CN106189834A - A kind of seagoing vessel fuel oil tank fire-retardant paint - Google Patents
A kind of seagoing vessel fuel oil tank fire-retardant paint Download PDFInfo
- Publication number
- CN106189834A CN106189834A CN201610544168.8A CN201610544168A CN106189834A CN 106189834 A CN106189834 A CN 106189834A CN 201610544168 A CN201610544168 A CN 201610544168A CN 106189834 A CN106189834 A CN 106189834A
- Authority
- CN
- China
- Prior art keywords
- fuel oil
- oil tank
- water
- polymer
- retardant paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of seagoing vessel fuel oil tank fire-retardant paint, by weight, it is made up of following raw material: sulfonation oils and fats 28 30, lactic acid polymer 8 10, oxybenzoic acid compounds 5.5 7.5, non-polymer plasticizer 3.5 5.5, carbomer 0.5 1, lemon blue 1.5 2.5, blanc fixe 46, alkali earth metal aluminate 0.5 1.5, waterglass steel 46, nanometer colloid 1.6 2.2, silicone hydrophober 0.5 1, glacial acetic acid 1.5 2, water 30 32.The present invention has high-weatherability, high dirt resistance and hypotoxicity, and coating chemical stability is good, has the tack of excellence, has higher fire line, can be directly used for fuel oil tank fire prevention, and its prices of raw materials are low, Harmful chemicals consumption is few.
Description
Technical field
The present invention relates to paint field, particularly belong to a kind of seagoing vessel fuel oil tank fire-retardant paint.
Background technology
The hull bottom position of boats and ships, is dipped in water for a long time, suffers the electrochemical corrosion of sea water.In ocean the most varied
Marine attaching organism, they can upper attachment alow, affect the ship speed of a ship or plane, increase fuel consumption.In national defence more serious
It is the fighting capacity that have impact on naval vessels.Therefore it is required that shipbottom paint has excellent resistance to water, rust-preventing characteristic；Hull bottom outermost layer paint is wanted to prevent
The only attachment of marine attaching organism, little to human toxicity during construction, boats and ships waterline position is by sea beat, the most water-fast but also resistance to
Shine.Supernatant shell and superstructure structure are irradiated by wave spilling and sunburst, and paint film marine climate to be stood is strong
Strong change.Walking about frequently because of personnel in position, deck, easily collides during handling goods, therefore paint film must have higher wearability with
Adhesive force.Paint used in ship oil tank wants resistance to oil and seawater alternate；Water tank paints in addition to requiring good water resistance, to water quality
Can not have an impact.
Summary of the invention
It is an object of the invention to provide a kind of seagoing vessel fuel oil tank fire-retardant paint, high-weatherability, high dirt resistance and hypotoxicity,
Coating chemical stability is good, has the tack of excellence, has higher fire line, can be directly used for fuel oil tank fire prevention, its former material
Price is low, Harmful chemicals consumption is few for material.
The technical solution used in the present invention is as follows:
A kind of seagoing vessel fuel oil tank fire-retardant paint, by weight, is made up of following raw material: sulfonation oils and fats 28-30, lactic acid are polymerized
Thing 8-10, oxybenzoic acid compounds 5.5-7.5, non-polymer plasticizer 3.5-5.5, carbomer 0.5-1, lemon blue
1.5-2.5, blanc fixe 4-6, alkali earth metal aluminate 0.5-1.5, waterglass steel 4-6, nanometer colloid 1.6-2.2, organosilicon
Class hydrophober 0.5-1, glacial acetic acid 1.5-2, water 30-32；The concrete preparation method of this paint is as follows: first, the most successively will
Sulfonation oils and fats, lactic acid polymer, oxybenzoic acid compounds, non-polymer plasticizer, carbomer, lemon blue, barite
The water of powder, alkali earth metal aluminate and half is put in high-speed stirred tank and is stirred, and obtains stirring compound；Then, successively by water
Fiberglass 4-6, nanometer colloid 1.6-2.2, silicone hydrophober 0.5-1, glacial acetic acid 1.5-2, water are put at a high speed in order
Mixing and stirring in agitator tank, rotating speed 1880-2000 turns/min, is finished product fire-retardant paint.
A kind of seagoing vessel fuel oil tank fire-retardant paint, is made up of following raw material: sulfonation oils and fats 29, lactic acid polymer 9, adjacent hydroxyl
Benzoic acid derivative 6.5, non-polymer plasticizer 4.5, carbomer 0.8, lemon blue 2, blanc fixe 5, alkaline-earth metal aluminic acid
Salt 1, waterglass steel 5, nanometer colloid 1.9, silicone hydrophober 0.7, glacial acetic acid 1.7, water 31.
The alkali earth metal aluminate of the present invention can be with waterglass steel, the fully dispersed rear fire insulation forming densification of blanc fixe
Layer, high-weatherability, high dirt resistance and hypotoxicity, coating chemical stability is good, has the tack of excellence, has higher fire prevention
Property, can be directly used for fuel oil tank fire prevention, its prices of raw materials are low, Harmful chemicals consumption is few.
Detailed description of the invention
A kind of seagoing vessel fuel oil tank fire-retardant paint, by weight, is made up of following raw material: sulfonation oils and fats 29, lactic acid are poly-
Compound 9, oxybenzoic acid compounds 6.5, non-polymer plasticizer 4.5, carbomer 0.8, lemon blue 2, blanc fixe 5,
Alkali earth metal aluminate 1, waterglass steel 5, nanometer colloid 1.9, silicone hydrophober 0.7, glacial acetic acid 1.7, water 31；This paint
Concrete preparation method as follows: first, the most successively by sulfonation oils and fats, lactic acid polymer, oxybenzoic acid compounds,
The water of non-polymer plasticizer, carbomer, lemon blue, blanc fixe, alkali earth metal aluminate and half puts into high-speed stirred tank
Middle stirring, obtains stirring compound；Then, successively by waterglass steel 5, nanometer colloid 1.9, silicone hydrophober 0.7, ice vinegar
Acid 1.8, water put into mixing and stirring in high-speed stirred tank, 1940 turns/min of rotating speed in order, are finished product fire-retardant paint.
The test performance of the paint that preparation method of the present invention draws is as follows:
Wet rubbing is washed, 27 days > 12000 times
Film thickness, 200-2500 μm does not ftractures
Anti-aging test (100 hours Qq-uvb) invariant color, hydrophobicity is obvious
Fire resistance is at 500 DEG C, and deflection is 10-15%.
Common paint properties to take second place.
Claims (2)
1. a seagoing vessel fuel oil tank fire-retardant paint, by weight, it is characterised in that be made up of following raw material: sulfonation oils and fats
28-30, lactic acid polymer 8-10, oxybenzoic acid compounds 5.5-7.5, non-polymer plasticizer 3.5-5.5, carbomer
0.5-1, lemon blue 1.5-2.5, blanc fixe 4-6, alkali earth metal aluminate 0.5-1.5, waterglass steel 4-6, nanometer colloid
1.6-2.2, silicone hydrophober 0.5-1, glacial acetic acid 1.5-2, water 30-32；The concrete preparation method of this paint is as follows: first
First, the most successively by sulfonation oils and fats, lactic acid polymer, oxybenzoic acid compounds, non-polymer plasticizer, card ripple
The water of nurse, lemon blue, blanc fixe, alkali earth metal aluminate and half is put in high-speed stirred tank and is stirred, and obtains stirring mixing
Material；Then, successively by waterglass steel 4-6, nanometer colloid 1.6-2.2, silicone hydrophober 0.5-1, glacial acetic acid 1.5-2, water
Putting into mixing and stirring in high-speed stirred tank in order, rotating speed 1880-2000 turns/min, is finished product fire-retardant paint.
Seagoing vessel fuel oil tank fire-retardant paint the most according to claim 1, it is characterised in that be made up of following raw material: sulfonated oil
Fat 29, lactic acid polymer 9, oxybenzoic acid compounds 6.5, non-polymer plasticizer 4.5, carbomer 0.8, lemon blue 2,
Blanc fixe 5, alkali earth metal aluminate 1, waterglass steel 5, nanometer colloid 1.9, silicone hydrophober 0.7, glacial acetic acid 1.7,
Water 31.