CN106147397A - A kind of paint ink dispersion formula - Google Patents
A kind of paint ink dispersion formula Download PDFInfo
- Publication number
- CN106147397A CN106147397A CN201610701778.4A CN201610701778A CN106147397A CN 106147397 A CN106147397 A CN 106147397A CN 201610701778 A CN201610701778 A CN 201610701778A CN 106147397 A CN106147397 A CN 106147397A
- Authority
- CN
- China
- Prior art keywords
- auxiliary agent
- dispersant
- white
- formula
- paint ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of paint ink dispersion formula, described paint ink dispersion formula, by percentage to the quality, including following components: white carbon black 10% 30%, dispersant 20% 50%, Degussa A200 Nano carbon white 0.001% 0.002%, auxiliary agent 0.0001% 0.0004%, remaining is water;Described auxiliary agent is the adjuvant component of chemistry formula (I).The present invention, by adding Nano carbon white and dispersant in ink system and controlling the suitable metering ratio of ink system, well reduces dispersant usage amount increase system stability effect such that it is able to play.
Description
Technical field
The present invention relates to Inkjet Ink Technology field, specifically a kind of paint ink dispersion formula.
Background technology
Neutral writing ink mill base is the pigment dispersion system of high degree of dispersion, is by pigment and the medium warp such as surfactant, water
Milled processed, makes pigment particles be dispersed in uniformly and stably in water-based system under the effect of shearing force.It is currently used for neutral ink
The paint ink dispersion formula of water, consisting of: pigment, surfactant, auxiliary agent, deionized water etc..Wherein, dispersant
Screening with auxiliary agent has decisive role for preparation and the final products performance of dispersion.
Summary of the invention
It is an object of the invention to provide a kind of paint ink dispersion formula.
For achieving the above object, the present invention provides following technical scheme:
A kind of paint ink dispersion formula, by percentage to the quality, including following components: white carbon black 10%-30%, point
Powder 20%-50%, Degussa A200 Nano carbon white 0.001%-0.002%, auxiliary agent 0.0001%-0.0004%, remaining
For water;Described auxiliary agent is the adjuvant component of chemistry formula (I),
As the further scheme of the present invention: by percentage to the quality, including following components: white carbon black 15%-25%, dispersion
Agent 30%-40%, Degussa A200 Nano carbon white 0.001%-0.002%, auxiliary agent 0.0001%-0.0004%, remaining is
Water;Described auxiliary agent is the adjuvant component of chemistry formula (I),
As the further scheme of the present invention: by percentage to the quality, including following components: white carbon black 20%, dispersant
35%, Degussa A200 Nano carbon white 0.002%, auxiliary agent 0.0003%, remaining is water;Described auxiliary agent is chemistry formula (I)
Adjuvant component,
As the further scheme of the present invention: the mesh number of described white carbon black is 2000 mesh.
As the further scheme of the present invention: the component of described dispersant is mainly 1-tertbutyloxycarbonyl-2-cyanopyrrole
Alkanone, laurate, sodium stearate, zinc oxide, methyl methacrylate.
As the further scheme of the present invention: the preparation method of described paint ink dispersion formula is:
By above-mentioned metering ratio by white carbon black, dispersant, Degussa A200 Nano carbon white, auxiliary agent and water mixed pulp, subsequently
Temperature is raised to 60 DEG C-70 DEG C and maintains 10min-15min, after filtration and get final product.
As the further scheme of the present invention: temperature is raised to 65 DEG C by described preparation method and maintains 13min.
Compared with prior art, the invention has the beneficial effects as follows:
A kind of paint ink dispersion formula prepared by the present invention, such recipe Nano carbon white and dispersant
Synergism can play and well reduce dispersant usage amount increase system stability effect.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the technical scheme of this patent is described in more detail.
Embodiment 1
A kind of paint ink dispersion formula, by percentage to the quality, including following components: white carbon black 10%, dispersant
50%, Degussa A200 Nano carbon white 0.001%, auxiliary agent 0.0001%, remaining is water;Described auxiliary agent is chemistry formula (I)
Adjuvant component,
The mesh number of described white carbon black is 2000 mesh.
The component of described dispersant be mainly 1-tertbutyloxycarbonyl-2-cyano pyrrolidone, laurate, sodium stearate,
Zinc oxide, methyl methacrylate.
The preparation method of described paint ink dispersion formula is:
By above-mentioned metering ratio by white carbon black, dispersant, Degussa A200 Nano carbon white, auxiliary agent and water mixed pulp, subsequently
Temperature is raised to 60 DEG C and maintains 10min, after filtration and get final product.
Embodiment 2
A kind of paint ink dispersion formula, by percentage to the quality, including following components: white carbon black 15%, dispersant
40%, Degussa A200 Nano carbon white 0.001%, auxiliary agent 0.0001%, remaining is water;Described auxiliary agent is chemistry formula (I)
Adjuvant component,
The mesh number of described white carbon black is 2000 mesh.
The component of described dispersant be mainly 1-tertbutyloxycarbonyl-2-cyano pyrrolidone, laurate, sodium stearate,
Zinc oxide, methyl methacrylate.
The preparation method of described paint ink dispersion formula is:
By above-mentioned metering ratio by white carbon black, dispersant, Degussa A200 Nano carbon white, auxiliary agent and water mixed pulp, subsequently
Temperature is raised to 60 DEG C and maintains 10min, after filtration and get final product.
Embodiment 3
A kind of paint ink dispersion formula, by percentage to the quality, including following components: white carbon black 20%, dispersant
35%, Degussa A200 Nano carbon white 0.002%, auxiliary agent 0.0003%, remaining is water;Described auxiliary agent is chemistry formula (I)
Adjuvant component,
The mesh number of described white carbon black is 2000 mesh.
The component of described dispersant be mainly 1-tertbutyloxycarbonyl-2-cyano pyrrolidone, laurate, sodium stearate,
Zinc oxide, methyl methacrylate.
The preparation method of described paint ink dispersion formula is:
By above-mentioned metering ratio by white carbon black, dispersant, Degussa A200 Nano carbon white, auxiliary agent and water mixed pulp, subsequently
Temperature is raised to 65 DEG C and maintains 13min, after filtration and get final product.
Embodiment 4
A kind of paint ink dispersion formula, by percentage to the quality, including following components: white carbon black 25%, dispersant
30%, Degussa A200 Nano carbon white 0.002%, auxiliary agent 0.0004%, remaining is water;Described auxiliary agent is chemistry formula (I)
Adjuvant component,
The mesh number of described white carbon black is 2000 mesh.
The component of described dispersant be mainly 1-tertbutyloxycarbonyl-2-cyano pyrrolidone, laurate, sodium stearate,
Zinc oxide, methyl methacrylate.
The preparation method of described paint ink dispersion formula is:
By above-mentioned metering ratio by white carbon black, dispersant, Degussa A200 Nano carbon white, auxiliary agent and water mixed pulp, subsequently
Temperature is raised to 70 DEG C and maintains 15min, after filtration and get final product.
Embodiment 5
A kind of paint ink dispersion formula, by percentage to the quality, including following components: white carbon black 30%, dispersant
20%, Degussa A200 Nano carbon white 0.002%, auxiliary agent 0.0004%, remaining is water;Described auxiliary agent is chemistry formula (I)
Adjuvant component,
The mesh number of described white carbon black is 2000 mesh.
The component of described dispersant be mainly 1-tertbutyloxycarbonyl-2-cyano pyrrolidone, laurate, sodium stearate,
Zinc oxide, methyl methacrylate.
The preparation method of described paint ink dispersion formula is:
By above-mentioned metering ratio by white carbon black, dispersant, Degussa A200 Nano carbon white, auxiliary agent and water mixed pulp, subsequently
Temperature is raised to 70 DEG C and maintains 15min, after filtration and get final product.
Comparative example 1
Dispersant uses Byk190 (Bi Ke chemical company of Germany), and remaining is same as in Example 5.
Comparative example 2
Dispersant uses Huntsman 3503 (Huntsman Corporation of the U.S.), and remaining is same as in Example 5.
Comparative example 3
Dispersant uses TEGO Dispers 710 (Guangzhou Yuan Tai synthetic material company limited), remaining and embodiment 5 phase
With.
Test experiments:
A kind of paint ink dispersion formula 1g that respectively prepared by Example 1-5 and comparative example 1-3 joins 1L water
In, seal after stirring, preserve respectively six months under lucifuge room temperature, measure performance, the results are shown in Table 1.
Table 1
Project | Parameter 1 | Parameter 2 | Parameter 3 |
Embodiment 1 | Stably dispersing | Three months without precipitation | The compatibility is good |
Embodiment 2 | Stably dispersing | Three months without precipitation | The compatibility is good |
Embodiment 3 | Stably dispersing | Four months without precipitation | The compatibility is good |
Embodiment 4 | Stably dispersing | Five months without precipitation | The compatibility is good |
Embodiment 5 | Stably dispersing | Six months five precipitations | The compatibility is good |
Comparative example 1 | Stably dispersing | Three months without precipitation | The compatibility is good |
Comparative example 2 | Dispersion instability | Two months without precipitation | The compatibility is bad |
Comparative example 3 | Dispersion instability | One month without precipitation | The compatibility is bad |
By above-mentioned table 1 it can be seen that such recipe Nano carbon white and dispersant synergism can play very
Good minimizing dispersant usage amount increases system stability effect.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of the spirit or essential attributes of the present invention, it is possible to realize the present invention in other specific forms.Therefore, no matter
From the point of view of which point, all should regard embodiment as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit requires rather than described above limits, it is intended that all by fall in the implication of equivalency and scope of claim
Change is included in the present invention.
Although moreover, it will be appreciated that this specification is been described by according to embodiment, but the most each embodiment only wraps
Containing an independent technical scheme, this narrating mode of description is only that for clarity sake those skilled in the art should
Description can also be formed those skilled in the art through appropriately combined as an entirety, the technical scheme in each embodiment
May be appreciated other embodiments.
Claims (7)
1. a paint ink dispersion formula, it is characterised in that by percentage to the quality, including following components: white carbon black
10%-30%, dispersant 20%-50%, Degussa A200 Nano carbon white 0.001%-0.002%, auxiliary agent 0.0001%-
0.0004%, remaining is water;Described auxiliary agent is the adjuvant component of chemistry formula (I),
A kind of paint ink dispersion formula the most according to claim 1, it is characterised in that by percentage to the quality,
Including following components: white carbon black 15%-25%, dispersant 30%-40%, Degussa A200 Nano carbon white 0.001%-
0.002%, auxiliary agent 0.0001%-0.0004%, remaining is water;Described auxiliary agent is the adjuvant component of chemistry formula (I),
A kind of paint ink dispersion formula the most according to claim 1 and 2, it is characterised in that with mass percent
Meter, including following components: white carbon black 20%, dispersant 35%, Degussa A200 Nano carbon white 0.002%, auxiliary agent 0.0003%,
Remaining is water;Described auxiliary agent is the adjuvant component of chemistry formula (I),
A kind of paint ink dispersion formula the most according to claim 3, it is characterised in that the mesh number of described white carbon black is
2000 mesh.
A kind of paint ink dispersion formula the most according to claim 4, it is characterised in that the component of described dispersant
Predominantly 1-tertbutyloxycarbonyl-2-cyano pyrrolidone, laurate, sodium stearate, zinc oxide, methyl methacrylate.
6. according to the arbitrary described a kind of paint ink dispersion formula of claim 1-5, it is characterised in that described pigment inks
The preparation method of aqueous dispersion formula is:
By above-mentioned metering ratio by white carbon black, dispersant, Degussa A200 Nano carbon white, auxiliary agent and water mixed pulp, subsequently by temperature
Degree is raised to 60 DEG C-70 DEG C and maintains 10min-15min, after filtration and get final product.
A kind of paint ink dispersion formula the most according to claim 6, it is characterised in that will in described preparation method
Temperature is raised to 65 DEG C and maintains 13min.