CN106145874A - Absorbent-type Maifanitum brunisolic soil potter's clay microballon is prepared porous and is catchmented the method for sponge brick - Google Patents
Absorbent-type Maifanitum brunisolic soil potter's clay microballon is prepared porous and is catchmented the method for sponge brick Download PDFInfo
- Publication number
- CN106145874A CN106145874A CN201610518646.8A CN201610518646A CN106145874A CN 106145874 A CN106145874 A CN 106145874A CN 201610518646 A CN201610518646 A CN 201610518646A CN 106145874 A CN106145874 A CN 106145874A
- Authority
- CN
- China
- Prior art keywords
- porous
- sponge brick
- maifanitum
- catchmented
- clay
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
nullThe present invention provides absorbent-type Maifanitum brunisolic soil potter's clay microballon to prepare porous to catchment the method for sponge brick，Comprise the following steps: porous is catchmented the dispensing of sponge brick: cement 15～20wt%、Particle diameter is 100～250 m Maifanitum brunisolic soil perforate hollow potter's clay microballons 60～75wt%、The sodium silicate 5～15wt% of modulus 3.2～3.5、The flyash 5～10wt% of loss on ignition 1.1% and polyvinyl alcohol High hydrophilous resin fiber 1.5～5.0wt% proportion sample mix homogeneously，Compound is sized mixing with the ratio of mud of 0.5～0.7，Add the aluminium powder cream that compound gross weight is 0.2～1.0%，Aluminium powder cream hydration reaction generates bubble，Form porous and expand water suction serosity，The water suction serosity that expands of preparation is stirred in the die trial pouring sponge brick press into，Through striking off、Compacting、The demoulding、Dry，Make porous to catchment sponge brick.
Description
Technical field
The present invention relates to absorbent-type Maifanitum brunisolic soil potter's clay microballon prepare porous and catchment the method for sponge brick, belong to material
Technology is led.
Background technology
Due to EI Nino and La Nina Phenomenon, there is extreme change in the weather of China, and rainfall distributed pole is uneven, south
North drought and waterlogging are uneven, and in same area, in 1 year, rainfall is the most unequal, and hydropenia has restricted expanding economy and the people
Life, the existing precipitation of Appropriate application, road surface, community, road, the effective precipitation in public leisure square are rationally collected, store,
Utilize, alleviate drought and water shortage season with water, the thermal capacity of water is big, can absorb heat also can heat release, improve miniclimate.
Summary of the invention
Utilize the Maifanitum brunisolic soil perforate hollow potter's clay microballon of perforate as base material, using sodium silicate as binding agent, water
Mud is that the porous sponge brick that catchments increases mechanical strength and cementation, and the resin fibre of flyash and the water suction of polyvinyl alcohol height is strong
Water absorbing agent, brunisolic soil main component, based on kaolinite and Vermiculitum, belongs to clay mineral, and plasticity is strong, and iron manganese content is high, viscosity
Greatly, after high-temperature firing, comprcssive strength is big, and Maifanitum particle diameter more small specific surface is long-pending the biggest, and absorbability is the strongest, and Maifanitum is in water
Heavy metal ion adsorbed, substantially the cation in Maifanitum swaps with the heavy metal cation in water, Jing Guoli
Son exchange Maifanitum has adsorbed the heavy metal cation in water, the pH value of regulation water, uses dilatant slurry, reduces the close of serosity
Degree, a catchment face of sponge brick of the porous made is dovetail channel-shaped, and the porous moisture that sponge brick absorbs that catchments enters dovetail groove,
Being flowed into collector pipe again by the effect of gravity, the collector pipe sponge brick that porous catchmented links together, in rainwater catchment to collecting-tank.
Its technical scheme is: absorbent-type Maifanitum brunisolic soil potter's clay microballon is prepared porous and catchmented the method for sponge brick, first
Step, porous are catchmented the dispensing of sponge brick: cement 15～20wt%, particle diameter are that the 100～250 m hollow potter's clay of Maifanitum brunisolic soil are micro-
Pearl 60～75wt%, the sodium silicate 5～15wt% of modulus 3.2～3.5, the flyash 5～10wt% of loss on ignition 1.1% and polyethylene
Alcohol High hydrophilous resin fiber 1.5～5.0wt%, the percentage by weight sum of above each component is 100%；
Second step, porous catchment sponge brick expand water suction serosity preparation: by the first step percentage by weight sample, first by particle diameter
It is that 100～250 m Maifanitum brunisolic soil perforate hollow potter's clay microballons are put in feed bin, elevator sends into distributing device, distributing device
Being evenly distributed on governing belt balance by Maifanitum brunisolic soil perforate hollow potter's clay microballon, spray thrower is by the silicon of modulus 3.2～3.5
Acid sodium is uniformly sprayed at the outer surface of Maifanitum brunisolic soil perforate hollow potter's clay microballon, and the hollow potter's clay of Maifanitum brunisolic soil perforate is micro-
Pearl enters internal coiling drum agitation device with governing belt balance, makes the outer surface of each Maifanitum brunisolic soil perforate hollow potter's clay microballon
The most uniformly adhering to sodium silicate, sodium silicate is inorganic bond, is hydrophilic, and cohesive force is strong, intensity is higher, acid resistance, heat-resisting
Property is good, and hydrophilicity does not affect caking property, compound be cement 15～20wt%, particle diameter be 100～250 m Maifanitum brunisolic soils
Perforate hollow potter's clay microballon 60～75wt%, the sodium silicate 5～15wt% of modulus 3.2～3.5, the flyash 5 of loss on ignition 1.1%～
10wt% and polyvinyl alcohol High hydrophilous resin fiber 1.5～5.0wt%, then compound is sized mixing with the ratio of mud of 0.5～0.7, ash
For compound, being eventually adding the aluminium powder cream that compound gross weight is 0.2～1.0%, hydration reaction generates bubble, forms porous swollen
The serosity of swollen water suction, reduces the weight of sponge brick, and polyvinyl alcohol High hydrophilous resin fiber has extremely strong water absorption, after water suction
Sponge brick comprcssive strength is constant；
3rd step, porous are catchmented the preparation of sponge brick: the expansion water suction serosity prepared by second step stirs and pours sponge brick into
In the die trial of press, by 1.2～2.0:1 volume ratio compactings, ratio 1.2～2.0 is the volume before compacting, and ratio 1 is compacting
After volume, through striking off, suppressing, the demoulding, dry, make porous and catchment sponge brick, a catchment face of sponge brick of porous is swallow
Stern notch shape, the porous moisture that sponge brick absorbs that catchments enters in dovetail groove, and collector pipe embeds in dovetail groove, and collector pipe embeds dovetail
A part of arc surface in groove is opening shape, and another part arc surface is closed, and rainwater catchments through porous the remittance of sponge brick
Collection, enters in dovetail groove, is flowed into collector pipe again by the effect of gravity, and the collector pipe sponge brick that single porous catchmented is connected to one
Rising, the rainwater that collector pipe collects enters in collecting-tank.
The preparation of Maifanitum brunisolic soil perforate hollow potter's clay microballon: first by particle diameter 80～200 m Maifanitum, 200～400 m
Brunisolic soil stirs by weight 20～30:70～85 compounds, and the percentage by weight sum of two kinds of components is 100%, mixing
Material is sized mixing by the ratio of mud of 0.5～0.7, and ash becomes, for Maifanitum, the compound being grouped into, through centrifugal rotation with brunisolic soil two kinds
High velocity jet forms microballon, then through 800～950 DEG C of expansion, 1000～1500 DEG C fire, quickly cool down, formation wall thickness 50～100
M, particle diameter is the Maifanitum brunisolic soil perforate hollow potter's clay microballon of 100～250 m, Maifanitum and the mixing of brunisolic soil bi-material,
Through high-temperature firing, the Maifanitum and the brunisolic soil that define modification are combined potter's clay resistance to compression microballon, and the component of material is different, modified
The chemical property of material is the most different, and brunisolic soil main component, based on kaolinite, Vermiculitum, belongs to clay mineral, and plasticity is strong, ferrum
Fe content is high, and after high-temperature firing, comprcssive strength is big, and Maifanitum particle diameter more small specific surface is long-pending the biggest, and absorbability is the strongest, Maifanitum
Heavy metal ion adsorbed in water, substantially the cation in Maifanitum swaps with the heavy metal cation in water,
The heavy metal cation in water, the pH value of regulation water has been adsorbed through ion exchange Maifanitum.
The modulus of sodium silicate is most important, and when modulus is more than 3.5, along with the increase of modulus, sodium silicate is hardening to become fragile, viscous
Knot property is deteriorated, and when modulus is less than 3.2, caking property declines.
Flyash is strong water absorbent, through high temperature sintering, has higher activity.
A rainwater part for accumulation is pooled in collecting-tank by the porous sponge brick that catchments by collector pipe, and another part penetrates into
In soil, increasing soil water content, in summer high-temperature season, the heat on surface can also be transmitted to by the porous sponge brick that catchments
In soil, reducing the temperature on sponge tile floor surface, the thermal capacity of water is big, and can absorb heat also can heat release.
The present invention has the following advantages.
1, preparation Materials Inorganic environment-friendly materials used by sponge brick, do not result in harm, the recyclable energy of sponge brick to environment
Secondary uses.
2, the resin fibre of preparation sponge brick flyash and the water suction of polyvinyl alcohol height is strong water absorbent, can absorb sponge brick table
The moisture in face enters internal, when reaching some, is fallen to entering in collector pipe by the effect of gravity.
3, in compound, add aluminium powder cream, form the serosity that porous expands, reduce the density of serosity.
4, the cation in Maifanitum swaps with the heavy metal cation in water, through ion exchange Maifanitum absorption
Heavy metal cation in water, the pH value of regulation water.
Accompanying drawing explanation
Fig. 1 is the axle geodesic structure schematic diagram of the sea brick of the embodiment of the present invention.
Fig. 2 is the end TV structure schematic diagram of the sea brick of the embodiment of the present invention.
Fig. 3 is the structural representation that the monolithic sponge brick of the embodiment of the present invention is linked together by collector pipe.
Wherein in figure 1, sponge brick 2, dovetail groove 3, collector pipe.
Detailed description of the invention
Embodiment 1.
In embodiment as shown in Figures 1 to 3, absorbent-type Maifanitum brunisolic soil potter's clay microballon is prepared porous and is catchmented sponge brick
Method, the first step, the preparation of Maifanitum brunisolic soil perforate hollow potter's clay microballon: first by particle diameter 100 m Maifanitum, 300 m palm fibre
Loam stirs by weight 30:70 compound, and compound is sized mixing by the ratio of mud of 0.6, through centrifugal rotation high velocity jet
Form microballon, then through 820 DEG C of expansion, 1250 DEG C of high-temperature firings, quickly cool down, formation wall thickness 80 m, particle diameter is the wheat meal of 200 m
Stone brunisolic soil perforate hollow potter's clay microballon.
Second step, porous are catchmented the dispensing of sponge brick: take cement 20wt%, particle diameter is 200 m Maifanitum brunisolic soil perforates
Hollow potter's clay microballon 60wt%, the sodium silicate 12wt% of modulus 3.2, the flyash 6wt% of loss on ignition 1.1% and polyvinyl alcohol height are inhaled
Water-resin fiber 2.0wt%.
3rd step, porous catchment sponge brick expand water suction serosity preparation: by the first step percentage by weight sample, first will
Particle diameter is that 200 m Maifanitum brunisolic soil perforate hollow potter's clay microballons are put in feed bin, elevator send into distributing device, and distributing device will
Maifanitum brunisolic soil perforate hollow potter's clay microballon is evenly distributed on governing belt balance, and spray thrower is by equal for the sodium silicate of modulus 3.2
The even outer surface being sprayed at Maifanitum brunisolic soil perforate hollow potter's clay microballon, enters internal coiling drum agitation with governing belt balance
Device, sizes mixing compound with the ratio of mud of 0.6, adds the aluminium powder cream that compound gross weight is 0.5%, and hydration reaction generates gas
Bubble, forms porous and expands the serosity of water suction, reduce the weight of sponge brick, and polyvinyl alcohol High hydrophilous resin fiber has extremely strong suction
Aqueous, the sponge brick comprcssive strength after water suction is constant, heavy metal ion adsorbed, substantially in Maifanitum in water of Maifanitum
Cation and water in heavy metal cation carry out ion exchange, adsorbed the heavy metal in water through ion exchange Maifanitum
Cation, the pH value of regulation water.
4th step, absorbent-type porous are catchmented the preparation of sponge brick: the expansion water suction serosity prepared by second step stirs
Pour in the die trial of sponge brick press, suppress by the volume ratio of 1.5:1, through striking off, suppressing, the demoulding, dry, make porous
Catchment sponge brick 1, and a catchment face of sponge brick 1 of porous is dovetail groove 2 shape, and the porous moisture that sponge brick 1 absorbs that catchments enters
In dovetail groove 2, being installed with collector pipe 3 in dovetail groove 2, rainwater catchments the collecting of sponge brick 1 through porous, enters dovetail groove 2
In, being flowed into collector pipe 3 again by the effect of gravity, the collector pipe 3 sponge brick 1 that single porous catchmented links together, and collector pipe 3 converges
The rainwater of collection enters in collecting-tank, through precipitation, filters, reuses.
The above, be only presently preferred embodiments of the present invention, is not the restriction that the present invention makees other form, appoints
What those skilled in the art changed possibly also with the technology contents of the disclosure above or be modified as equivalent variations etc.
Effect embodiment, every without departing from technical solution of the present invention content, according to the technical spirit of type of the present invention, above example is made
Any simple modification, equivalent variations and remodeling, still fall within the protection domain of type technical scheme of the present invention.
Claims (1)
1. absorbent-type Maifanitum brunisolic soil potter's clay microballon is prepared porous and is catchmented the method for sponge brick, comprises the following steps:
The first step, porous are catchmented the dispensing of sponge brick: cement 15～20wt%, particle diameter are that 100～250 m Maifanitum brunisolic soils are opened
Hole hollow potter's clay microballon 60～75wt%, the sodium silicate 5～15wt% of modulus 3.2～3.5, the flyash 5 of loss on ignition 1.1%～
10wt% and polyvinyl alcohol High hydrophilous resin fiber 1.5～5.0wt%, the percentage by weight sum of above each component is 100%；
Second step, porous catchment sponge brick expand water suction serosity preparation: by the first step percentage by weight sample, first by particle diameter
It is that 100～250 m Maifanitum brunisolic soil perforate hollow potter's clay microballons are put in feed bin, elevator sends into distributing device, distributing device
Being evenly distributed on governing belt balance by Maifanitum brunisolic soil perforate hollow potter's clay microballon, spray thrower is by the silicon of modulus 3.2～3.5
Acid sodium is uniformly sprayed at the outer surface of Maifanitum brunisolic soil perforate hollow potter's clay microballon, and the hollow potter's clay of Maifanitum brunisolic soil perforate is micro-
Pearl enters internal coiling drum agitation device with governing belt balance, then is sized mixing with the ratio of mud of 0.5～0.7 by compound, is eventually adding
Compound gross weight be 0.2～1.0% aluminium powder cream stir, aluminium powder cream hydration reaction generate bubble, formed porous expand inhale
The serosity of water；
3rd step, porous are catchmented the preparation of sponge brick: the expansion water suction serosity prepared by second step stirs and pours sponge brick into
In the die trial of press, through striking off, suppressing, the demoulding, drying, make porous and catchment sponge brick (1), porous is catchmented sponge brick (1)
A face be dovetail groove (2) shape, collector pipe (3) embeds in dovetail groove (2), and collector pipe (3) embeds in dovetail groove (2)
Cyclotomy cambered surface is opening shape, and another part arc surface is closed, and rainwater catchments the collecting of sponge brick (1) through porous, enters
In dovetail groove (2), being entered collector pipe (3) by the effect of gravity, collector pipe (3) the sponge brick (1) that single porous catchmented is connected to
Together, the rainwater that collector pipe (3) collects enters in collecting-tank.