 20Mpa, 21Mpa, 24Mpa and 25Mpa), move
Dynamic speed be 0.3-1.2m/s (such as 0.3m/s, 0.4m/s, 0.6m/s, 0.7m/s, 0.8m/s, 1.0Mpa, 1.1m/s and
The scope between any one or two in 1.2m/s);The sprayed on material of the spraying coating process is net for the air of powder shaped
Change material, polymer binder and the mixed composition of water, and the form of sprayed on material is the paint pattern with mobility
Sprayable material.
A kind of infiltration road surface with air-cleaning function as described above, it is further preferred that by weight, it is described
Sprayed on material includes following component:Material for air purification, 10-20 parts (such as 10 parts, 12 parts, 15 parts, 16 parts, 17 parts, 19 parts and
The scope between any one or two in 20 parts);Polymer binder, 20-30 parts (such as 20 parts, 22 parts, 25 parts,
The scope between any one or two in 26 parts, 27 parts, 29 parts and 30 parts);Water, 50-60 parts (such as 50 parts, 52 parts,
The scope between any one or two in 55 parts, 56 parts, 57 parts, 59 parts and 60 parts).
A kind of infiltration road surface with air-cleaning function as described above, it is further preferred that upper in step 2)
Above layer ground surface material when use spraying coating process sprayed on material, spray pressure for 15-18MPa (such as 15Mpa, 16Mpa,
The scope between any one or two in 17Mpa and 18Mpa);
When using spraying coating process sprayed on material above existing infiltration road surface, according to the top layer hole on existing infiltration road surface
Rate adjusts spray pressure:
1) porosity is 10-15%, spray pressure 20-25MPa, translational speed 0.6-0.8m/s;
2) porosity is 15-20%, spray pressure 15-20Mpa, translational speed 0.8-1.0m/s;
3) porosity is more than 20%, spray pressure 11-15MPa, translational speed 1.0-1.2m/s.
Coating thickness is more than 1 μm.
Compared with immediate prior art, technical scheme provided by the invention has following excellent effect:
1st, the infiltration road surface with air-cleaning function prepared by the present invention, technique is simple to operation, and cost of material is low, suitable
Close industrialized production.
2nd, the present invention uses basalt fibre extraordinary with cement compatibility to interweave in ground surface material, can be notable
Improving the intensity on infiltration road surface will not also impact to seepage rate.
3rd, the present invention adds air-cleaning function material in ground surface material, while road surface itself of seeping water has sky more again
Gap feature, these material for air purification not only can adsorb pollutant (such as vehicle exhaust) by suction-operated, can also be
Pollutant is decomposed under visible ray and ultraviolet irradiation, therefore the present invention can meet the work(of infiltration and purification of air simultaneously
Energy.
4th, the clearance of PARA FORMALDEHYDE PRILLS(91,95) reaches more than 65%, PM2.5 is gone in the infiltration road surface for preparing of the present invention 24 hours
Reach more than 90% except rate reaches more than the 45%, clearance to oxynitrides;The 28 days compression strength in the infiltration road surface reaches
More than 50MPa, permeable amount reach 200L/ (m2Min more than).
Embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation
Example is only the part of the embodiment of the present invention, rather than whole embodiments.It is general based on the embodiment in the present invention, this area
The every other embodiment that logical technical staff is obtained, belongs to the scope of protection of the invention.
Embodiment 1
A kind of preparation method on the infiltration road surface with air-cleaning function, preparation method comprise the following steps:
1) underpavement material is prepared first, and it is the thick of 12-15mm to weigh particle diameter according to the required proportioning in underpavement
Gather materials 80kg, 42.5 grades of portland cements 20kg, 10mm chopped basalt fibre 1kg and water 25kg after mix, and in mulling
Stir to obtain underpavement slurry in machine, underpavement slurry is coated uniformly on above basic unit road surface, coating thickness is
100mm。
2) after underpavement after normal temperature is curing, upper strata ground surface material is then prepared, according in the road surface of upper strata
Required proportioning weighs each raw material;
The present embodiment material for air purification is by 2.75kg nano titanium oxides, 0.55kg nano zine oxides, 0.275kg activity
Charcoal, 0.55kg h-mordenites, 0.55kg activated aluminas, 0.275kg diatomite and 0.055kgMOF materials ZIF-8 compositions
(gross weight 5kg);Above-mentioned material is mixed evenly stand-by;
Material for air purification 5kg after first will be well mixed mixes with high polymer binder (bisphenol A type epoxy resin 9kg)
After uniformly composition, then again by chopped basalt fibre 2kg that said composition and particle diameter are 5-9mm coarse aggregates 80kg, 5mm
Mixed with colouring agent (chrome yellow) 2kg, and the overlying roaduay fabric slurry that stirred to obtain in puddle mixer, overlying roaduay fabric slurry is uniformly applied
Overlay on above the underpavement material in step 1), coating thickness 40mm.It is again plastic use after normal temperature is curing.
Embodiment 2
A kind of preparation method on the infiltration road surface with air-cleaning function, preparation method comprise the following steps:
1) underpavement material is prepared first, and it is the thick of 12-15mm to weigh particle diameter according to the required proportioning in underpavement
Gather materials 80kg, 42.5 grades of portland cements 18kg, 10mm chopped basalt fibre 2kg and water 18kg after mix, and in mulling
Stir to obtain underpavement slurry in machine, underpavement slurry is coated uniformly on above basic unit road surface, coating thickness is
90mm。
2) after underpavement after normal temperature is curing, upper strata ground surface material is then prepared, according in the road surface of upper strata
Required proportioning weighs each raw material,
Material for air purification is by 1.8kg nano titanium oxides, 1.08kg nano zine oxides, 0.18kg activity in the present embodiment
Charcoal, 0.36kg h-mordenites, 0.36kg activated aluminas, 0.18kg diatomite and 0.036kgMOF materials ZIF-8 compositions;
Above-mentioned material is mixed evenly stand-by;
High polymer binder is by 8kg bisphenol A type epoxy resins, 2kg polyurethane resins, 2kg acrylic acid trees in the present embodiment
Fat forms;Above-mentioned material is mixed evenly stand-by;
Composition is obtained after first the material for air purification 4kg prepared is well mixed with high polymer binder 10kg, then
Said composition is mixed with particle diameter for 5-9mm coarse aggregates 85kg, 5mm chopped basalt fibre 2kg and colouring agent (chrome yellow) 4kg again
Close, and the overlying roaduay fabric slurry that stirred to obtain in puddle mixer, lower floor overlying roaduay fabric slurry being coated uniformly in step 1)
Above ground surface material, coating thickness 45mm.It is again plastic use after normal temperature is curing.
Embodiment 3
A kind of preparation method on the infiltration road surface with air-cleaning function, preparation method comprise the following steps:
1) underpavement material is prepared first, and it is the thick of 12-15mm to weigh particle diameter according to the required proportioning in underpavement
Gather materials 85kg, 42.5 grades of portland cements 20kg, 10mm chopped basalt fibre 1kg and water 25kg after mix, and in mulling
Stir to obtain underpavement slurry in machine, underpavement slurry is coated uniformly on above basic unit road surface, coating thickness is
110mm;
2) after underpavement after normal temperature is curing, upper strata ground surface material is then prepared, according in the road surface of upper strata
Required proportioning weighs each raw material,
First material for air purification (nano titanium oxide) 20kg is mixed with high polymer binder (acrylic resin) 9kg
After even composition, then again by chopped basalt fibre 2kg that said composition and particle diameter are 5-9mm coarse aggregates 80kg, 5mm and
Colouring agent (molybdenum chromium is bright red) 1kg is mixed, and the overlying roaduay fabric slurry that stirred to obtain in puddle mixer, and overlying roaduay fabric slurry is uniform
Above the underpavement material in step 1), coating thickness 30mm.It is again plastic make after normal temperature is curing
With.
The properties on prepared infiltration road surface are listed in the table below 1 in above-described embodiment 1, embodiment 2 and embodiment 3.
The properties on infiltration road surface in the embodiment 1-3 of table 1
Classification | Embodiment 1 | Embodiment 2 | Embodiment 3 |
Porosity (%) 15-20 on upper strata road surface | 18 | 20 | 16 |
Porosity (%) 20-25 of underpavement | 20 | 25 | 23 |
The clearance (%) of PARA FORMALDEHYDE PRILLS(91,95) in 24h | 75 | 80 | 78 |
(%) is reached to PM2.5 clearance in 24h | 45 | 50 | 48 |
(%) is reached to the clearance of oxynitrides in 24h | 95 | 98 | 96 |
The 28 days compression strength (MPa) in road surface | 55 | 60 | 62 |
Road surface permeable amount L/ (m2·min) | 210 | 215 | 207 |
The clearance of PARA FORMALDEHYDE PRILLS(91,95) is most in the infiltration road surface 24h of 1-3 of the embodiment of the present invention it can be seen from the data in table 1
Up to 80% (minimum also to have 75%), 50% (minimum also to have 45%) is reached to PM2.5 clearance, to oxynitrides
Clearance reaches 98% (minimum also to have 95%), it is seen that infiltration road surface of the invention can have extraordinary purification of air energy
Power.Moreover, 28 days compression strength on embodiments of the invention 1-3 infiltration road surface reach 62MPa (minimum also to have 55MPa), can
The pavement strength needs of car lane can be met completely by seeing;And road surface permeable amount reaches 215L/ (m2Min it is) (minimum
There are 207L/ (m2Min)), it is seen that 1-3 of embodiment of the present invention water seepage road has very strong absorbability in face of water.
Embodiment 4
Spraying coating process processing, i.e., overlying roaduay in embodiment 3 are carried out after the infiltration pavement forming prepared with embodiment 3
Handled again using spraying coating process after the shaping of face.
Spraying coating process uses high-pressure airless spraying gun, and the sprayed on material of spraying coating process is material for air purification, the height of powder shaped
Molecular adhesion agent and the mixed composition of water, and the form of sprayed on material is the sprayable material of the paint pattern with mobility
Material.
In the present embodiment in sprayed on material material for air purification each component:11kg nano titanium oxides, 2.2kg nano oxygens
Change zinc, 1.1kg activated carbons, 2.2kg h-mordenites, 2.2kg activated aluminas, 1.1kg diatomite, 0.22kgMOF materials
ZIF-8.Then it is to be used to weigh each raw material mixing by required proportioning.
In the present embodiment in sprayed on material polymer binder each component:21.2kg bisphenol A type epoxy resins, 3.53kg
Polyurethane, 5.3kg acrylic resins.Then it is to be used to weigh each raw material mixing by required proportioning.
Sprayed on material includes following component in the present embodiment:20kg material for air purification, 30kg polymer binders, 60kg
Water.It is sprayed on material to weigh each raw material mixing composition by required proportioning.
Use spraying coating process spraying it is above-mentioned prepare sprayed on material when high-pressure airless spraying gun spray pressure for 18MPa,
Translational speed is 0.3m/s, and coating thickness is more than 1 μm.
Embodiment 5
Spraying coating process processing, i.e., overlying roaduay in embodiment 3 are carried out after the infiltration pavement forming prepared with embodiment 3
Handled again using spraying coating process after the shaping of face.
Spraying coating process uses high-pressure airless spraying gun, and the sprayed on material of spraying coating process is material for air purification, the height of powder shaped
Molecular adhesion agent and the mixed composition of water, and the form of sprayed on material is the sprayable material of the paint pattern with mobility
Material.
In the present embodiment in sprayed on material material for air purification each component:11kg nano titanium oxides, 2.2kg nano oxygens
Change zinc, 1.1kg activated carbons, 2.2kg h-mordenites, 2.2kg activated aluminas, 1.1kg diatomite, 0.22kgMOF materials
ZIF-8.Then it is to be used to weigh each raw material mixing by required proportioning.
In the present embodiment in sprayed on material polymer binder each component:21.2kg bisphenol A type epoxy resins, 3.53kg
Polyurethane, 5.3kg acrylic resins.Then it is to be used to weigh each raw material mixing by required proportioning.
Sprayed on material includes following component in the present embodiment:15kg material for air purification, 22kg polymer binders, 55kg
Water.It is sprayed on material to weigh each raw material mixing composition by required proportioning.
Use spraying coating process spraying it is above-mentioned prepare sprayed on material when high-pressure airless spraying gun spray pressure for 15MPa,
Translational speed is 0.8m/s, and coating thickness is more than 1 μm.
Embodiment 6
Spraying coating process processing, i.e., overlying roaduay in embodiment 3 are carried out after the infiltration pavement forming prepared with embodiment 3
Handled again using spraying coating process after the shaping of face.
Spraying coating process uses high-pressure airless spraying gun, and the sprayed on material of spraying coating process is material for air purification, the height of powder shaped
Molecular adhesion agent and the mixed composition of water, and the form of sprayed on material is the sprayable material of the paint pattern with mobility
Material.
In the present embodiment in sprayed on material material for air purification each component:11kg nano titanium oxides, 2.2kg nano oxygens
Change zinc, 1.1kg activated carbons, 2.2kg h-mordenites, 2.2kg activated aluminas, 1.1kg diatomite, 0.22kgMOF materials
ZIF-8.Then it is to be used to weigh each raw material mixing by required proportioning.
In the present embodiment in sprayed on material polymer binder each component:21.2kg bisphenol A type epoxy resins, 3.53kg
Polyurethane, 5.3kg acrylic resins.Then it is to be used to weigh each raw material mixing by required proportioning.
Sprayed on material includes following component in the present embodiment:12kg material for air purification, 28kg polymer binders, 52kg
Water.It is sprayed on material to weigh each raw material mixing composition by required proportioning.
Use spraying coating process spraying it is above-mentioned prepare sprayed on material when high-pressure airless spraying gun spray pressure for 16MPa,
Translational speed is 1.0m/s, and coating thickness is more than 1 μm.
Embodiment 7
Directly pass through spraying coating process sprayed on material for existing infiltration road surface (selection porosity is more than 20% road surface)
Handled.
Spraying coating process uses high-pressure airless spraying gun, and the sprayed on material of spraying coating process is material for air purification, the height of powder shaped
Molecular adhesion agent and the mixed composition of water, and the form of sprayed on material is the sprayable material of the paint pattern with mobility
Material.
Sprayed on material includes following component in the present embodiment:30kg nano titanium oxides, 25kg polyurethane binder, 60kg
Water.It is sprayed on material to weigh each raw material mixing composition by required proportioning.
Use spraying coating process spraying it is above-mentioned prepare sprayed on material when high-pressure airless spraying gun spray pressure for 11MPa,
Translational speed is 0.8m/s, and coating thickness is more than 1 μm.
The properties on the infiltration road surface prepared into embodiment 7 of above-described embodiment 4 are listed in the table below 2.
The properties on infiltration road surface in the embodiment 4-7 of table 2
Classification | Embodiment 4 | Embodiment 5 | Embodiment 6 | Embodiment 7 |
The clearance (%) of PARA FORMALDEHYDE PRILLS(91,95) in 24h | 82 | 85 | 83 | 70 |
(%) is reached to PM2.5 clearance in 24h | 50 | 52 | 54 | 46 |
(%) is reached to the clearance of oxynitrides in 24h | 97 | 98 | 98 | 92 |
Road surface permeable amount L/ (m2·min) | 215 | 218 | 210 | 203 |
By 4-6 of the embodiment of the present invention it can be seen from the data in table 2 sprayed again on infiltration road surface prepared by the present invention
Material for air purification, the clearance of PARA FORMALDEHYDE PRILLS(91,95) is up to 85% (minimum also to have 82%) in the road surface 24h that seeps water, to PM2.5's
Clearance reaches 54% (minimum also to have 52%), reaches 98% (minimum also to have 97%) to the clearance of oxynitrides, it is seen that
The present invention sprays material for air purification again on infiltration road surface can have extraordinary air-filtering ability.And road surface permeable amount
Reach 218L/ (m2Min it is) (minimum also to have 210L/ (m2Min)), it is seen that 4-6 of embodiment of the present invention water seepage road has in face of water
There is very strong absorbability.Embodiment 7 is to spray material for air purification again on existing infiltration road surface, from above-mentioned properties
Learn, spray purification of air again on existing infiltration road surface, reached good air-filtering ability to a certain extent, still
The beneficial effect reached is again without the technology for spraying purification of air again on the infiltration road surface for preparing of the present invention and being reached
Effect is more preferable.
It can be seen from the above, present invention offers following advantageous effects:
1st, the infiltration road surface with air-cleaning function prepared by the present invention, technique is simple to operation, and cost of material is low, suitable
Close industrialized production.
2nd, the present invention uses basalt fibre extraordinary with cement compatibility to interweave in ground surface material, can be notable
Improving the intensity on infiltration road surface will not also impact to seepage rate.
3rd, the present invention adds air-cleaning function material in ground surface material, while road surface itself of seeping water has sky more again
Gap feature, these material for air purification not only can be by suction-operateds, can also be right under visible ray and ultraviolet irradiation
Pollutant is decomposed, therefore the present invention can meet the function of infiltration and purification of air simultaneously.
4th, the clearance in the infiltration road surface of preparation of the invention 24 hours for formaldehyde reach more than 65%, for
PM2.5 clearance reaches more than the 45%, clearance for oxynitrides and reaches more than 90%;The infiltration road surface resists for 28 days
Compressive Strength reaches more than 50MPa, and permeable amount reaches 200L/ (m2Min more than).
The as shown by data of Tables 1 and 2, the purification air that the infiltration road surface prepared using technical scheme is reached
Function and water seepage function are superior to spray the performance that air purifying paint obtains directly on existing road surface, are prepared in the present invention
It is superior to again using the air purification function obtained by spraying coating process spraying air purifying paint and water seepage function on infiltration road surface
Air purifying paint, the performance on existing infiltration road surface obtained by direct spraying air purifying paint are not sprayed.Again show that this
It is low and do not have air that infiltration road surface with air-cleaning function prepared by invention efficiently solves infiltration pavement seepage rate now
Purification function the problem of, and technique is simple to operation, and cost of material is low, is adapted to industrialized production, can be widely used.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
God and principle within, any modification, equivalent substitution and improvements made etc., accompanying claims protection domain of the present invention it
It is interior.
Claims (10)
1. a kind of infiltration road surface with air-cleaning function, it is characterised in that the water seepage road face includes upper strata road surface with
Layer road surface;
By weight, the raw material on the upper strata road surface includes following component:Coarse aggregate, 5-95 parts;Basalt fibre, 1-5 parts;
High polymer binder, 1-10 parts;Colouring agent, 1-5 parts;Material for air purification, 1-5 parts;
By weight, the raw material of the underpavement includes following component:Inorganic adhesive, 1-20 parts;Coarse aggregate, 1-90
Part;Basalt fibre, 1-5 parts;Water, 8-25 parts.
2. there is the infiltration road surface of air-cleaning function as claimed in claim 1, it is characterised in that in the upper strata road surface
Material for air purification include selected from nano titanium oxide, nano zine oxide, MOF materials, activated carbon, molecular sieve, activated alumina,
One or more in activated carbon fiber and diatomite.
3. there is the infiltration road surface of air-cleaning function as claimed in claim 1, it is characterised in that the upper strata road surface is hollow
Gas scavenging material include selected from nano titanium oxide, nano zine oxide, MOF materials, activated carbon, molecular sieve, activated alumina and
Diatomite;
And by weight, the material for air purification includes following component:Nano titanium oxide, 20-50 parts;It is nano oxidized
Zinc, 10-30 parts;MOF materials, 1-5 parts;Activated carbon, 5-10 parts;Molecular sieve, 10-25 parts;Activated alumina, 10-20 parts;Diatom
Soil, 5-10 parts.
4. there is the infiltration road surface of air-cleaning function as claimed in claim 2, it is characterised in that
The nano titanium oxide is anatase titanium dioxide carbon dioxide;
The particle diameter of the nano titanium oxide, the nano zine oxide and the MOF materials is 20-50nm;
The activated carbon, activated alumina, activated carbon fiber and diatomaceous particle diameter are respectively less than 30 μm;
The particle diameter of the molecular sieve is less than 50 μm;And the molecular sieve is h-mordenite, Hydrogen soap zeolite, dealuminated Mordenite boiling
One or more compositions in stone and BX type molecular sieves;
The MOF materials are ZIF-8, any one or more in ZIF-67 and Ni-ZIF-8.
5. there is the infiltration road surface of air-cleaning function as claimed in claim 1, it is characterised in that
In the upper strata road surface, the colouring agent is inorganic pigment;The chopped basalt that the basalt fibre is 5mm is fine
Dimension;The high polymer binder is one or more groups in bisphenol A type epoxy resin, polyurethane resin and acrylic resin
Into;The particle diameter of the coarse aggregate is 5-9mm;
In the underpavement, the inorganic binder is 42.5 grades of portland cements;The basalt fibre is 10mm's
Be chopped basalt fibre;The particle diameter of the coarse aggregate is 12-15mm.
6. there is the infiltration road surface of air-cleaning function as claimed in claim 1, it is characterised in that the thickness on the upper strata road surface
Spend for 25-45mm, the porosity on upper strata road surface is 15-20%;
The thickness of the underpavement is 50-110mm, and the porosity of underpavement is 20-25%.
7. there is the infiltration road surface of air-cleaning function as claimed in claim 1, it is characterised in that in the road surface of upper strata, institute
High polymer binder is stated to be made up of bisphenol A type epoxy resin, polyurethane resin and acrylic resin;And by weight, it is described
High polymer binder includes following component:Bisphenol A type epoxy resin, 60-80 parts;Polyurethane resin, 10-20 parts;Acrylic acid tree
Fat, 10-20 parts.
8. a kind of preparation method on the infiltration road surface with air-cleaning function any one of claim 1-7, it is special
Sign is that the preparation method comprises the following steps:
1) prepare underpavement material first, according to the required proportioning in the underpavement weigh inorganic adhesive, coarse aggregate,
Mixed after basalt fibre and water, and the underpavement slurry that stirs to obtain, underpavement slurry is coated uniformly on basic unit road
Above face, coating thickness 50-110mm;
2) upper strata ground surface material is then prepared, each raw material is weighed according to the required proportioning in the upper strata road surface, it is first that air is net
Change after material be well mixed with high polymer binder and obtain composition, then again by said composition and coarse aggregate, basalt fibre and
Colouring agent mixes, and the overlying roaduay fabric slurry that stirs to obtain, lower floor road overlying roaduay fabric slurry being coated uniformly in step 1)
Above plane materiel material, coating thickness 25-45mm.
9. the preparation method on the infiltration road surface with air-cleaning function as claimed in claim 8, it is characterised in that in step
2) handled again using spraying coating process above the upper strata ground surface material in or directly on existing infiltration road surface;
The spraying coating process uses high-pressure airless spraying gun, and the spray pressure of high-pressure airless spraying gun is 11-25Mpa, and translational speed is
0.3-1.2m/s;
The sprayed on material of the spraying coating process is material for air purification, polymer binder and the mixed combination of water of powder shaped
Thing, and the form of sprayed on material is the sprayable material of the paint pattern with mobility.
10. the preparation method on the infiltration road surface with air-cleaning function as claimed in claim 9, it is characterised in that by weight
Part meter is measured, the sprayed on material includes following component:Material for air purification, 10-20 parts;Polymer binder, 20-30 parts;Water,
50-60 parts.