Long acting antibiotic type blister packaging materials
Technical field
The present invention relates to a kind of blister packaging materials, particularly to a kind of long acting antibiotic type blister packaging materials.
Background technology
Existing blister package covers aluminium foil, is with the pure aluminum foil of 20~30 μm as carrier layer, at top layer printed patterns
And after protective layer, be coated with one layer of PUR through inversion set at medial surface, be used for sealing the organic resin sheets such as PVC, PE, PP, COC
Material, initial sealing temperatures is 140 DEG C.
Owing to directly having sealed tablet in bubble-cap up for safekeeping, the protection of environment in bubble-cap was both required that used PUR possessed
Long-acting viscosity, keeps gnotobasis in requiring again bubble-cap for a long time.And in use, after a bubble-cap is opened, adjacent bubble
The sealing of cover is often affected, and in its bubble-cap, environment is broken, and is unfavorable for that the preservation of tablet uses, easily causes wave
Take.
Summary of the invention
The present invention is directed to the deficiencies in the prior art, it is proposed that a kind of long acting antibiotic type blister packaging materials, it is by bubble
Add antimicrobial component in cover packaging material, thus realize from antibiotic property.
A kind of long acting antibiotic type blister packaging materials, it includes,
Base layer, it is hard that thickness is 20~30 μm or soft state aluminium foil;
Adhesive linkage, including double-layer structure, one layer of aluminium foil tack coat being to be bonded in aluminium foil surface, another layer is resin-bonded
Layer;
Antibiotic layer, it is containing nanometer Ag2O or nano-TiO2Aqueous binder, described antibiotic layer is sprayed at described resin
Tack coat side;
Wherein, described aluminium foil tack coat is made up of aluminium foil binding agent and nano antibacterial agent, and described aluminium foil binder formula is:
Sodium silicate, 37~45%;Silicon dioxide, 1~5%;Aluminium hydroxide, 0.25~1.5%;Sodium dichromate, 0.05~0.5%;Sulfur
Acid magnesium, 0.5~2%;PH adjusting agent, 0~4%;Surplus is water;Described nano antibacterial agent is ZnO/Ag or TiO2/ Ag, Qi Zhongzai
Silver amount is 5~15%, and described nano antibacterial agent is scattered in described aluminium foil binding agent.
Preferably, described long acting antibiotic type blister packaging materials, wherein, described pH adjusting agent is sodium hydroxide, hydrogen-oxygen
Changing potassium, silicic acid and the mixed aqueous solution of phosphoric acid, the ratio of described sodium hydroxide, potassium hydroxide, silicic acid and phosphoric acid is: 1:1:5:1.
Preferably, described long acting antibiotic type blister packaging materials, wherein, described aluminium foil binding agent pH is 5~7.
Preferably, described long acting antibiotic type blister packaging materials, wherein, described resin-bonded layer adhesive therefor is joined
Fang Wei:
Matrix resin, for POE resin, content is 70~85%, and number-average molecular weight is 20000~25000;
Cross-linking agent, for acrylic amide cross-linking agent, content is 5~7%, and described acrylic amide cross-linker molecules formula is:
Assistant crosslinking agent, for Triallyl isocyanurate, content is 1~3%;
Auxiliary antioxidant, for tricresyl phosphite (2,4-di-tert-butyl-phenyl) ester, content is 1~2%;
Viscosifier, for γ-methacryloxypropyl trimethyl silane with described acrylic amide cross-linking agent with quality
Than the mixture for 10:1, content is 5~8%;
Surplus is compatilizer, and described compatilizer is nano silicon.
Preferably, described long acting antibiotic type blister packaging materials, wherein, also include assisted resin, described auxiliary tree
Fat is the one in ethylene vinyl acetate copolymer resin or epoxy resin or two kinds, and content is 5~20%, number-average molecular weight
It is 5000~10000.
Preferably, described long acting antibiotic type blister packaging materials, wherein, described resin-bonded layer adhesive therefor is joined
Fang Wei:
Matrix resin, for POE resin, content is 70%, and number-average molecular weight is 20000;
Assisted resin, for ethylene vinyl acetate copolymer resin, content is 5%, and number-average molecular weight is 5000;
Cross-linking agent, content is 3%;
Assistant crosslinking agent, for Triallyl isocyanurate, content is 3%;
Auxiliary antioxidant, for tricresyl phosphite (2,4-di-tert-butyl-phenyl) ester, content is 2%;
Viscosifier, for γ-methacryloxypropyl trimethyl silane with described acrylic amide cross-linking agent with quality
Than the mixture for 10:1, content is 8%;
Surplus is compatilizer, and described compatilizer is nano silicon.
Preferably, described long acting antibiotic type blister packaging materials, wherein, described resin-bonded layer adhesive therefor is joined
Fang Wei:
Matrix resin, for POE resin, content is 85%, and number-average molecular weight is 25000;
Cross-linking agent, content is 5%;
Assistant crosslinking agent, for Triallyl isocyanurate, content is 1%;
Auxiliary antioxidant, for tricresyl phosphite (2,4-di-tert-butyl-phenyl) ester, content is 1%;
Viscosifier, for γ-methacryloxypropyl trimethyl silane with described acrylic amide cross-linking agent with quality
Than the mixture for 10:1, content is 5%;
Surplus is compatilizer, and described compatilizer is nano silicon.
Preferably, described long acting antibiotic type blister packaging materials, wherein, described antibiotic layer uses containing nanometer Ag2O
Or nano-TiO2Aqueous polyurethane adhesive.
Preferably, described long acting antibiotic type blister packaging materials, wherein, described aluminium foil binding agent uses following steps
Prepare:
1) in reactor, add water, heat up, start stirring;
2) when temperature rises to more than 80 DEG C, be kept stirring for, by sodium silicate, silicon dioxide, aluminium hydroxide, sodium dichromate,
Magnesium sulfate puts in reactor successively, and constant temperature stirs more than 1 hour;
3) it is kept stirring for, cooling, pH adjusting agent is put in reactor, stir 15~30 minutes, regulate pH to 5~7;
4) filter, obtain described aluminium foil binding agent.
Preferably, described long acting antibiotic type blister packaging materials, wherein, described resin-bonded layer uses following steps
Prepare:
1) by matrix resin, cross-linking agent, assistant crosslinking agent mix homogeneously;
2) auxiliary antioxidant, viscosifier and compatilizer use the mode of mixing spraying join 1) in mixture, and
Mixing further;
3) by step 2) mixture prepared pours extruder into and carries out blending extrusion, and temperature controls at 100~160 DEG C, squeezes
Go out thing through curtain coating, cooling, baking oven sizing, traction, coiling process, prepared described resin-bonded layer.
The present invention compared with prior art, possesses following beneficial effect:
1, the present invention coats antibiotic layer at bubble-cap medial surface, and described antibiotic layer is containing nanometer Ag2O or nano-TiO2's
Aqueous binder, uses this antibiotic layer can realize bubble-cap from antibiotic property;
2, being mixed with nano antibacterial agent in aluminium foil tack coat, antibiotic layer combines antibacterial, improves blister material anti-microbial property;
2, aluminium foil tack coat side is bonded in aluminium foil surface, resin-bonded layer side and the polychlorostyrene of antibiotic layer will be coated with
Ethylene or other stiff sheet carry out sealing, being dried, and hardening time is short, and film forming is fast;Heat-sealing temperature is when 150 DEG C, with polyvinyl chloride hard
The heat seal strength of sheet is more than 9.8 newton/15 millimeter (9.8N/15mm), improves more than 40%.
Detailed description of the invention
By particular specific embodiment, embodiments of the present invention being described below, those skilled in the art can be by this explanation
Content disclosed by book understands other advantages and effect of the present invention easily.
Embodiment 1
A kind of long acting antibiotic type blister packaging materials, it includes,
Base layer, it is hard that thickness is 20 μm or soft state aluminium foil;
Adhesive linkage, including double-layer structure, one layer of aluminium foil tack coat being to be bonded in aluminium foil surface, another layer is resin-bonded
Layer;
Antibiotic layer, it is containing nanometer Ag2O or nano-TiO2Aqueous binder, described antibiotic layer is sprayed at described resin
Tack coat side;
Wherein, described aluminium foil tack coat is made up of aluminium foil binding agent and nano antibacterial agent, and described aluminium foil binder formula is:
Sodium silicate, 37%;Silicon dioxide, 5%;Aluminium hydroxide, 1.5%;Sodium dichromate, 0.5%;Magnesium sulfate, 2%;PH adjusting agent,
1%;Surplus is water;Described nano antibacterial agent is ZnO/Ag or TiO2/ Ag, wherein silver carrying amount is 5%, and described nano antibacterial agent divides
Dissipate in described aluminium foil binding agent.
Described pH adjusting agent is the mixed aqueous solution of sodium hydroxide, potassium hydroxide, silicic acid and phosphoric acid, described sodium hydroxide,
The ratio of potassium hydroxide, silicic acid and phosphoric acid is: 1:1:5:1.
Described aluminium foil binding agent pH is 5~7.
Described aluminium foil binding agent is adopted and is prepared by the following steps:
1) in reactor, add water, heat up, start stirring;
2) when temperature rises to more than 80 DEG C, be kept stirring for, by sodium silicate, silicon dioxide, aluminium hydroxide, sodium dichromate,
Magnesium sulfate puts in reactor successively, and constant temperature stirs more than 1 hour;
3) it is kept stirring for, cooling, pH adjusting agent is put in reactor, stir 15 minutes, regulate pH to 5~7;
4) filter, obtain described aluminium foil binding agent.
Further, described resin-bonded layer adhesive therefor formula is:
Matrix resin, for POE resin, content is 70%, and number-average molecular weight is 20000;
Assisted resin, for ethylene vinyl acetate copolymer resin, content is 5%, and number-average molecular weight is 5000;
Cross-linking agent, content is 3%;
Assistant crosslinking agent, for Triallyl isocyanurate, content is 3%;
Auxiliary antioxidant, for tricresyl phosphite (2,4-di-tert-butyl-phenyl) ester, content is 2%;
Viscosifier, for γ-methacryloxypropyl trimethyl silane with described acrylic amide cross-linking agent with quality
Than the mixture for 10:1, content is 8%;
Surplus is compatilizer, and described compatilizer is nano silicon.
Wherein, described antibiotic layer uses containing nanometer Ag2O or nano-TiO2Aqueous polyurethane adhesive.
Described resin-bonded layer is adopted and is prepared by the following steps:
1) by matrix resin, cross-linking agent, assistant crosslinking agent mix homogeneously;
2) auxiliary antioxidant, viscosifier and compatilizer use the mode of mixing spraying join 1) in mixture, and
Mixing further;
3) by step 2) mixture prepared pours extruder into and carries out blending extrusion, and temperature controls at 100 DEG C, extrudate warp
Curtain coating, cooling, baking oven sizing, traction, coiling process, prepare described resin-bonded layer.
Embodiment 2
A kind of long acting antibiotic type blister packaging materials, it includes,
Base layer, it is hard that thickness is 30 μm or soft state aluminium foil;
Adhesive linkage, including double-layer structure, one layer of aluminium foil tack coat being to be bonded in aluminium foil surface, another layer is resin-bonded
Layer;
Antibiotic layer, it is containing nanometer Ag2O or nano-TiO2Aqueous binder, described antibiotic layer is sprayed at described resin
Tack coat side;
Wherein, described aluminium foil tack coat is made up of aluminium foil binding agent and nano antibacterial agent, and described aluminium foil binder formula is:
Sodium silicate, 45%;Silicon dioxide, 1%;Aluminium hydroxide, 0.25%;Sodium dichromate, 0.05%;Magnesium sulfate, 0.5%;PH regulator
Agent, 4%;Surplus is water;Described nano antibacterial agent is ZnO/Ag or TiO2/ Ag, wherein silver carrying amount is 15%, described nano-antibacterial
Agent is scattered in described aluminium foil binding agent.
Described pH adjusting agent is the mixed aqueous solution of sodium hydroxide, potassium hydroxide, silicic acid and phosphoric acid, described sodium hydroxide,
The ratio of potassium hydroxide, silicic acid and phosphoric acid is: 1:1:5:1.
Described aluminium foil binding agent pH is 5~7.
Described aluminium foil binding agent is adopted and is prepared by the following steps:
1) in reactor, add water, heat up, start stirring;
2) when temperature rises to more than 80 DEG C, be kept stirring for, by sodium silicate, silicon dioxide, aluminium hydroxide, sodium dichromate,
Magnesium sulfate puts in reactor successively, and constant temperature stirs more than 1 hour;
3) it is kept stirring for, cooling, pH adjusting agent is put in reactor, stir 30 minutes, regulate pH to 5~7;
4) filter, obtain described aluminium foil binding agent.
Separately, described resin-bonded layer adhesive therefor formula is:
Matrix resin, for POE resin, content is 85%, and number-average molecular weight is 25000;
Cross-linking agent, content is 5%;
Assistant crosslinking agent, for Triallyl isocyanurate, content is 1%;
Auxiliary antioxidant, for tricresyl phosphite (2,4-di-tert-butyl-phenyl) ester, content is 1%;
Viscosifier, for γ-methacryloxypropyl trimethyl silane with described acrylic amide cross-linking agent with quality
Than the mixture for 10:1, content is 5%;
Surplus is compatilizer, and described compatilizer is nano silicon.
Described antibiotic layer uses containing nanometer Ag2O or nano-TiO2Aqueous polyurethane adhesive.
Described resin-bonded layer is adopted and is prepared by the following steps:
1) by matrix resin, cross-linking agent, assistant crosslinking agent mix homogeneously;
2) auxiliary antioxidant, viscosifier and compatilizer use the mode of mixing spraying join 1) in mixture, and
Mixing further;
3) by step 2) mixture prepared pours extruder into and carries out blending extrusion, and temperature controls at 160 DEG C, extrudate warp
Curtain coating, cooling, baking oven sizing, traction, coiling process, prepare described resin-bonded layer.
Embodiment 3
A kind of long acting antibiotic type blister packaging materials, it includes,
Base layer, it is hard that thickness is 25 μm or soft state aluminium foil;
Adhesive linkage, including double-layer structure, one layer of aluminium foil tack coat being to be bonded in aluminium foil surface, another layer is resin-bonded
Layer;
Antibiotic layer, it is containing nanometer Ag2O or nano-TiO2Aqueous binder, described antibiotic layer is sprayed at described resin
Tack coat side;
Wherein, described aluminium foil tack coat is made up of aluminium foil binding agent and nano antibacterial agent, and described aluminium foil binder formula is:
Sodium silicate, 40%;Silicon dioxide, 3%;Aluminium hydroxide, 1%;Sodium dichromate, 0.2%;Magnesium sulfate, 1%;PH adjusting agent, 2%;
Surplus is water;Described nano antibacterial agent is ZnO/Ag or TiO2/ Ag, wherein silver carrying amount is 10%, and described nano antibacterial agent disperses
In described aluminium foil binding agent.
Described pH adjusting agent is the mixed aqueous solution of sodium hydroxide, potassium hydroxide, silicic acid and phosphoric acid, described sodium hydroxide,
The ratio of potassium hydroxide, silicic acid and phosphoric acid is: 1:1:5:1.
Described aluminium foil binding agent pH is 5~7.
Described aluminium foil binding agent is adopted and is prepared by the following steps:
1) in reactor, add water, heat up, start stirring;
2) when temperature rises to more than 80 DEG C, be kept stirring for, by sodium silicate, silicon dioxide, aluminium hydroxide, sodium dichromate,
Magnesium sulfate puts in reactor successively, and constant temperature stirs more than 1 hour;
3) it is kept stirring for, cooling, pH adjusting agent is put in reactor, stir 15~30 minutes, regulate pH to 5~7;
4) filter, obtain described aluminium foil binding agent.
Described resin-bonded layer adhesive therefor formula is:
Matrix resin, for POE resin, content is 80%, and number-average molecular weight is 22000;
Cross-linking agent, for acrylic amide cross-linking agent, content is 6%, and described acrylic amide cross-linker molecules formula is:
Assistant crosslinking agent, for Triallyl isocyanurate, content is 2%;
Auxiliary antioxidant, for tricresyl phosphite (2,4-di-tert-butyl-phenyl) ester, content is 1.5%;
Viscosifier, for γ-methacryloxypropyl trimethyl silane with described acrylic amide cross-linking agent with quality
Than the mixture for 10:1, content is 6%;
Surplus is compatilizer, and described compatilizer is nano silicon.
Also including that assisted resin, described assisted resin are ethylene vinyl acetate copolymer resin, content is 15%, and number is all
Molecular weight is 7000.
Described resin-bonded layer is adopted and is prepared by the following steps:
1) by matrix resin, cross-linking agent, assistant crosslinking agent mix homogeneously;
2) auxiliary antioxidant, viscosifier and compatilizer use the mode of mixing spraying join 1) in mixture, and
Mixing further;
3) by step 2) mixture prepared pours extruder into and carries out blending extrusion, and temperature controls at 140 DEG C, extrudate warp
Curtain coating, cooling, baking oven sizing, traction, coiling process, prepare described resin-bonded layer.
With (aluminium foil side) surface outside above-described embodiment 1, embodiment 2, the bubble-cap of embodiment 3 and common blister with 1 ×
106/cm3Coating is containing colibacillary culture medium, after being placed on 37 DEG C, cultivating 72h under 85% humidity environment, at microscope
The escherichia coli of (resin-bonded layer) inside lower observation bubble-cap, occur in that escherichia coli in common blister, and embodiment 1, implement
Escherichia coli the most do not occur in the blister material of example 2 and embodiment 3.
The principle of above-described embodiment only illustrative present invention and effect thereof, not for limiting the present invention.Any ripe
Above-described embodiment all can be modified under the spirit and the scope of the present invention or change by the personage knowing this technology.Cause
This, have usually intellectual such as complete with institute under technological thought without departing from disclosed spirit in art
All equivalences become are modified or change, and must be contained by the claim of the present invention.