CN106188704A - A kind of high-cleanness automobile cushion and preparation method thereof - Google Patents
A kind of high-cleanness automobile cushion and preparation method thereof Download PDFInfo
- Publication number
- CN106188704A CN106188704A CN201610645367.8A CN201610645367A CN106188704A CN 106188704 A CN106188704 A CN 106188704A CN 201610645367 A CN201610645367 A CN 201610645367A CN 106188704 A CN106188704 A CN 106188704A
- Authority
- CN
- China
- Prior art keywords
- cleanness
- automobile cushion
- parts
- silicone rubber
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
nullThe invention discloses a kind of high-cleanness automobile cushion and preparation method thereof,Its raw material includes by weight: 80 100 parts of butadiene-styrene rubber,10 50 parts of silicone rubber,10 30 parts of graphite,10 20 parts of Suzhou soil,Cellulose 15 parts,Calcium carbonate 1 10 parts,Magnesium carbonate 15 parts,Vulcanizing agent 15 parts,Silane coupler 3 15 parts,10 20 parts of age resistor,Reinforcing agent 10 20 parts,The present invention is by silicone rubber、Butadiene-styrene rubber、Age resistor、Reinforcing agent、Cellulose、Silicon powder、Calcium carbonate、Magnesium carbonate、Suzhou soil、The component such as vulcanizing agent and silane coupler is processed by proportioning and preparation method,Final acquisition has silicone rubber and the rubber composition of butadiene-styrene rubber good characteristic concurrently,There is preferable abrasion resistance properties,So that it will not be worn when actually used easily,Substantially prolongs its service life.
Description
Technical field
The present invention relates to field of rubber technology, be specifically related to a kind of high-cleanness automobile cushion and preparation method thereof.
Background technology
The factors such as elastomeric material is high with its cost performance, and range is extensive, the application in daily production and life is extremely
Extensively, but during it uses, often it uses environment the most changeable, and then makes the most easily to grind when actually used
Damage, and then cause its serviceability to there will be during life-time service greatly reducing.If rubber blanket is commonly used product
Product, and commercial car back seat rubber be rotation driver for having a rest use, the most also add practice driver, accordingly, it would be desirable to wear-resisting the most not
The dirtiest.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of high-cleanness automobile cushion and preparation method thereof, improves automobile and sits
The anti-wear performance of pad and the cleaning of automobile cushion, improve the service life of automobile cushion.
In order to solve above-mentioned technical problem, the technical solution used in the present invention is:
A kind of high-cleanness automobile cushion, its raw material includes by weight:
Preferably, a kind of high-cleanness automobile cushion, its raw material includes by weight:
Preferably, a kind of high-cleanness automobile cushion, its raw material includes by weight:
Preferably, reinforcing agent is white carbon black.
Preferably, age resistor is N-phenyl-α-aniline or age resistor CPPD.
Preferably, vulcanizing agent is cumyl peroxide.
Preferably, silicone rubber is methyl silicone rubber or vinylsiloxane rubber or phenyl siloxane rubber.
The preparation method of a kind of high-cleanness automobile cushion, comprises the following steps:
Step 1: respectively silicone rubber and butadiene-styrene rubber are carried out cold plastication by mill;
Step 2: the silicone rubber after step 1 is plasticated, butadiene-styrene rubber, cellulose, calcium carbonate, magnesium carbonate, Suzhou soil, sulfuration
Agent, age resistor, reinforcing agent, silane coupler mixing, gained mixture is carried out twice mixing;
Step 3: the step 2 mixture after mixing is parked process, and the storage period is 15h;
Step 4: the mixture after step 3 being processed carries out post vulcanization process, first cure temperature is 1150 DEG C, sulfur
The change time is 20min;Second segment curing temperature is 160 DEG C, and cure time is 6h.
Beneficial effects of the present invention:
The present invention is by silicone rubber, butadiene-styrene rubber, age resistor, reinforcing agent, calcium carbonate, cellulose, magnesium carbonate, Suzhou soil, sulfur
The component such as agent and silane coupler is processed by proportioning and preparation method, and final acquisition has silicone rubber and butadiene-styrene rubber concurrently
The rubber composition of good characteristic, has preferable abrasion resistance properties, so that it will not be ground when actually used easily
Damage, substantially prolongs its service life.
Detailed description of the invention
Describe the present invention below by way of specific embodiment.
Embodiment 1
The present invention proposes a kind of high-cleanness automobile cushion, and its raw material includes by weight:
Reinforcing agent is white carbon black, and age resistor is N-phenyl-α-aniline, and vulcanizing agent is cumyl peroxide, and silicone rubber is first
Base silicone rubber.
Invention additionally discloses the preparation method of a kind of high-cleanness automobile cushion, comprise the following steps:
Step 1: respectively silicone rubber and butadiene-styrene rubber are carried out cold plastication by mill;
Step 2: the silicone rubber after step 1 is plasticated, butadiene-styrene rubber, calcium carbonate, cellulose, magnesium carbonate, sodium carbonate, sulfuration
Agent, age resistor, reinforcing agent, silane coupler mixing, gained mixture is carried out twice mixing;
Step 3: the step 2 mixture after mixing is parked process, and the storage period is 15h;
Step 4: the mixture after step 3 being processed carries out post vulcanization process, first cure temperature is 1150 DEG C, sulfur
The change time is 20min;Second segment curing temperature is 160 DEG C, and cure time is 6h.
Embodiment 2
The present invention proposes a kind of high-cleanness automobile cushion, and its raw material includes by weight:
Reinforcing agent is white carbon black, and age resistor is N-phenyl-α-aniline, and vulcanizing agent is cumyl peroxide, and silicone rubber is first
Base silicone rubber.
Invention additionally discloses the preparation method of a kind of high-cleanness automobile cushion, comprise the following steps:
Step 1: respectively silicone rubber and butadiene-styrene rubber are carried out cold plastication by mill;
Step 2: the silicone rubber after step 1 is plasticated, butadiene-styrene rubber, calcium carbonate, cellulose, magnesium carbonate, Suzhou soil, sulfuration
Agent, age resistor, reinforcing agent, silane coupler mixing, gained mixture is carried out twice mixing;
Step 3: the step 2 mixture after mixing is parked process, and the storage period is 15h;
Step 4: the mixture after step 3 being processed carries out post vulcanization process, first cure temperature is 1150 DEG C, sulfur
The change time is 20min;Second segment curing temperature is 160 DEG C, and cure time is 6h.
Embodiment 3
The present invention proposes a kind of high-cleanness automobile cushion, and its raw material includes by weight:
Reinforcing agent is white carbon black, and age resistor is N-phenyl-α-aniline, and vulcanizing agent is cumyl peroxide, and silicone rubber is second
Thiazolinyl silicone rubber.
Invention additionally discloses the preparation method of a kind of high-cleanness automobile cushion, comprise the following steps:
Step 1: respectively silicone rubber and butadiene-styrene rubber are carried out cold plastication by mill;
Step 2: the silicone rubber after step 1 is plasticated, butadiene-styrene rubber, calcium carbonate, cellulose, magnesium carbonate, Suzhou soil, sulfuration
Agent, age resistor, reinforcing agent, silane coupler mixing, gained mixture is carried out twice mixing;
Step 3: the step 2 mixture after mixing is parked process, and the storage period is 15h;
Step 4: the mixture after step 3 being processed carries out post vulcanization process, first cure temperature is 1150 DEG C, sulfur
The change time is 20min;Second segment curing temperature is 160 DEG C, and cure time is 6h.
Embodiment 4
The present invention proposes a kind of high-cleanness automobile cushion, and its raw material includes by weight:
Reinforcing agent is white carbon black, and age resistor is N-phenyl-α-aniline, and vulcanizing agent is cumyl peroxide, and silicone rubber is benzene
Base silicone rubber.
Invention additionally discloses the preparation method of a kind of high-cleanness automobile cushion, comprise the following steps:
Step 1: respectively silicone rubber and butadiene-styrene rubber are carried out cold plastication by mill;
Step 2: the silicone rubber after step 1 is plasticated, butadiene-styrene rubber, calcium carbonate, cellulose, magnesium carbonate, Suzhou soil, sulfuration
Agent, age resistor, reinforcing agent, silane coupler mixing, gained mixture is carried out twice mixing;
Step 3: the step 2 mixture after mixing is parked process, and the storage period is 15h;
Step 4: the mixture after step 3 being processed carries out post vulcanization process, first cure temperature is 1150 DEG C, sulfur
The change time is 20min;Second segment curing temperature is 160 DEG C, and cure time is 6h.
Invention described above embodiment, is not intended that limiting the scope of the present invention.Any in the present invention
Spirit and principle within amendment, equivalent and the improvement etc. made, should be included in the claim protection model of the present invention
Within enclosing.
Claims (8)
1. a high-cleanness automobile cushion, it is characterised in that its raw material includes by weight:
A kind of high-cleanness automobile cushion the most according to claim 1, it is characterised in that its raw material includes by weight:
A kind of high-cleanness automobile cushion the most according to claim 1, it is characterised in that its raw material includes by weight:
A kind of high-cleanness automobile cushion the most according to claim 1, it is characterised in that reinforcing agent is white carbon black.
A kind of high-cleanness automobile cushion the most according to claim 1, it is characterised in that age resistor is N-phenyl-α-aniline
Or age resistor CPPD.
A kind of high-cleanness automobile cushion the most according to claim 1, it is characterised in that vulcanizing agent is peroxidating diisopropyl
Benzene.
A kind of high-cleanness automobile cushion the most according to claim 1, it is characterised in that silicone rubber is methyl silicone rubber or second
Thiazolinyl silicone rubber or phenyl siloxane rubber.
8. the preparation method of a high-cleanness automobile cushion, it is characterised in that comprise the following steps:
Step 1: respectively silicone rubber and butadiene-styrene rubber are carried out cold plastication by mill;
Step 2: silicone rubber after step 1 is plasticated, butadiene-styrene rubber, cellulose, calcium carbonate, magnesium carbonate, Suzhou soil, vulcanizing agent,
Age resistor, reinforcing agent, silane coupler mix, gained mixture is carried out twice mixing;
Step 3: the step 2 mixture after mixing is parked process, and the storage period is 15h;
Step 4: the mixture after step 3 being processed carries out post vulcanization process, and first cure temperature is 1150 DEG C, during sulfuration
Between be 20min;Second segment curing temperature is 160 DEG C, and cure time is 6h.