CN106189551A - A kind of electric power distributing cabinet coating material - Google Patents
A kind of electric power distributing cabinet coating material Download PDFInfo
- Publication number
- CN106189551A CN106189551A CN201610530054.8A CN201610530054A CN106189551A CN 106189551 A CN106189551 A CN 106189551A CN 201610530054 A CN201610530054 A CN 201610530054A CN 106189551 A CN106189551 A CN 106189551A
- Authority
- CN
- China
- Prior art keywords
- parts
- electric power
- coating material
- power distributing
- distributing cabinet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of electric power distributing cabinet coating material, composed of the following components: 2 mercaptobenzimidazoles, N, N' bis-(2 naphthyl) p-phenylenediamine, N cyclohexyl thio phthalimide, α-cyanogen is for acrylate, Benzoinum, diethyl aminomalonate, carbamate, prestox silicone oil, Cylindrin, Mentholum, styrene-acrylic emulsion, benzothiazole, phenyl isocyanate, essence of Niobe, Benzenecarbonyl chloride., phenoxyethanol, propylene glycol methyl ether acetate, isoamyl propionate, zineb, M Cr, dibenzothiazyl disulfide, zinc fluoride, esterase, andalusite powder, methyl isobutyl carbinol, urethane acrylate, antibacterial peptide, IPPP, nano titanium oxide, albite powder, sodium metasilicate.Product of the present invention has the most superior fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improves properties of product.
Description
Technical field
The present invention relates to a kind of electric power distributing cabinet coating material, belong to electric power distributing cabinet technical field.
Background technology
Power distribution cabinet sub-power power distribution cabinet and light distribution cabinet, metering cabinet, be the final stage device of distribution system.Power distribution cabinet is electricity
The general designation of motivation control centre.Power distribution cabinet uses, loop less occasion relatively decentralized in duty ratio;Motor control center is used for
The occasion that load is concentrated, loop is more.They distribute to load nearby the electric energy of a certain for upper level controller switching equipment circuit.This
Level equipment reply load provides protection, monitors and control.Electric power distributing cabinet needs to use suitable mode to be protected, it is necessary to
Suitable coating material is used to be protected.
Summary of the invention
It is an object of the invention to provide a kind of electric power distributing cabinet coating material, in order to electric power distributing cabinet is better achieved
By the use function of coating material, make product have fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improve product serviceability.
To achieve these goals, technical scheme is as follows.
A kind of electric power distributing cabinet coating material, is made up of the component of following mass fraction: 2-mercaptobenzimidazole 16~
20 parts, N, N '-two (2-naphthyl) p-phenylenediamine 18~22 parts, N-cyclohexyl thio phthalimide 14~18 parts, α-cyanogen are for propylene
Acid esters 12~16 parts, Benzoinum 18~22 parts, diethyl aminomalonate 14~18 parts, carbamate 12~16 parts, eight first
Base silicone oil 18~22 parts, Cylindrin 14~18 parts, Mentholum 12~16 parts, styrene-acrylic emulsion 18~22 parts, benzothiazole 14~18
Part, phenyl isocyanate 14~18 parts, essence of Niobe 12~16 parts, Benzenecarbonyl chloride. 18~22 parts, phenoxyethanol 14~18 parts,
Propylene glycol methyl ether acetate 12~16 parts, isoamyl propionate 18~22 parts, zineb 14~18 parts, M Cr 12~16
Part, dibenzothiazyl disulfide 18~22 parts, zinc fluoride 14~18 parts, esterase 12~16 parts, andalusite powder 18~
22 parts, methyl isobutyl carbinol 14~18 parts, urethane acrylate 14~18 parts, antibacterial peptide 14~18 parts, tricresyl phosphate isopropyl
Base phenyl ester 14~18 parts, nano titanium oxide 14~18 parts, albite powder 14~18 parts, sodium metasilicate 14~18 parts.
Further, above-mentioned electric power distributing cabinet coating material, it is made up of the component of following mass fraction: 2-sulfydryl benzo
Imidazoles 16 parts, N, N '-two (2-naphthyl) p-phenylenediamine 18 parts, N-cyclohexyl thio phthalimide 14 parts, α-cyanogen are for acrylate
12 parts, Benzoinum 18 parts, diethyl aminomalonate 14 parts, carbamate 12 parts, prestox silicone oil 18 parts, Cylindrin 14
Part, Mentholum 12 parts, styrene-acrylic emulsion 18 parts, benzothiazole 14 parts, phenyl isocyanate 14 parts, essence of Niobe 12 parts, benzene first
Acyl chlorides 18 parts, phenoxyethanol 14 parts, propylene glycol methyl ether acetate 12 parts, isoamyl propionate 18 parts, zineb 14 parts, butenoic acid first
Ester 12 parts, dibenzothiazyl disulfide 18 parts, zinc fluoride 14 parts, esterase 12 parts, 18 parts of andalusite powder, methyl tert-butyl
Base methanol 14 parts, urethane acrylate 14 parts, antibacterial peptide 14 parts, IPPP 14 parts, nano titanium oxide 14
Part, 14 parts of albite powder, sodium metasilicate 14 parts.
Further, above-mentioned electric power distributing cabinet coating material, it is made up of the component of following mass fraction: 2-sulfydryl benzo
Imidazoles 18 parts, N, N '-two (2-naphthyl) p-phenylenediamine 20 parts, N-cyclohexyl thio phthalimide 16 parts, α-cyanogen are for acrylate
14 parts, Benzoinum 20 parts, diethyl aminomalonate 16 parts, carbamate 14 parts, prestox silicone oil 20 parts, Cylindrin 16
Part, Mentholum 14 parts, styrene-acrylic emulsion 20 parts, benzothiazole 16 parts, phenyl isocyanate 16 parts, essence of Niobe 14 parts, benzene first
Acyl chlorides 20 parts, phenoxyethanol 16 parts, propylene glycol methyl ether acetate 14 parts, isoamyl propionate 20 parts, zineb 16 parts, butenoic acid first
Ester 14 parts, dibenzothiazyl disulfide 20 parts, zinc fluoride 16 parts, esterase 14 parts, 20 parts of andalusite powder, methyl tert-butyl
Base methanol 16 parts, urethane acrylate 16 parts, antibacterial peptide 16 parts, IPPP 16 parts, nano titanium oxide 16
Part, 16 parts of albite powder, sodium metasilicate 16 parts.
Further, above-mentioned electric power distributing cabinet coating material, it is made up of the component of following mass fraction: 2-sulfydryl benzo
Imidazoles 20 parts, N, N '-two (2-naphthyl) p-phenylenediamine 22 parts, N-cyclohexyl thio phthalimide 18 parts, α-cyanogen are for acrylate
16 parts, Benzoinum 22 parts, diethyl aminomalonate 18 parts, carbamate 16 parts, prestox silicone oil 22 parts, Cylindrin 18
Part, Mentholum 16 parts, styrene-acrylic emulsion 22 parts, benzothiazole 18 parts, phenyl isocyanate 18 parts, essence of Niobe 16 parts, benzene first
Acyl chlorides 22 parts, phenoxyethanol 18 parts, propylene glycol methyl ether acetate 16 parts, isoamyl propionate 22 parts, zineb 18 parts, butenoic acid first
Ester 16 parts, dibenzothiazyl disulfide 22 parts, zinc fluoride 18 parts, esterase 16 parts, 22 parts of andalusite powder, methyl tert-butyl
Base methanol 18 parts, urethane acrylate 18 parts, antibacterial peptide 18 parts, IPPP 18 parts, nano titanium oxide 18
Part, 18 parts of albite powder, sodium metasilicate 18 parts.
Further, above-mentioned electric power distributing cabinet coating material preparation method step is as follows:
(1) by 2-mercaptobenzimidazole, the N of described mass fraction, N '-two (2-naphthyl) p-phenylenediamine, N-cyclohexyl sulfur
For phthalimide, α-cyanogen for acrylate, Benzoinum, diethyl aminomalonate, carbamate, prestox silicone oil, Herba Imperatae
Element, Mentholum, styrene-acrylic emulsion, benzothiazole, phenyl isocyanate, essence of Niobe, Benzenecarbonyl chloride., phenoxyethanol, propylene glycol
Methyl ether acetate, isoamyl propionate, zineb, M Cr, dibenzothiazyl disulfide are mixed, and ultrasonic high speed is divided
Dissipating, ultrasonic frequency is 20~40KHz, rate of dispersion 5000~about 5400r/min, and jitter time is 30~60min;
(2) zinc fluoride of described mass fraction, esterase, andalusite powder, methyl isobutyl carbinol, poly-ammonia are added
Ester acrylate, ultrasonic high speed dispersion, ultrasonic frequency is 20~35KHz, rate of dispersion 4800~about 5200r/min, point
The scattered time is 30~50min;
(3) add the antibacterial peptide of described mass fraction, IPPP, nano titanium oxide, albite powder,
Sodium metasilicate, ultrasonic high speed dispersion, ultrasonic frequency is 20~30KHz, rate of dispersion 4600~about 4800r/min, dispersion
Time is 20~40min;This product is prepared after mix homogeneously.
This beneficial effect of the invention is: a kind of electric power distributing cabinet coating material in the present invention, by following components group
Become: 2-mercaptobenzimidazole, N, N '-two (2-naphthyl) p-phenylenediamine, N-cyclohexyl thio phthalimide, α-cyanogen are for acrylic acid
Ester, Benzoinum, diethyl aminomalonate, carbamate, prestox silicone oil, Cylindrin, Mentholum, styrene-acrylic emulsion, benzo
Thiazole, phenyl isocyanate, essence of Niobe, Benzenecarbonyl chloride., phenoxyethanol, propylene glycol methyl ether acetate, isoamyl propionate, generation
Gloomy zinc, M Cr, dibenzothiazyl disulfide, zinc fluoride, esterase, andalusite powder, methyl isobutyl carbinol,
Urethane acrylate, antibacterial peptide, IPPP, nano titanium oxide, albite powder, sodium metasilicate.This
Bright product has the most superior fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improves properties of product.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is described, in order to be better understood from the present invention.
Embodiment 1
Electric power distributing cabinet coating material in the present embodiment, is made up of the component of following mass fraction: 2-sulfydryl benzo
Imidazoles 16 parts, N, N '-two (2-naphthyl) p-phenylenediamine 18 parts, N-cyclohexyl thio phthalimide 14 parts, α-cyanogen are for acrylate
12 parts, Benzoinum 18 parts, diethyl aminomalonate 14 parts, carbamate 12 parts, prestox silicone oil 18 parts, Cylindrin 14
Part, Mentholum 12 parts, styrene-acrylic emulsion 18 parts, benzothiazole 14 parts, phenyl isocyanate 14 parts, essence of Niobe 12 parts, benzene first
Acyl chlorides 18 parts, phenoxyethanol 14 parts, propylene glycol methyl ether acetate 12 parts, isoamyl propionate 18 parts, zineb 14 parts, butenoic acid first
Ester 12 parts, dibenzothiazyl disulfide 18 parts, zinc fluoride 14 parts, esterase 12 parts, 18 parts of andalusite powder, methyl tert-butyl
Base methanol 14 parts, urethane acrylate 14 parts, antibacterial peptide 14 parts, IPPP 14 parts, nano titanium oxide 14
Part, 14 parts of albite powder, sodium metasilicate 14 parts.
Above-mentioned electric power distributing cabinet coating material preparation method step is as follows:
(1) by 2-mercaptobenzimidazole, the N of described mass fraction, N '-two (2-naphthyl) p-phenylenediamine, N-cyclohexyl sulfur
For phthalimide, α-cyanogen for acrylate, Benzoinum, diethyl aminomalonate, carbamate, prestox silicone oil, Herba Imperatae
Element, Mentholum, styrene-acrylic emulsion, benzothiazole, phenyl isocyanate, essence of Niobe, Benzenecarbonyl chloride., phenoxyethanol, propylene glycol
Methyl ether acetate, isoamyl propionate, zineb, M Cr, dibenzothiazyl disulfide are mixed, and ultrasonic high speed is divided
Dissipating, ultrasonic frequency is 20kHz, rate of dispersion about 5400r/min, and jitter time is 60min;
(2) zinc fluoride of described mass fraction, esterase, andalusite powder, methyl isobutyl carbinol, poly-ammonia are added
Ester acrylate, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5200r/min, and jitter time is
50min;
(3) add the antibacterial peptide of described mass fraction, IPPP, nano titanium oxide, albite powder,
Sodium metasilicate, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 4800r/min, and jitter time is
40min;This product is prepared after mix homogeneously.
Embodiment 2
Electric power distributing cabinet coating material in the present embodiment, is made up of the component of following mass fraction: 2-sulfydryl benzo
Imidazoles 18 parts, N, N '-two (2-naphthyl) p-phenylenediamine 20 parts, N-cyclohexyl thio phthalimide 16 parts, α-cyanogen are for acrylate
14 parts, Benzoinum 20 parts, diethyl aminomalonate 16 parts, carbamate 14 parts, prestox silicone oil 20 parts, Cylindrin 16
Part, Mentholum 14 parts, styrene-acrylic emulsion 20 parts, benzothiazole 16 parts, phenyl isocyanate 16 parts, essence of Niobe 14 parts, benzene first
Acyl chlorides 20 parts, phenoxyethanol 16 parts, propylene glycol methyl ether acetate 14 parts, isoamyl propionate 20 parts, zineb 16 parts, butenoic acid first
Ester 14 parts, dibenzothiazyl disulfide 20 parts, zinc fluoride 16 parts, esterase 14 parts, 20 parts of andalusite powder, methyl tert-butyl
Base methanol 16 parts, urethane acrylate 16 parts, antibacterial peptide 16 parts, IPPP 16 parts, nano titanium oxide 16
Part, 16 parts of albite powder, sodium metasilicate 16 parts.
Above-mentioned electric power distributing cabinet coating material preparation method step is as follows:
(1) by 2-mercaptobenzimidazole, the N of described mass fraction, N '-two (2-naphthyl) p-phenylenediamine, N-cyclohexyl sulfur
For phthalimide, α-cyanogen for acrylate, Benzoinum, diethyl aminomalonate, carbamate, prestox silicone oil, Herba Imperatae
Element, Mentholum, styrene-acrylic emulsion, benzothiazole, phenyl isocyanate, essence of Niobe, Benzenecarbonyl chloride., phenoxyethanol, propylene glycol
Methyl ether acetate, isoamyl propionate, zineb, M Cr, dibenzothiazyl disulfide are mixed, and ultrasonic high speed is divided
Dissipating, ultrasonic frequency is 30kHz, rate of dispersion about 5200r/min, and jitter time is 45min;
(2) zinc fluoride of described mass fraction, esterase, andalusite powder, methyl isobutyl carbinol, poly-ammonia are added
Ester acrylate, ultrasonic high speed dispersion, ultrasonic frequency is 27kHz, rate of dispersion about 5000r/min, and jitter time is
40min;
(3) add the antibacterial peptide of described mass fraction, IPPP, nano titanium oxide, albite powder,
Sodium metasilicate, ultrasonic high speed dispersion, ultrasonic frequency is 25kHz, rate of dispersion about 4700r/min, and jitter time is
30min;This product is prepared after mix homogeneously.
Embodiment 3
Electric power distributing cabinet coating material in the present embodiment, is made up of the component of following mass fraction: 2-sulfydryl benzo
Imidazoles 20 parts, N, N '-two (2-naphthyl) p-phenylenediamine 22 parts, N-cyclohexyl thio phthalimide 18 parts, α-cyanogen are for acrylate
16 parts, Benzoinum 22 parts, diethyl aminomalonate 18 parts, carbamate 16 parts, prestox silicone oil 22 parts, Cylindrin 18
Part, Mentholum 16 parts, styrene-acrylic emulsion 22 parts, benzothiazole 18 parts, phenyl isocyanate 18 parts, essence of Niobe 16 parts, benzene first
Acyl chlorides 22 parts, phenoxyethanol 18 parts, propylene glycol methyl ether acetate 16 parts, isoamyl propionate 22 parts, zineb 18 parts, butenoic acid first
Ester 16 parts, dibenzothiazyl disulfide 22 parts, zinc fluoride 18 parts, esterase 16 parts, 22 parts of andalusite powder, methyl tert-butyl
Base methanol 18 parts, urethane acrylate 18 parts, antibacterial peptide 18 parts, IPPP 18 parts, nano titanium oxide 18
Part, 18 parts of albite powder, sodium metasilicate 18 parts.
Above-mentioned electric power distributing cabinet coating material preparation method step is as follows:
(1) by 2-mercaptobenzimidazole, the N of described mass fraction, N '-two (2-naphthyl) p-phenylenediamine, N-cyclohexyl sulfur
For phthalimide, α-cyanogen for acrylate, Benzoinum, diethyl aminomalonate, carbamate, prestox silicone oil, Herba Imperatae
Element, Mentholum, styrene-acrylic emulsion, benzothiazole, phenyl isocyanate, essence of Niobe, Benzenecarbonyl chloride., phenoxyethanol, propylene glycol
Methyl ether acetate, isoamyl propionate, zineb, M Cr, dibenzothiazyl disulfide are mixed, and ultrasonic high speed is divided
Dissipating, ultrasonic frequency is 40kHz, rate of dispersion 5000r/min, and jitter time is 30min;
(2) zinc fluoride of described mass fraction, esterase, andalusite powder, methyl isobutyl carbinol, poly-ammonia are added
Ester acrylate, ultrasonic high speed dispersion, ultrasonic frequency is 35kHz, rate of dispersion 4800r/min, and jitter time is 30min;
(3) add the antibacterial peptide of described mass fraction, IPPP, nano titanium oxide, albite powder,
Sodium metasilicate, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 4600r/min, and jitter time is
20min;This product is prepared after mix homogeneously.
Performance measurement is carried out for the product in embodiment 1, embodiment 2 and embodiment 3 and certain commercially available prod, measured
Data are as shown in table 1.Fire protection flame retarding level estimate uses UL94 standard.
Table 1 the performance test results
Visible, product of the present invention has the most corrosion-resistant, fire protection flame retarding, anti-mildew, anti-microbial property.
The above is the preferred embodiment of the present invention, it is noted that for those skilled in the art
For, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications are also considered as
Protection scope of the present invention.
Claims (5)
1. an electric power distributing cabinet coating material, it is characterised in that: it is made up of the component of following mass fraction: 2-sulfydryl benzo
Imidazoles 16~20 parts, N, N'-bis-(2-naphthyl) p-phenylenediamine 18~22 parts, N-cyclohexyl thio phthalimide 14~18 parts, α-
Cyanogen is for acrylate 12~16 parts, Benzoinum 18~22 parts, diethyl aminomalonate 14~18 parts, carbamate 12~16
Part, prestox silicone oil 18~22 parts, Cylindrin 14~18 parts, Mentholum 12~16 parts, styrene-acrylic emulsion 18~22 parts, benzothiazole
14~18 parts, phenyl isocyanate 14~18 parts, essence of Niobe 12~16 parts, Benzenecarbonyl chloride. 18~22 parts, phenoxyethanol 14
~18 parts, propylene glycol methyl ether acetate 12~16 parts, isoamyl propionate 18~22 parts, zineb 14~18 parts, M Cr
12~16 parts, dibenzothiazyl disulfide 18~22 parts, zinc fluoride 14~18 parts, esterase 12~16 parts, andalusite powder
18~22 parts of end, methyl isobutyl carbinol 14~18 parts, urethane acrylate 14~18 parts, antibacterial peptide 14~18 parts, phosphoric acid
Triisopropyl phenyl ester 14~18 parts, nano titanium oxide 14~18 parts, albite powder 14~18 parts, sodium metasilicate 14~18
Part.
Electric power distributing cabinet coating material the most according to claim 1, it is characterised in that: described electric power distributing cabinet coating
Material is made up of the component of following mass fraction: 2-mercaptobenzimidazole 16 parts, N, N'-bis-(2-naphthyl) p-phenylenediamine 18 parts,
N-cyclohexyl thio phthalimide 14 parts, α-cyanogen for acrylate 12 parts, Benzoinum 18 parts, diethyl aminomalonate 14 parts,
Carbamate 12 parts, prestox silicone oil 18 parts, Cylindrin 14 parts, Mentholum 12 parts, styrene-acrylic emulsion 18 parts, benzothiazole 14
Part, phenyl isocyanate 14 parts, essence of Niobe 12 parts, Benzenecarbonyl chloride. 18 parts, phenoxyethanol 14 parts, propylene glycol methyl ether acetate
12 parts, isoamyl propionate 18 parts, zineb 14 parts, M Cr 12 parts, dibenzothiazyl disulfide 18 parts, zinc fluoride 14
Part, esterase 12 parts, 18 parts of andalusite powder, methyl isobutyl carbinol 14 parts, urethane acrylate 14 parts, antibacterial peptide
14 parts, IPPP 14 parts, nano titanium oxide 14 parts, 14 parts of albite powder, sodium metasilicate 14 parts.
3. according to the electric power distributing cabinet coating material described in claim 1 to 2, it is characterised in that: described electric power distributing cabinet is used
Coating material is made up of the component of following mass fraction: 2-mercaptobenzimidazole 18 parts, N, N'-bis-(2-naphthyl) p-phenylenediamine 20
Part, N-cyclohexyl thio phthalimide 16 parts, α-cyanogen are for acrylate 14 parts, Benzoinum 20 parts, diethyl aminomalonate 16
Part, carbamate 14 parts, prestox silicone oil 20 parts, Cylindrin 16 parts, Mentholum 14 parts, styrene-acrylic emulsion 20 parts, benzothiazole
16 parts, phenyl isocyanate 16 parts, essence of Niobe 14 parts, Benzenecarbonyl chloride. 20 parts, phenoxyethanol 16 parts, propylene glycol monomethyl ether acetic acid
Ester 14 parts, isoamyl propionate 20 parts, zineb 16 parts, M Cr 14 parts, dibenzothiazyl disulfide 20 parts, zinc fluoride 16
Part, esterase 14 parts, 20 parts of andalusite powder, methyl isobutyl carbinol 16 parts, urethane acrylate 16 parts, antibacterial peptide
16 parts, IPPP 16 parts, nano titanium oxide 16 parts, 16 parts of albite powder, sodium metasilicate 16 parts.
4. according to the electric power distributing cabinet coating material described in claims 1 to 3, it is characterised in that: described electric power distributing cabinet is used
Coating material is made up of the component of following mass fraction: 2-mercaptobenzimidazole 20 parts, N, N'-bis-(2-naphthyl) p-phenylenediamine 22
Part, N-cyclohexyl thio phthalimide 18 parts, α-cyanogen are for acrylate 16 parts, Benzoinum 22 parts, diethyl aminomalonate 18
Part, carbamate 16 parts, prestox silicone oil 22 parts, Cylindrin 18 parts, Mentholum 16 parts, styrene-acrylic emulsion 22 parts, benzothiazole
18 parts, phenyl isocyanate 18 parts, essence of Niobe 16 parts, Benzenecarbonyl chloride. 22 parts, phenoxyethanol 18 parts, propylene glycol monomethyl ether acetic acid
Ester 16 parts, isoamyl propionate 22 parts, zineb 18 parts, M Cr 16 parts, dibenzothiazyl disulfide 22 parts, zinc fluoride 18
Part, esterase 16 parts, 22 parts of andalusite powder, methyl isobutyl carbinol 18 parts, urethane acrylate 18 parts, antibacterial peptide
18 parts, IPPP 18 parts, nano titanium oxide 18 parts, 18 parts of albite powder, sodium metasilicate 18 parts.
Electric power distributing cabinet coating material the most according to claim 1, it is characterised in that: described electric power distributing cabinet coating
Material preparation method step is as follows:
(1) by 2-mercaptobenzimidazole, the N of described mass fraction, N'-bis-(2-naphthyl) p-phenylenediamine, N-cyclohexyl thio phthalein
Acid imide, α-cyanogen for acrylate, Benzoinum, diethyl aminomalonate, carbamate, prestox silicone oil, Cylindrin,
Mentholum, styrene-acrylic emulsion, benzothiazole, phenyl isocyanate, essence of Niobe, Benzenecarbonyl chloride., phenoxyethanol, propylene glycol monomethyl ether
Acetate, isoamyl propionate, zineb, M Cr, dibenzothiazyl disulfide are mixed, ultrasonic high speed dispersion, super
Frequency of sound wave is 20~40KHz, and rate of dispersion about 5000~5400r/min, jitter time is 30~about 60min;
(2) zinc fluoride of described mass fraction, esterase, andalusite powder, methyl isobutyl carbinol, polyurethane third are added
Olefin(e) acid ester, ultrasonic high speed dispersion, ultrasonic frequency is 20~35KHz, and rate of dispersion is about 4800~5200r/min, during dispersion
Between be 30~about 50min;
(3) antibacterial peptide of described mass fraction, IPPP, nano titanium oxide, albite powder, inclined silicon are added
Acid sodium, ultrasonic high speed dispersion, ultrasonic frequency is 20~30KHz, and rate of dispersion is about 4600~4800r/min, jitter time
It is 20~about 40min;This product is prepared after mix homogeneously.