CN103087592B - Multifunctional nano antiseptic marine paint

Info

Publication number: CN103087592B
Application number: CN201210571498.8A
Authority: CN
Inventors: 姜美青; 魏仲兴; 刘振海; 宋吉勇
Original assignee: Individual
Current assignee: Jiang Meiqing
Priority date: 2012-12-26
Filing date: 2012-12-26
Publication date: 2015-06-03
Anticipated expiration: 2032-12-26
Also published as: CN103087592A

Abstract

The invention relates to a multifunctional nano antiseptic marine paint. The nano antiseptic marine paint is prepared from chlorinated rubber, dimethylbenzene, a resin modifying agent, nano silica, nano graphite, nano attapulgite, a solvent, talcum powder, chlorinated paraffin, a change agent, a coupling agent, rosin, a dispersant, bentonite, mica flour, nanometer alumina powder, an inorganic pigment, nanocrystalline iron oxide, titanium pigment, nano ceramic clay, nano silica and the like. The defects in the prior art are solved by the finally prepared nano antiseptic marine paint disclosed by the invention; and the multifunctional nano antiseptic marine paint which is good in decay resistance, high in smoothness, excellent in antifouling property and good in stability is provided.

Description

A kind of Multifunctional nano antiseptic marine paint

Technical field

The present invention relates to a kind of paint field, relate to a kind of Multifunctional nano antiseptic marine paint by it.

Background technology

Offshore steel structure platform in prior art, hull, the above position of boats and ships waterline, cabin and ship deck and hull superstructure in ship, and the use of land steel construction paint decoration, the coating that marine ship steel structure surface adopts common chlorinated rubber to paint, its shortcoming is that the aquatic organisms such as the marine alga of the surface flatness poor normal time of paint steeping in ocean in the seawater can adhere to hull surface corrosion hull, the more important thing is that corrosion resistance nature is poor, antifouling property is poor, the antifouling time is short, and stability is bad, paint sticking power on hull is also very poor, tight for the aging dropping situations of ship steel structure top coat of often steeping in seawater

Retrieve known through widely, existing ship steel structure paint is difficult to accomplish water-tolerant simultaneously, and Corrosion Protection is good, high glossy, and decorate properties waits multiple requirements well, therefore in the urgent need to working out a kind of Multifunctional nano antiseptic marine paint.

Summary of the invention

Goal of the invention: the present invention provides a kind of corrosion resistance nature and sticking power better to solve deficiency of the prior art, and high glossy, antifouling property is excellent, a kind of Multifunctional nano antiseptic marine paint of good stability.

Technical scheme: a kind of Multifunctional nano antiseptic marine paint of institute of the present invention art comprises the raw material of following three kinds of components:

	Priming paint	Intermediate coat	Finish paint
				Nanometer chlorinated rubber liquid	30 parts	35 parts	40 parts
Solvent	15 parts	12 parts	10 parts
				Talcum powder	3 parts	2 parts	2 parts
Chlorinated paraffin	10 parts	9 parts	8 parts
				Short change agent (polyamide wax)	5 parts	6 parts	7 parts
Coupling agent (positive peptide acid fat)	3 parts	2 parts	3 parts
				Rosin	2 parts	Nothing	Nothing
Dispersion agent	0.2 part	0.5 part	1 part
				Wilkinite	1 part	1 part	1 part
Mica powder	Nothing	8 parts	5 parts
				Aluminium powder	21 parts	Nothing	Nothing
Nano alumina powder	4 parts	Nothing	Nothing
				Mineral dye	Nothing	15 parts	9 parts
Nano-sized iron oxide	3.8	3.5	2 parts
				Titanium dioxide	Nothing	4 parts	9 parts
Nano ceramics soil	Nothing	Nothing	2 parts
				Nano silicon	2 parts	2 parts	1 part

Above-mentioned nanometer chlorinated rubber liquid is that component proportioning is as follows:

Chlorinated rubber 40 parts

Dimethylbenzene 40 parts

Resin modifying agent 5 parts

Nano silicon 5 parts

Nano-graphite 2 parts

U.S. 8 parts, the soil of nano-silicon

The manufacture method that above-mentioned nanometer chlorinated rubber liquid is concrete, the dimethylbenzene of 40 parts is added in stainless steel charging basket and fully stirs, add 40 parts of chlorinated rubbers again, then high speed dispersion is until be split into uniform solution, add resin modifying agent 5 parts, nano silicon 5 parts, nano-graphite 2 parts, U.S. 8 parts, the soil of nano-silicon more successively, warming while stirring to 50 DEG C, high speed dispersion 60 minutes, filters and obtains nanometer chlorinated rubber liquid.

Embodiment

Embodiment 1:

The preparation of the anticorrosion boats and ships priming paint of a kind of multifunctional nano: first nanometer chlorinated rubber liquid 35 parts, solvent 15 parts are put into that reaction vessel is put into rosin 2 parts, chlorinated paraffin 10 parts while stirring successively in proportion, shortly become agent 5 parts, coupling agent 3 parts, dispersion agent 0.2 part of high-speed stirring disperse 30 minutes, putting into talcum powder 3 parts, wilkinite 1 part, aluminium powder 21 parts, nano alumina powder 4 parts, nano-sized iron oxide 3.8 parts, nano silicon 2 parts successively in proportion, high speed dispersion 60 minutes, until solution all stirs all even, make finished product.

Embodiment 2:

The preparation of the anticorrosion boats and ships intermediate coat of a kind of multifunctional nano: first nanometer chlorinated rubber liquid 35 parts, solvent 12 parts are put into that reaction vessel is put into chlorinated paraffin 9 parts while stirring successively in proportion, shortly become agent 6 parts, coupling agent 2 parts, dispersion agent 0.5 part of high-speed stirring disperse 30 minutes, putting into talcum powder 2 parts, wilkinite 1 part, mica powder 9 parts, mineral dye 15 parts, nano-sized iron oxide 3.5 parts, titanium dioxide 4 parts, nano silicon 2 parts successively in proportion, high speed dispersion 60 minutes, until solution all stirs all even, make finished product.

Embodiment 3:

The preparation of the anticorrosion boats and ships intermediate coat of a kind of multifunctional nano: first nanometer chlorinated rubber liquid 40 parts, solvent 10 parts are put into that reaction vessel is put into chlorinated paraffin 8 parts while stirring successively in proportion, shortly become agent 7 parts, coupling agent 3 parts, dispersion agent 1 part of high-speed stirring disperse 30 minutes, putting into talcum powder 2 parts, wilkinite 1 part, mica powder 5 parts, mineral dye 9 parts, nano-sized iron oxide 2 parts, titanium dioxide 9 parts, nano ceramics soil 2 parts, nano silicon 1 part successively in proportion, high speed dispersion 60 minutes, until solution all stirs all even, make finished product.

In sum the anticorrosion boats and ships priming paint of previously prepared good a kind of multifunctional nano, intermediate coat, finish paint are applied to successively the surface of hull and steel construction, solve deficiency of the prior art provide a kind of corrosion resistance nature and sticking power better, high glossy, antifouling property is excellent, a kind of Multifunctional nano antiseptic marine paint of good stability.

Claims

1. a Multifunctional nano antiseptic marine paint, is characterized in that Multifunctional nano antiseptic marine paint is priming paint, intermediate coat, finish paint three kinds of components containing nanometer chlorinated rubber liquid;

Described nanometer chlorinated rubber liquid, is made up of chlorinated rubber 40 parts, dimethylbenzene 40 parts, resin modifying agent 5 parts, nano silicon 5 parts, nano-graphite 2 parts, nano-silicon magnesia 8 parts;

Described multifunctional nano anticorrosion boats and ships priming paint component is as follows:

Nanometer chlorinated rubber liquid 30 parts, solvent 15 parts, talcum powder 3 parts, clorafin 10 parts, short change agent 5 parts, coupling agent 3 parts, rosin 2 parts, dispersion agent 0.2 part, wilkinite 1 part, aluminium powder 21 parts, nano alumina powder 4 parts, nano-sized iron oxide 3.8 parts, nano silicon 2 parts;

Described multifunctional nano anticorrosion boats and ships intermediate coat component is as follows:

Nanometer chlorinated rubber liquid 35 parts, solvent 12 parts, talcum powder 2 parts, clorafin 9 parts, short change agent 6 parts, coupling agent 2 parts, dispersion agent 0.5 part, wilkinite 1 part, mica powder 9 parts, mineral dye 15 parts, nano-sized iron oxide 3.5 parts, titanium dioxide 4 parts, nano silicon 2 parts;

Described multifunctional nano anticorrosion boats and ships finish paint component is as follows:

Nanometer chlorinated rubber liquid 40 parts, solvent 10 parts, talcum powder 2 parts, clorafin 8 parts, short change agent 7 parts, coupling agent 3 parts, dispersion agent 1 part, wilkinite 1 part, mica powder 5 parts, mineral dye 9 parts, nano-sized iron oxide 2 parts, titanium dioxide 9 parts, nano ceramics soil 2 parts, nano silicon 1 part.

2. Multifunctional nano antiseptic marine paint according to claim 1, is characterized in that described short change agent is polyamide wax.

3. Multifunctional nano antiseptic marine paint according to claim 1, is characterized in that described coupling agent is orthotitanate.

4. Multifunctional nano antiseptic marine paint according to claim 1, is characterized in that described mineral dye is ferric oxide series.